Fabrication of Wood-Rubber Composites Using Rubber Compound as a Bonding Agent Instead of Adhesives.

ABSTRACT: Differing from the hot-pressing method in the manufacturing of traditional wood-rubber composites (WRCs), this study was aimed at fabricating WRCs using rubber processing to improve water resistance and mechanical properties. Three steps were used to make WRCs, namely, fiber-rubber mixing, tabletting, and the vulcanization molding process. Ninety-six WRC panels were made with wood fiber contents of 0%-50% at rotor rotational speeds of 15-45 rpm and filled coefficients of 0.55-0.75. Four regression equations, i.e., the tensile strength (Ts), elongation at break (Eb), hardness (Ha) and rebound resilience (Rr) as functions of fiber contents, rotational speed and filled coefficient, were derived and a nonlinear programming model were developed to obtain the optimum composite properties. Although the Ts, Eb and Rr of the panels were reduced, Ha was considerably increased by 17%-58% because of the wood fiber addition. Scanning electron microscope images indicated that fibers were well embedded in rubber matrix. The 24 h water absorption was only 1%-3%, which was much lower than commercial wood-based composites.

SUBMITTER: Shao D

PROVIDER: S-EPMC5456808 | biostudies-other | 2016 Jun

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

The Effect of Silica-Filler on Polyurethane Adhesives Based on Renewable Resource for Wood Bonding.

Project description:The aim of the study was to evaluate the applicability and performance of polyglycerol- and sucrose-based polyols as components of a simplified formulation of polyurethane adhesives. Colloidal silica was used as a viscosity control and reinforcing agent. The adhesives were examined in terms of reactivity, thermal stability, viscosity, work of adhesion, wetting, surface energy, and bonding strength on wooden substrates. Silica was found to increase gelling time, but markedly improved bonding strength and adhesion with substrates. Bonded solid beech wood samples prepared at 80, 110, and 130 °C showed shear strengths between 7.1 MPa and 9.9 MPa with 100% wood failure. The renewable resource-based polyols were demonstrated to be useful in formulation of polyurethane adhesives for furniture industry-especially with silica as a filler.

| S-EPMC7598712 | biostudies-literature

Fabrication of PVA–Silica Sol Wood Composites via Delignification and Freezing Pretreatment

Project description: Not available

| S-EPMC11243807 | biostudies-literature

Hydrogen-Bonding-Aided Fabrication of Wood Derived Cellulose Scaffold/Aramid Nanofiber into High-Performance Bulk Material.

Project description:Preparing a lightweight yet high-strength bio-based structural material with sustainability and recyclability is highly desirable in advanced applications for architecture, new energy vehicles and spacecraft. In this study, we combined cellulose scaffold and aramid nanofiber (ANF) into a high-performance bulk material. Densification of cellulose microfibers containing ANF and hydrogen bonding between cellulose microfibers and ANF played a crucial role in enhanced physical and mechanical properties of the hybrid material. The prepared material showed excellent tensile strength (341.7 MPa vs. 57.0 MPa for natural wood), toughness (4.4 MJ/m3 vs. 0.4 MJ/m3 for natural wood) and Young's modulus (24.7 GPa vs. 7.2 GPa for natural wood). Furthermore, due to low density, this material exhibited a superior specific strength of 285 MPa·cm3·g-1, which is remarkably higher than some traditional building materials, such as concrete, alloys. In addition, the cellulose scaffold was infiltrated with ANFs, which also improved the thermal stability of the hybrid material. The facile and top-down process is effective and scalable, and also allows one to fully utilize cellulose scaffolds to fabricate all kinds of advanced bio-based materials.

| S-EPMC8469447 | biostudies-literature

Temperature dependence of the interfacial bonding characteristics of silica/styrene butadiene rubber composites: a molecular dynamics simulation study.

Project description:Based on our previous studies on the modification of in-chain styrene butadiene rubber (SBR) using 3-mercaptopropionic acid as well as its composites filled with silica, we further constructed two types of models (amorphous and layered) to investigate the temperature dependence of the interfacial bonding characteristics of silica/SBR composites via molecular dynamics (MD) simulation. The competing effects of rubber-rubber interactions and filler-rubber interactions were identified, and the relationship between the competing effects and the temperature was determined. Besides this, the effect of temperature on the mobility and distribution of SBR chains on the surface of silica was investigated. It was found that the stronger the interfacial interactions, the less sensitive the motion of SBR chains to temperature. Finally, the number and length of hydrogen bonds as a function of temperature were analyzed. These simulated results deepened the understanding of interface temperature dependence of the silica/SBR composites and gave a molecular level explanation for the existence of an optimum modifier content (14.2 wt%) that is temperature independent.

| S-EPMC9076183 | biostudies-literature

Adhesives for Achieving Durable Bonds with Acetylated Wood.

Project description:Acetylation of wood imparts moisture durability, decay resistance, and dimensional stability to wood; however, making durable adhesive bonds with acetylated wood can be more difficult than with unmodified wood. The usual explanation is that the acetylated surface has fewer hydroxyl groups, resulting in a harder-to-wet surface and in fewer hydrogen bonds between wood and adhesive. This concept was evaluated using four different adhesives (resorcinol⁻formaldehyde, emulsion polymer isocyanate, epoxy, and melamine⁻formaldehyde) with unmodified wood, acetylated wood, and acetylated wood that had been planed. Strikingly, acetylation did not hinder adhesive bonds with a waterborne resorcinol⁻formaldehyde adhesive that bonded equally well to both unmodified and acetylated yellow poplar. An epoxy adhesive bonded better to the acetylated wood than to the unmodified wood, in contrast to an emulsion polymer isocyanate, which gave less durable bonds to acetylated than to unmodified wood. Planing of the acetylated wood surface prior to bonding reduced bond durability for the epoxy adhesive and increased the amount of surface hydroxyl groups, as measured using X-ray photoelectron spectroscopic analysis of the trifluoroacetic anhydride-treated wood. These experiments showed that wood modification is useful in understanding wood-adhesive interactions, in addition to determining how to develop adhesives for acetylated woods.

| S-EPMC6418570 | biostudies-literature

Highly Conducting, Sustainable, Nanographitic Rubber Composites.

Project description:Environmentally friendly multifunctional rubber composites are reported. Graphitic nanocarbon (NC) deriving from cracking of biogas (methane/carbon dioxide) and natural rubber extracted directly from the Hevea brasiliensis tree are the two components of these composites produced via latex technology. While maintaining and enhancing the intrinsic thermal and mechanical characteristics of rubber, the presence of NC shows a significant improvement on the electrical response. For a 10 wt % NC content, a 1010-fold increase in conductivity has been achieved with a conductivity value of 7.5 S·m-1, placing these composites among the best obtained using other carbon fillers. In addition, the piezoresistive behavior has also been verified. These promising green composites have a potential use in a variety of applications such as sealing of electronic devices and sensors.

| S-EPMC6641372 | biostudies-literature

Fabrication of Al/Mg/Al Composites via Accumulative Roll Bonding and Their Mechanical Properties.

Project description:Al(1060)/Mg(AZ31)/Al(1060) multilayered composite was successfully produced using an accumulative roll bonding (ARB) process for up to four cycles at an elevated temperature (400 °C). The microstructure evolution of the composites and the bonding characteristics at the interfaces between Al and Mg layers with increasing ARB cycles were characterized through optical microscopy, field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM). It was found that the grains of Al and Mg layers were significantly refined and Al₃Mg₂ and Al12 Mg17 intermetallic compound layers formed at the Al/Mg bonding interfaces. The strength increased gradually and the ultimate tensile strength (UTS) reached a maximum value of about 240 MPa at the third pass. Furthermore, the strengthening mechanism of the composite was analyzed based on the fracture morphologies.

| S-EPMC5457262 | biostudies-other

Bioinspired Fabrication of DNA-Inorganic Hybrid Composites Using Synthetic DNA.

Project description:Nucleic acid nanostructures have attracted significant interest as potential therapeutic and diagnostic platforms due to their intrinsic biocompatibility and biodegradability, structural and functional diversity, and compatibility with various chemistries for modification and stabilization. Among the fabrication approaches for such structures, the rolling circle techniques have emerged as particularly promising, producing morphologically round, flower-shaped nucleic acid particles: typically hybrid composites of long nucleic acid strands and inorganic magnesium pyrophosphate (Mg2PPi). These constructs are known to form via anisotropic nucleic acid-driven crystallization in a sequence-independent manner, rendering monodisperse and densely packed RNA or DNA-inorganic composites. However, it still remains to fully explore how flexible polymer-like RNA or DNA strands (acting as biomolecular additives) mediate the crystallization process of Mg2PPi and affect the structure and properties of the product crystals. To address this, we closely examined nanoscale details to mesoscopic features of Mg2PPi/DNA hybrid composites fabricated by two approaches, namely rolling circle amplification (RCA)-based in situ synthesis and long synthetic DNA-mediated crystallization. Similar to the DNA constructs fabricated by RCA, the rapid crystallization of Mg2PPi was retarded on a short-range order when we precipitated the crystals in the presence of presynthesized long DNA, which resulted in effective incorporation of biomolecular additives such as DNA and enzymes. These findings further provide a more feasible way to encapsulate bioactive enzymes within DNA constructs compared to in situ RCA-mediated synthesis, i.e., by not only protecting them from possible denaturation under the reaction conditions but also preventing nonselective association of proteins arising from the RCA reaction mixtures.

| S-EPMC6439439 | biostudies-literature

High performance graphene oxide based rubber composites.

Project description:In this paper, graphene oxide/styrene-butadiene rubber (GO/SBR) composites with complete exfoliation of GO sheets were prepared by aqueous-phase mixing of GO colloid with SBR latex and a small loading of butadiene-styrene-vinyl-pyridine rubber (VPR) latex, followed by their co-coagulation. During co-coagulation, VPR not only plays a key role in the prevention of aggregation of GO sheets but also acts as an interface-bridge between GO and SBR. The results demonstrated that the mechanical properties of the GO/SBR composite with 2.0 vol.% GO is comparable with those of the SBR composite reinforced with 13.1 vol.% of carbon black (CB), with a low mass density and a good gas barrier ability to boot. The present work also showed that GO-silica/SBR composite exhibited outstanding wear resistance and low-rolling resistance which make GO-silica/SBR very competitive for the green tire application, opening up enormous opportunities to prepare high performance rubber composites for future engineering applications.

| S-EPMC3752610 | biostudies-literature

Peanut meal-based wood adhesives enhanced by urea and epichlorohydrin.

Project description:Peanut meal (PM) has recently emerged as a potential protein source for wood adhesives, owing to superior features such as high availability, renewability and eco-friendliness. However, the poor properties of unmodified PM-based wood adhesives, compared with their petroleum-derived counterparts, limit their use in high-performance applications. In order to promote the application of PM-based wood adhesives in plywood industry, urea (U) and epichlorohydrin (ECH) were used to enhance the properties of the adhesives and the modification mechanism was investigated. PM-based wood adhesives made with U and ECH were shown to possess sufficient water resistance and exhibited higher apparent viscosity and solid content than without. Fourier-transform infrared spectroscopy results suggested that U denatured PM protein and expose more reactive groups, allowing ECH to react better with U-treated PM protein to form a dense, cross-linked network which was the main reason for the improvement of the properties. The crystallinity increased from 2.7% to 11% compared with the control, indicating that the molecular structure of the resultant adhesive modified by U and ECH became more regular and compact owing to the cross-linked network structure. Thermogravimetry tests showed that decomposition temperature of the protein skeleton structure increased from 307°C to 314°C after U and ECH modification. Scanning electron microscopy images revealed that using U and ECH for adhesives resulted in a smooth protein surface which prevented moisture penetration and improved water resistance. PM-based adhesives thus represent potential candidates to replace petroleum-derived adhesives in the plywood industry, which will effectively promote the rapid development of eco-friendly adhesives and increase the added value of PM.

| S-EPMC6894569 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data