In Situ TEM Study of Microstructure Evolution of Zr-Nb-Fe Alloy Irradiated by 800 keV Kr2+ Ions.

ABSTRACT: The microstructure evolution of Zr-1.1Nb-1.51Fe-0.26Cu-0.72Ni zirconium alloy, irradiated by 800 keV Kr2+ ions at 585 K using the IVEM-Tandem Facility at Argonne National Laboratory, was observed by in situ transmission electron microscopy. A number of β-Nb precipitates with a body-centered cubic (BCC) structure were distributed in the as-received zirconium alloy with micrometer-size grains. Kr2+ ion irradiation induced the growth of β-Nb precipitates, which could be attributed to the segregation of the dissolved niobium atoms in the zirconium lattice and the migration to the existing precipitates. The size of precipitates was increased with increasing Kr2+ ion fluence. During Kr2+ iron irradiation, the zirconium crystals without Nb precipitates tended to transform to the nanocrystals, which was not observed in the zirconium crystals with Nb nanoparticles. The existing Nb nanoparticles were the key factor that constrained the nanocrystallization of zirconium crystals. The thickness of the formed Zr-nanocrystal layer was about 300 nm, which was consistent with the depth of Kr2+ iron irradiation. The mechanism of the precipitate growth and the formation of zirconium nanocrystal was analyzed and discussed.

SUBMITTER: Lei P

PROVIDER: S-EPMC5506974 | biostudies-other | 2017 Apr

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

The Influence of Severe Plastic Deformation on Microstructure and In Vitro Biocompatibility of the New Ti-Nb-Zr-Ta-Fe-O Alloy Composition.

Project description:In this work, severe plastic deformation (SPD) of the newly designed Ti-Nb-Zr-Ta-Fe-O GUM metal was successfully conducted at room temperature using high speed high pressure torsion (HSHPT) followed by cold rolling (CR) to exploit the suitability of the processed alloy for bone staples. The Ti-31.5Nb-3.1Zr-3.1Ta-0.9Fe-0.16O GUM alloy was fabricated in a levitation melting furnace using a cold crucible and argon protective atmosphere. The as-cast specimens were subjected to SPD, specifically HSHPT, and then processed by the CR method to take the advantages of both grain refinement and larger dimensions. This approach creates the opportunity to obtain temporary orthopedic implants nanostructured by SPD. The changes induced by HSHPT technology from the coarse dendrite directly into the ultrafine grained structure were examined by optical microscopy, scanning electron microscopy and X-ray diffraction. The structural investigations showed that by increasing the deformation, a high density of grain boundaries is accumulated, leading gradually to fine grain size. In addition, the in vitro biocompatibility studies were conducted in parallel on the GUM alloy specimens in the as-cast state, and after HSHPT- and HSHPT+CR- processing. For comparative purposes, in vitro behavior of the bone-derived MC3T3-E1 cells on the commercially pure titanium has also been investigated regarding the viability and proliferation, morphology and osteogenic differentiation. The results obtained support the appropriateness of the HSHPT technology for developing compression staples able to ensure a better fixation of bone fragments.

| S-EPMC7663053 | biostudies-literature

Structural and Magnetic Studies of Bulk Nanocomposite Magnets Derived from Rapidly Solidified Pr-(Fe,Co)-(Zr,Nb)-B Alloy.

Project description:In the present study, the phase constitution, microstructure and magnetic properties of the nanocrystalline magnets, derived from fully amorphous or partially crystalline samples by annealing, were analyzed and compared. The melt-spun ribbons (with a thickness of ~30 µm) and suction-cast 0.5 mm and 1 mm thick plates of the Pr9Fe50Co13Zr1Nb4B23 alloy were soft magnetic in the as-cast state. In order to modify their magnetic properties, the annealing process was carried out at various temperatures from 923K to 1033K for 5 min. The Rietveld refinement of X-ray diffraction patterns combined with the partial or no known crystal structures (PONKCS) method allowed one to quantify the component phases and calculate their crystalline grain sizes. It was shown that the volume fraction of constituent phases and their crystallite sizes for the samples annealed at a particular temperature, dependent on the rapid solidification conditions, and thus a presence or absence of the crystallization nuclei in the as-cast state. Additionally, a thermomagnetic analysis was used as a complementary method to confirm the phase constitution. The hysteresis loops have shown that most of the samples exhibit a remanence enhancement typical for the soft/hard magnetic nanocomposite. Moreover, for the plates annealed at the lowest temperatures, the highest coercivities up to ~1150 kA/m were measured.

| S-EPMC7177373 | biostudies-literature

Electrochemical and biological characterization of Ti-Nb-Zr-Si alloy for orthopedic applications.

Project description:The performance of current biomedical titanium alloys is limited by inflammatory and severe inflammatory conditions after implantation. In this study, a novel Ti-Nb-Zr-Si (TNZS) alloy was developed and compared with commercially pure titanium, and Ti-6Al-4V alloy. Electrochemical parameters of specimens were monitored during 1 h and 12 h immersion in phosphate buffered saline (PBS) as a normal, PBS/hydrogen peroxide (H2O2) as an inflammatory, and PBS/H2O2/albumin/lactate as a severe inflammatory media. The results showed an effect of the H2O2 in inflammatory condition and the synergistic behavior of H2O2, albumin, and lactate in severe inflammatory condition towards decreasing the corrosion resistance of titanium biomaterials. Electrochemical tests revealed a superior corrosion resistance of the TNZS in all conditions due to the presence of silicide phases. The developed TNZS was tested for subsequent cell culture investigation to understand its biocompatibility nature. It exhibited favorable cell-materials interactions in vitro compared with Ti-6Al-4V. The results suggest that TNZS alloy might be a competitive biomaterial for orthopedic applications.

| S-EPMC9911760 | biostudies-literature

Synthesis and Characterization of a Novel Biocompatible Alloy, Ti-Nb-Zr-Ta-Sn.

Project description:Many current-generation biomedical implants are fabricated from the Ti-6Al-4V alloy because it has many attractive properties, such as low density and biocompatibility. However, the elastic modulus of this alloy is much larger than that of the surrounding bone, leading to bone resorption and, eventually, implant failure. In the present study, we synthesized and performed a detailed analysis of a novel low elastic modulus Ti-based alloy (Ti-28Nb-5Zr-2Ta-2Sn (TNZTS alloy)) using a variety of methods, including scanning electron microscopy, transmission electron microscopy, X-ray diffraction, and tensile test. Additionally, the in vitro biocompatibility of the TNZTS alloy was evaluated using SCP-1, SaOs-2, and THP-1 cell lines and primary human osteoblasts. Compared to Ti-6Al-4V, the elastic modulus of TNZTS alloy was significantly lower, while measures of its in vitro biocompatibility are comparable. O2 plasma treatment of the surface of the alloy significantly increased its hydrophilicity and, hence, its in vitro biocompatibility. TNZTS alloy specimens did not induce the release of cytokines by macrophages, indicating that such scaffolds would not trigger inflammatory responses. The present results suggest that the TNZTS alloy may have potential as an alternative to Ti-6Al-4V.

| S-EPMC8509052 | biostudies-literature

Nano-Topographical Control of Ti-Nb-Zr Alloy Surfaces for Enhanced Osteoblastic Response.

Project description:Nano-scale surface roughening of metallic bio-implants plays an important role in the clinical success of hard tissue reconstruction and replacement. In this study, the nano-topographical features of titanium-niobium-zirconium (TNZ) alloy surfaces were controlled by using the target-ion induced plasma sputtering (TIPS) technique to improve the in vitro osteoblastic response. The TIPS technique is a novel strategy for etching the surface of metallic bio-implants using bombardment of target metal cations, which were accelerated by an extremely high negative bias voltage applied to the substrates. The nano-topography of the TNZ surfaces was successfully controlled by modulating experimental variables (such as the ion etching energy and the type of substrate or target materials) of TIPS. As a result, various nanopatterns (size: 10-210 nm) were fabricated on the surface of the TNZ alloys. Compared with the control group, experimental groups with nanopattern widths of ≥130 nm (130 and 210 nm groups) exhibited superior cell adhesion, proliferation, and differentiation. Our findings demonstrate that TIPS is a promising technology that can impart excellent biological functions to the surface of metallic bio-implants.

| S-EPMC8229642 | biostudies-literature

Realistic microstructure evolution of complex Ta-Nb-Hf-Zr high-entropy alloys by simulation techniques.

Project description:Over last 15 years high-entropy alloys (HEAs) and complex concentrated alloys (CCAs) have gained much appreciation for their numerous superior properties. In this paper we have shown a novel simulation methodology to realistically predict the nanometer level local structural features of complex Ta0.25Nb0.25Hf0.25Zr0.25 HEA. This involves prediction of the morphology of the short-range clustering (SRCs), their quantitative atomic composition at the nano level and the thermodynamic aspects. An alloy structure model containing 11664 atoms was created and this was subjected to structure evolution at 1800?°C. The structure evolution technique is based on a combined hybrid Monte Carlo and molecular dynamics (MC/MD) approach. The simulated results from this work are further validated against experiments and material characterizations reported in literature and done by high-resolution transmission electron micrograph (HRTEM) for the nano-level microstructure, atom probe tomography (APT) for the local chemical compositions and X-ray diffraction at synchrotron sources for the local lattice relaxation effects. This work qualitatively and quantitatively reproduces the materials characterization results reasonably well from the developed simulation methodologies. The structure evolution methods as described in this work are based on independent computer simulations and does not involve any manual intervention for input based on experiments on evolving SRCs. This work shows the potential of utilizing MC/MD based computational methods to reduce the number of costly experimental characterizations and accelerate the pace for materials development.

| S-EPMC6841691 | biostudies-literature

Novel Ti-Zr-Hf-Fe Nanostructured Alloy for Biomedical Applications.

Project description:The synthesis and characterization of Ti40Zr20Hf20Fe20 (atom %) alloy, in the form of rods (f = 2 mm), prepared by arc-melting, and subsequent Cu mold suction casting, is presented. The microstructure, mechanical and corrosion properties, as well as in vitro biocompatibility of this alloy, are investigated. This material consists of a mixture of several nanocrystalline phases. It exhibits excellent mechanical behavior, dominated by high strength and relatively low Young's modulus, and also good corrosion resistance, as evidenced by the passive behavior in a wide potential window and the low corrosion current densities values. In terms of biocompatibility, this alloy is not cytotoxic and preosteoblast cells can easily adhere onto its surface and differentiate into osteoblasts.

| S-EPMC5452764 | biostudies-other

How 10 at% Al Addition in the Ti-V-Zr-Nb High-Entropy Alloy Changes Hydrogen Sorption Properties.

Project description:Al0.10Ti0.30V0.25Zr0.10Nb0.25 was prepared to evaluate the effect of 10% aluminum into the previously reported quaternary alloy, Ti0.325V0.275Zr0.125Nb0.275. The as-cast quinary alloy formed a single-phase body centered cubic solid solution and transformed into a body centered tetragonal after hydrogenation. The alloy had a storage capacity of 1.6 H/M (2.6 wt.%) with fast absorption kinetics at room temperature, reaching full capacity within the first 10 min. The major improvements of Al addition (10%) were related to the desorption and cycling properties of the material. The temperature for hydrogen release was significantly decreased by around 100 °C, and the quinary alloy showed superior cycling stability and higher reversible storage capacity than its quaternary counterpart, 94% and 85% of their respective initial capacity, after 20 hydrogenation cycles without phase decomposition.

| S-EPMC8122896 | biostudies-literature

Microstructure Evolution and Toughening Mechanism of a Nb-18Si-5HfC Eutectic Alloy Created by Selective Laser Melting.

Project description:Because of their superior mechanical performance at ultra-high temperatures, refractory niobium-silicon-based alloys are attractive high-temperature structural alloys, particularly as structural components in gas turbine engines. However, the development of niobium-silicon-based alloys for applications is limited because of the trade-off between room temperature fracture toughness and high-temperature strength. Here, we report on the fabrication of a Nb-18Si alloy with dispersion of hafnium carbide (HfC) particles through selective laser melting (SLM). XRD and SEM-BSE were used to examine the effects of scanning speed on the microstructure and the phase structure of the deposited Nb-18Si-5HfC alloy. The results show that when the scanning speed rises, the solid solubility of the solid solution improves, the interlamellar spacing of eutectics slowly decrease into nano-scale magnitude, and the corresponding hafnium carbide distribution becomes more uniform. We also discover the hafnium carbide particles dispersion in the inter-lamella structure, which contributes to its high fracture toughness property of 20.7 MPa∙m1/2 at room temperature. Hardness and fracture toughness are simultaneously improved because of the control of microstructure morphology and carbide distribution.

| S-EPMC8840692 | biostudies-literature

Gamma-ray, fast neutron and ion shielding characteristics of low-density and high-entropy Mg-Al-Ti-V-Cr-Fe-Zr-Nb alloy systems using Phy-X/PSD and SRIM programs.

Project description:This study aimed to assess the radiation shielding properties of ten low-density high-entropy alloys (LWHEAs) using Phy-X/PSD software to analyze various shielding parameters, such as attenuation coefficients (μm and μ), mean free path (λ), effective atomic number (Zeff), and removal cross-section (ΣR), in the energy range of Image 1 to Image 2. A comprehensive evaluation was performed to compare the attenuation outcomes provided by HEAs with a range of shielding materials documented in the literature. The study also calculated the build-up factors (BUFs) of the alloys by using the GP-fitting interpolation method. The stopping power of the alloys against H1/He+2 ions was analyzed using the SRIM Monte Carlo code, considering total stopping power (TSP) and projected range (PR). The results indicated that HEA8 (Al3.88Cr14.95Mo27.58Nb26.71Ti13.76Zr13.11) had the best performance in terms of shielding against γ-rays, fast neutrons, and H1/He+2 ions, as it achieved the highest values of parameters such as μm, μ, Zeff, and ΣR, along with the lowest values of HVL, TVL, λ, BUFs (Image 3 Image 4), TSP, and PR. On the other hand, HEA10 (Mg10.77Al11.96Mn24.35Fe24.75Cu28.17) had the lowest BUFs in both lower (Image 5 Image 4) and higher (Image 6 Image 4) energy regions. The order of μm for the alloys was found to be HEA5<HEA6<HEA9<HEA7<HEA10<HEA4<HEA2<HEA3<HEA1<HEA8. The study concluded that LWHEAs possess superior radiation shielding properties compared to conventional materials, making them a promising new class of materials for radiation shielding applications.

| S-EPMC10395150 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data