The Effect of ZrO₂ Nanoparticles on the Microstructure and Properties of Sintered WC-Bronze-Based Diamond Composites.

ABSTRACT: Metal matrix-impregnated diamond composites are widely used in diamond tool manufacturing. In order to satisfy the increasing engineering requirements, researchers have paid more and more attention to enhancing conventional metal matrices by applying novel methods. In this work, ZrO₂ nanoparticles were introduced into the WC-bronze matrix with and without diamond grits via hot pressing to improve the performance of conventional diamond composites. The effects of ZrO₂ nanoparticles on the microstructure, density, hardness, bending strength, and wear resistance of diamond composites were investigated. The results indicated that the hardness and relative density increased, while the bending strength decreased when the content of ZrO₂ nanoparticles increased. The grinding ratio of diamond composites increased significantly by 60% as a result of nano-ZrO₂ addition. The enhancement mechanism was discussed. Diamond composites showed the best overall properties with the addition of 1 wt % ZrO₂ nanoparticles, thus paving the way for further applications.

SUBMITTER: Sun Y

PROVIDER: S-EPMC5503043 | biostudies-other | 2016 May

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Effect of Curing Rate on the Microstructure and Macroscopic Properties of Epoxy Fiberglass Composites.

Project description:Curing rates of an epoxy amine system were varied via different curing cycles, and glass-fiber epoxy composites were prepared using the same protocol, with the aim of investigating the correlation between microstructure and composite properties. It was found that the fast curing cycle resulted in a non-homogenous network, with a larger percentage of a softer phase. Homogenized composite properties, namely storage modulus and quasi-static intra-laminar shear strength, remained unaffected by the change in resin microstructure. However, fatigue tests revealed a significant reduction in fatigue life for composites cured at fast curing rates, while composites with curing cycles that allowed a pre-cure until the critical gel point, were unaffected by the rate of reaction. This result was explained by the increased role of epoxy microstructure on damage initiation and propagation in the matrix during fatigue life. Therefore, local non-homogeneities in the epoxy matrix, corresponding to regions with variable crosslink density, can play a significant role in limiting the fatigue life of composites and must be considered in the manufacturing of large scale components, where temperature gradients and significant exotherms are expected.

| S-EPMC6415024 | biostudies-literature

The Hardness and Strength Properties of WC-Co Composites.

Project description:The industrially-important WC-Co composite materials provide a useful, albeit complicated materials system for understanding the combined influences on hardness and strength properties of the constituent WC particle strengths, the particle sizes, their contiguities, and of Co binder hardness and mean free paths, and in total, the volume fraction of constituents. A connection is made here between the composite material properties, especially including the material fracture toughness, and the several materials-type considerations of: (1) related hardness stress-strain behaviors; (2) dislocation (viscoplastic) thermal activation characterizations; (3) Hall-Petch type reciprocal square root of particle or grain size dependencies; and (4) indentation and conventional fracture mechanics results. Related behaviors of MgO and Al₂O₃ crystal and polycrystal materials are also described for the purpose of making comparisons.

| S-EPMC5448685 | biostudies-other

Effects of MgO modified ?-TCP nanoparticles on the microstructure and properties of ?-TCP/Mg-Zn-Zr composites.

Project description:The mechanical properties and corrosion resistance of magnesium alloy composites were improved by the addition of MgO surface modified tricalcium phosphate ceramic nanoparticles (m-?-TCP). Mg-3Zn-0.8Zr composites with unmodified (MZZT) and modified (MZZMT) nanoparticles were produced by high shear mixing technology. Effects of MgO m-?-TCP nanoparticles on the microstructure, mechanical properties, electrochemical corrosion properties and cytocompatibility of Mg-Zn-Zr/?-TCP composites were investigated. After hot extrusion deformation and dynamic recrystallization, the grain size of MZZMT was the half size of MZZT and the distribution of m-?-TCP particles in the matrix was more uniform than ?-TCP particles. The yield tensile strength (YTS), ultimate tensile strength (UTS), and corrosion potential (Ecorr) of MZZMT were higher than MZZT; the corrosion current density (Icorr) of MZZMT was lower than MZZT. Cell proliferation of co-cultured MZZMT and MZZT composite samples were roughly the same and the cell number at each time point is higher for MZZMT than for MZZT samples.

| S-EPMC5935024 | biostudies-literature

Zn-Mg-WC Nanocomposites for Bioresorbable Cardiovascular Stents: Microstructure, Mechanical Properties, Fatigue, Shelf Life, and Corrosion.

Project description:Zinc (Zn) and Zn alloys have been studied as potential materials for bioresorbable stents (BRSs) in the last decade due to their favorable biodegradability and biocompatibility. However, most Zn alloys lack the necessary combination of strength, ductility, fatigue resistance, corrosion rate (CR), and thermal stability needed for such applications. In this study, nanoparticles made of tungsten carbide (WC) were successfully incorporated into Zn alloyed with 0.5 wt % magnesium (Mg) and evaluated for their suitability for BRS applications. Specifically, the resulting Zn-0.5Mg-WC nanocomposite's microstructure, mechanical properties, in vitro CR, and thermal stability were evaluated. The Zn-0.5Mg-WC nanocomposite had excellent mechanical strength [ultimate tensile strength (UTS) > 250 MPa], elongation to failure (>30%), and a suitable in vitro CR (∼0.02 mm/y) for this clinical application. Moreover, the Zn-0.5Mg-WC nanocomposite survived 10 million cycles of tensile loading (stress ratio, R = 0.053) when the maximum stress was 80% of the yield stress. Its ductility was also retained during a 90-day thermal stability study, indicating an excellent shelf life. Stent prototypes were fabricated using this composition and were successfully deployed during bench testing without fracture. These results show that the Zn-0.5Mg-WC nanocomposite is a promising material for BRS applications. In vivo studies are underway to validate both biocompatibility, stent function, and degradation.

| S-EPMC9310700 | biostudies-literature

The Effect of Oxygen Partial Pressure on Microstructure and Properties of Fe40Al Alloy Sintered under Vacuum.

Project description:This paper presents the results of studies on the influence of oxygen partial pressure (vacuum level in the chamber) on the properties of FeAl intermetallics. One of the problems in the application of classical methods of prepared Fe-Al intermetallic is the occurrence of oxides. Applying a vacuum during sintering should reduce this effect. In order to analyze the effect of oxygen partial pressure on sample properties, five samples were processed (by a pressure-assisted induction sintering-PAIS method) under the following pressures: 3, 8, 30, 80, and 300 mbar (corresponding to oxygen partial pressures of 0.63, 1.68, 6.3, 16.8, and 63 mbar, respectively). The chemical and phase composition, hardness, density, and microstructure observations indicate that applying a vacuum significantly impacts intermetallic samples. The compact sintered at pressure 3 mbar is characterized by the most homogeneous microstructure, the highest density, high hardness, and nearly homogeneous chemical composition.

| S-EPMC5507053 | biostudies-other

Optimized Microstructure and Improved Magnetic Properties of Pr-Dy-Al-Ga Diffused Sintered Nd-Fe-B Magnets.

Project description:The grain boundary diffusion process (GBDP) has become an important technique in improving the coercivity and thermal stability of Dy-free sintered Nd-Fe-B magnets. The influence of Dy70Al10Ga20 and (Pr75Dy25)70Al10Ga20 alloys by the GBDP on sintered Nd-Fe-B magnets are investigated in this paper. After diffusing Dy70Al10Ga20 and (Pr75Dy25)70Al10Ga20 alloys, the coercivity (Hcj) of the magnets increased from 13.58 kOe to 20.10 kOe and 18.11 kOe, respectively. Meanwhile, the remanence of the magnets decreased slightly. The thermal stability of the diffused magnets was improved by the GBDP. The microstructure shows continuous Rare-earth-rich (RE-rich) grain boundary phases and (Dy, Pr/Nd)2Fe14B core-shell structures which contribute to improving the coercivity. Moreover, the Dy concentration on the surface of the (Pr75Dy25)70Al10Ga20 diffused magnets decreased with the Pr substitution for the Dy element. The openness of the recoil loops for the (Pr75Dy25)70Al10Ga20 diffused magnets is smaller than that of the original magnets and Dy70Al10Ga20 diffused magnets. The results show that the (Pr75Dy25)70Al10Ga20 alloys can effectively optimize the microstructure and improve the magnetic properties and thermal stability of the sintered Nd-Fe-B magnets.

| S-EPMC8156186 | biostudies-literature

Microstructure and nonohmic properties of SnO₂-Ta₂O₅-ZnO system doped with ZrO₂.

Project description:The microstructure and nonohmic properties of SnO₂-Ta₂O₅-ZnO varistor system doped with different amounts of ZrO₂ (0-2.0 mol%) were investigated. The proposed samples were sintered at 1400°C for 2 h with conventional ceramic processing method. By X-ray diffraction, SnO₂ cassiterite phase was found in all the samples, and no extra phases were identified in the detection limit. The doping of ZrO₂ would degrade the densification of the varistor ceramics but inhibit the growth of SnO₂ grains. In the designed range, varistors with 1.0 mol% ZrO₂ presented the maximum nonlinear exponent of 15.9 and lowest leakage current of 110 μA/cm², but the varistor voltage increased monotonously with the doping amount of ZrO₂.

| S-EPMC3918401 | biostudies-other

Effect of SiC nanowhisker on the microstructure and mechanical properties of WC-Ni cemented carbide prepared by spark plasma sintering.

