Silk: Optical Properties over 12.6 Octaves THz-IR-Visible-UV Range.

ABSTRACT: Domestic (Bombyx mori) and wild (Antheraea pernyi) silk fibers were characterised over a wide spectral range from THz 8 cm -1 ( λ = 1.25 mm, f = 0.24 THz) to deep-UV 50 × 10 3 cm - 1 ( λ = 200 nm, f = 1500 THz) wavelengths or over a 12.6 octave frequency range. Spectral features at β-sheet, α-coil and amorphous fibroin were analysed at different spectral ranges. Single fiber cross sections at mid-IR were used to determine spatial distribution of different silk constituents and revealed an α-coil rich core and more broadly spread β-sheets in natural silk fibers obtained from wild Antheraea pernyi moths. Low energy T-ray bands at 243 and 229 cm -1 were observed in crystalline fibers of domestic and wild silk fibers, respectively, and showed no spectral shift down to 78 K temperature. A distinct 20±4 cm-1 band was observed in the crystalline Antheraea pernyi silk fibers. Systematic analysis and assignment of the observed spectral bands is presented. Water solubility and biodegradability of silk, required for bio-medical and sensor applications, are directly inferred from specific spectral bands.

SUBMITTER: Balcytis A

PROVIDER: S-EPMC5507002 | biostudies-other | 2017 Mar

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:Graphitic carbon nitride (g-C₃N₄) and titanium dioxide (TiO₂) were chosen as a model system to investigate photocatalytic abilities of heterojunction system under UV and visible light conditions. The use of g-C₃N₄ has been shown to be effective in the reduction in recombination through the interaction between the two interfaces of TiO₂ and g-C₃N₄. A simple method of preparing g-C₃N₄ through the pyrolysis of melamine was employed, which was then added to undoped TiO₂ material to form the g-C₃N₄-TiO₂ system. These materials were then fully characterized by X-ray diffraction (XRD), Brunauer Emmett Teller (BET), and various spectroscopic techniques including Raman, X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FT-IR), diffuse absorbance, and photoluminescence analysis. Photocatalysis studies were conducted using the model dye, rhodamine 6G utilizing visible and UV light irradiation. Raman spectroscopy confirmed that a composite of the materials was formed as opposed to a mixture of the two. Using XPS analysis, a shift in the nitrogen peak to that indicative of substitutional nitrogen was detected for all doped samples. This is then mirrored in the diffuse absorbance results, which show a clear decrease in band gap values for these samples, showing the effective band gap alteration achieved through this preparation process. When g-C₃N₄-TiO₂ samples were analyzed under visible light irradiation, no significant improvement was observed compared that of pure TiO₂. However, under UV light irradiation conditions, the photocatalytic ability of the doped samples exhibited an increased reactivity when compared to the undoped TiO₂ (0.130 min-1), with 4% g-C₃N₄-TiO₂ (0.187 min-1), showing a 43.9% increase in reactivity. Further doping to 8% g-C₃N₄-TiO₂ lead to a decrease in reactivity against rhodamine 6G. BET analysis determined that the surface area of the 4% and 8% g-C₃N₄-TiO₂ samples were very similar, with values of 29.4 and 28.5 m²/g, respectively, suggesting that the actual surface area is not a contributing factor. This could be due to an overloading of the system with covering of the active sites resulting in a lower reaction rate. XPS analysis showed that surface hydroxyl radicals and oxygen vacancies are not being formed throughout this preparation. Therefore, it can be suggested that the increased photocatalytic reaction rates are due to successful interfacial interactions with the g-C₃N₄-doped TiO₂ systems.

Dataset Information

Silk: Optical Properties over 12.6 Octaves THz-IR-Visible-UV Range.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets