Cold-Curing Structural Epoxy Resins: Analysis of the Curing Reaction as a Function of Curing Time and Thickness.

ABSTRACT: The curing reaction of a commercial cold-curing structural epoxy resin, specifically formulated for civil engineering applications, was analyzed by thermal analysis as a function of the curing time and the sample thickness. Original and remarkable results regarding the effects of curing time on the glass transition temperature and on the residual heat of reaction of the cold-cured epoxy were obtained. The influence of the sample thickness on the curing reaction of the cold-cured resin was also deeply investigated. A highly exothermal reaction, based on a self-activated frontal polymerization reaction, was supposed and verified trough a suitable temperature signal acquisition system, specifically realized for this measurement. This is one of the first studies carried out on the curing behavior of these peculiar cold-cured epoxy resins as a function of curing time and thickness.

SUBMITTER: Corcione CE

PROVIDER: S-EPMC5456125 | biostudies-other | 2014 Sep

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:We investigated the influence of anion type (salicylate, [(MOB)MIm][Sal], vs chloride, [(MOB)MIm][Cl]) of imidazolium-based ionic liquid (IL) and its content on the curing kinetics of bisphenol A diglicydyl ether (DGEBA of molecular weight M n = 340 g/mol). Further physicochemical properties (i.e., glass transition temperature, T g, and conductivity, σdc) of produced polymers were investigated. The polymerization of the studied systems was examined at various molar ratios (1:1, 10:1, and 20:1) at different reaction temperatures (T reaction = 353-383 K) by using differential scanning calorimetry (DSC). Interestingly, both DGEBA/IL compositions studied herein revealed significantly different reaction kinetics and yielded materials of completely distinct physical properties. Surprisingly, in contrast to [(MOB)MIm][Cl], for the low concentration of [(MOB)MIm][Sal] in the reaction mixture, an additional step in the kinetic curves, likely due to the combined enhanced initiation activity of anion (salicylate)-cation (imidazolium-based), was noted. To thoroughly analyze the kinetics of all studied systems, including the two-step kinetics of DGEBA/[(MOB)MIm][Sal], we applied a new approach that relies on the combination of the two phenomenological Avrami equations. Analysis of the determined constant rates revealed that the reaction occurring in the presence of the salicylate anion is characterized by higher activation energy with respect to those with the chloride. Moreover, DGEBA/[(MOB)MIm][Sal] cured materials have higher T g in comparison to DGEBA polymerized with [(MOB)MIm][Cl] independent of the IL concentration. This fact might indicate that, most likely, the products of hardening are highly cross-linked (high T g) or oligomeric linear polymers (low T g) in the former and latter cases, respectively. Such a change in the chemical structure of the polymer is also reflected in the dc conductivity measured at the glass transition temperature, which is much higher for DGEBA cured with [(MOB)MIm][Cl]. Herein, we have clearly demonstrated that the type of anion has a crucial impact on the polymerization mechanism, kinetics, and properties of produced materials.

Dataset Information

Cold-Curing Structural Epoxy Resins: Analysis of the Curing Reaction as a Function of Curing Time and Thickness.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets