Mechanical Strength Improvements of Carbon Nanotube Threads through Epoxy Cross-Linking.

ABSTRACT: Individual Carbon Nanotubes (CNTs) have a great mechanical strength that needs to be transferred into macroscopic fiber assemblies. One approach to improve the mechanical strength of the CNT assemblies is by creating covalent bonding among their individual CNT building blocks. Chemical cross-linking of multiwall CNTs (MWCNTs) within the fiber has significantly improved the strength of MWCNT thread. Results reported in this work show that the cross-linked thread had a tensile strength six times greater than the strength of its control counterpart, a pristine MWCNT thread (1192 MPa and 194 MPa, respectively). Additionally, electrical conductivity changes were observed, revealing 2123.40 S·cm-1 for cross-linked thread, and 3984.26 S·cm-1 for pristine CNT thread. Characterization suggests that the obtained high tensile strength is due to the cross-linking reaction of amine groups from ethylenediamine plasma-functionalized CNT with the epoxy groups of the cross-linking agent, 4,4-methylenebis(N,N-diglycidylaniline).

SUBMITTER: Yu Q

PROVIDER: S-EPMC5456468 | biostudies-other | 2016 Jan

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Synergistic effect of functionalized graphene oxide and carbon nanotube hybrids on mechanical properties of epoxy composites.

Project description:Epoxy resin was grafted to graphene oxide (GO) via esterification reaction and 3D structure hybrids were prepared by combining 1D carbon nanotube (CNT) and 2D functionalized GO through π-stacking interaction. Epoxy composites filled with 3D structure hybrids were fabricated. The results show that functionalized GO effectively improves the dispersibility of CNTs in epoxy matrix due to good compatibility. Excellent mechanical properties were achieved by epoxy composites filled with 3D structure hybrids. The fracture surface analysis indicated improved interfacial interaction between 3D structure hybrids and epoxy matrix, which may due to the covalent bonding formed between the epoxy molecular chain grafted on EGO and the hardener agent during the curing process. In the 3D structure filler network, the mechanisms of crack deflection/bifurcation induced by functionalized GO make the crack path tortuous, which causes the cracks to encounter more CNTs and then promote the mechanisms of CNT fracture and crack bridging, resulting in more energy dissipation. This is the key mechanism for its excellent reinforcing and toughening effects.

| S-EPMC9090624 | biostudies-literature

Cross-Linking and Evaluation of the Thermo-Mechanical Behavior of Epoxy Based Poly(ionic Liquid) Thermosets.

Project description:Poly(ionic liquids) (PILs) and ionenes are polymers containing ionic groups in their repeating units. The unique properties of these polymers render them as interesting candidates for a variety of applications, such as gas separation membranes and polyelectrolytes. Due to the vast number of possible structures, numerous synthesis protocols to produce monomers with different functional groups for task-specific PILs are reported in literature. A difunctional epoxy-IL resin was synthesized and cured with multifunctional amine and anhydride hardeners and the thermal and thermomechanical properties of the networks were assessed via differential scanning calorimetry and dynamic mechanical analysis. By the selection of suitable hardeners, the glass transition onset temperature (Tg,onset) of the resulting networks was varied between 18 °C and 99 °C. Copolymerization of epoxy-IL with diglycidyl ether of bisphenol A (DGEBA) led to a further increase of the Tg,onset. The results demonstrate the potential of epoxy chemistry for tailorable PIL networks, where the hardener takes the place of the ligands without requiring an additional synthesis step and can be chosen from a broad range of commercially available compounds.

| S-EPMC8620924 | biostudies-literature

Additive Manufactured Carbon Nanotube/Epoxy Nanocomposites for Heavy-Duty Applications.

Project description:A solid epoxy resin formulation containing 2.5 wt % carbon nanotubes is 3D printed into self-standing parts, which after thermal curing result in CNTs/epoxy nanocomposites with mechanical properties attractive for heavy-duty applications.

| S-EPMC7804968 | biostudies-literature

Structurally Stable, High-Strength Graphene Oxide/Carbon Nanotube/Epoxy Resin Aerogels as Three-Dimensional Skeletal Precursors for Wave-Absorbing Materials.

Project description:Three-dimensional (3D) graphene oxide aerogel (GOA) is one of the best fillers for composites for microwave absorption. However, its further development has been hindered by the poor mechanical properties. Methodology to improve the mechanical properties of the aerogel remains an urgent challenge. Herein, graphene oxide/carbon nanotube/epoxy resin composite aerogel (GCEA) was successfully prepared by a facile method. The results showed that the prepared GCEA with the hierarchical and 3D cross-linked structures exhibited excellent compression performance, structural and thermal stability, high hydrophilicity, and microwave absorption. The prepared GCEA recovered from multiple large strain cycles without significant permanent deformation. The minimum reflection loss (RL) was -39.60 dB and the maximum effective absorption bandwidth (EAB) was 2.48 GHz. The development of the enhanced GO aerogels will offer a new approach to the preparation of 3D microwave-absorbing skeletal materials with good mechanical properties.

| S-EPMC9601949 | biostudies-literature

Effects of Wet-Pressing and Cross-Linking on the Tensile Properties of Carbon Nanotube Fibers.

Project description:To increase the strength of carbon nanotube (CNT) fibers (CNTFs), the mean size of voids between bundles of CNTs was reduced by wet-pressing, and the CNTs were cross-linked. Separate and simultaneous physical (roller pressing) and chemical methods (cross-linking) were tested to confirm each method's effects on the CNTF strength. By reducing the fraction of pores, roller pressing decreased the cross-sectional area from 160 μm² to 66 μm² and increased the average load-at-break from 2.83 ± 0.25 cN to 4.41 ± 0.16 cN. Simultaneous injection of crosslinker and roller pressing augmented the cross-linking effect by increasing the infiltration of the crosslinker solution into the CNTF, so the specific strength increased from 0.40 ± 0.05 N/tex to 0.67 ± 0.04 N/tex. To increase the strength by cross-linking, it was necessary that the size of the pores inside the CNTF were reduced, and the infiltration of the solution was increased. These results suggest that combined physical and chemical treatment is effective to increase the strength of CNTFs.

| S-EPMC6266003 | biostudies-literature

Piezoresistive Multi-Walled Carbon Nanotube/Epoxy Strain Sensor with Pattern Design.

Project description:Carbon nanotube/polymer-based composites have led to studies that enable the realization of low-cost, high-sensitivity piezoresistive strain sensors. This study investigated the characteristics of piezoresistive multi-walled carbon nanotube (MWCNT)/epoxy composite strain sensors subjected to tensile and compressive loads in one direction at relatively small amounts of strain. A patterned sensor was designed to overcome the disadvantage of the load direction sensitivity differences in the existing sensors. The dispersion state of the MWCNTs in the epoxy polymer matrix with the proposed dispersion process was verified by scanning electron microscopy. An MWCNT/epoxy patterned strain sensor and a patch-type strain sensor were directly attached to an acrylic cantilever beam on the opposite side of a commercial metallic strain gauge. The proposed patterned sensor had gauge factors of 2.52 in the tension direction and 2.47 in the compression direction. The measured gauge factor difference for the patterned sensor was less than that for the conventional patch-type sensor. Moreover, the free-vibration frequency response characteristics were compared with those of metal strain gauges to verify the proposed patch-type sensor. The designed drive circuit compensated for the disadvantages due to the high drive voltage, and it was confirmed that the proposed sensor had higher sensitivity than the metallic strain gauge. In addition, the hysteresis of the temperature characteristics of the proposed sensor is presented to show its temperature range. It was verified that the patterned sensor developed through various studies could be applied as a strain sensor for structural health monitoring.

| S-EPMC6926730 | biostudies-literature

Molecular Mechanics of the Moisture Effect on Epoxy/Carbon Nanotube Nanocomposites.

Project description:The strong structural integrity of polymer nanocomposite is influenced in the moist environment; but the fundamental mechanism is unclear, including the basis for the interactions between the absorbed water molecules and the structure, which prevents us from predicting the durability of its applications across multiple scales. In this research, a molecular dynamics model of the epoxy/single-walled carbon nanotube (SWCNT) nanocomposite is constructed to explore the mechanism of the moisture effect, and an analysis of the molecular interactions is provided by focusing on the hydrogen bond (H-bond) network inside the nanocomposite structure. The simulations show that at low moisture concentration, the water molecules affect the molecular interactions by favorably forming the water-nanocomposite H-bonds and the small cluster, while at high concentration the water molecules predominantly form the water-water H-bonds and the large cluster. The water molecules in the epoxy matrix and the epoxy-SWCNT interface disrupt the molecular interactions and deteriorate the mechanical properties. Through identifying the link between the water molecules and the nanocomposite structure and properties, it is shown that the free volume in the nanocomposite is crucial for its structural integrity, which facilitates the moisture accumulation and the distinct material deteriorations. This study provides insights into the moisture-affected structure and properties of the nanocomposite from the nanoscale perspective, which contributes to the understanding of the nanocomposite long-term performance under the moisture effect.

