Increased Durability of Concrete Made with Fine Recycled Concrete Aggregates Using Superplasticizers.

ABSTRACT: This paper evaluates the influence of two superplasticizers (SP) on the durability properties of concrete made with fine recycled concrete aggregate (FRCA). For this purpose, three families of concrete were tested: concrete without SP, concrete made with a regular superplasticizer and concrete made with a high-performance superplasticizer. Five volumetric replacement ratios of natural sand by FRCA were tested: 0%, 10%, 30%, 50% and 100%. Two natural gravels were used as coarse aggregates. All mixes had the same particle size distribution, cement content and amount of superplasticizer. The w/c ratio was calibrated to obtain similar slump. The results showed that the incorporation of FRCA increased the water absorption by immersion, the water absorption by capillary action, the carbonation depth and the chloride migration coefficient, while the use of superplasticizers highly improved these properties. The incorporation of FRCA jeopardized the SP's effectiveness. This research demonstrated that, from a durability point of view, the simultaneous incorporation of FRCA and high-performance SP is a viable sustainable solution for structural concrete production.

SUBMITTER: Cartuxo F

PROVIDER: S-EPMC5456471 | biostudies-other | 2016 Feb

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:This paper is the outcome of experiments on the shear performance of reinforced concrete beams with approved composite-recycled aggregates. The strength grade of composite-recycled aggregate concrete (CRAC) was between 30 MPa and 60 MPa. The shear span-to-depth ratio varied from 1 to 3. The adaptability of HRB400 rebar, with critical yield strength of 400 MPa, used as stirrups was also verified. As the composite technology overcame the shortcomings of recycled coarse aggregate, CRAC had similar mechanical properties with those of conventional concrete. Details on the shear behaviors of test beams under a four-point loading test are presented. The results indicated that the changes of CRAC strain, stirrup strain, and shear-crack width depended on the failure patterns, which are controlled by the shear-span to depth ratio. The stirrups yield at the failure of reinforced CRAC beams. The shear cracking resistance and the shear capacity of reinforced CRAC beams can be predicted by the statistical equations. Based on the design codes GB50010, ACI318-19, Model Code 2010 and DIN-1045-1-2008 for conventional reinforced concrete beams, the shear strengths provided by CRAC and stirrups are statistical analyzed. The rationality of the design equations is examined by the utilization level of shear strength provided by CRAC. The maximum shear-crack widths are extracted from the test data of reinforced CRAC beams at normal service state. Comparatively, by specifying the lower limit of shear strength provided by the CRAC with various shear-span to depth ratios, China code GB50010 gives a rational method for utilizing CRAC. Under the premise that the design of shear capacity would give considerations to meet the normal serviceability, the factored strength of HRB400 rebar should be 360 MPa for the calculation of shear strength provided by stirrups. The design methods in codes of GB50010, ACI318-19 and Model Code 2010 are conservative for the shear capacity of reinforced CRAC beams.

Project description:To alleviate the heavy burden on landfilling, construction and demolition wastes (C&DWs) are recycled and reused as aggregates in cementitious materials. However, the inherent characteristics of recycled fine aggregates (RFA), such as the high crushing index and high-water absorption, magnify the reusing difficulty. Nevertheless, attributing to the high porosity and high level of calcium hydroxides existing in the old mortar, RFA is featured with a high specific surface area and a high alkalinity. These features are useful to augment the total photo-degradation of SO2 by nano-TiO2 (NT) intermixed mortar, leading RFA to be an excellent potential carrier to load nano-TiO2 and prepare the composite photocatalyst. Hence, this study proposed to load NT onto the surface of RFAs and river sands (RSs) (the control) by the soaking method, preparing composite photocatalysts denoted as NT@RFA and NT@RS, respectively. The prepared composite photocatalysts were then utilized as sands in photocatalytic mortar to evaluate for SO2 degradation. Experiments identified a 50% higher amount of NT was loaded onto the surface of FRA relative to the control. This higher loading amount plus higher alkalinity ultimately translated into a higher photocatalytic activity. In addition, the mortar containing NT@RFA exhibited 46.3% higher physiochemical absorption and 23.9% higher photocatalytic activity than that containing NT@RS. In addition, the durability, embodied by the reuse and anti-abrasive properties, of NT@RFA exceeded that of NT@RS. The overall findings reveal that the NT@RFA not only garners beneficial effect from the high porosity but also generates positive effect from the high alkalinity. Though a number of studies deal with building materials with NT, this study is the first to load NT onto RFA and prepare composite photocatalysts which were then used as fine aggregates in building materials. Consequently, this study proves the potential high-added-value reusability of RFA in green construction materials and provides a low-cost, high-efficiency approach to degrade atmospheric SO2.

Dataset Information

Increased Durability of Concrete Made with Fine Recycled Concrete Aggregates Using Superplasticizers.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets