Role of Chloride in the Corrosion and Fracture Behavior of Micro-Alloyed Steel in E80 Simulated Fuel Grade Ethanol Environment.
Ontology highlight
ABSTRACT:
SUBMITTER: Joseph OO
PROVIDER: S-EPMC5456821 | biostudies-other | 2016 Jun
REPOSITORIES: biostudies-other
Similar Datasets
Project description:Microbially influenced corrosion (MIC) is a costly problem that impacts hydrocarbon production and processing equipment, water distribution systems, ships, railcars, and other types of metallic infrastructure. In particular, MIC is known to cause considerable damage to hydrocarbon fuel infrastructure including production, transportation, and storage systems, often times with catastrophic environmental contamination results. As the production and use of alternative fuels such as fuel-grade ethanol (FGE) increase, it is important to consider MIC of engineered materials exposed to these "newer fuels" as they enter existing infrastructure. Reports of suspected MIC in systems handling FGE and water prompted an investigation of the microbial diversity associated with these environments. Small subunit ribosomal RNA gene pyrosequencing surveys indicate that acetic-acid-producing bacteria (Acetobacter spp. and Gluconacetobacter spp.) are prevalent in environments exposed to FGE and water. Other microbes previously implicated in corrosion, such as sulfate-reducing bacteria and methanogens, were also identified. In addition, acetic-acid-producing microbes and sulfate-reducing microbes were cultivated from sampled environments containing FGE and water. Results indicate that complex microbial communities form in these FGE environments and could cause significant MIC-related damage that may be difficult to control. How to better manage these microbial communities will be a defining aspect of improving mitigation of global infrastructure corrosion.
| S-EPMC4513208 | biostudies-literature
Project description:A porous and low-density protective film on a steel surface in the corrosive environment can undergo deterioration even in the presence of organic inhibitors due to infiltration of aggressive ions into the pinholes and/or pores. This phenomenon is related to the localized corrosion that takes place even in the presence of an optimal concentration of organic corrosion inhibitors in the given medium. To overcome this issue, we have designed an organic protective film on a steel surface with the help of titania nanoparticles (TNPs) combined with an organic corrosion inhibitor derived from Aganonerion polymorphum leaf extract (APLE), all to be studied in a simulated ethanol fuel blend (SEFB). The TNPs with varied diameters and concentrations have been studied for examining their effect on the inhibition capacity of 1000 ppm APLE on the steel surface in SEFB medium using electrochemical and surface analysis techniques. Enhanced corrosion inhibition of the surficial film was observed in the presence of both the APLE inhibitor and small amounts of TNPs. A direct agreement was observed between the experimental and molecular dynamics theoretical investigations showcasing high binding energy between inhibitor molecules and steel substrates, resulting in a much higher adhesion of the protective film, good thermal stability of the adsorbent film, and electron abundance for the supply of steel substrate of inhibitor species.
| S-EPMC6648484 | biostudies-literature
Project description:Hybrid sol-gel coatings, named U(X):TEOS, based on ureasilicate matrices (U(X)) enriched with tetraethoxysilane (TEOS), were synthesized. The influence of TEOS addition was studied on both the structure of the hybrid sol-gel films as well as on the electrochemical properties. The effect of TEOS on the structure of the hybrid sol-gel films was investigated by solid state Nuclear Magnetic Resonance. The dielectric properties of the different materials were investigated by electrochemical impedance spectroscopy. The corrosion behavior of the hybrid coatings on HDGS was studied in chloride-contaminated simulated concrete pore solutions (SCPS) by polarization resistance measurements. The roughness of the HDGS coated with hybrids was also characterized by atomic force microscopy. The structural characterization of the hybrid materials proved the effective reaction between Jeffamine® and 3-isocyanate propyltriethoxysilane (ICPTES) and indicated that the addition of TEOS does not seem to affect the organic structure or to increase the degree of condensation of the hybrid materials. Despite the apparent lack of influence on the hybrids architecture, the polarization resistance measurements confirmed that TEOS addition improves the corrosion resistance of the hybrid coatings (U(X):TEOS) in chloride-contaminated SCPS when compared to samples prepared without any TEOS (U(X)). This behavior could be related to the decrease in roughness of the hybrid coatings (due TEOS addition) and to the different metal coating interaction resulting from the increase of the inorganic component in the hybrid matrix.
| S-EPMC5503348 | biostudies-literature
Project description:Chloride is reported to play a significant role in corrosion reactions, products and kinetics of ferrous metals. To enhance the understanding of the effects of soil environments, especially the saline soils with high levels of chloride, on the corrosion of ductile iron and carbon steel, a 3-month corrosion test was carried out by exposing ferrous metals to soils of six chloride concentrations. The surface morphology, rust compositions and corrosion kinetics were comprehensively studied by visual observation, scanning electron microscopy (SEM), X-Ray diffraction (XRD), weight loss, pit depth measurement, linear polarization and electrochemical impedance spectroscopy (EIS) measurements. It showed that chloride ions influenced the characteristics and compositions of rust layers by diverting and participating in corrosion reactions. α-FeOOH, γ-FeOOH and iron oxides were major corrosion products, while β-Fe8O8(OH)8Cl1.35 rather than β-FeOOH was formed when high chloride concentrations were provided. Chloride also suppressed the decreasing of corrosion rates, whereas increased the difficulty in the diffusion process by thickening the rust layers and transforming the rust compositions. Carbon steel is more susceptible to chloride attacks than ductile iron. The corrosion kinetics of ductile iron and carbon steel corresponded with the probabilistic and bilinear model respectively.
| S-EPMC5537275 | biostudies-literature
Project description:The Cl--induced corrosion of metals and alloys is of relevance to a wide range of engineered materials, structures, and systems. Because of the challenges in studying pitting corrosion in a quantitative and statistically significant manner, its kinetics remain poorly understood. Herein, by direct, nano- to micro-scale observations using vertical scanning interferometry (VSI), we examine the temporal evolution of pitting corrosion on AISI 1045 carbon steel over large surface areas in Cl--free, and Cl--enriched solutions. Special focus is paid to examine the nucleation and growth of pits, and the associated formation of roughened regions on steel surfaces. By statistical analysis of hundreds of individual pits, three stages of pitting corrosion, namely, induction, propagation, and saturation, are quantitatively distinguished. By quantifying the kinetics of these processes, we contextualize our current understanding of electrochemical corrosion within a framework that considers spatial dynamics and morphology evolutions. In the presence of Cl- ions, corrosion is highly accelerated due to multiple autocatalytic factors including destabilization of protective surface oxide films and preservation of aggressive microenvironments within the pits, both of which promote continued pit nucleation and growth. These findings offer new insights into predicting and modeling steel corrosion processes in mid-pH aqueous environments.
| S-EPMC5964123 | biostudies-literature
Project description:Chloride-induced steel corrosion is the most concerning issue for the durability of concrete structures. Concrete and steel samples were obtained from a 30-year-old reinforced concrete bridge. The chloride content was measured by a potentiometric titration method and the microstructure of concrete was obtained by scanning electron microscopy and mercury intrusion porosimetry. The rust phases of the steel were detected by X-ray diffraction and Raman analysis. It was found that the convection depth for chloride transport in cracked concrete was significantly larger than that in uncracked concrete. The concrete in a pier column facing upstream had greater porosity due to the water impact and calcium leaching. The coefficients of variability of chloride diffusivity of concrete for the bridge deck and the pier column were significantly different. Rust phases including lepidocrocite, goethite, akaganeite, magnetite, and maghemite were detected using Raman spectroscopy and X-ray diffraction. The major phases of steel rust in the atmospheric zone were lepidocrocite and goethite, while they were lepidocrocite and maghemite in the tidal zone. The results of this study would provide information concerning the chloride-induced steel corrosion under a marine environment in order to predict long-term behaviors of a reinforced concrete structure.
| S-EPMC7503823 | biostudies-literature
Project description:Microbially-induced corrosion of carbon steel in anoxic groundwater
| PRJEB19087 | ENA
Project description:Corrosion-induced damage to concrete reinforced with bars is a serious problem regarding technical and economic aspects and strongly depends on used materials, corrosion environment, and service life. Tests described in this paper refer to a two-year evaluation of the effectiveness of protection provided by zinc-coated low-carbon reinforcing steel of grade B500SP in concrete against chloride corrosion. Performed tests were comparative and included measurements conducted on four groups of concrete test elements with dimensions of 40 mm × 40 mm × 140 mm reinforced with a bar having a diameter of ?8 mm. Particular groups were a combination of different types of concrete with or without chloride additives, with galvanized or black steel. Chlorides as CaCl2 were added to the concrete mix in the amount of 3% of cement weight in concrete. Reinforced concrete specimens were periodically monitored within two years using the following techniques: linear polarization resistance (LPR) and electrochemical impedance spectroscopy (EIS). Polarization measurements were conducted in a three-electrode arrangement, in which a rebar in concrete served as a working electrode, stainless steel sheet was used as an auxiliary electrode, and Cl-/AgCl,Ag was a reference electrode. Comparative tests of changes in the density of corrosion current in concrete specimens without chloride additives basically demonstrated no development of corrosion, and possible passivation was expected in case of black steel. Higher densities of corrosion current were observed for galvanized steel during first days of testing. The reason was the dissolution of zinc after the contact with initially high pH of concrete pore solution. Six-month measurements demonstrated a higher density of corrosion current in concrete specimens with high concentration of chlorides, which unambiguously indicated corrosion in concrete reinforced with galvanized or black steel. Densities of corrosion current determined for selected specimens dramatically decreased after an 18-month interval in measurements. Corrosion was even inhibited on black steel as an insulating barrier of corrosion products was formed. The above observations were confirmed with structural studies using scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) techniques. Results obtained from corrosion (LPR, EIS) and structural (SEM, EDS) tests on specimens of concrete reinforced with steel B500SP demonstrated a very favorable impact of zinc coating on steel by providing two-year protection against corrosion in the environment with very high chloride content.
| S-EPMC7435989 | biostudies-literature
Project description:Fuel ethanol is now considered a global energy commodity that is fully competitive with gasoline. We have determined genome copy number differences that are common to five industrially important fuel ethanol yeast strains responsible for the production of billions of gallons of fuel ethanol per year from sugarcane. The fuel strains used were CAT1, BG1, PE2, SA1, and VR1 (note that two independent isolates were analyzed, denoted by "-1" and "-2"). These array-CGH data were compared with array-CGH data from nine other non-fuel industrial yeasts: An ale brewing strain ("Sc-ale"), four wine strains (GSY2A, GSY3A, GSY10A, GSY11B), and 4 bakers' yeast strains (GSY149, GSY150, GSY154, GSY155). Our results reveal significant amplifications of the telomeric SNO and SNZ genes only in the fuel strains, whose protein products are involved in the biosynthesis of vitamins B6 (pyridoxine) and B1 (thiamin). We show that these amplifications allow these yeasts to grow efficiently, especially at high sugar concentrations, regardless of the presence or absence of either of the two vitamins. Our results reveal important genetic adaptations that have been selected for in the industrial environment, which may be required for the efficient fermentation of biomass-derived sugars from other renewable feedstocks. A strain or line experiment design type assays differences between multiple strains, cultivars, serovars, isolates, lines from organisms of a single species. Strain Name: fuel strains used for aCGH Strain_or_line_design
2010-06-25 | E-GEOD-13875 | biostudies-arrayexpress
Project description:This article describes the susceptibility of 316L stainless steel to stress corrosion cracking (SCC) in a nitrite-containing chloride solution. Slow strain rate testing (SSRT) in 30 wt. % MgCl₂ solution established SCC susceptibility, as evidenced by post-SSRT fractography. Addition of nitrite to the chloride solution, which is reported to have inhibitive influence on corrosion of stainless steels, was found to increase SCC susceptibility. The susceptibility was also found to increase with nitrite concentration. This behaviour is explained on the basis of the passivation and pitting characteristics of 316L steel in chloride solution.
| S-EPMC5456438 | biostudies-other