Anodization Mechanism on SiC Nanoparticle Reinforced Al Matrix Composites Produced by Power Metallurgy.

ABSTRACT: Specimens of aluminum-based composites reinforced by silicon carbide nanoparticles (Al/SiCnp) produced by powder metallurgy (PM) were anodized under voltage control in tartaric-sulfuric acid (TSA). In this work, the influence of the amount of SiCnp on the film growth during anodizing was investigated. The current density versus time response and the morphology of the porous alumina film formed at the composite surface are compared to those concerning a commercial aluminum alloy (AA1050) anodized under the same conditions. The processing method of the aluminum alloys influences the efficiency of the anodizing process, leading to a lower thicknesses for the unreinforced Al-PM alloy regarding the AA1050. The current density versus time response is strongly dependent on the amount of SiCnp. The current peaks and the steady-state current density recorded at each voltage step increases with the SiCnp volume fraction due to the oxidation of the SiCnp. The formation mechanism of the anodic film on Al/SiCnp composites is different from that occurring in AA1050, partly due the heterogeneous distribution of the reinforcement particles in the metallic matrix, but also to the entrapment of SiCnp in the anodic film.

SUBMITTER: Ferreira SC

PROVIDER: S-EPMC5456428 | biostudies-other | 2014 Dec

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Microstructural, Tribology and Corrosion Properties of Optimized Fe3O4-SiC Reinforced Aluminum Matrix Hybrid Nano Filler Composite Fabricated through Powder Metallurgy Method.

Project description:Hybrid reinforcement's novel composite (Al-Fe3O4-SiC) via powder metallurgy method was successfully fabricated. In this study, the aim was to define the influence of SiC-Fe3O4 nanoparticles on microstructure, mechanical, tribology, and corrosion properties of the composite. Various researchers confirmed that aluminum matrix composite (AMC) is an excellent multifunctional lightweight material with remarkable properties. However, to improve the wear resistance in high-performance tribological application, hardening and developing corrosion resistance was needed; thus, an optimized hybrid reinforcement of particulates (SiC-Fe3O4) into an aluminum matrix was explored. Based on obtained results, the density and hardness were 2.69 g/cm3, 91 HV for Al-30Fe3O4-20SiC, after the sintering process. Coefficient of friction (COF) was decreased after adding Fe3O4 and SiC hybrid composite in tribology behaviors, and the lowest COF was 0.412 for Al-30Fe3O4-20SiC. The corrosion protection efficiency increased from 88.07%, 90.91%, and 99.83% for Al-30Fe3O4, Al-15Fe3O4-30SiC, and Al-30Fe3O4-20SiC samples, respectively. Hence, the addition of this reinforcement (Al-Fe3O4-SiC) to the composite shows a positive outcome toward corrosion resistance (lower corrosion rate), in order to increase the durability and life span of material during operation. The accomplished results indicated that, by increasing the weight percentage of SiC-Fe3O4, it had improved the mechanical properties, tribology, and corrosion resistance in aluminum matrix. After comparing all samples, we then selected Al-30Fe3O4-20SiC as an optimized composite.

| S-EPMC7560354 | biostudies-literature

Microstructure and mechanical behavior of metallic glass fiber-reinforced Al alloy matrix composites.

Project description:Metallic glass-reinforced metal matrix composites are an emerging class of composite materials. The metallic nature and the high mechanical strength of the reinforcing phase offers unique possibilities for improving the engineering performance of composites. Understanding the structure at the amorphous/crystalline interfaces and the deformation behavior of these composites is of vital importance for their further development and potential application. In the present work, Zr-based metallic glass fibers have been introduced in Al7075 alloy (Al-Zn-Mg-Cu) matrices using spark plasma sintering (SPS) producing composites with low porosity. The addition of metallic glass reinforcements in the Al-based matrix significantly improves the mechanical behavior of the composites in compression. High-resolution TEM observations at the interface reveal the formation of a thin interdiffusion layer able to provide good bonding between the reinforcing phase and the Al-based matrix. The deformation behavior of the composites was studied, indicating that local plastic deformation occurred in the matrix near the glassy reinforcements followed by the initiation and propagation of cracks mainly through the matrix. The reinforcing phase is seen to inhibit the plastic deformation and retard the crack propagation. The findings offer new insights into the mechanical behavior of metal matrix composites reinforced with metallic glasses.

| S-EPMC4828712 | biostudies-literature

Properties Comparison of Ti-Al-Si Alloys Produced by Various Metallurgy Methods.

Project description:Melting metallurgy is still the most frequently used and simplest method for the processing of metallic materials. Some of the materials (especially intermetallics) are very difficult to prepare by this method due to the high melting points, poor fluidity, or formation of cracks and pores after casting. This article describes the processing of Ti-Al-Si alloys by arc melting, and shows the microstructure, phase composition, hardness, fracture toughness, and compression tests of these alloys. These results are compared with the same alloys prepared by powder metallurgy by the means of a combination of mechanical alloying and spark plasma sintering. Ti-Al-Si alloys processed by melting metallurgy are characterized by a very coarse structure with central porosity. The phase composition is formed by titanium aluminides and titanium silicides, which are full of cracks. Ti-Al-Si alloys processed by the powder metallurgy route have a relatively homogeneous fine-grained structure with higher hardness. However, these alloys are very brittle. On the other hand, the fracture toughness of arc-melted samples is immeasurable using Palmqvist's method because the crack is stopped by a large area of titanium aluminide matrix.

| S-EPMC6803991 | biostudies-literature

Aluminium matrix tungsten aluminide and tungsten reinforced composites by solid-state diffusion mechanism.

Project description:In-situ processing of tungsten aluminide and tungsten reinforced aluminium matrix composites from elemental tungsten (W) and aluminium (Al) was investigated by thermal analysis and pulsed current processing (PCP). The formation mechanism of tungsten aluminides in 80 at.% Al-20 at.% W system was controlled by atomic diffusion. The particle size of W and Al in the starting powder mixture regulated the phase formation and microstructure. PCP of micron sized elemental Al and W resulted in formation of particulate reinforcements, W, Al4W and Al12W, dispersed in Al matrix. W particles were surrounded by a ~3 μm thick dual-layer structure of Al12W and Al4W. The hardness of Al matrix, containing Al12W reinforcements, was increased by 50% compared to pure Al, from 0.3 GPa to 0.45 GPa and W reinforcements showed a hardness of 4.35 GPa. On PCP of 80 at.% Al-20 at.% W mixture with particle size of W and Al ~70 nm, resulted in formation of Al4W as major phase along with small fractions of Al5W and unreacted W phase. This suggested strongly that the particle size of the starting elemental Al and W could be the controlling parameter in processing and tailoring of phase evolution, microstructure of particulate reinforced Al matrix composite.

| S-EPMC5620082 | biostudies-literature

Balancing Strength and Ductility in Al Matrix Composites Reinforced by Few-Layered MoS2 through In-Situ Formation of Interfacial Al12Mo.

Project description:In this work, few-layered MoS2 (FLM) nanosheet-reinforced Al matrix composites are developed through powder metallurgy and hot extrusion. The microstructure, mechanical properties, and strengthening mechanisms have been systematically investigated. It is found that Al12Mo and Al2S3 can be formed in-situ during the sintering process, resulting in the improvement of interfacial bonding between FLM and Al matrix. With 1.5 wt.% of FLM addition, an improved tensile strength of 234 MPa with a high elongation of 17% can be obtained. Moreover, the strengthening mechanisms are also demonstrated to be grain refinement, dislocation strengthening, and load transfer, and the calculation indicates that load transfer is the main contribution factor. This work will inspire more new designs of metal matrix composites with balanced strength and ductility.

| S-EPMC8269559 | biostudies-literature

A powder-metallurgy-based strategy toward three-dimensional graphene-like network for reinforcing copper matrix composites.

Project description:Three-dimensional graphene network is a promising structure for improving both the mechanical properties and functional capabilities of reinforced polymer and ceramic matrix composites. However, direct application in a metal matrix remains difficult due to the reason that wetting is usually unfavorable in the carbon/metal system. Here we report a powder-metallurgy based strategy to construct a three-dimensional continuous graphene network architecture in a copper matrix through thermal-stress-induced welding between graphene-like nanosheets grown on the surface of copper powders. The interpenetrating structural feature of the as-obtained composites not only promotes the interfacial shear stress to a high level and thus results in significantly enhanced load transfer strengthening and crack-bridging toughening simultaneously, but also constructs additional three-dimensional hyperchannels for electrical and thermal conductivity. Our approach offers a general way for manufacturing metal matrix composites with high overall performance.

| S-EPMC7265306 | biostudies-literature

Improving thermal conductivity of Al/SiC composites by post-oxidization of reaction-bonded silicon carbide preforms.

Project description:High thermal conductivity aluminium-based silicon carbide (Al/SiC) composites were successfully fabricated through post-oxidization of reaction-bonded silicon carbide preforms (RS preforms), utilizing vacuum pressure infiltration technology. The study investigated the regulation of interfacial reactions in conventional sintering and reaction sintering. Conventional sintering introduced a large amount of SiO2, which negatively impacted the thermal conductivity of the Al/SiC composite, but the reaction sintering not. The proposed post-oxidization treatment of RS preforms effectively removed residual carbon from the SiC particle surfaces, thereby forestalling the formation of Al4C3. Furthermore, the post-oxidization treatment effectively formed lightweight SiO2 deposits onto the surface of SiC particles, improving Al-SiC interfacial wettability and reducing thermal resistance, thereby enhancing composite thermal conductivity. Notably, the thermal conductivity of the post-oxidized sample exhibited an increase of 6.5% compared to the untreated sample. The study also evaluated the impact of particle size distribution on volume fraction and thermal properties. The optimized Al/SiC composites yielded thermal conductivity, coefficient of thermal expansion, bending strength, and Young's modulus values of 237.3 W/m K, 8.5 × 10-6/°C, 325 MPa, and 75.9 GPa, respectively.

| S-EPMC11258292 | biostudies-literature

Comparison of Cyclic Hysteresis Behavior between Cross-Ply C/SiC and SiC/SiC Ceramic-Matrix Composites.

