The Characterization of Fixation of Ba, Pb, and Cu in Alkali-Activated Fly Ash/Blast Furnace Slag Matrix.

ABSTRACT: The fixation of heavy metals (Ba, Cu, Pb) in an alkali-activated matrix was investigated. The matrix consisted of fly ash and blast furnace slag (BFS). The mixture of NaOH and Na-silicate was used as alkaline activator. Three analytical techniques were used to describe the fixation of heavy metals-X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) equipped with energy dispersive X-ray spectroscopy (EDS), and X-ray powder diffraction (XRD). All heavy metals formed insoluble salts after alkaline activation. Ba was fixed as BaSO₄, and only this product was crystalline. EDS mapping showed that Ba was cumulated in some regions and formed clusters. Pb was present in the form of Pb(OH)₂ and was dispersed throughout the matrix on the edges of BFS grains. Cu was fixed as Cu(OH)₂ and also was cumulated in some regions and formed clusters. Cu was present in two different chemical states; apart from Cu(OH)₂, a Cu-O bond was also identified.

SUBMITTER: Koplik J

PROVIDER: S-EPMC5456941 | biostudies-other | 2016 Jun

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Effect of Na₃PO₄ on the Hydration Process of Alkali-Activated Blast Furnace Slag.

Project description:In recent years, the utilization of different non-traditional cements and composites has been increasing. Alkali-activated cementitious materials, especially those based on the alkali activation of blast furnace slag, have considerable potential for utilization in the building industry. However, alkali-slag cements exhibit very rapid setting times, which are too short in some circumstances, and these materials cannot be used for some applications. Therefore, it is necessary to find a suitable retarding admixture. It was shown that the sodium phosphate additive has a strong effect on the heat evolution during alkali activation and effectively retards the hydration reaction of alkali-activated blast furnace slag. The aim of the work is the suggestion of a reaction mechanism of retardation mainly based on Raman and X‑ray photoelectron spectroscopy.

| S-EPMC5503029 | biostudies-other

Geopolymer Based on Mechanically Activated Air-cooled Blast Furnace Slag.

Project description:An efficient solution to increase the sustainability of building materials is to replace Portland cement with alkali-activated materials (AAM). Precursors for those systems are often based on water-cooled ground granulated blast furnace slags (GGBFS). Quenching of blast furnace slag can be done also by air but in that case, the final product is crystalline and with a very low reactivity. The present study aimed to evaluate the cementitious properties of a mechanically activated (MCA) air-cooled blast furnace slag (ACBFS) used as a precursor in sodium silicate alkali-activated systems. The unreactive ACBFS was processed in a planetary ball mill and its cementing performances were compared with an alkali-activated water-cooled GGBFS. Mixes based on mechanically activated ACBFS reached the 7-days compressive strength of 35 MPa and the 28-days compressive strength 45 MPa. The GGBFS-based samples showed generally higher compressive strength values.

| S-EPMC7085006 | biostudies-literature

Self-Sensing Properties of Alkali Activated Blast Furnace Slag (BFS) Composites Reinforced with Carbon Fibers.

Project description:In recent years, several researchers have shown the good performance of alkali activated slag cement and concretes. Besides their good mechanical properties and durability, this type of cement is a good alternative to Portland cements if sustainability is considered. Moreover, multifunctional cement composites have been developed in the last decades for their functional applications (self-sensing, EMI shielding, self-heating, etc.). In this study, the strain and damage sensing possible application of carbon fiber reinforced alkali activated slag pastes has been evaluated. Cement pastes with 0, 0.29 and 0.58 vol % carbon fiber addition were prepared. Both carbon fiber dosages showed sensing properties. For strain sensing, function gage factors of up to 661 were calculated for compressive cycles. Furthermore, all composites with carbon fibers suffered a sudden increase in their resistivity when internal damages began, prior to any external signal of damage. Hence, this material may be suitable as strain or damage sensor.

| S-EPMC5452839 | biostudies-other

Properties of Foamed Mortar Prepared with Granulated Blast-Furnace Slag.

