ZrB₂-CNTs Nanocomposites Fabricated by Spark Plasma Sintering.

ABSTRACT: ZrB₂-based nanocomposites with and without carbon nanotubes (CNTs) as reinforcement were prepared at 1600 °C by spark plasma sintering. The effects of CNTs on the microstructure and mechanical properties of nano-ZrB₂ matrix composites were studied. The results indicated that adding CNTs can inhibit the abnormal grain growth of ZrB₂ grains and improve the fracture toughness of the composites. The toughness mechanisms were crack deflection, crack bridging, debonding, and pull-out of CNTs. The experimental results of the nanograined ZrB₂-CNTs composites were compared with those of the micro-grained ZrB₂-CNTs composites. Due to the small size and surface effects, the nanograined ZrB₂-CNTs composites exhibited stronger mechanical properties: the hardness, flexural strength and fracture toughness were 18.7 ± 0.2 GPa, 1016 ± 75 MPa, and 8.5 ± 0.4 MPa·m1/2, respectively.

SUBMITTER: Jin H

PROVIDER: S-EPMC5456984 | biostudies-other | 2016 Nov

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Simultaneous Spark Plasma Sintering of Multiple Complex Shapes.

Project description:This work addresses the two great challenges of the spark plasma sintering (SPS) process: The sintering of complex shapes and the simultaneous production of multiple parts. A new controllable interface method is employed to concurrently consolidate two nickel gear shapes by SPS. A graphite deformable sub-mold is specifically designed for the mutual densification of both complex parts in a unique 40 mm powder deformation space. An energy efficient SPS configuration is developed to allow the sintering of a large-scale powder assembly under electric current lower than 900 A. The stability of the developed process is studied by electro-thermal-mechanical (ETM) simulation. The ETM simulation reveals that homogeneous densification conditions can be attained by inserting an alumina powder at the sample/punches interfaces, enabling the energy efficient heating and the thermal confinement of the nickel powder. Finally, the feasibility of the fabrication of the two near net shape gears with a very homogeneous microstructure is demonstrated.

| S-EPMC6416649 | biostudies-literature

Microstructure and Electrical Properties of AZO/Graphene Nanosheets Fabricated by Spark Plasma Sintering.

Project description:In this study we report on the sintering behavior, microstructure and electrical properties of Al-doped ZnO ceramics containing 0-0.2 wt. % graphene sheets (AZO-GNSs) and processed using spark plasma sintering (SPS). Our results show that the addition of <0.25 wt. % GNSs enhances both the relative density and the electrical resistivity of AZO ceramics. In terms of the microstructure, the GNSs are distributed at grain boundaries. In addition, the GNSs are also present between ZnO and secondary phases (e.g., ZnAl₂O₄) and likely contribute to the measured enhancement of Hall mobility (up to 105.1 cm²·V-1·s-1) in these AZO ceramics. The minimum resistivity of the AZO-GNS composite ceramics is 3.1 × 10-4 Ω·cm which compares favorably to the value of AZO ceramics which typically have a resistivity of 1.7 × 10-3 Ω·cm.

| S-EPMC5509084 | biostudies-other

Data on the influence of TiN on wear and corrosion behavior of Ti-6Al-4V alloy fabricated through spark plasma sintering.

Project description:Data about bulk properties of Ti-6Al-4V based composites specimen achieved by powder metallurgy route using spark plasma sintering (SPS) technique is presented, with focus on the effect of TiN particles on wear and corrosion behavior of the resultant composites. Two microsized kind of powders are combined; Ti-6Al-4V and TiN. The powder mixing and SPS processing has been enhanced and consolidated.

| S-EPMC6141763 | biostudies-literature

Spark Plasma Sintering of LiFePO4: AC Field Suppressing Lithium Migration.

Project description:Our work proposes a comparison between Spark Plasma Sintering of LiFePO4 carried out using an Alternating Current (AC) and Direct Current (DC). It quantifies the Li-ion migration using DC, and it validates such hypothesis using impedance spectroscopy, X-ray photoelectron spectroscopy and inductively coupled plasma optical emission spectroscopy. The use of an AC field seems effective to inhibit undesired Li-ion migration and achieve high ionic conductivity as high as 4.5 × 10-3 S/cm, which exceeds by one order of magnitude samples processed under a DC field. These results anticipate the possibility of fabricating a high-performance all-solid-state Li-ion battery by preventing undesired Li loss during SPS processing.

| S-EPMC8198947 | biostudies-literature

Effect of Sintering Temperature on Structural, Dielectric, and Magnetic Properties of Multiferroic YFeO₃ Ceramics Fabricated by Spark Plasma Sintering.

Project description:Based on precursor powders with a size of 200-300 nm prepared by the low-temperature solid reaction method, phase-pure YFeO₃ ceramics are fabricated using spark plasma sintering (SPS) at different temperatures. X-ray diffraction (XRD) and scanning electron microscopy (SEM) reveal that the high-purity YFeO₃ ceramics can be prepared using SPS, while the results from X-ray photoelectron spectroscopy (XPS) show that the concentration of oxygen vacancies resulting from transformation from Fe3+ to Fe2+ is low. The relative density of the 1000 °C-sintered sample is as high as 97.7%, which is much higher than those of the samples sintered at other temperatures. The present dielectric and magnetic properties are much better than those of the samples fabricated by conventional methods. These findings indicate that the YFeO₃ ceramics prepared by the low temperature solid reaction and SPS methods possess excellent dielectric and magnetic properties, making them suitable for potential applications involving magnetic storage.

| S-EPMC5503393 | biostudies-other

A strategy to optimize the thermoelectric performance in a spark plasma sintering process.

Project description:Spark plasma sintering (SPS) is currently widely applied to existing alloys as a means of further enhancing the alloys' figure of merit. However, the determination of the optimal sintering condition is challenging in the SPS process. This report demonstrates a systematic way to independently optimize the Seebeck coefficient S and the ratio of electrical to thermal conductivity (?/?) and thus achieve the maximum figure of merit zT = S(2)(?/?)T. Sb2-xInxTe3 (x = 0-0.2) were chosen as examples to validate the method. Although high sintering temperature and pressure are helpful in enhancing the compactness and electrical conductivity of pressed samples, the resultant deteriorated Seebeck coefficient and increasing thermal conductivity eventually offset the benefit. We found that the optimal sintering temperature coincides with temperatures at which the maximum Seebeck coefficient begins to degrade, whereas the optimal sintering pressure coincided with the pressure at which the ?/? ratio reaches a maximum. Based on this principle, the optimized sintering conditions were determined, and the zT of Sb1.9In0.1Te3 is raised to 0.92 at 600 K, showing an approximately 84% enhancement. This work develops a facile strategy for selecting the optimal SPS sintering condition to further enhance the zT of bulk specimens.

| S-EPMC4791595 | biostudies-literature

Densification in transparent SiO<sub>2</sub> glasses prepared by spark plasma sintering.

Project description:Recently, spark plasma sintering (SPS) has become an attractive method for the preparation of solid-state ceramics. As SPS is a pressure-assisted low-temperature process, it is important to examine the effects of temperature and pressure on the structural properties of the prepared samples. In the present study, we examined the correlation between the preparation conditions and the physical and structural properties of SiO2 glasses prepared by SPS. Compared with the conventional SiO2 glass, the SPS-SiO2 glasses exhibit a higher density and elastic modulus, but a lower-height first sharp diffraction peak of the X-ray total structure factor. Micro-Raman and micro-IR spectra suggest the formation of heterogeneous regions at the interface between the SiO2 powders and graphite die. Considering the defect formation observed in optical absorption spectra, reduction reaction mainly affects the densification of SPS-SiO2 glass. Hence, the reaction at the interface is important for tailoring the structure and physical properties of solid-state materials prepared by the SPS technique.

| S-EPMC9427799 | biostudies-literature

Enhanced Multiferroic Properties of YMnO₃ Ceramics Fabricated by Spark Plasma Sintering Along with Low-Temperature Solid-State Reaction.

Project description:Based on precursor powders with a size of 200-300 nm prepared by the low-temperature solid-state reaction method, phase-pure YMnO₃ ceramics are fabricated using spark plasma sintering (SPS). X-ray diffraction (XRD) and scanning electron microscopy (SEM) reveal that the high-purity YMnO₃ ceramics can be prepared by SPS at 1000 °C for 5 minutes with annealing at 800 °C for 2 h. The relative density of the sample is as high as 97%, which is much higher than those of the samples sintered by other methods. The present dielectric and magnetic properties are much better than those of the samples fabricated by conventional methods and SPS with ball-milling precursors, and the ferroelectric loops at room temperature can be detected. These findings indicate that the YMnO₃ ceramics prepared by the low temperature solid reaction method and SPS possess excellent dielectric lossy ferroelectric properties at room temperature, and magnetic properties at low temperature (10 K), making them suitable for potential multiferroic applications.

| S-EPMC5459049 | biostudies-other

Corrosion Behavior and Strength of Dissimilar Bonding Material between Ti and Mg Alloys Fabricated by Spark Plasma Sintering.

Project description:Ti and solution treated Mg alloys such as AZ31B (ST), AZ61 (ST), AZ80 (ST) and AZ91 (ST) were successfully bonded at 475 °C by spark plasma sintering, which is a promising new method in welding field. The formation of Ti₃Al intermetallic compound was found to be an important factor in controlling the bonding strength and galvanic corrosion resistance of dissimilar materials. The maximum bonding strength and bonding efficiency at 193 MPa and 96% were obtained from Ti/AZ91 (ST), in which a thick and uniform nano-level Ti₃Al layer was observed. This sample also shows the highest galvanic corrosion resistance with a measured galvanic width and depth of 281 and 19 µm, respectively. The corrosion resistance of the matrix on Mg alloy side was controlled by its Al content. AZ91 (ST) exhibited the highest corrosion resistance considered from its corrode surface after corrosion test in Kroll's etchant. The effect of Al content in Mg alloy on bonding strength and corrosion behavior of Ti/Mg alloy (ST) dissimilar materials is discussed in this work.

| S-EPMC5509276 | biostudies-other

Spark Plasma Sintering of Lithium Aluminum Germanium Phosphate Solid Electrolyte and its Electrochemical Properties.

Project description:Sodium superionic conductor (NASICON)-type lithium aluminum germanium phosphate (LAGP) has attracted increasing attention as a solid electrolyte for all-solid-state lithium-ion batteries (ASSLIBs), due to the good ionic conductivity and highly stable interface with Li metal. However, it still remains challenging to achieve high density and good ionic conductivity in LAGP pellets by using conventional sintering methods, because they required high temperatures (>800 °C) and long sintering time (>6 h), which could cause the loss of lithium, the formation of impurity phases, and thus the reduction of ionic conductivity. Herein, we report the utilization of a spark plasma sintering (SPS) method to synthesize LAGP pellets with a density of 3.477 g cm-3, a relative high density up to 97.6%, and a good ionic conductivity of 3.29 × 10-4 S cm-1. In contrast to the dry-pressing process followed with high-temperature annealing, the optimized SPS process only required a low operating temperature of 650 °C and short sintering time of 10 min. Despite the least energy and short time consumption, the SPS approach could still achieve LAGP pellets with high density, little voids and cracks, intimate grain-grain boundary, and high ionic conductivity. These advantages suggest the great potential of SPS as a fabrication technique for preparing solid electrolytes and composite electrodes used in ASSLIBs.

| S-EPMC6722947 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data