Evaluation of Functionalized Porous Titanium Implants for Enhancing Angiogenesis in Vitro.
Ontology highlight
ABSTRACT:
SUBMITTER: Roland L
PROVIDER: S-EPMC5502997 | biostudies-other | 2016 Apr
REPOSITORIES: biostudies-other
Similar Datasets
Project description:Titanium is widely used as a bone implant material due to its biocompatibility and high resilience. Since its Young's modulus differs from bone tissue, the resulting "stress shielding" could lead to scaffold loosening. However, by using a scaffold-shaped geometry, the Young's modulus can be adjusted. Also, a porous geometry enables vascularisation and bone ingrowth inside the implant itself. Additionally, growth factors can improve these effects. In order to create a deposit and release system for these factors, the titanium scaffolds could be coated with degradable polymers. Therefore, in the present study, synthetic poly-?-caprolactone (PCL) and the biopolymer poly(3-hydroxybutyrate) (P(3HB)) were tested for coating efficiency, cell adhesion, and biocompatibility to find a suitable coating material. The underlying scaffold was created from titanium by Selective Laser Melting (SLM) and coated with PCL or P(3HB) via dip coating. To test the biocompatibility, Live Cell Imaging (LCI) as well as vitality and proliferation assays were performed. In addition, cell adhesion forces were detected via Single Cell Force Spectroscopy, while the coating efficiency was observed using environmental scanning electron microscopy (ESEM) and energy-dispersive X-ray (EDX) analyses. Regarding the coating efficiency, PCL showed higher values in comparison to P(3HB). Vitality assays revealed decent vitality values for both polymers, while values for PCL were significantly lower than those for blank titanium. No significant differences could be observed between PCL and P(3HB) in proliferation and cell adhesion studies. Although LCI observations revealed decreasing values in cell number and populated area over time on both polymer-coated scaffolds, these outcomes could be explained by the possibility of coating diluent residues accumulating in the culture medium. Overall, both polymers fulfill the requirements regarding biocompatibility. Nonetheless, since only PCL coating ensured the maintenance of the porous implant structure, it is preferable to be used as a coating material for creating a deposit and release system for growth factors.
| S-EPMC5744279 | biostudies-literature
Project description:PurposeComplex bony orbital defects are reconstructively challenging due to loss of intraoperative anatomical landmarks and adjacent support. Presized and precontoured porous polyethylene-titanium implants (Medpor Titan 3D Orbital Floor Implant) are designed to reestablish normal orbital floor and medial wall anatomy and are modeled after anatomically averaged orbits. This is the first study to report clinical outcomes with this implant.MethodsThis retrospective case series reviewed clinical data and outcomes for patients undergoing orbital reconstruction with a presized and precontoured porous polyethylene-titanium orbital implant from January 2016 to June 2018.ResultsA total of 34 orbits of 33 patients were identified (mean age: 43 ± 16 years, 70% men). Most bony defects were a result of trauma and included large orbital floor deformities (100%), medial wall defects (74%), disrupted inferomedial struts (68%), and broken posterior ledges (82%). Symptomatic diplopia (73%) and enophthalmos (89%, mean: 3.7 ± 2.1 mm) were common preoperatively. Many cases were revisions (44%). Mean follow up was 7.8 ± 6.7 months. All patients had improved globe positioning, enophthalmos, and hypoglobus. Seven patients had persistent postoperative diplopia: 6 responded to prism therapy and 1 required strabismus surgery. One patient required retrobulbar hematoma drainage and 1 patient required implant explantation due to chronic infection.ConclusionsCommercially available presized and precon toured porous polyethylene-titanium implants are useful for complex orbital bony defects and can achieve functional improve ments in diplopia, enophthalmos, and extraocular motility with a low incidence of postoperative complications or revisional surgery.
| S-EPMC7982351 | biostudies-literature
Project description:BackgroundThe improvement of bone ingrowth into prosthesis and enhancement of the combination of the range between the bone and prosthesis are important for long-term stability of artificial joints. They are the focus of research on uncemented artificial joints. Porous materials can be of potential use to solve these problems.Objectives/purposesThis research aims to observe the characteristics of the new porous Ti-25Nb alloy and its biocompatibility in vitro, and to provide basic experimental evidence for the development of new porous prostheses or bone implants for bone tissue regeneration.MethodsThe Ti-25Nb alloys with different porosities were fabricated using powder metallurgy. The alloys were then evaluated based on several characteristics, such as mechanical properties, purity, pore size, and porosity. To evaluate biocompatibility, the specimens were subjected to methylthiazol tetrazolium (MTT) colorimetric assay, cell adhesion and proliferation assay using acridine staining, scanning electron microscopy, and detection of inflammation factor interleukin-6 (IL-6).ResultsThe porous Ti-25Nb alloy with interconnected pores had a pore size of 200 µm to 500 µm, which was favorable for bone ingrowth. The compressive strength of the alloy was similar to that of cortical bone, while with the elastic modulus closer to cancellous bone. MTT assay showed that the alloy had no adverse reaction to rabbit bone marrow mesenchymal stem cells, with a toxicity level of 0 to 1. Cell adhesion and proliferation experiments showed excellent cell growth on the surface and inside the pores of the alloy. According to the IL-6 levels, the alloy did not cause any obvious inflammatory response.ConclusionAll porous Ti-25Nb alloys showed good biocompatibility regardless of the percentage of porosity. The basic requirement of clinical orthopedic implants was satisfied, which made the alloy a good prospect for biomedical application. The alloy with 70% porosity had the optimum mechanical properties, as well as suitable pore size and porosity, which allowed more bone ingrowth.