Project description:Foamed mortar with a density of 1300 kg/m³ was prepared. In the initial laboratory trials, water-to-cement (w/c) ratios ranging from 0.54 to 0.64 were tested to determine the optimal value for foamed mortar corresponding to the highest compressive strength without compromising its fresh state properties. With the obtained optimal w/c ratio of 0.56, two types of foamed mortar were prepared, namely cement-foamed mortar (CFM) and slag-foamed mortar (SFM, 50% cement was replaced by slag weight). Four different curing conditions were adopted for both types of foamed mortar to assess their compressive strength, ultrasonic pulse velocity (UPV) and thermal insulation performance. The test results indicated that utilizing 50% of slag as cement replacement in the production of foamed mortar improved the compressive strength, UPV and thermal insulation properties. Additionally, the initial water curing of seven days gained higher compressive strength and increased UPV values as compared to the air cured and natural weather curing samples. However, this positive effect was more pronounced in the case of compressive strength than in the UPV and thermal conductivity of foamed mortar.

| S-EPMC5455276 | biostudies-other

Reactivation of a Retarded Suspension of Ground Granulated Blast-Furnace Slag.

Project description:An effective retarded suspension of ground granulated blast-furnace slag (GGBFS) needs a strong activator to reactivate the hydration. In this research study, sodium hydroxide (NaOH) as an alkali activator in two different concentrations (30 and 50 wt.%) was used to overcome the retardation and give the hardened GGBFS the reasonable strength. The study was carried out with a mixture of GGBFS, a solution of 1.0 wt.% d-gluconic acid (C₆H12O₇) as a retarder in the mixing water and a methyl cellulose as a stabilizer. The reactivation was executed after seven different periods (up to 28 days) after the system was retarded. The following investigations were performed: slump test, measurement of ultrasonic (US) velocity, compressive strength and gross density, thermogravimetry (TG) and scanning electron microscopy (SEM). The analyses of the hardened samples were carried out seven, 28 and 90 days after the reactivation. The result of the study is an effective reactivation of a retarded suspension. In this case, the activator with 50 wt.% NaOH shows a very high performance. The setting time of the reactivated binders is much longer compared to the reference, but, in the longer term, the compressive strength and the progress of the hydration exceed the performance of the reference.

| S-EPMC5456691 | biostudies-other

Properties of Concrete Using Treated Low-Class Recycled Coarse Aggregate and Blast Furnace Slag Sand.

Project description:Since high quality natural aggregates are becoming scarce, it is important that industrial recycled products and by-products are used as aggregates for concrete. In Japan, the use of recycled aggregate (RG) is encouraged. Since, strength and durability of recycled aggregate concrete is lower than that of normal aggregate concrete, the use of recycled aggregate has not been significant. In order to improve physical properties of concrete using recycled coarse aggregate, blast furnace slag sand has been proposed. Recently, blast furnace slag sand is expected to improve durability, freezing, and thawing damage of concrete in Japan. Properties of fresh and hardened concrete bleeding, compressive strength, and resistance to freezing and thawing which are caused by the rapid freezing and thawing test using liquid nitrogen is a high loader than the JIS A 1148 A method that were investigated. As a result, concrete using treated low-class recycled coarse aggregate and 50% or 30% replacement of crushed sand with blast furnace slag sand showed the best results, in terms of bleeding, resistance to freezing and thawing.

| S-EPMC7078881 | biostudies-literature

Influence of Fly Ash Additive on the Properties of Concrete with Slag Cement.

Project description:This paper presents research on the impact of fly ash addition on selected physical and mechanical parameters of concrete made with slag cement. Experimental tests were carried out to measure the migration of chloride ions in concrete, the tightness of concrete exposed to water under pressure, and the compressive strength and tensile strength of concrete during splitting. Six series of concrete mixes made with CEM IIIA 42.5 and 32.5 cement were tested. The base concrete mix was modified by adding fly ash as a partial cement substitute in the amounts of 25% and 33%. A comparative analysis of the obtained results indicates a significant improvement in tightness, especially in concrete based on CEM IIIA 32.5 cement and resistance to chloride ion penetration for the concretes containing fly ash additive. In the concretes containing fly ash additive, a slower rate of initial strength increase and high strength over a long period of maturation are shown. In accordance with the presented research results, it is suggested that changes to the European standardization system be considered, to allow the use of fly ash additive in concrete made with CEM IIIA 42.5 or 32.5 cement classes. Such a solution is not currently acceptable in standards in some European Countries.

| S-EPMC7435652 | biostudies-literature

Effect of the Formation of Amorphous Networks on the Structure and Hydration Characteristics of Granulated Blast Furnace Slag.

Project description:The slag obtained in the process of pig iron smelting has been widely used, but the variational hydration activity always is a significant factor affecting its quality. In this experiment, the laboratory simulated slag was prepared by adjusting the chemical composition and cooling method. The experiment primary characterized the structure and hydration process with different types of slag by using MAS NMR, XRD, compressive strength, ICP, SEM, and hydration heat, then obtained the influence of the composition of the network former S/A (the mass ratio of SiO2 and Al2O3 in chemical composition) and amorphous phase content on its structure and hydration activity. The result shows that lowering the S/A value can reduce the degree of vitreous polymerization in the slag; reducing the S/A value of the slag can make the slag hydration time advance, and consequently, the cumulative exotherm increases, the liquid phase Ca/Si and Al/Si ionic ratio increases, and the hydration product changes from C-S-H gel to C-A-S-H gel, which ultimately leads to an increase in compressive strength. In the high S/A value slag, the formation of the trace crystal phase of gehlenite is beneficial to reduce the degree of polymerization of the amorphous.

| S-EPMC7143658 | biostudies-literature

Resistance to Chemical Attack of Hybrid Fly Ash-Based Alkali-Activated Concretes.

Project description:The environmental impacts related to Portland cement production in terms of energy consumption, the massive use of natural resources and CO2 emissions have led to the search for alternative cementitious materials. Among these materials, alkali-activated cements based on fly ash (FA) have been considered for concrete production with greater sustainability. In the present article, the chemical durability properties (resistance to sulphates, chloride permeability, and resistance to carbonation) of a hybrid alkali-activated concrete based on fly ash-ordinary Portland cement (FA/OPC) with proportions of 80%/20% were evaluated. It is noted that the FA was a low-quality pozzolan with a high unburned carbon content (20.67%). The results indicated that FA/OPC concrete had good durability with respect to the OPC concrete, with 95% less expansion in the presence of sodium sulphate and a 2% strength loss at 1100 days, compared with the 56% strength loss of the OPC concrete. In addition, FA/OPC showed lower chloride permeability. On the contrary, the FA/OPC was more susceptible to carbonation. However, the residual compressive strength was 23 MPa at 360 days of CO2 exposure. Based on the results, FA/OPC, using this type of FA, can be used as a replacement for OPC in the presence of these aggressive agents in the service environment.

| S-EPMC7435788 | biostudies-literature

Studying the Hydration of a Retarded Suspension of Ground Granulated Blast-Furnace Slag after Reactivation.

Project description:This article presents a combined use of a retarder (d-gluconic acid) and an alkaline activator (sodium hydroxide) in a binder system based on ground granulated blast-furnace slag. The properties of the retarder are extending the dormant hydration period and suppressing the generation of strength-giving phases. Different retarder concentrations between 0.25 and 1.00 wt.% regulate the intensity and the period of the retardation and also the characteristics of the strength development. The activator concentration of 30 and 50 wt.% regulates the overcoming of the dormant period and thereby the solution of the slag and hence the formation of the hydration products. The research objective is to produce a mineral binder system based on two separate liquid components. The highest concentration of retarder and activator generates the highest compressive strength and mass of hydration products-after 90 days of hydration a compressive strength of more than 50 N/mm². The main phases are calcium silicate hydrate and hydrotalcite. Generally, the combination of retarder and activator shows a high potential in the performance increase of the hydration process.

| S-EPMC5457240 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data