| S-EPMC5666489 | biostudies-literature

Hydrophilic Modification of Multi-Walled Carbon Nanotube for Building Photonic Crystals with Enhanced Color Visibility and Mechanical Strength.

Project description:Low color visibility and poor mechanical strength of polystyrene (PS) photonic crystal films have been the main shortcomings for the potential applications in paints or displays. This paper presents a simple method to fabricate PS/MWCNTs (multi-walled carbon nanotubes) composite photonic crystal films with enhanced color visibility and mechanical strength. First, MWCNTs was modified through radical addition reaction by aniline 2,5-double sulfonic acid diazonium salt to generate hydrophilic surface and good water dispersity. Then the MWCNTs dispersion was blended with PS emulsion to form homogeneous PS/MWCNTs emulsion mixtures and fabricate composite films through thermal-assisted method. The obtained films exhibit high color visibility under natural light and improved mechanical strength owing to the light-adsorption property and crosslinking effect of MWCNTs. The utilization of MWCNTs in improving the properties of photonic crystals is significant for various applications, such as in paints and displays.

| S-EPMC6273566 | biostudies-literature

Enhanced durability of carbon nanotube grafted hierarchical ceramic microfiber-reinforced epoxy composites.

Project description:As carbon nanotube (CNT) infused hybrid composites are increasingly identified as next-generation aerospace materials, it is vital to evaluate their long-term structural performance under aging environments. In this work, the durability of hierarchical, aligned CNT grafted aluminoborosilicate microfiber-epoxy composites (CNT composites) are compared against baseline aluminoborosilicate composites (baseline composites), before and after immersion in water at 25 °C (hydro) and 60 °C (hydrothermal), for extended durations (90 d and 180 d). The addition of CNTs is found to reduce water diffusivities by approximately 1.5 times. The mechanical properties (bending strength and modulus) and the damage sensing capabilities (DC conductivity) of CNT composites remain intact regardless of exposure conditions. The baseline composites show significant loss of strength (44 %) after only 15 d of hydrothermal aging. This loss of mechanical strength is attributed to fiber-polymer interfacial debonding caused by accumulation of water at high temperatures. In situ acoustic and DC electrical measurements of hydrothermally aged CNT composites identify extensive stress-relieving micro-cracking and crack deflections that are absent in the aged baseline composites. These observations are supported by SEM images of the failed composite cross-sections that highlight secondary matrix toughening mechanisms in the form of CNT pullouts and fractures which enhance the service life of composites and maintain their properties under accelerated aging environments.

| S-EPMC5695714 | biostudies-literature

Electrical Resistance Sensing of Epoxy Curing Using an Embedded Carbon Nanotube Yarn.

Project description:Curing effects were investigated by using the electrical response of a single carbon nanotube yarn (CNTY) embedded in an epoxy resin during the polymerization process. Two epoxy resins of different viscosities and curing temperatures were investigated, varying also the concentration of the curing agent. It is shown that the kinetics of resin curing can be followed by using the electrical response of an individual CNTY embedded in the resin. The electrical resistance of an embedded CNTY increased (~ 9%) after resin curing for an epoxy resin cured at 130 °C with viscosity of ~ 59 cP at the pouring/curing temperature ("Epon 862"), while it decreased (~ -9%) for a different epoxy cured at 60 °C, whose viscosity is about double at the corresponding curing temperature. Lowering the curing temperature from 60 °C to room temperature caused slower and smoother changes of electrical resistance over time and smaller (positive) residual resistance. Increasing the concentration of the curing agent caused a faster curing kinetics and, consequently, more abrupt changes of electrical resistance over time, with negative residual electrical resistance. Therefore, the resin viscosity and curing kinetics play a paramount role in the CNTY wicking, wetting and resin infiltration processes, which ultimately govern the electrical response of the CNTY immersed into epoxy.

| S-EPMC7309011 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data