Influence of Sintering Temperature on the Microstructure and Mechanical Properties of In Situ Reinforced Titanium Composites by Inductive Hot Pressing.

ABSTRACT: This research is focused on the influence of processing temperature on titanium matrix composites reinforced through Ti, Al, and B₄C reactions. In order to investigate the effect of Ti-Al based intermetallic compounds on the properties of the composites, aluminum powder was incorporated into the starting materials. In this way, in situ TixAly were expected to form as well as TiB and TiC. The specimens were fabricated by the powder metallurgy technique known as inductive hot pressing (iHP), using a temperature range between 900 °C and 1400 °C, at 40 MPa for 5 min. Raising the inductive hot pressing temperature may affect the microstructure and properties of the composites. Consequently, the variations of the reinforcing phases were investigated. X-ray diffraction, microstructural analysis, and mechanical properties (Young's modulus and hardness) of the specimens were carried out to evaluate and determine the significant influence of the processing temperature on the behavior of the composites.

SUBMITTER: Arevalo C

PROVIDER: S-EPMC5457192 | biostudies-other | 2016 Nov

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:In this paper, the microstructure, the room-temperature and high-temperature tensile mechanical properties of monolithic TA15 alloy and TiB whisker-reinforced TA15 titanium matrix composites (TiBw/TA15) fabricated by vacuum hot-pressing sintering were investigated. The microstructure results showed that there were no obvious differences in the microstructure between monolithic TA15 alloy and TiBw/TA15 composites, except whether or not the grain boundaries contained TiBw. After sintering, the matrix microstructure presented a typical Widmanstätten structure and the size of primary β grain was consistent with the size of spherical TA15 titanium metallic powders. This result demonstrated that TiBw was not the only factor limiting grain coarsening of the primary β grain. Moreover, the grain coarsening of α colonies was obvious, and high-angle grain boundaries (HAGBs) were distributed within the primary β grain. In addition, TiBw played an important role in the microstructure evolution. In the composites, TiBw were randomly distributed in the matrix and surrounded by a large number of low-angle grain boundaries (LAGBs). Globularization of α phase occurred prior, near the TiBw region, because TiBw provided the nucleation site for the equiaxed α phase. The room-temperature and high-temperature tensile results showed that TiBw distributed at the primary β grain boundaries can strengthen the grain boundary, but reduce the connectivity of the matrix. Therefore, compared to the monolithic TA15 alloy fabricated by the same process, the tensile strength of the composites increased, and the tensile elongation decreased. Moreover, with the addition of TiBw, the fracture mechanism was changed to a mixture of brittle fracture and ductile failure (composites) from ductile failure (monolithic TA15 alloy). The fracture surfaces of TiBw/TA15 composites were the grain boundaries of the primary β grain where the majority of TiB whiskers distributed, i.e., the surfaces of the spherical TA15 titanium metallic powders.

Project description:Nano-carbon reinforced titanium matrix/hydroxyapatite (HA) biocomposites were successfully prepared by spark plasma sintering (SPS). The microstructure, mechanical properties, biocompatibility, and the relationship between microstructure and properties of biocomposites were systematically investigated. Results showed there are some new phases in sintered composites, such as ?-Ti, TiO?, ZrO?, etc. Moreover, a small amount of Ti17P10, CaTiO?, Ca?(PO?)? were also detected. The reaction that may occur during the preparation process is suppressed to some extent, which is because that the addition of second phases can prevent the direct contact of titanium with HA and reduce the contact areas. Transmission electron microscope (TEM) analysis proved the existence of elemental diffusion and chemical reactions in sintered composites. Compared with results of composites prepared by hot-pressed sintering before, mechanical properties (microhardness, compressive strength, and shear strength) of 0.5-GNFs composites prepared by SPS were increased by about 2.8, 4.8, and 4.1 times, respectively. The better mechanical properties of 0.5-GNFs composite in nano-carbon reinforced composites are mainly due to the lower degree of agglomeration of tubular carbon nanotubes (CNTs) compared to lamellar graphene nanoflakes (GNFs). Moreover, the strengthening and toughening mechanisms of nano-carbon reinforced titanium alloy/HA biocomposite prepared by spark plasma sintering (SPS) mainly included second phase strengthening, grain refinement strengthening, solution strengthening, graphene extraction, carbon nanotubes bridging, crack tail stripping, etc. In addition, in vitro bioactivity test revealed that the addition of nano-carbon was beneficial to promote the adhesion and proliferation of cells on the surface of titanium alloy/HA composite, because nano-carbon can enhance the formation of mineralized necks in the composites after transplantation, stimulate biomineralization and promote bone regeneration.

Dataset Information

Influence of Sintering Temperature on the Microstructure and Mechanical Properties of In Situ Reinforced Titanium Composites by Inductive Hot Pressing.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets