Studies on the Alkali-Silica Reaction Rim in a Simplified Calcium-Alkali-Silicate System.

ABSTRACT: This work is intended to provide a better understanding about the properties and roles of the reaction rim in an alkali-silica reaction. A simplified calcium-alkali-silicate system was created to simulate the multiple interactions among reactive silica, alkaline solution and portlandite near the aggregate surface during the formation and evolution of the reaction rim in an alkali-silica reaction. A transport barrier preventing the migration of calcium and silicate through itself was found on the interface between the alkali silicate and the calcium hydroxide. The barrier was mainly composed of calcium alkali silicate with silicon-oxygen organizations of Q² and Q³ according to the results of 29Si nuclear magnetic resonance, the calcium to silica mole ratio ranging from 0.22 to 0.53 and the alkali to silica ratio ranging from 0.20 to 0.26 based the location of the elemental compositional analysis and the storage period of the system.

SUBMITTER: Zheng K

PROVIDER: S-EPMC5510727 | biostudies-other | 2016 Aug

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Elastic Modulus of the Alkali-Silica Reaction Rim in a Simplified Calcium-Alkali-Silicate System Determined by Nano-Indentation.

Project description:This work aims at providing a better understanding of the mechanical properties of the reaction rim in the alkali-silica reaction. The elastic modulus of the calcium alkali silicate constituting the reaction rim, which is formed at the interface between alkali silicate and Ca(OH)₂ in a chemically-idealized system of the alkali-silica reaction, was studied using nano-indentation. In addition, the corresponding calcium to silica mole ratio of the calcium alkali silicate was investigated. The results show that the elastic modulus of the calcium alkali silicate formed at the interface increased with the increase of the calcium to silica mole ratio and vice versa. Furthermore, the more calcium that was available for interaction with alkali silicate to form calcium alkali silicate, the higher the calcium to silica mole ratio and, consequently, the higher the elastic modulus of the formed calcium alkali silicate. This work provides illustrative evidence from a mechanical point of view on how the occurrence of cracks due to the alkali-silica reaction (ASR) is linked to the formation of the reaction rim. It has to be highlighted, however, that the simplified calcium-alkali-silicate system in this study is far from the real condition in concrete.

| S-EPMC5457071 | biostudies-other

Blastfurnace Hybrid Cement with Waste Water Glass Activator: Alkali-Silica Reaction Study.

Project description:Hybrid systems represent a new sustainable type of cement combining the properties of ordinary Portland cement and alkali-activated materials. In this study, a hybrid system based on blast furnace slag and Portland clinker was investigated. The economic aspects and appropriate waste management resulted in the usage of technological waste from water glass production (WG-waste) as an alkaline activator. Although the Portland clinker content was very low, the incorporation of this by-product significantly improved the mechanical properties. Nevertheless, the high amount of alkalis in combination with possible reactive aggregates raises concerns about the risk of alkali-silica reaction (ASR). The results obtained from expansion measurement, the uranyl acetate fluorescence method, and microstructure characterization revealed that the undesirable effects of alkali-silica reaction in mortars based on the hydration of hybrid cement are minimal.

| S-EPMC7475897 | biostudies-literature

Microstructural Changes Due to Alkali-Silica Reaction during Standard Mortar Test.

Project description:The microstructural development of mortar bars with silica glass aggregate undergoing alkali-silica reaction (ASR) under the conditions of American Society for Testing and Materials (ASTM) Standard Test C1260 was analyzed using scanning electron microscopy and qualitative X-ray microanalysis. Cracking in the aggregate, the hydrated paste, and the paste-aggregate interface was important in the development of the microstructure. Cracks were characterized according to their location, their relationship to other cracks, and whether they are filled with ASR gel. Expansion of the bars was approximately 1% at 12 days and 2% at 53 days. They fell apart by 63 days. The bars contained two zones, an inner region that was undergoing ASR and an outer and much more highly damaged zone that extended further inward over time. Evidence of ASR was present even during the period when specimens were immersed in water, prior to immersion in NaOH solution.

| S-EPMC5458818 | biostudies-other

Preparation of a Composite Calcium Silicate Board with Carbide Slag and Coal-Based Solid Waste Activated by Different Alkali Activators.

Project description:Overall performance of composite calcium silicate boards (CCSBs) was investigated to further promote their application. The alkali activators were used to fully hydrate the calcium and silicon raw materials, which further improved the comprehensive performance of the CCSBs made of four pure industrial solid wastes. Within the range of dosage in this study, single doping of different proportions of the alkali activator improved the flexural strength of the CCSB. Based on this, the mechanical properties of the CCSB were further improved as the compounded alkali activator was optimized. Flexural strength is improved when the average pore diameter was refined. The freeze-thaw cycle test shows that a compound-doped alkali activator can effectively reduce the mass loss and strength loss, thereby improving the frost resistance of this material. This research discussed an economically affordable approach to prepare the CCSB material made of industrial solid waste.

| S-EPMC7178769 | biostudies-literature

Modeling Time-Dependent Behavior of Concrete Affected by Alkali Silica Reaction in Variable Environmental Conditions.

Project description:Alkali Silica Reaction (ASR) is known to be a serious problem for concrete worldwide, especially in high humidity and high temperature regions. ASR is a slow process that develops over years to decades and it is influenced by changes in environmental and loading conditions of the structure. The problem becomes even more complicated if one recognizes that other phenomena like creep and shrinkage are coupled with ASR. This results in synergistic mechanisms that can not be easily understood without a comprehensive computational model. In this paper, coupling between creep, shrinkage and ASR is modeled within the Lattice Discrete Particle Model (LDPM) framework. In order to achieve this, a multi-physics formulation is used to compute the evolution of temperature, humidity, cement hydration, and ASR in both space and time, which is then used within physics-based formulations of cracking, creep and shrinkage. The overall model is calibrated and validated on the basis of experimental data available in the literature. Results show that even during free expansions (zero macroscopic stress), a significant degree of coupling exists because ASR induced expansions are relaxed by meso-scale creep driven by self-equilibriated stresses at the meso-scale. This explains and highlights the importance of considering ASR and other time dependent aging and deterioration phenomena at an appropriate length scale in coupled modeling approaches.

| S-EPMC5459070 | biostudies-other

Theoretical Studies of a Silica Functionalized Acrylamide for Calcium Scale Inhibition.

Project description:The calcium carbonate (CaCO3) scale is one of the most common oilfield scales and oil and gas production bane. CaCO3 scale can lead to a sudden halt in production or, worst-case scenario, accidents; therefore, CaCO3 scale formation prevention is essential for the oil and gas industry. Scale inhibitors are chemicals that can mitigate this problem. We used two popular theoretical techniques in this study: Density Functional Theory (DFT) and Ab Initio Molecular Dynamics (AIMD). The objective was to investigate the inhibitory abilities of mixed oligomers, specifically acrylamide functionalized silica (AM-Silica). DFT studies indicate that Ca2+ does not bind readily to acryl acid and acrylamide; however, it has a good binding affinity with PAM and Silica functionalized PAM. The highest binding affinity occurs in the silica region and not the -CONH functional groups. AIMD calculations corroborate the DFT studies, as observed from the MD trajectory that Ca2+ binds to PAM-Silica by forming bonds with silicon; however, Ca2+ initially forms a bond with silicon in the presence of water molecules. This bonding does not last long, and it subsequently bonds with the oxygen atoms present in the water molecule. PAM-Silica is a suitable calcium scale inhibitor because of its high binding affinity with Ca2+. Theoretical studies (DFT and AIMD) have provided atomic insights on how AM-Silica could be used as an efficient scale inhibitor.

| S-EPMC9230130 | biostudies-literature

Development of highly inhomogeneous temperature profile within electrically heated alkali silicate glasses.

Project description:According to Joule's well-known first law, application of electric field across a homogeneous solid should produce heat uniformly in proportion to the square of electrical current. Here we report strong departure from this expectation for common, homogeneous ionic solids such as alkali silicate glasses when subjected even to moderate fields (~100?V/cm). Unlike electronically conducting metals and semiconductors, with time the heating of ionically conducting glass becomes extremely inhomogeneous with the formation of a nanoscale alkali-depletion region, such that the glass melts near the anode, even evaporates, while remaining solid elsewhere. In situ infrared imaging shows and finite element analysis confirms localized temperatures more than thousand degrees above the remaining sample depending on whether the field is DC or AC. These observations unravel the origin of recently discovered electric field induced softening of glass. The observed highly inhomogeneous temperature profile point to the challenges for the application of Joule's law to the electrical performance of glassy thin films, nanoscale devices, and similarly-scaled phenomena.

| S-EPMC6391379 | biostudies-literature

Calcium sulfate-Cu<sup>2+</sup> delivery system improves 3D-Printed calcium silicate artificial bone to repair large bone defects.

