Effects of Incorporating High-Volume Fly Ash into Tricalcium Silicate on the Degree of Silicate Polymerization and Aluminum Substitution for Silicon in Calcium Silicate Hydrate.

ABSTRACT: This study assesses the quantitative effects of incorporating high-volume fly ash (HVFA) into tricalcium silicate (C₃S) paste on the hydration, degree of silicate polymerization, and Al substitution for Si in calcium silicate hydrate (C-S-H). Thermogravimetric analysis and isothermal conduction calorimetry showed that, although the induction period of C₃S hydration was significantly extended, the degree of hydration of C₃S after the deceleration period increased due to HVFA incorporation. Synchrotron-sourced soft X-ray spectromicroscopy further showed that most of the C₃S in the C₃S-HVFA paste was fully hydrated after 28 days of hydration, while that in the pure C₃S paste was not. The chemical shifts of the Si K edge peaks in the near-edge X-ray fine structure of C-S-H in the C₃S-HVFA paste directly indicate that Al substitutes for Si in C-S-H and that the additional silicate provided by the HVFA induces an enhanced degree of silicate polymerization. This new spectromicroscopic approach, supplemented with 27Al and 29Si magic-angle spinning nuclear magnetic resonance spectroscopy and transmission electron microscopy, turned out to be a powerful characterization tool for studying a local atomic binding structure of C-S-H in C₃S-HVFA system and presented results consistent with previous literature.

SUBMITTER: Bae S

PROVIDER: S-EPMC5459114 | biostudies-other | 2017 Feb

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Fly ash derived calcium silicate hydrate as a highly efficient and fast adsorbent for Cu(ii) ions: role of copolymer functionalization.

Project description:The environmental issues caused by heavy metal accumulation from polluted water are becoming serious and threaten human health and the ecosystem. The adsorption technology represented by calcium silicate hydrate has attracted much attention, but suffers from high manufacturing costs and poor stability bottlenecks. Here, we have proposed a "trash-to-treasure" conversion strategy to prepare a thin sheet calcium silicate hydrate material (ACSH) using solid waste fly ash as silicon source and a small amount of Acumer2000 as modifier. The obtained materials showed fast adsorption rates, superior adsorption capacities and remarkable long-term stability for Cu(ii) removal. Under the conditions of 0.5 g L-1 adsorbent concentration and 100 mL Cu(ii) solution with a concentration of 100 mg L-1, ACSH can adsorb 95.6% Cu(ii) within 5 min. The adsorption isotherms conformed to Langmuir models and the maximum adsorption capacity was 532 mg g-1. Using X-ray diffraction, scanning electron microscopy, X-ray photoelectron spectroscopy, Fourier transform infrared spectroscopy, specific surface area and pore structure analysis, it was found that the excellent adsorption performance could be attributed to the ultrahigh surface area (356 m2 g-1), abundant pores and multiple active sites induced by Acumer2000 modification. Moreover, the encapsulation effect from carboxylate and long carbon chains in Acumer2000 endowed modified samples with strong corrosion resistance to CO2, which effectively inhibited the formation of by-product CaCO3 and retained the remarkable adsorption performance for more than 100 days. Interestingly enough, the advantages of ACSH in economy and performance could been maintained in ACSH based adsorptive membranes. This work is of great significance for solid waste utilization as well as the preparation of high quality, cost-effective and long-term stability calcium silicate hydrate materials.

| S-EPMC9377387 | biostudies-literature

Recyclability of Concrete Pavement Incorporating High Volume of Fly Ash.

Project description:Recyclable concrete pavement was made from fly ash and crushed limestone sand and gravel as aggregates so that the concrete pavement could be recycled to raw materials for cement production. With the aim to use as much fly ash as possible for the sustainable development of society, while achieving adequate strength development, pavement concrete having a cement-replacement ratio of 40% by mass was experimentally investigated, focusing on the strength development at an early age. Limestone powder was added to improve the early strength; flexural strength at two days reached 3.5 MPa, the minimum strength for traffic service in Japan. The matured fly ash concrete made with a cement content of 200 kg/m3 achieved a flexural strength almost equal to that of the control concrete without fly ash. Additionally, Portland cement made from the tested fly ash concrete was tested to confirm recyclability, with the cement quality meeting the Japanese classification of ordinary Portland cement. Limestone-based recyclable fly ash concrete pavement is, thus, a preferred material in terms of sustainability.

| S-EPMC5455502 | biostudies-other

Multiscale understanding of tricalcium silicate hydration reactions.