| S-EPMC3834032 | biostudies-literature
Project description:PurposeThe reconstruction of a tendon insertion on metal prostheses is a challenge in orthopedics. Of the available metal prostheses, porous metal prostheses have been shown to have better biocompatibility for tissue integration. Therefore, this study is aimed at identifying an appropriate porous structure for the reconstruction of a tendon insertion on metal prostheses.MethodsTi6Al4V specimens with a diamond-like porous structure with triply periodic minimal surface pore sizes of 300, 500, and 700 μm and a porosity of 58% (designated Ti300, Ti500, and Ti700, respectively) were manufactured by selective laser melting and were characterized with micro-CT and scanning electron microscopy for their porosity, pore size, and surface topography. The porous specimens were implanted into the patellar tendon of rabbits. Tendon integration was evaluated after implantation into the tendon at 4, 8, and 12 weeks by histology, and the fixation strength was evaluated with a pull-out test at week 12.ResultsThe average pore sizes of the Ti300, Ti500, and Ti700 implants were 261, 480, and 668 μm, respectively. The Ti500 and Ti700 implants demonstrated better tissue growth than the Ti300 implant at weeks 4, 8, and 12. At week 12, the histological score of the Ti500 implant was 13.67 ± 0.58, and it had an area percentage of type I collagen of 63.90% ± 3.41%; both of these results were significantly higher than those for the Ti300 and Ti700 implants. The pull-out load at week 12 was also the highest in the Ti500 group.ConclusionTi6Al4V implants with a diamond-like porous structure with triply periodic minimal surface pore size of 500 μm are suitable for tendon integration.
| S-EPMC9061050 | biostudies-literature
Project description:Material properties of implants such as volume porosity and nanoscale surface modification have been shown to enhance cell-material interactions in vitro and osseointegration in vivo. Porous tantalum (Ta) and titanium (Ti) coatings are widely used for non-cemented implants, which are fabricated using different processing routes. In recent years, some of those implants are being manufactured using additive manufacturing. However, limited knowledge is available on direct comparison of additively manufactured porous Ta and Ti structures towards early stage osseointegration. In this study, we have fabricated porous Ta and Ti6Al4V (Ti64) implants using laser engineered net shaping (LENS™) with similar volume fraction porosity to compare the influence of surface characteristics and material chemistry on in vivo response using a rat distal femur model for 5 and 12 weeks. We have also assessed whether surface modification on Ti64 can elicit similar in vivo response as porous Ta in a rat distal femur model for 5 and 12 weeks. The harvested implants were histologically analyzed for osteoid surface per bone surface. Field emission scanning electron microscopy (FESEM) was done to assess the bone-implant interface. The results presented here indicate comparable performance of porous Ta and surface modified porous Ti64 implants towards early stage osseointegration at 5 weeks post implantation through seamless bone-material interlocking. However, a continued and extended efficacy of porous Ta is found in terms of higher osteoid formation at 12 weeks post-surgery.
| S-EPMC6690615 | biostudies-literature
Project description:Titanium is widely used in bone prostheses due to its excellent biocompatibility and osseointegration capacity. To understand the effect of sandblasted acid-etched (SAE) Ti implants on the biological responses of human osteoblast (HOb), their proteomic profiles were analysed using nLC-MS/MS. The cells were cultured with the implant materials, and 2544 distinct proteins were detected in samples taken after 1, 3 and 7 days. Comparative analyses of proteomic data were performed using Perseus software. The expression of proteins related to EIF2, mTOR, insulin-secretion and IGF pathways showed marked differences in cells grown with SAE-Ti in comparison with cells cultured without Ti. Moreover, the proteomic profiles obtained with SAE-Ti were compared over time. The affected proteins were related to adhesion, immunity, oxidative stress, coagulation, angiogenesis, osteogenesis and extracellular matrix formation functions. The proliferation, mineralisation and osteogenic gene expression in HObs cultured with SAE-Ti were characterised in vitro. The results showed that the osteoblasts exposed to this material increase their mineralisation rate and expression of COLI, RUNX2, SP7, CTNNB1, CAD13, IGF2, MAPK2 and mTOR. Overall, the observed proteomic profiles can explain the SAE-Ti osteogenic properties, widening our knowledge of key signalling pathways taking part in the early stages of the osseointegration process in this type of implantations.