Project description:In this paper, the comparison of cyclic hysteresis behavior between cross-ply C/SiC and SiC/SiC ceramic-matrix composites (CMCs) has been investigated. The interface slip between fibers and the matrix existed in the matrix cracking mode 3 and mode 5, in which matrix cracking and interface debonding occurred in the 0° plies are considered as the major reason for hysteresis loops of cross-ply CMCs. The hysteresis loops of cross-ply C/SiC and SiC/SiC composites corresponding to different peak stresses have been predicted using present analysis. The damage parameter, i.e., the proportion of matrix cracking mode 3 in the entire matrix cracking modes of the composite, and the hysteresis dissipated energy increase with increasing peak stress. The damage parameter and hysteresis dissipated energy of C/SiC composite under low peak stress are higher than that of SiC/SiC composite; However, at high peak stress, the damage extent inside of cross-ply SiC/SiC composite is higher than that of C/SiC composite as more transverse cracks and matrix cracks connect together.

| S-EPMC5456556 | biostudies-other

Evaluation of Mechanical and Tribological Aspect of Self-Lubricating Cu-6Gr Composites Reinforced with SiC-WC Hybrid Particles.

Project description:Because of their high thermal conductivity, good corrosion resistance, and great mechanical qualities, copper matrix composites are appealing materials utilized in a variety of industries. This study investigates the mechanical properties of copper-graphite (Cu-Gr) matrix composites reinforced with silicon carbide (SiC) and tungsten carbide (WC) particles by hot pressing using powder metallurgy method. The goal is to investigate the influence of the reinforcement ratio on the mechanical characteristics of copper composite materials generated (density, hardness, flexural strength, and wear resistance). SEM, EDS, and X-RD analysis were used to perform metallographic examinations. The highest relative density with a value of 98.558% was determined in the C3 sample. The findings revealed that when the reinforcement ratio was raised, the hardness rose. The highest hardness value was observed in the C6 sample with an increase of 12.52%. Sample C4 (with the lowest SiC and WC particles ratio) had the highest bending stress (233.18 MPa). Bending stress increased by 35.56% compared to the C1 sample. The lowest specific wear rates were found in the C4 sample, with a decrease of 82.57% compared to the C1 sample. The lowest wear rate (6.853 × 10-7 mm3/Nm) also occurred in the C4 sample. The microstructural analysis showed that the hybrid reinforcement particles exhibited a homogeneous distribution in the copper matrix. X-RD analysis showed that there was no intermediate reaction between the parent matrix and the hybrid reinforcements. A good interfacial bond was observed between the matrix structure and the hybrid reinforcements. The motivation of this research was to utilise the advantages of the unique features of SiC-WC hybrid particles to improve the performance of newly developed Cu-6Gr composites for wear-resistance applications.

| S-EPMC9268748 | biostudies-literature

Mechanism and Catalysis of Oxidative Degradation of Fiber-Reinforced Epoxy Composites.

Project description:Carbon fiber-reinforced polymer (CFRP) materials are widely used in aerospace and recreational equipment, but there is no efficient procedure for their end-of-life recycling. Ongoing work in the chemistry and engineering communities emphasizes recovering carbon fibers from such waste streams by dissolving or destroying the polymer binding. By contrast, our goal is to depolymerize amine-cured epoxy CFRP composites catalytically, thus enabling not only isolation of high-value carbon fibers, but simultaneously opening an approach to recovery of small molecule monomers that can be used to regenerate precursors to new composite resin. To do so will require understanding of the molecular mechanism(s) of such degradation sequences. Prior work has shown the utility of hydrogen peroxide as a reagent to affect epoxy matrix decomposition [1]. Herein we describe the chemical transformations involved in that sequence: the reaction proceeds by oxygen atom transfer to the polymer's linking aniline group, forming an N-oxide intermediate. The polymer is then cleaved by an elimination and hydrolysis sequence. We find that elimination is the slower step. Scandium trichloride is an efficient catalyst for this step, reducing reaction time in homogeneous model systems and neat cured matrix blocks. The conditions can be applied to composed composite materials, from which pristine carbon fibers can be recovered.

| S-EPMC6166884 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data