The Effect of Welding Energy on the Microstructural and Mechanical Properties of Ultrasonic-Welded Copper Joints.

ABSTRACT: The effects of welding energy on the mechanical and microstructural characteristics of ultrasonic-welded pure copper plates were investigated. Complex dynamic recrystallization and grain growth occurred inside the weld zone during ultrasonic welding. At a low welding energy, a thin band of straight weld interfaces was observed and had an ultra-fine grain structure. With an increase in welding energy, the weld interface progressively changed from flat to sinusoidal, and eventually turned into a convoluted wavy pattern, bearing similarities to shear instabilities, as observed in fluid dynamics. The lap shear load of the joints initially increased and then remained stable as the welding energy increased. The tensile characteristics of the joints significantly depended on the development of plastic deformation at the interface. The influence of the microstructure on the hardness was also discussed.

SUBMITTER: Yang J

PROVIDER: S-EPMC5459195 | biostudies-other | 2017 Feb

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Microstructure and Mechanical Properties of an Ultrasonic Spot Welded Aluminum Alloy: The Effect of Welding Energy.

Project description:The aim of this study is to evaluate the microstructures, tensile lap shear strength, and fatigue resistance of 6022-T43 aluminum alloy joints welded via a solid-state welding technique-ultrasonic spot welding (USW)-at different energy levels. An ultra-fine necklace-like equiaxed grain structure is observed along the weld line due to the occurrence of dynamic crystallization, with smaller grain sizes at lower levels of welding energy. The tensile lap shear strength, failure energy, and critical stress intensity of the welded joints first increase, reach their maximum values, and then decrease with increasing welding energy. The tensile lap shear failure mode changes from interfacial fracture at lower energy levels, to nugget pull-out at intermediate optimal energy levels, and to transverse through-thickness (TTT) crack growth at higher energy levels. The fatigue life is longer for the joints welded at an energy of 1400 J than 2000 J at higher cyclic loading levels. The fatigue failure mode changes from nugget pull-out to TTT crack growth with decreasing cyclic loading for the joints welded at 1400 J, while TTT crack growth mode remains at all cyclic loading levels for the joints welded at 2000 J. Fatigue crack basically initiates from the nugget edge, and propagates with "river-flow" patterns and characteristic fatigue striations.

| S-EPMC5458998 | biostudies-other

The Effect of Ultrasonic Peening Treatment on Fatigue Performance of Welded Joints.

Project description:Ultrasonic peening treatment (UPT) as a method of severe plastic deformation was used to treat cruciform welded joints of Q345 steel. The application of UPT achieves material surface nanocrystallization of the peening zone, reduces stress concentration, and produces residual compressive stresses at the welded toe. Micro-structure, hardness, stress relief, S-N curve, and the fatigue fracture mechanism of cruciform welded joint of Q345 steel, both before and after UPT, were analyzed in detail. The main results show that: stress concentration and residual tensile stress are the main reasons to reduce fatigue strength of cruciform welded joints. The fatigue life of cruciform welded joints is improved for surface hardening, compressive stress, and grain refinement by UPT. Residual compressive stress caused by UPT is released with the increase of fatigue life. A very significant fatigue strength improvement happens when UPT is replenished repeatedly after a certain number of cycles.

| S-EPMC5456831 | biostudies-other

EBSD Characterization of the Microstructure of 7A52 Aluminum Alloy Joints Welded by Friction Stir Welding.

Project description:The microstructure and texture of materials significantly influence the mechanical properties and fracture behavior; the effect of microstructure in different zones of friction stir-welded joints of 7A52 aluminum alloy on fracture behavior was investigated in this paper. The microstructural characteristics of sections of the welded joints were tested using the electron backscattered diffraction (EBSD) technique. The results indicate that the fracture is located at the advancing side of the thermomechanically affected zone (AS-TMAZ) and the stir zone (SZ) interface. The AS-TMAZ microstructure is vastly different from the microstructure and texture of other areas. The grain orientation is disordered, and the grain shape is seriously deformed under the action of stirring force. The grain size grows unevenly under the input of friction heat, resulting in a large amount of recrystallization, and there is a significant difference in the Taylor factor between adjacent grains and the AS-TMAZ-SZ interface. On the contrary, there are fine and uniform equiaxed grains in the nugget zone, the microstructure is uniform, and the Taylor factor is small at adjacent grains. Therefore, the uneven transition of microstructure and texture in the AS-TMAZ and the SZ provide conditions for crack initiation, which become the weak point of mechanical properties.

| S-EPMC8585471 | biostudies-literature

Microstructure and Mechanical Properties of Welded Joints of 1.4462 Duplex Steel Made by the K-TIG Method.

Project description:K-TIG (Keyhole Tungsten Inert Gas) method is a new, emerging welding technology that offers a significant acceleration of the joining process, even for very thick plates. However, its potential for welding of certain materials is still unknown. Particularly challenging are duplex steels as this technology does not allow the use of a filler material, which is crucial for these steels and for weld joint microstructure adjustment. In order to demonstrate the suitability of this technology for single-pass welding of 1.4462 duplex steel detailed studies of the microstructure of the weld joints obtained for different linear energies were carried out and discussed with respect to their mechanical properties. According to the results obtained, the heat-affected zone (HAZ) shows a microstructure similar to the HAZ of duplex steel welded with the traditional TIG multi-pass methods. However, the weld, due to the lack of filler material, had a microstructure different to that typical for duplex steel welded joints and was also characterized by an increased content of ferrite. However, all joints, both in terms of microstructure and mechanical properties, met the requirements of the relevant standards. Moreover, the K-TIG process can be carried out in the linear energy range typical of duplex steel welding, although further optimization is needed.

| S-EPMC8708518 | biostudies-literature

Spark plasma welding joining of copper- AISI4140 steel: Microstructures and mechanical properties

Project description: Not available

| S-EPMC10641177 | biostudies-literature

Microstructural Characterization and Mechanical Behavior of NiTi Shape Memory Alloys Ultrasonic Joints Using Cu Interlayer.

Project description:NiTi shape memory alloys (SMAs) are a class of functional materials which can be significantly deformed and recover their original shape via a reversible martensitic phase transformation. Developing effective joining techniques can expand the application of SMAs in the medical and engineering fields. In this study, ultrasonic spot welding (USW), a solid-state joining technique, was used to join NiTi sheets using a Cu interlayer in between the two joining sheets. The influence of USW process on the microstructural characteristics and mechanical behavior of the NiTi joints was investigated. Compared with conventional fusion welding techniques, no intermetallic compounds formed in the joints, which is extreme importance for this particular class of alloys. The joining mechanisms involve a combination of shear plastic deformation, mechanical interlocking and formation of micro-welds. A better bonding interface was obtained with higher welding energy levels, which contributed to a higher tensile load. An interfacial fracture mode occurred and the fracture surfaces exhibited both brittle and ductile-like characteristics with the existence of tear ridges and dimples. The fracture initiated at the weak region of the joint border and then propagated through it, leading to tearing of Cu foil at the fracture interface.

| S-EPMC6213582 | biostudies-other

Fabrication and Mechanical Properties of Tungsten Inert Gas Welding Ring Welded Joint of 7A05-T6/5A06-O Dissimilar Aluminum Alloy.

Project description:In this paper, Tungsten Inert Gas Welding (TIG) and single-sided welding and double-sided forming have been used to weld the 7A05-T6/5A06-O dissimilar aluminum alloy circular welded joint of a ring-stiffened closed cylindrical sandwich shell. Microstructural characterization and mechanical properties of welded joints were investigated by use of scanning electron microscopy (SEM), backscatter electron diffraction (EBSD) and transmission electron microscopy (TEM), respectively. Hardness distribution and tensile properties of the welded joints were examined. The results showed the failure of the welded joints produced in the fusion zone (FZ). The tensile strength and yield strength of the welded joints were, respectively, 78.87% and 97.24% of the 5A06-O base metal (BM), and the elongation reached 84.29% of 7A05-T6 base metal. Welding high heat input led to the coarse grain size in the fusion zone, and the long-term similar quenching effect can lead to the full dissolution of the strengthening zone of the fusion zone resulting in the reductions of strength and hardness. Around 7A05 heat-affected zone (HAZ), there is an obvious hardening zone and softening zone, the solid solution precipitates into the Rayleigh brilliant η′ (MgZn₂) phase, which results in natural aging strengthening, thus obtaining high hardness. η′ (MgZn₂) enhanced phase dissolved fully and the dislocation density decreased rapidly in the HAZ region resulted in a softening zone with a lower hardness at about (10⁻18) mm from the center of the weld center.

| S-EPMC6073191 | biostudies-literature

Analysis of Selected Properties of Welded Joints of the HSLA Steels.

Project description:This paper presents research of the impact toughness and hardness distribution in specific zones of a 'single V'butt multiple-pass welded joints of the high-strength low-alloyed steels. Obtained values of the impact toughness are analyzed in correlation with a microstructure in specific zones of the welded joint, together with the micro hardness distribution found in the related zones. Based on the carried out analysis and results obtained in experiments, the applied technology of welding was evaluated. The original conclusions on influence of the selected welding procedure manual metal arc (MMA) for the root passes and metal active gas (MAG) for the filling and covering passes) on impact toughness of the high-strength low-alloyed steels are drawn. The paper also presents discussion on the valid standards and recommendations related to welding of those steels, from the aspect of applications in design of steel welded constructions.

| S-EPMC7143795 | biostudies-literature

Microstructure and Mechanical Properties of Butt Joints between Stainless Steel SUS304L and Aluminum Alloy A6061-T6 by TIG Welding.

Project description:The tungsten inert gas (TIG) welding method most commonly used to weld ferrous metals, nonferrous metals, and other metals since it is simple, easily implemented, and achieves consistent high-quality welds. In this study, butt joints produced between aluminum alloy A6061-T6 and stainless steel SUS304L have been achieved by using TIG welding with ER4047 filler metal. The macrostructure and microstructure of the resulting specimens were analyzed by means of an optical microscope (OM), a scanning electron microscope (SEM), and an energy dispersive X-ray spectrometer (EDS). A uniform intermetallic layer was found at the interface between the stainless steel and the weld seam having a thickness of 2 µm, and the intermetallic compound (IMC) includes Fe?Al13, Fe?Al?, and FeAl? phases. The micro-hardness and tensile strength of the weld joints were also investigated. Due to Si content in the compensating metal, there was a prevention of iron diffusion into the aluminum, thus hindering the development of the IMC layer and reducing its thickness in such a way that the weld joint strength increases. The analyzed results show that the average micro-hardness of the stainless steel, weld seam, aluminum alloys, and IMC layer were 218 HV, 88.3 HV, 63.3 HV, and 411 HV, respectively. The fracture occurred at the brazed interface, and the ultimate tensile strength value reached 225 MPa.

| S-EPMC6073269 | biostudies-literature

TEM Microstructure, Mechanical Properties and Temperature Estimation in the 5XXX Series Al-Mg-Si Aluminum Alloy with W-Ni-Fe Tungsten Composite Friction-Welded Joints.

Project description:The temperature distributions, microstructure, and mechanical properties of tungsten composite with aluminum alloy friction-welded joints are presented in this paper. The effects of welding parameters on flash diameter, shortening, joint efficiency, microhardness, and microstructure were studied. Empirical temperature models for heating and cooling phases are proposed in this study. The predicted maximum temperatures at the periphery and in the axis of aluminum specimens were close to 550 °C and 480 °C at the interface, respectively. Moreover, the peak temperature in the weld zone was studied analytically. A maximum tensile strength of 234 MPa was reached for the following welding parameters: friction time of 3.5 s and friction force of 12.5 kN. The efficiency of the welded samples decreased after reaching the maximum value, with an increase of friction time and force. Maximum hardness at the interface and the half-radius reached 100 HV and 80 HV in the aluminum alloy joints, respectively. Dynamic recrystallisation areas on the aluminum alloy side were observed. Transmission electron microscopy observations of the microstructure in the aluminum alloy revealed the presence of a high dislocation density compared to the parent material.

| S-EPMC8839506 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data