Project description:Ultrafine tungsten carbide-nickel (WC-Ni) cemented carbides with varied fractions of silicon carbide (SiC) nanowhisker (0-3.75 wt.%) were fabricated by spark plasma sintering at 1350°C under a uniaxial pressure of 50 MPa with the assistance of vanadium carbide (VC) and tantalum carbide (TaC) as WC grain growth inhibitors. The effects of SiC nanowhisker on the microstructure and mechanical properties of the as-prepared WC-Ni cemented carbides were investigated. X-ray diffraction analysis revealed that during spark plasma sintering (SPS) Ni may react with the applied SiC nanowhisker, forming Ni2Si and graphite. Scanning electron microscopy examination indicated that, with the addition of SiC nanowhisker, the average WC grain size decreased from 400 to 350 nm. However, with the additional fractions of SiC nanowhisker, more and more Si-rich aggregates appeared. With the increase in the added fraction of SiC nanowhisker, the Vickers hardness of the samples initially increased and then decreased, reaching its maximum of about 24.9 GPa when 0.75 wt.% SiC nanowhisker was added. However, the flexural strength of the sample gradually decreased with increasing addition fraction of SiC nanowhisker.

| S-EPMC4070577 | biostudies-other

Effect of Kaolin Clay and ZnO-Nanoparticles on the Radiation Shielding Properties of Epoxy Resin Composites.

Project description:The use of radiation is mandatory in modern life, but the harms of radiation cannot be avoided. To minimize the effect of radiation, protection is required for the safety of the environment and human life. Hence, inventing a better shield than a conventional shielding material is the priority of researchers. Due to this reason, this current research deals with an innovative shielding material named EKZ samples having a composition of (epoxy resin (90-40) wt %-kaolin clay (10-25) wt %-ZnO-nano particles (0-35) wt %). The numerous compositional variations of (epoxy resin, kaolin clay, and ZnO-nano particles on the prepared EKZ samples varied the density of the samples from 1.24 to 1.95 g/cm3. The radiation shielding parameter of linear attenuation coefficient (LAC), half value layer (HVL), tenth value layer (TVL), and radiation protection efficiency (RPE) were measured to evaluate the radiation diffusion efficiency of newly made EKZ samples. These radiation shielding parameters were measured with the help of the HPGe detector utilizing the three-point sources (Am-241, Cs-137, and Co-60). The obtained results exposed that the value of linear attenuation coefficient (LAC) and radiation protection efficiency (RPE) was maximum, yet the value of half value layer (HVL), and tenth value layer (TVL), were minimum due to the greater amount of kaolin clay and ZnO-nanoparticles, whereas the amount of epoxy resin was lesser. In addition, it has been clear that as-prepared EKZ samples are suitable for low-dose shielding applications as well as EKZ-35 showed a better shielding ability.

| S-EPMC9698053 | biostudies-literature

Improved Microstructure and Hardness Properties of Low-Temperature Microwave-Sintered Y2O3 Stabilized ZrO2 Ceramics with Additions of Nano TiO2 Powders.

Project description:This paper reports the improvement of microstructural and hardness properties of 3 mol% yttria-stabilized zirconia (3Y-TZP) ceramics with nano TiO2 powders (with 0, 0.9, 1.8, and 2.7 wt%) added using a low-temperature microwave-assisted sintering of 1250 °C. Even at such a low sintering temperature, all sintered samples had the main phase of tetragonal zirconia (t-ZrO2) without the appearance of the secondary monoclinic phase or TiO2 phase, and had high relative densities, larger than 95%. The grain growth was well developed, and the grain sizes were around 300-600 nm. The Ti and O elements appeared at the grain and grain boundary and increased with the increased nano TiO2 contents identified by the element analysis, although the TiO2 phase did not appear in the X-ray pattern. The Vickers hardness was in the range of 10.5 to 14.5 GPa, which first increased with increasing content till 0.9 wt% and then decreased. With citric acid corrosion treatment for 10 h, the Vickers hardness only decreased from 14.34 GPa to 13.55 GPa with the addition of 0.9 wt% nano TiO2 powder. The experiment results showed that 0.9 wt% nano TiO2 addition can improve the densification as well as the Vickers hardness under a low temperature of microwave-assisted sintering.

| S-EPMC7177508 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data