Project description:There are still limitations in artificial bone materials used in clinical practice, such as difficulty in repairing large bone defects, the mismatch between the degradation rate and tissue growth, difficulty in vascularization, an inability to address bone defects of various shapes, and risk of infection. To solve these problems, our group designed stereolithography (SLA) 3D-printed calcium silicate artificial bone improved by a calcium sulfate-Cu2+ delivery system. SLA technology endows the scaffold with a three-dimensional tunnel structure to induce cell migration to the center of the bone defect. The calcium sulfate-Cu2+ delivery system was introduced to enhance the osteogenic activity of calcium silicate. Rapid degradation of calcium sulfate (CS) induces early osteogenesis in the three-dimensional tunnel structure. Calcium silicate (CSi) which degrades slowly provides mechanical support and promotes bone formation in bone defect sites for a long time. The gradient degradation of these two components is perfectly matched to the rate of repair in large bone defects. On the other hand, the calcium sulfate delivery system can regularly release Cu2+ in the temporal and spatial dimensions, exerting a long-lasting antimicrobial effect and promoting vascular growth. This powerful 3D-printed calcium silicate artificial bone which has rich osteogenic activity is a promising material for treating large bone defects and has excellent potential for clinical application.

| S-EPMC10634439 | biostudies-literature

The production and application of carbon nanomaterials from high alkali silicate herbaceous biomass.

Project description:Herein, value-added materials such as activated carbon and carbon nanotubes were synthesized from low-value Miscanthus?×?giganteus lignocellulosic biomass. A significant drawback of using Miscanthus in an energy application is the melting during the combustion due to its high alkali silicate content. An application of an alternative approach was proposed herein for synthesis of activated carbon from Miscanthus?×?giganteus, where the produced activated carbon possessed a high surface area and pore volume of 0.92?cm3.g-1 after two activation steps using phosphoric acid and potassium hydroxide. The SBET of the raw biomass, after first activation and second activation methods showed 17, 1142 and 1368?m2.g-1, respectively. Transforming this otherwise waste material into a useful product where its material properties can be utilized is an example of promoting the circular economy by valorising waste lignocellulosic biomass to widely sought-after high surface area activated carbon and subsequently, unconventional multi-walled carbon nanotubes. This was achieved when the activated carbon produced was mixed with nitrogen-based material and iron precursor, where it produced hydrophilic multi-wall carbon nanotubes with a contact angle of ??=?9.88°, compared to the raw biomass. synthesised materials were tested in heavy metal removal tests using a lead solution, where the maximum lead absorption was observed for sample AC-K, with a 90% removal capacity after the first hour of testing. The synthesis of these up-cycled materials can have potential opportunities in the areas of wastewater treatment or other activated carbon/carbon nanotube end uses with a rapid cycle time.

| S-EPMC7018825 | biostudies-literature

Post-tilleyite, a dense calcium silicate-carbonate phase.

Project description:Calcium carbonate is a relevant constituent of the Earth's crust that is transferred into the deep Earth through the subduction process. Its chemical interaction with calcium-rich silicates at high temperatures give rise to the formation of mixed silicate-carbonate minerals, but the structural behavior of these phases under compression is not known. Here we report the existence of a dense polymorph of Ca5(Si2O7)(CO3)2 tilleyite above 8 GPa. We have structurally characterized the two phases at high pressures and temperatures, determined their equations of state and analyzed the evolution of the polyhedral units under compression. This has been possible thanks to the agreement between our powder and single-crystal XRD experiments, Raman spectroscopy measurements and ab-initio simulations. The presence of multiple cation sites, with variable volume and coordination number (6-9) and different polyhedral compressibilities, together with the observation of significant amounts of alumina in compositions of some natural tilleyite assemblages, suggests that post-tilleyite structure has the potential to accommodate cations with different sizes and valencies.

| S-EPMC6536543 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data