Compression Properties and Electrical Conductivity of In-Situ 20 vol.% Nano-Sized TiCx/Cu Composites with Different Particle Size and Morphology.

ABSTRACT: The compression properties and electrical conductivity of in-situ 20 vol.% nano-sized TiCx/Cu composites fabricated via combustion synthesis and hot press in Cu-Ti-CNTs system at various particles size and morphology were investigated. Cubic-TiCx/Cu composite had higher ultimate compression strength (σUCS), yield strength (σ0.2), and electric conductivity, compared with those of spherical-TiCx/Cu composite. The σUCS, σ0.2, and electrical conductivity of cubic-TiCx/Cu composite increased by 4.37%, 20.7%, and 17.8% compared with those of spherical-TiCx/Cu composite (526 MPa, 183 MPa, and 55.6% International Annealed Copper Standard, IACS). Spherical-TiCx/Cu composite with average particle size of ~94 nm exhibited higher ultimate compression strength, yield strength, and electrical conductivity compared with those of spherical-TiCx/Cu composite with 46 nm in size. The σUCS, σ0.2, and electrical conductivity of spherical-TiCx/Cu composite with average size of ~94 nm in size increased by 17.8%, 33.9%, and 62.5% compared with those of spherical-TiCx/Cu composite (417 MPa, 121 MPa, and 40.3% IACS) with particle size of 49 nm, respectively. Cubic-shaped TiCx particles with sharp corners and edges led to stress/strain localization, which enhanced the compression strength of the composites. The agglomeration of spherical-TiCx particles with small size led to the compression strength reduction of the composites.

SUBMITTER: Zhang D

PROVIDER: S-EPMC5459066 | biostudies-other | 2017 May

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

The electrical conductivity of Al2O3 under shock-compression.

Project description:Sapphire (Al2O3) crystals are used below 100 GPa as anvils and windows in dynamic-compression experiments because of their transparency and high density. Above 100 GPa shock pressures, sapphire becomes opaque and electrically conducting because of shock-induced defects. Such effects prevent temperature and dc conductivity measurements of materials compressed quasi-isentropically. Opacities and electrical conductivities at ~100 GPa are non-equilibrium, rather than thermodynamic parameters. We have performed electronic structure calculations as a guide in predicting and interpreting shock experiments and possibly to discover a window up to ~200 GPa. Our calculations indicate shocked sapphire does not metallize by band overlap at ~300 GPa, as suggested previously by measured non-equilibrium data. Shock-compressed Al2O3 melts to a metallic liquid at ~500 GPa and 10,000 K and its conductivity increases rapidly to ~2000 Ω(-1)cm(-1) at ~900 GPa. At these high shock temperatures and pressures sapphire is in thermal equilibrium. Calculated conductivity of Al2O3 is similar to those measured for metallic fluid H, N, O, Rb, and Cs. Despite different materials, pressures and temperatures, and compression techniques, both experimental and theoretical, conductivities of all these poor metals reach a common end state typical of strong-scattering disordered materials.

| S-EPMC4523845 | biostudies-literature

Influence of Nanoparticles on Thermal and Electrical Conductivity of Composites.

Project description:This review analyzes thermal and electrically conductive properties of composites and how they can be influenced by the addition of special nanoparticles. Composite functional characteristics-such as thermal and electrical conductivity, phase changes, dimensional stability, magnetization, and modulus increase-are tuned by selecting suitable nanoparticle filler material. The conductivity of composites can be related to the formation of conductive pathways as nanofiller materials form connections in the bulk of a composite matrix. With increasing use of nanomaterial containing composites and relatively little understanding of the toxicological effects thereof, adequate disposal and recyclability have become an increasing environmental concern.

| S-EPMC7240543 | biostudies-literature

Direction Dependent Electrical Conductivity of Polymer/Carbon Filler Composites.

Project description:The method of measuring electrical volume resistivity in different directions was applied to characterize the filler orientation in melt mixed polymer composites containing different carbon fillers. For this purpose, various kinds of fillers with different geometries and aspect ratios were selected, namely carbon black (CB), graphite (G) and expanded graphite (EG), branched multiwalled carbon nanotubes (b-MWCNTs), non-branched multiwalled carbon nanotubes (MWCNTs), and single-walled carbon nanotubes (SWCNTs). As it is well known that the shaping process also plays an important role in the achieved electrical properties, this study compares results for compression molded plates with random filler orientations in the plane as well as extruded films, which have, moreover, conductivity differences between extrusion direction and perpendicular to the plane. Additionally, the polymer matrix type (poly (vinylidene fluoride) (PVDF), acrylonitrile butadiene styrene (ABS), polyamide 6 (PA6)) and filler concentration were varied. For the electrical measurements, a device able to measure the electrical conductivity in two directions was developed and constructed. The filler orientation was analyzed using the ratio σin/th calculated as in-plane conductivity σin-plane (σin) divided by through-plane conductivity σthrough-plane (σth). The ratio σin/th is expected to increase with more pronounced filler orientation in the processing direction. In the extruded films, alignment within the plane was assigned by dividing the in-plane conductivity in the extrusion direction (x) by the in-plane conductivity perpendicular to the extrusion direction (y). The conductivity ratios depend on filler type and concentration and are higher the higher the filler aspect ratio and the closer the filler content is to the percolation concentration.

| S-EPMC6523830 | biostudies-other

Thermal Conductivity of Diamond/SiC Nano-Polycrystalline Composites and Phonon Scattering at Interfaces.

Project description:To compare the thermal properties of heterogeneous and homogeneous interfaces, polycrystalline composites are proposed. Thermal properties of heterogeneous and homogeneous interfaces in the composites are investigated using molecular dynamics simulations. The results indicate that when the inflow of heat arises from the same material, phonon scattering at heterogeneous interfaces is stronger than that at homogeneous interfaces. The phonon wave packet simulations indicate that the stronger phonon scattering at heterogeneous interfaces is caused by the combined actions of transmission coefficients and transmission time.

| S-EPMC6640988 | biostudies-literature

MMS6 protein regulates crystal morphology during nano-sized magnetite biomineralization in vivo.

Project description:Biomineralization, the process by which minerals are deposited by organisms, has attracted considerable attention because this mechanism has shown great potential to inspire bottom-up material syntheses. To understand the mechanism for morphological regulation that occurs during biomineralization, many regulatory proteins have been isolated from various biominerals. However, the molecular mechanisms that regulate the morphology of biominerals remain unclear because there is a lack of in vivo evidence. Magnetotactic bacteria synthesize intracellular magnetosomes that comprise membrane-enveloped single crystalline magnetite (Fe(3)O(4)). These nano-sized magnetite crystals (<100 nm) are bacterial species dependent in shape and size. Mms6 is a protein that is tightly associated with magnetite crystals. Based on in vitro experiments, this protein was first implicated in morphological regulation during nano-sized magnetite biomineralization. In this study, we analyzed the mms6 gene deletion mutant (Δmms6) of Magnetospirillum magneticum (M. magneticum) AMB-1. Surprisingly, the Δmms6 strain was found to synthesize the smaller magnetite crystals with uncommon crystal faces, while the wild-type and complementation strains synthesized highly ordered cubo-octahedral crystals. Furthermore, deletion of mms6 gene led to drastic changes in the profiles of the proteins tightly bound to magnetite crystals. It was found that Mms6 plays a role in the in vivo regulation of the crystal structure to impart the cubo-octahedral morphology to the crystals during biomineralization in magnetotactic bacteria. Magnetotactic bacteria synthesize magnetite crystals under ambient conditions via a highly controlled morphological regulation system that uses biological molecules.

| S-EPMC3057814 | biostudies-literature

Role of the particle size polydispersity in the electrical conductivity of carbon nanotube-epoxy composites.

Project description:Carbon nanotubes (CTNs) with large aspect-ratios are extensively used to establish electrical connectedness in polymer melts at very low CNT loadings. However, the CNT size polydispersity and the quality of the dispersion are still not fully understood factors that can substantially alter the desired characteristics of CNT nanocomposites. Here we demonstrate that the electrical conductivity of polydisperse CNT-epoxy composites with purposely-tailored distributions of the nanotube length L is a quasiuniversal function of the first moment of L. This finding challenges the current understanding that the conductivity depends upon higher moments of the CNT length. We explain the observed quasiuniversality by a combined effect between the particle size polydispersity and clustering. This mechanism can be exploited to achieve controlled tuning of the electrical transport in general CNT nanocomposites.

| S-EPMC5624922 | biostudies-literature

Tunneling Conductivity and Piezoresistivity of Composites Containing Randomly Dispersed Conductive Nano-Platelets.

Project description:In this study, a three-dimensional continuum percolation model was developed based on a Monte Carlo simulation approach to investigate the percolation behavior of an electrically insulating matrix reinforced with conductive nano-platelet fillers. The conductivity behavior of composites rendered conductive by randomly dispersed conductive platelets was modeled by developing a three-dimensional finite element resistor network. Parameters related to the percolation threshold and a power-low describing the conductivity behavior were determined. The piezoresistivity behavior of conductive composites was studied employing a reoriented resistor network emulating a conductive composite subjected to mechanical strain. The effects of the governing parameters, i.e., electron tunneling distance, conductive particle aspect ratio and size effects on conductivity behavior were examined.

| S-EPMC5453361 | biostudies-other

Fabrication of in-situ grown graphene reinforced Cu matrix composites.

Project description:Graphene/Cu composites were fabricated through a graphene in-situ grown approach, which involved ball-milling of Cu powders with PMMA as solid carbon source, in-situ growth of graphene on flaky Cu powders and vacuum hot-press sintering. SEM and TEM characterization results indicated that graphene in-situ grown on Cu powders guaranteed a homogeneous dispersion and a good combination between graphene and Cu matrix, as well as the intact structure of graphene, which was beneficial to its strengthening effect. The yield strength of 244 MPa and tensile strength of 274 MPa were achieved in the composite with 0.95 wt.% graphene, which were separately 177% and 27.4% enhancement over pure Cu. Strengthening effect of in-situ grown graphene in the matrix was contributed to load transfer and dislocation strengthening.

| S-EPMC4725871 | biostudies-other

Thermal Conductivity and Electrical Resistivity of Melt-Mixed Polypropylene Composites Containing Mixtures of Carbon-Based Fillers.

Project description:Melt-mixed composites based on polypropylene (PP) with various carbon-based fillers were investigated with regard to their thermal conductivity and electrical resistivity. The composites were filled with up to three fillers by selecting combinations of graphite nanoplatelets (GNP), carbon fibers (CF), carbon nanotubes (CNT), carbon black (CB), and graphite (G) at a constant filler content of 7.5 vol%. The thermal conductivity of PP (0.26 W/(m·K)) improved most using graphite nanoplatelets, whereas electrical resistivity was the lowest when using multiwalled CNT. Synergistic effects could be observed for different filler combinations. The PP composite, which contains a mixture of GNP, CNT, and highly structured CB, simultaneously had high thermal conductivity (0.5 W/(m·K)) and the lowest electrical volume resistivity (4 Ohm·cm).

| S-EPMC6630210 | biostudies-literature

Enhanced Thermoelectric Performance of Cu₂SnSe₃-Based Composites Incorporated with Nano-Fullerene.

Project description:In this study, nano-sized fullerene C60 powder was sufficiently mixed with Cu₂SnSe₃ powder by ball milling method, and the C60/Cu₂SnSe₃ composites were prepared by spark plasma sintering technology. The fullerene C60 distributed uniformly in the form of clusters, and the average cluster size was less than 1 μm. With increasing C60 content, the electrical conductivity of C60/Cu₂SnSe₃ composites decreased, while the Seebeck coefficient was enhanced. The thermal conductivity of composites decreased significantly, which resulted from the phonon scattering by the C60 clusters located on the grain boundaries of the Cu₂SnSe₃ matrix. The highest figure of merit ZT of 0.38 was achieved at 700 K for 0.8% C60/Cu₂SnSe₃ composite.

| S-EPMC5509047 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data