Project description:Tricalcium silicate, the main constituent of Portland cement, hydrates to produce crystalline calcium hydroxide and calcium-silicate-hydrates (C-S-H) nanocrystalline gel. This hydration reaction is poorly understood at the nanoscale. The understanding of atomic arrangement in nanocrystalline phases is intrinsically complicated and this challenge is exacerbated by the presence of additional crystalline phase(s). Here, we use calorimetry and synchrotron X-ray powder diffraction to quantitatively follow tricalcium silicate hydration process: i) its dissolution, ii) portlandite crystallization and iii) C-S-H gel precipitation. Chiefly, synchrotron pair distribution function (PDF) allows to identify a defective clinotobermorite, Ca11Si9O28(OH)2.8.5H2O, as the nanocrystalline component of C-S-H. Furthermore, PDF analysis also indicates that C-S-H gel contains monolayer calcium hydroxide which is stretched as recently predicted by first principles calculations. These outcomes, plus additional laboratory characterization, yielded a multiscale picture for C-S-H nanocomposite gel which explains the observed densities and Ca/Si atomic ratios at the nano- and meso- scales.

| S-EPMC5986785 | biostudies-literature

Ab initio mechanism revealing for tricalcium silicate dissolution.

Project description:Dissolution of minerals in water is ubiquitous in nature and industry, especially for the calcium silicate species. However, the behavior of such a complex chemical reaction is still unclear at atomic level. Here, we show that the ab initio molecular dynamics and metadynamics simulations enable quantitative analyses of reaction pathways, thermodynamics and kinetics of the calcium ion dissolution from the tricalcium silicate (Ca3SiO5) surface. The calcium sites with different coordination environments lead to different reaction pathways and free energy barriers. The low free energy barriers result in that the detachment of the calcium ion is a ligand exchange and auto-catalytic process. Moreover, the water adsorption, proton exchange and diffusion of water into the surface layer accelerate the leaching of the calcium ion from the surface step by step. The discovery in this work thus would be a landmark for revealing the mechanism of tricalcium silicate hydration.

| S-EPMC8913775 | biostudies-literature

Synthesis and characterization of aluminosilicate and zinc silicate from sugarcane bagasse fly ash for adsorption of aflatoxin B1.

Project description:Sugarcane bagasse fly ash, a residual product resulting from the incineration of biomass to generate power and steam, is rich in SiO2. Sodium silicate is a fundamental material for synthesizing highly porous silica-based adsorbents to serve circular practices. Aflatoxin B1 (AFB1), a significant contaminant in animal feeds, necessitates the integration of adsorbents, crucial for reducing aflatoxin concentrations during the digestive process of animals. This research aimed to synthesize aluminosilicate and zinc silicate derived from sodium silicate based on sugarcane bagasse fly ash, each characterized by a varied molar ratio of aluminum (Al) to silicon (Si) and zinc (Zn) to silicon (Si), respectively. The primary focus of this study was to evaluate their respective capacities for adsorbing AFB1. It was revealed that aluminosilicate exhibited notably superior AFB1 adsorption capabilities compared to zinc silicate and silica. Furthermore, the adsorption efficacy increased with higher molar ratios of Al:Si for aluminosilicate and Zn:Si for zinc silicate. The N2 confirmed AFB1 adsorption within the pores of the adsorbent. In particular, the aluminosilicate variant with a molar ratio of 0.08 (Al:Si) showcased the most substantial AFB1 adsorption capacity, registering at 88.25% after an in vitro intestinal phase. The adsorption ability is directly correlated with the presence of surface acidic sites and negatively charged surfaces. Notably, the kinetics of the adsorption process were best elucidated through the application of the pseudo-second-order model, effectively describing the behavior of both aluminosilicate and zinc silicate in adsorbing AFB1.

| S-EPMC11196643 | biostudies-literature

Understanding silicate hydration from quantitative analyses of hydrating tricalcium silicates.

Project description:Silicate hydration is prevalent in natural and technological processes, such as, mineral weathering, glass alteration, zeolite syntheses and cement hydration. Tricalcium silicate (Ca3SiO5), the main constituent of Portland cement, is amongst the most reactive silicates in water. Despite its widespread industrial use, the reaction of Ca3SiO5 with water to form calcium-silicate-hydrates (C-S-H) still hosts many open questions. Here, we show that solid-state nuclear magnetic resonance measurements of (29)Si-enriched triclinic Ca3SiO5 enable the quantitative monitoring of the hydration process in terms of transient local molecular composition, extent of silicate hydration and polymerization. This provides insights on the relative influence of surface hydroxylation and hydrate precipitation on the hydration rate. When the rate drops, the amount of hydroxylated Ca3SiO5 decreases, thus demonstrating the partial passivation of the surface during the deceleration stage. Moreover, the relative quantities of monomers, dimers, pentamers and octamers in the C-S-H structure are measured.

| S-EPMC4820784 | biostudies-literature

Nanoscale silicate melt textures determine volcanic ash surface chemistry.

Project description:Explosive volcanic eruptions produce vast quantities of silicate ash, whose surfaces are subsequently altered during atmospheric transit. These altered surfaces mediate environmental interactions, including atmospheric ice nucleation, and toxic effects in biota. A lack of knowledge of the initial, pre-altered ash surface has required previous studies to assume that the ash surface composition created during magmatic fragmentation is equivalent to the bulk particle assemblage. Here we examine ash particles generated by controlled fragmentation of andesite and find that fragmentation generates ash particles with substantial differences in surface chemistry. We attribute this disparity to observations of nanoscale melt heterogeneities, in which Fe-rich nanophases in the magmatic melt deflect and blunt fractures, thereby focusing fracture propagation within aureoles of single-phase melt formed during diffusion-limited growth of crystals. In this manner, we argue that commonly observed pre-eruptive microtextures caused by disequilibrium crystallisation and/or melt unmixing can modify fracture propagation and generate primary discrepancies in ash surface chemistry, an essential consideration for understanding the cascading consequences of reactive ash surfaces in various environments.

| S-EPMC10789741 | biostudies-literature

Fly Ash from Lignite Combustion as a Filler for Rubber Mixes. Part I: Physical Valorization of Fly Ash.

Project description:The potential use of fly ash (FA) originating from lignite combustion at the Belchatow Power Plant (Poland) as filler for rubber mixes was evaluated. Samples of fly ash collected from heaps created in different years were compared according to their chemical and phase composition, particle size distribution, and morphology. The sieve fractionation of fly ash results in size fractions of different chemical structures, phase compositions, and morphologies, reflected in changes to their specific surface area, surface energy, and activity in rubber mixes. Fractionation turned out to be more effective than grinding from the point of view of using ash as a filler for rubber mixes, because it results in higher specific surface area (SSA) and chemical composition differentiation. Carbon black can be replaced by up to 40% by weight with the fly ash fraction (FFA) of dimensions below 125 µm, without any significant deterioration in the mechanical properties of styrene butadiene rubber (SBR) vulcanizates filled with 50 phr of active carbon black (N 220). Despite the larger fly ash fraction of grain dimensions in the range between 125 and 250 µm presenting the highest specific surface area, the particle size adversely affects its strengthening effect in rubber. Taking into account all the tests performed, ranging from morphology, Payne effect and bound rubber, to mechanical and abrasion tests, the highest potential effectivity is presented by a sample containing 30 phr of N 220 and 20 phr of FFA of grain sizes from 63 to 125 µm. The obtained results indicate that fractionation seems to be an effective physical method of fly ash valorization.

| S-EPMC9324915 | biostudies-literature

Remineralization of early enamel lesions with a novel prepared tricalcium silicate paste.

Project description:To evaluate the remineralization potential of prepared tricalcium silicate (TCS) paste compared to silver diamine fluoride-potassium iodide (SDF-KI) and casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) on artificial enamel lesions. Thirty permanent sound molars were collected for the study. After cleaning, root cutting, and applying acid-resistant nail varnish, leaving a 4 × 4 mm buccal window, the teeth were subjected to demineralization process. The teeth were divided into three treatment groups (n = 10). In each group, the teeth were sectioned buccolingually to obtain two halves (30 self-control and 30 experimental halves). The self-control halves were subjected to cross-sectional microhardness (CSMH), energy-dispersive X-ray spectroscopy at 50, 100, and 150 µm from the external enamel surface, and micromorphological analysis at the superficial enamel surface. The experimental halves were subjected to the same tests after 30 days of remineralization. Three-way analysis of variance (ANOVA) outcomes showed no significant difference in CSMH after treatment among the three different groups at the different levels (p > 0.05). Meanwhile, three-way ANOVA outcomes showed a significant difference in calcium/ phosphate ratio after treatment among the three different groups at the different levels. (p < 0.05). The tricalcium silicate paste used in this study showed potential remineralization in subsurface enamel lesions.

| S-EPMC9200717 | biostudies-literature

Characterization, Physical Properties, and Biocompatibility of Novel Tricalcium Silicate-Chitosan Endodontic Sealer.

Project description:Objective The purpose of this study was to compare the characteristics, physical properties, and biocompatibility of the novel tricalcium silicate-chitosan (TCS-C) sealer with AH Plus and Sure-Seal Root.Materials and methods The TCS-C powder was prepared by mixing tricalcium silicate with 2% water-soluble chitosan at a 5:1 ratio, followed by sufficient addition of 10 g/mL ratio of double-distilled water to form a homogeneous cement. Material characterizations (the Fourier Transform InfraRed [FTIR] and X-ray diffraction [XRD]), physical property investigations (flow and film thickness), and cytotoxicity tests in 3T3 mouse embryo fibroblast cell (MTT assay method) were performed on sealers, and the results were compared with those of the commercial products.Statistical analysis Statistical analysis was performed on flow and film thickness. The normality of the data was tested using the Shapiro-Wilk test. Statistical analysis was performed with one-way analysis of variance (ANOVA). The level of significance was set at p < 0.05.Results The TCS-C showed a mean flow of 31.98 ± 0.68 mm, compared with Sure Seal Root at 26.38 ± 0.69 mm and AH Plus at 26.50 ± 0.12 mm. The TCS-C showed a mean film thickness of 60 ± 10.0 mm compared with Sure-Seal Root at 50 ± 10.0 mm and AH Plus at 40 ± 15.8 mm. The TCS-C exhibited low to no cytotoxicity in fibroblast cell at all concentrations and exposure times.Conclusion Adding water-soluble chitosan may improve the physical and biologic properties of tricalcium silicate cement. The novel TCS-C sealer did not fully meet the physical properties of an endodontic sealer, but it was not cytotoxic to fibroblast cells.

| S-EPMC9949928 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data