The Solidification Behavior of AA2618 Aluminum Alloy and the Influence of Cooling Rate.

ABSTRACT: In AA2618 aluminum alloy, the iron- and nickel-rich intermetallics formed during solidification are of great effect on the mechanical properties of the alloy at both room temperature and elevated temperatures. However, the solidification behavior of the alloy and the formation mechanism of the intermetallics during solidification of the alloy are not clear. This research fills the gap and contributes to understanding the intermetallic of the alloy. The results showed that cooling rate was of great influence on the formation of the intermetallics. Under the condition of slow cooling, the as-cast microstructures of the alloy were complex with many coarse eutectic compounds including Al₉FeNi, Al₇(CuNi)₅, Si, Al₂Cu and Al₂CuMg. The phase Al₉FeNi was the dominant intermetallic compound, which precipitated at the earlier stage of the solidification by eutectic reaction L → α-Al + Al₉FeNi. Increasing the cooling rate would suppress the formation of the coarse eutectic intermetallics. Under the condition of near-rapid cooling, the as-cast microstructures of the alloy consisted of metastable intermetallics Al₉FeNi and Al₂Cu; the equilibrium eutectic compounds were suppressed. This research concluded that intermetallics could be refined to a great extent by near-rapid cooling.

SUBMITTER: Liu Y

PROVIDER: S-EPMC5456450 | biostudies-other | 2014 Dec

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

The recalescence rate of cooling curve for undercooled solidification.

Project description:Recalescence rate (R) in cooling curve is well known that affected by undercooling in solidification, but the accurate relationship of them is not clear yet. In this paper, based on the undercooled solidification of Fe-B alloy, the factor affected on recalescence process was investigated. The relationship R = VΔT/D was first found, where V is the growth velocity, ΔT the recalescence degree (approximate the undercooling), D the focus region diameter dependent on the distance of the pyrometer. With this result the solidification interface growth velocity can be predicted from recalescence of cooling curve, vice versa. In addition, an approximate relation between growth velocity and the size of the critical nucleus was shown.

| S-EPMC6987091 | biostudies-literature

Influence of Retrogression Time on the Fatigue Crack Growth Behavior of a Modified AA7475 Aluminum Alloy.

Project description:This paper investigates the effect of retrogression time on the fatigue crack growth of a modified AA7475 aluminum alloy. Tests including tensile strength, fracture toughness, and fatigue limits were performed to understand the changes in properties with different retrogression procedures at 180 °C. The microstructure was characterized using scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The findings indicated that as the retrogression time increased, the yield strength decreased from 508 MPa to 461 MPa, whereas the fracture toughness increased from 48 MPa√m to 63.5 MPa√m. The highest fracture toughness of 63.5 MPa√m was seen after 5 h of retrogression. The measured diameter of η' precipitates increased from 6.13 nm at the retrogression 1 h condition to 6.50 nm at the retrogression 5 h condition. Prolonged retrogression also increased the chance of crack initiation, with slower crack growth rate in the long transverse direction compared to the longitudinal direction. An empirical relationship was established between fracture toughness and the volume fraction of age-hardening precipitates, with increasing number density of precipitates seen with increasing retrogression time.

| S-EPMC10095606 | biostudies-literature

Dynamic Recrystallization Behavior and Processing Map of the 6082 Aluminum Alloy.

Project description:Multiple hot-compression tests were carried out on the 6082 aluminum (Al) alloy using a Gleeble-1500 thermal simulation testing machine. Data on flow stresses of the 6082 Al alloy at deformation temperatures of 623 to 773 K and strain rates from 0.01 to 5 s-1 were attained. Utilizing electron backscatter diffraction (EBSD) and a transmission electron microscope (TEM), the dynamic recrystallization behaviors of the 6082 Al alloy during hot compression in isothermal conditions were explored. With the test data, a hot-working processing map for the 6082 Al alloy (based on dynamic material modeling (DMM)) was drawn. Using the work-hardening rate, the initial critical strain causing dynamic recrystallization was determined, and an equation for the critical strain was constructed. A dynamic model for the dynamic recrystallization of the 6082 Al alloy was established using analyses and test results from the EBSD. The results showed that the safe processing zone (with a high efficiency of power dissipation) mainly corresponded to a zone with deformation temperatures of 703 to 763 K and strain rates of 0.1 to 0.3 s-1. The alloy was mainly subjected to continuous dynamic recrystallization in the formation of the zone. According to the hot-working processing map and an analysis of the microstructures, it is advised that the following technological parameters be selected for the 6082 Al alloy during hot-forming: a range of temperatures between 713 and 753 K and strain rates between 0.1 and 0.2 s-1.

| S-EPMC7084686 | biostudies-literature

Influence of Composition on the Environmental Impact of a Cast Aluminum Alloy.

Project description:The influence of alloy composition on the environmental impact of the production of six aluminum casting alloys (Al Si12Cu1(Fe), Al Si5Mg, Al Si9Cu3Zn3Fe, Al Si10Mg(Fe), Al Si9Cu3(Fe)(Zn) and Al Si9) has been analyzed. In order to perform a more precise environmental impact calculation, Life Cycle Assessment (LCA) with ReCiPe Endpoint methodology has been used, with the EcoInvent v3 AlMg3 aluminum alloy dataset as a reference. This dataset has been updated with the material composition ranges of the mentioned alloys. The balanced, maximum and minimum environmental impact values have been obtained. In general, the overall impact of the studied aluminum alloys varies from 5.98 × 10-1 pts to 1.09 pts per kg, depending on the alloy composition. In the analysis of maximum and minimum environmental impact, the alloy that has the highest uncertainty is AlSi9Cu3(Fe)(Zn), with a range of ±9%. The elements that contribute the most to increase its impact are Copper and Tin. The environmental impact of a specific case, an LED luminaire housing made out of an Al Si12Cu1(Fe) cast alloy, has been studied, showing the importance of considering the composition. Significant differences with the standard datasets that are currently available in EcoInvent v3 have been found.

| S-EPMC5456811 | biostudies-literature

The Influence of Cryogenic Conditions on the Process of AA2519 Aluminum Alloy Cracking.

Project description:This study presents the results of tests involving determining quantities used to describe fracture toughness of a heat-treated AA2519 aluminum alloy applied in, among other things, constructing American military amphibians. These quantities were determined using the J-R curve method for two temperature values, 293 K and 77 K. The low temperature was provided by putting the tested specimen into a liquid nitrogen bath and keeping it there throughout the experiment. Based on the tests results, cryogenic conditions cause an increase in the maximum experimental value of the J-JQ integral, from 66.3 to 87.3 kJ/m2 Moreover, an analysis of the fatigue fracture microstructure revealed differences between specimens tested in ambient temperature and those tested in cryogenic temperature.

| S-EPMC7178225 | biostudies-literature

The Microstructure Evolution and Electrochemical Corrosion Behavior of 7A46 Aluminum Alloy in Different Quenching Conditions.

Project description:The quenching condition of aluminum alloy can affect the mechanical property and corrosion resistance of the profile. This paper is aimed at the low quench sensitivity of aluminum alloys. Scanning electron microscopy and transmission electron microscopy were used to analyze precipitate behaviors of the 7A46 aluminum alloy under different isothermal cooling conditions and microstructure evolutions of quench-induced precipitations. The effect of the different isothermal time on the corrosion resistance of the alloy, and the relationship between microstructure and corrosion resistance after quenching were revealed through electrochemical impedance spectroscopy and potentiodynamic polarization tests. Results show that corrosion sensitivity of the quenching-aged alloy is much higher than that of the double-aged (DA) alloy, and the corrosion resistance of the quenched alloy decreases firstly and then increases. Due to the high density of the matrix precipitates, the increased content of the impurity element, the discontinuity of the grain boundary precipitates and the widening of the precipitates free zone, the most serious degree of corrosion performance among the quenched alloys is 295 °C at 800 s, and the self-corrosion potential and self-current density is -0.919 V and 2.371 μA/cm2, respectively.

| S-EPMC8777919 | biostudies-literature

Influence of ordered L1<sub>2</sub> precipitation on strain-rate dependent mechanical behavior in a eutectic high entropy alloy.

Project description:Recent studies indicate that eutectic high-entropy alloys can simultaneously possess high strength and high ductility, which have potential industrial applications. The present study focuses on Al0.7CoCrFeNi, a lamellar dual-phase (fcc + B2) precipitation-strengthenable eutectic high entropy alloy. This alloy exhibits an fcc + B2 (B2 with bcc nano-precipitates) microstructure resulting in a combination of the soft and ductile fcc phase together with hard B2 phase. Low temperature annealing leads to the precipitation of ordered L12 intermetallic precipitates within the fcc resulting in enhanced strength. The strengthening contribution due to fine scale L12 is modeled using Orowan dislocation bowing and by-pass mechanism. The alloy was tested under quasi-static (strain-rate = 10-3 s-1) tensile loading and dynamic (strain-rate = 103 s-1) compressive loading. Due to the fine lamellar microstructure with a large number of fcc-bcc interfaces, the alloy show relatively high flow-stresses, ~1400 MPa under quasi-static loading and in excess of 1800 MPa under dynamic loading. Interestingly, the coherent nano-scale L12 precipitate caused a significant rise in the yield strength, without affecting the strain rate sensitivity (SRS) significantly. These lamellar structures had higher work hardening due to their capability for easily storing higher dislocation densities. The back-stresses from the coherent L12 precipitate were insufficient to cause improvement in twin nucleation, owing to elevated twinning stress under quasi-static testing. However, under dynamic testing high density of twins were observed.

| S-EPMC6478865 | biostudies-literature

Effect of Cooling Rate at the Eutectoid Transformation Temperature on the Corrosion Resistance of Zn-4Al Alloy.

Project description:The main purpose of this work was to experimentally determine the effect of the cooling rate during the eutectoid transformation on the corrosion resistance of a hypoeutectic Zn-4Al cast alloy in 5% NaCl solution. This was considered in relation to the alloy microstructure. For this purpose, metallographic and electrochemical studies were performed. It was found that the faster cooling promoted the formation of finer (? + ?) eutectoid structures, which translated into a higher hardness and lower corrosion current density. In the initial stage of corrosion processes the eutectoid structure in the eutectic areas were attacked. At the further stages of corrosion development, the phase ? was dissolved, and the ? phase appears to be protected by the formation of corrosion products.

| S-EPMC7178647 | biostudies-literature

Aluminum-copper alloy anode materials for high-energy aqueous aluminum batteries.

Project description:Aqueous aluminum batteries are promising post-lithium battery technologies for large-scale energy storage applications because of the raw materials abundance, low costs, safety and high theoretical capacity. However, their development is hindered by the unsatisfactory electrochemical behaviour of the Al metal electrode due to the presence of an oxide layer and hydrogen side reaction. To circumvent these issues, we report aluminum-copper alloy lamellar heterostructures as anode active materials. These alloys improve the Al-ion electrochemical reversibility (e.g., achieving dendrite-free Al deposition during stripping/plating cycles) by using periodic galvanic couplings of alternating anodic α-aluminum and cathodic intermetallic Al2Cu nanometric lamellas. In symmetric cell configuration with a low oxygen concentration (i.e., 0.13 mg L-1) aqueous electrolyte solution, the lamella-nanostructured eutectic Al82Cu18 alloy electrode allows Al stripping/plating for 2000 h with an overpotential lower than ±53 mV. When the Al82Cu18 anode is tested in combination with an AlxMnO2 cathode material, the aqueous full cell delivers specific energy of ~670 Wh kg-1 at 100 mA g-1 and an initial discharge capacity of ~400 mAh g-1 at 500 mA g-1 with a capacity retention of 83% after 400 cycles.

| S-EPMC8803968 | biostudies-literature

Surface Roughening Behavior of 6063 Aluminum Alloy during Bulging by Spun Tubes.

Project description:Severe surface roughening during the hydroforming of aluminum alloy parts can produce surface defects that severely restrict their application in the automobile and aerospace industry. To understand the relation between strain, grain size and surface roughness under biaxial stress conditions, hydro-bulging tests of aluminum alloy tubes were carried out, and the tubes with different grain sizes were prepared by a spinning and annealing process. The surface roughness was measured by a laser scanning confocal microscope to evaluate the surface roughening macroscopical behavior, and the corresponding microstructures were observed using electron back-scattered diffraction (EBSD) to reveal the roughening microscopic behavior. The results obtained show that the surface roughness increased with both strain and grain size under biaxial stress. No surface defects were observed on the surface when the grain size was less than 105 μm if the strain was less than 18%, or when the grain size was between 130 and 175 μm if the strain was less than 15.88% and 7.15%, respectively. The surface roughening microscopic behavior was identified as an inhomogeneous grain size distribution, which became more pronounced with increasing grain size and resulted in greater local deformation. Concentrated grain orientation also results in severe inhomogeneous deformation during plastics deformation, and serious surface roughening.

| S-EPMC5503364 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data