Flexural Behavior of HPFRCC Members with Inhomogeneous Material Properties.

ABSTRACT: In this paper, the flexural behavior of High-performance Fiber-Reinforced Cementitious Composite (HPFRCC) has been investigated, especially focusing on the localization of cracks, which significantly governs the flexural behavior of HPFRCC members. From four points bending tests with HPFRCC members, it was observed that almost evenly distributed cracks formed gradually, followed by a localized crack that determined the failure of the members. In order to investigate the effect of a localized crack on the flexural behavior of HPFRCC members, an analytical procedure has been developed with the consideration of intrinsic inhomogeneous material properties of HPFRCC such as cracking and ultimate tensile strengths. From the comparison, while the predictions with homogeneous material properties overestimated flexural strength and ductility of HPFRCC members, it was found that the analysis results considering localization effect with inhomogeneous material properties showed good agreement with the test results, not only the flexural strength and ductility but also the crack widths. The test results and the developed analysis procedure presented in this paper can be usefully applied for the prediction of flexural behaviors of HPFRCC members by considering the effect of localized cracking behavior.

SUBMITTER: Shin KJ

PROVIDER: S-EPMC5507054 | biostudies-other | 2015 Apr

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Investigation of inhomogeneous and anisotropic material behavior of porcine thoracic aorta using nano-indentation tests.

Project description:This study investigates the inhomogeneity and anisotropy of porcine descending thoracic aorta in three dimensions using a custom-made nano-indentation technique and a quasi-linear viscoelastic modeling approach. The indentation tests were conducted in axial, circumferential, and radial orientations with about 100 μm spatial resolution. The ratio of the elastic moduli obtained in different orientations was used to quantify the tissue local anisotropy. The distal sections were generally stiffer than the proximal ones in both axial and circumferential indentations. Four distinct layers were identified across the thickness with significantly different mechanical properties. The stiffness of the medial quadrant was significantly lower than all other quadrants in axial indentation. The anisotropic behavior of the tissue was more pronounced in the lateral quadrant of the distal sections. The results of this study can be used to better understand the mechanisms of aorta deformation and improve the spatial accuracy of computational models of aorta.

| S-EPMC5359050 | biostudies-literature

Importance of convective boundary layer flows with inhomogeneous material properties under linear and quadratic Boussinesq approximations around a horizontal cylinder.

Project description:This study investigates boundary layer flows with inhomogeneous material properties driven by natural convection using linear and quadratic Boussinesq approximations around a horizontal cylinder. The cylinder's surface was kept at a uniform temperature. The governing equations for the setup were formulated from the principles of mass continuity, momentum and energy under realistic assumptions. Four coupled partial differential equations were obtained and reduced using stream function to two. Using perturbation techniques with one spatial coordinate as the perturbation parameter, the partial differential equations were further reduced to a set of nonlinear coupled ordinary differential equations. The fluid's velocity, as well as the temperature distributions, were computed and analyzed using the Maple 17 platform. The results obtained were consistent with existing results from reference literature. Further analysis of the embedded flow parameters was also carried out and analyzed with relevant tables and graphical illustrations for the linear and quadratic Boussinesq approximations. The results of the study show a fundamental difference between the linear and quadratic Boussinesq approximation alongside an interconnection between constant and variable thermophysical properties.

| S-EPMC8167239 | biostudies-literature

The Structure and Flexural Properties of <i>Typha</i> Leaves.

Project description:The Typha leaf has a structure of lightweight cantilever beam, exhibiting excellent mechanical properties with low density. Especially, the leaf blade evolved high strength and low density with high porosity. In this paper, the structure of Typha leaf was characterized by microcomputed tomography (Micro-CT) and scanning electron microscopy (SEM), and the relationship with flexural properties was analyzed. The three-point bending test was performed on leaves to examine flexural properties, which indicated that the flexural properties vary from the base to the apex in gradient. The cross-sectional geometry shape of the leaf blade presented a strong influence on the optimized flexural stiffness. The load carrying capacity of the leaf depended on the development level of the epidermal tissue, the vascular bundle, the mechanical tissue, and the geometric properties. The investigation can be the basis for lightweight structure design and the application in the bionic engineering field.

| S-EPMC5662842 | biostudies-literature

Abnormal Stop Band Behavior Induced by Rotational Resonance in Flexural Metamaterial.

Project description:This paper investigates abnormal stop band behavior of resonance-based flexural elastic metamaterials under the rotational resonance motion. Due to the unique physics of flexural waves, we found that the stop band generated by the rotational resonance motion exhibits peculiar behavior which are quite different from general belief - it is shown that the negativity due to the rotational resonance does not provide any stop bands and the stop band generation due to the rotational resonance is governed by totally different band gap condition. To explain the peculiar behavior, a discrete Timoshenko beam model with both effective mass and rotational inertia as independent variables is introduced, and the wave behaviors of resonance-based flexural elastic metamaterial are precisely and fully described. The unique band gap condition, including the peculiar behavior, is derived with numerical validations. We expect our new model can provide a strong background for various flexural elastic metamaterials which can be effectively applied in various vibration devices.

| S-EPMC6155313 | biostudies-literature

Tensile and Flexural Properties of Cement Composites Reinforced with Flax Nonwoven Fabrics.

Project description:The aim of this study is to develop a process to produce high-performance cement-based composites reinforced with flax nonwoven fabrics, analyzing the influence of the fabric structure-thickness and entanglement-on mechanical behavior under flexural and tensile loadings. For this purpose, composite with flax nonwoven fabrics with different thicknesses were first prepared and their cement infiltration was evaluated with backscattered electron (BSE) images. The nonwoven fabrics with the optimized thickness were then subjected to a water treatment to improve their stability to humid environments and the fiber-matrix adhesion. For a fixed thickness, the effect of the nonwoven entanglement on the mechanical behavior was evaluated under flexural and direct tension tests. The obtained results indicate that the flax nonwoven fabric reinforcement leads to cement composites with substantial enhancement of ductility.

| S-EPMC5459217 | biostudies-literature

Application of Hydrophilic Silanol-Based Chemical Grout for Strengthening Damaged Reinforced Concrete Flexural Members.

Project description:In this study, hydrophilic chemical grout using silanol (HCGS) was adopted to overcome the performance limitations of epoxy materials used for strengthening existing buildings and civil engineering structures. The enhanced material performances of HCGS were introduced, and applied to the section enlargement method, which is one of the typical structural strengthening methods used in practice. To evaluate the excellent structural strengthening performance of the HCGS, structural tests were conducted on reinforced concrete beams, and analyses on the flexural behaviors of test specimens were performed by modified partial interaction theory (PIT). In particular, to improve the constructability of the section enlargement method, an advanced strengthening method was proposed, in which the precast panel was directly attached to the bottom of the damaged structural member by HCGS, and the degree of connection of the test specimens, strengthened by the section enlargement method, were quantitatively evaluated by PIT-based analysis.

| S-EPMC5455908 | biostudies-other

Data characterizing flexural properties of Al/Al2O3 syntactic foam core metal matrix sandwich.

Project description:Microstructural observations and flexural property datasets are provided for aluminum alloy matrix syntactic foam core sandwich composites. The tests are conducted in three-point bending configuration. The data supplied includes methods used for conducting microscopy and mechanical testing. Raw load-displacement data, which is used to plot stress-strain graphs, obtained during the flexural test is also included. Images from a DSLR camera are stitched together to form a detailed failure sequencing video. Failure of specimens is captured in sequential images using a digital camera. These images are stitched together to develop a video for visualization of failure mechanisms. Calculations are also included for a theoretical model that is used to estimate the flexural properties of the syntactic foam core sandwich.

| S-EPMC4773369 | biostudies-literature

Material properties of biomolecular condensates regulates RNA splicing and tumorigenesis

Project description:It remains largely unclear how material properties of biomolecular condensates impact physiological and pathological processes such as cancer. Here we show that AKAP95, a nuclear protein involved in gene regulation, plays an important role in tumorigenesis through directly regulating mRNA splicing. We show that AKAP95, through an intrinsic disordered region (IDR), forms liquid-like droplets in vitro and dynamic foci in nucleus. We have also identified key residues in IDR whose mutations to different residues perturb AKAP95 condensation in opposite directions. Importantly, the biological activity of AKAP95 in splice regulation is affected by either disruption of liquid condensation or enhancing the gelation of the assembly. We then show that the ability of AKAP95 in overcoming oncogene-induced senescence requires AKAP95 in an appropriate window of liquidity. These results thus link phase separation to tumorigenesis and uncover an important role of regulating the material property of protein condensates in disease including cancer.

2020-05-06 | GSE122308 | GEO

Physical/Chemical Properties and Resorption Behavior of a Newly Developed Ca/P/S-Based Bone Substitute Material.

Project description:Properly regulating the resorption rate of a resorbable bone implant has long been a great challenge. This study investigates a series of physical/chemical properties, biocompatibility and the behavior of implant resorption and new bone formation of a newly developed Ca/P/S-based bone substitute material (Ezechbone® Granule CBS-400). Experimental results show that CBS-400 is comprised majorly of HA and CSD, with a Ca/P/S atomic ratio of 54.6/39.2/6.2. After immersion in Hank's solution for 7 days, the overall morphology, shape and integrity of CBS-400 granules remain similar to that of non-immersed samples without showing apparent collapse or disintegration. With immersion time, the pH value continues to increase to 6.55 after 7 days, and 7.08 after 14 days. Cytotoxicity, intracutaneous reactivity and skin sensitization tests demonstrate the good biocompatibility features of CBS-400. Rabbit implantation/histological observations indicate that the implanted granules are intimately bonded to the surrounding new bone at all times. The implant is not merely a degradable bone substitute, but its resorption and the formation of new cancellous bone proceed at the substantially same pace. After implantation for 12 weeks, about 85% of the implant has been resorbed. The newly-formed cancellous bone ratio quickly increases to >40% at 4 weeks, followed by a bone remodeling process toward normal cancellous bone, wherein the new cancellous bone ratio gradually tapers down to about 30% after 12 weeks.

| S-EPMC7475886 | biostudies-literature

Painterly depiction of material properties.

Project description:Painters are masters of depiction and have learned to evoke a clear perception of materials and material attributes in a natural, three-dimensional setting, with complex lighting conditions. Furthermore, painters are not constrained by reality, meaning that they could paint materials without exactly following the laws of nature, while still evoking the perception of materials. Paintings have to our knowledge not been studied on a big scale from a material perception perspective. In this article, we studied the perception of painted materials and their attributes by using human annotations to find instances of 15 materials, such as wood, stone, fabric, etc. Participants made perceptual judgments about 30 unique segments of these materials for 10 material attributes, such as glossiness, roughness, hardness, etc. We found that participants were able to perform this task well while being highly consistent. Participants, however, did not consistently agree with each other, and the measure of consistency depended on the material attribute being perceived. Additionally, we found that material perception appears to function independently of the medium of depiction-the results of our principal component analysis agreed well with findings in former studies for photographs and computer renderings.

| S-EPMC7426625 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data