2023-03-11 | PXD035986 | Pride
Project description:Although titanium alloys remain the preferred biomaterials for the manufacture of biomedical implants today, such devices can fail within 15?years of implantation due to inadequate osseointegration. Furthermore, wear debris toxicity due to alloy metal ion release has been found to cause side-effects including neurotoxicity and chronic inflammation. Titanium, with its known biocompatibility, corrosion resistance, and high elastic modulus, could if harnessed in the form of a superficial scaffold or bridging device, resolve such issues. A novel three-dimensional culture approach was used to investigate the potential osteoinductive and osseointegrative capabilities of a laser-generated microporous, microrough medical grade IV titanium template on human skeletal stem cells (SSCs). Human SSCs seeded on a rough 90-µm pore surface of ethylene oxide-sterilized templates were observed to be strongly adherent, and to display early osteogenic differentiation, despite their inverted culture in basal conditions over 21?days. Limited cellular migration across the template surface highlighted the importance of high surface wettability in maximizing cell adhesion, spreading and cell-biomaterial interaction, while restricted cell ingrowth within the conical-shaped pores underlined the crucial role of pore geometry and size in determining the extent of osseointegration of an implant device. The overall findings indicate that titanium only devices, with appropriate optimizations to porosity and surface wettability, could yet play a major role in improving the long-term efficacy, durability, and safety of future implant technology.
| S-EPMC5732141 | biostudies-literature
Project description:Titanium is widely used in bone prostheses due to its excellent biocompatibility and osseointegration capacity. To understand the effect of sandblasted acid-etched (SAE) Ti implants on the biological responses of human osteoblast (HOb), their proteomic profiles were analyzed using nLC-MS/MS. The cells were cultured with the implant materials, and 2544 distinct proteins were detected in samples taken after 1, 3, and 7 days. Comparative analyses of proteomic data were performed using Perseus software. The expression of proteins related to EIF2, mTOR, insulin-secretion and IGF pathways showed marked differences in cells grown with SAE-Ti in comparison with cells cultured without Ti. Moreover, the proteomic profiles obtained with SAE-Ti were compared over time. The affected proteins were related to adhesion, immunity, oxidative stress, coagulation, angiogenesis, osteogenesis, and extracellular matrix formation functions. The proliferation, mineralization and osteogenic gene expression in HObs cultured with SAE-Ti were characterized in vitro. The results showed that the osteoblasts exposed to this material increase their mineralization rate and expression of COLI, RUNX2, SP7, CTNNB1, CAD13, IGF2, MAPK2, and mTOR. Overall, the observed proteomic profiles can explain the SAE-Ti osteogenic properties, widening our knowledge of key signaling pathways taking part in the early stages of the osseointegration process in this type of implantations.
| S-EPMC9804409 | biostudies-literature
Project description:An increasing interest in the fabrication of implants made of titanium and its alloys results from their capacity to be integrated into the bone system. This integration is facilitated by different modifications of the implant surface. Here, we assessed the bioactivity of amorphous titania nanoporous and nanotubular coatings (TNTs), produced by electrochemical oxidation of Ti6Al4V orthopedic implants' surface. The chemical composition and microstructure of TNT layers was analyzed by X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD). To increase their antimicrobial activity, TNT coatings were enriched with silver nanoparticles (AgNPs) with the chemical vapor deposition (CVD) method and tested against various bacterial and fungal strains for their ability to form a biofilm. The biointegrity and anti-inflammatory properties of these layers were assessed with the use of fibroblast, osteoblast, and macrophage cell lines. To assess and exclude potential genotoxicity issues of the fabricated systems, a mutation reversal test was performed (Ames Assay MPF, OECD TG 471), showing that none of the TNT coatings released mutagenic substances in long-term incubation experiments. The thorough analysis performed in this study indicates that the TNT5 and TNT5/AgNPs coatings (TNT5-the layer obtained upon applying a 5 V potential) present the most suitable physicochemical and biological properties for their potential use in the fabrication of implants for orthopedics. For this reason, their mechanical properties were measured to obtain full system characteristics.
| S-EPMC7073575 | biostudies-literature
Project description:Tumor resection and treatment of trauma-related regional large bone defects have major challenges in the field of orthopedics. Scaffolds that treat bone defects are the focus of bone tissue engineering. 3D printing porous titanium alloy scaffolds, prepared via electron beam melting technology, possess customized structure and strength. The addition of a growth factor coating to the scaffold introduces a specific form of biological activation. Vascular endothelial growth factor (VEGF) is key to angiogenesis and osteogenesis in vivo. We designed a porous titanium alloy scaffold/thermosensitive collagen hydrogel system, equipped with VEGF, to promote local osseointegration and angiogenesis. We also verified the VEGF release via thermosensitive collagen and proliferation and induction of the human umbilical vein endothelial cells (HUVECs) via the composite system in vitro. In vivo, using microscopic computed tomography (Micro-CT), histology, and immunohistochemistry analysis, we confirmed that the composite scaffold aids in angiogenesis-mediated bone regeneration, and promotes significantly more bone integration. We also discovered that the composite scaffold has excellent biocompatibility, provides bioactive VEGF for angiogenesis and osteointegration, and provides an important theoretical basis for the restoration of local blood supply and strengthening of bone integration.
| S-EPMC8634467 | biostudies-literature