Elevated Temperature Performance of Reactive Powder Concrete Containing Recycled Fine Aggregates.

ABSTRACT: This study examines the effect of elevated temperature on various properties of reactive powder concrete (RPC) containing varying percentages of recycled fine aggregates as sand replacement. Recycled fine aggregates were collected from two sources, i.e., demolished normal strength concrete and demolished RPC. The specimens were prepared using 25%, 50%, and 75% replacement of natural sand with recycled fine aggregates, exposed to two different curing conditions and were subjected to four temperatures, i.e., 25, 200, 400, and 600 °C. Later, the specimens were tested for mass loss, compressive strength test, split-tensile strength test, flexural strength test, and water absorption test at all temperature ranges. Results determined that although the mechanical properties degraded with the temperature rise, the recycled aggregates can be employed as a partial replacement of natural sand in RPC without causing a significant decrease in the performance of RPC, and can help to produce more sustainable RPC by using recycled aggregates.

SUBMITTER: Salahuddin H

PROVIDER: S-EPMC7504074 | biostudies-literature | 2020 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Elevated Temperature Performance of Reactive Powder Concrete Containing Recycled Fine Aggregates.

Salahuddin Hammad H Qureshi Liaqat Ali LA Nawaz Adnan A Abid Muhammad M Alyousef Rayed R Alabduljabbar Hisham H Aslam Fahid F Khan Summera Fahmi SF Tufail Rana Faisal RF

Materials (Basel, Switzerland) 20200824 17

This study examines the effect of elevated temperature on various properties of reactive powder concrete (RPC) containing varying percentages of recycled fine aggregates as sand replacement. Recycled fine aggregates were collected from two sources, i.e., demolished normal strength concrete and demolished RPC. The specimens were prepared using 25%, 50%, and 75% replacement of natural sand with recycled fine aggregates, exposed to two different curing conditions and were subjected to four temperat ...[more]

PMID: 32847121

Similar Datasets

Project description:This paper is the outcome of experiments on the shear performance of reinforced concrete beams with approved composite-recycled aggregates. The strength grade of composite-recycled aggregate concrete (CRAC) was between 30 MPa and 60 MPa. The shear span-to-depth ratio varied from 1 to 3. The adaptability of HRB400 rebar, with critical yield strength of 400 MPa, used as stirrups was also verified. As the composite technology overcame the shortcomings of recycled coarse aggregate, CRAC had similar mechanical properties with those of conventional concrete. Details on the shear behaviors of test beams under a four-point loading test are presented. The results indicated that the changes of CRAC strain, stirrup strain, and shear-crack width depended on the failure patterns, which are controlled by the shear-span to depth ratio. The stirrups yield at the failure of reinforced CRAC beams. The shear cracking resistance and the shear capacity of reinforced CRAC beams can be predicted by the statistical equations. Based on the design codes GB50010, ACI318-19, Model Code 2010 and DIN-1045-1-2008 for conventional reinforced concrete beams, the shear strengths provided by CRAC and stirrups are statistical analyzed. The rationality of the design equations is examined by the utilization level of shear strength provided by CRAC. The maximum shear-crack widths are extracted from the test data of reinforced CRAC beams at normal service state. Comparatively, by specifying the lower limit of shear strength provided by the CRAC with various shear-span to depth ratios, China code GB50010 gives a rational method for utilizing CRAC. Under the premise that the design of shear capacity would give considerations to meet the normal serviceability, the factored strength of HRB400 rebar should be 360 MPa for the calculation of shear strength provided by stirrups. The design methods in codes of GB50010, ACI318-19 and Model Code 2010 are conservative for the shear capacity of reinforced CRAC beams.

Project description:To alleviate the heavy burden on landfilling, construction and demolition wastes (C&DWs) are recycled and reused as aggregates in cementitious materials. However, the inherent characteristics of recycled fine aggregates (RFA), such as the high crushing index and high-water absorption, magnify the reusing difficulty. Nevertheless, attributing to the high porosity and high level of calcium hydroxides existing in the old mortar, RFA is featured with a high specific surface area and a high alkalinity. These features are useful to augment the total photo-degradation of SO2 by nano-TiO2 (NT) intermixed mortar, leading RFA to be an excellent potential carrier to load nano-TiO2 and prepare the composite photocatalyst. Hence, this study proposed to load NT onto the surface of RFAs and river sands (RSs) (the control) by the soaking method, preparing composite photocatalysts denoted as NT@RFA and NT@RS, respectively. The prepared composite photocatalysts were then utilized as sands in photocatalytic mortar to evaluate for SO2 degradation. Experiments identified a 50% higher amount of NT was loaded onto the surface of FRA relative to the control. This higher loading amount plus higher alkalinity ultimately translated into a higher photocatalytic activity. In addition, the mortar containing NT@RFA exhibited 46.3% higher physiochemical absorption and 23.9% higher photocatalytic activity than that containing NT@RS. In addition, the durability, embodied by the reuse and anti-abrasive properties, of NT@RFA exceeded that of NT@RS. The overall findings reveal that the NT@RFA not only garners beneficial effect from the high porosity but also generates positive effect from the high alkalinity. Though a number of studies deal with building materials with NT, this study is the first to load NT onto RFA and prepare composite photocatalysts which were then used as fine aggregates in building materials. Consequently, this study proves the potential high-added-value reusability of RFA in green construction materials and provides a low-cost, high-efficiency approach to degrade atmospheric SO2.

Dataset Information

Elevated Temperature Performance of Reactive Powder Concrete Containing Recycled Fine Aggregates.

Publications

Elevated Temperature Performance of Reactive Powder Concrete Containing Recycled Fine Aggregates.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets