Influence of Layer Thickness and Raster Angle on the Mechanical Properties of 3D-Printed PEEK and a Comparative Mechanical Study between PEEK and ABS.

ABSTRACT: Fused deposition modeling (FDM) is a rapidly growing 3D printing technology. However, printing materials are restricted to acrylonitrile butadiene styrene (ABS) or poly (lactic acid) (PLA) in most Fused deposition modeling (FDM) equipment. Here, we report on a new high-performance printing material, polyether-ether-ketone (PEEK), which could surmount these shortcomings. This paper is devoted to studying the influence of layer thickness and raster angle on the mechanical properties of 3D-printed PEEK. Samples with three different layer thicknesses (200, 300 and 400 μm) and raster angles (0°, 30° and 45°) were built using a polyether-ether-ketone (PEEK) 3D printing system and their tensile, compressive and bending strengths were tested. The optimal mechanical properties of polyether-ether-ketone (PEEK) samples were found at a layer thickness of 300 μm and a raster angle of 0°. To evaluate the printing performance of polyether-ether-ketone (PEEK) samples, a comparison was made between the mechanical properties of 3D-printed polyether-ether-ketone (PEEK) and acrylonitrile butadiene styrene (ABS) parts. The results suggest that the average tensile strengths of polyether-ether-ketone (PEEK) parts were 108% higher than those for acrylonitrile butadiene styrene (ABS), and compressive strengths were 114% and bending strengths were 115%. However, the modulus of elasticity for both materials was similar. These results indicate that the mechanical properties of 3D-printed polyether-ether-ketone (PEEK) are superior to 3D-printed ABS.

SUBMITTER: Wu W

PROVIDER: S-EPMC5512651 | biostudies-other | 2015 Sep

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Static and Dynamic Mechanical Properties of 3D Printed ABS as a Function of Raster Angle.

Project description:Due to the rapid growth of 3D printing popularity, including fused deposition modeling (FDM), as one of the most common technologies, the proper understanding of the process and influence of its parameters on resulting products is crucial for its development. One of the most crucial parameters of FDM printing is the raster angle and mutual arrangement of the following filament layers. Presented research work aims to evaluate different raster angles (45°, 55°, 55'°, 60° and 90°) on the static, as well as rarely investigated, dynamic mechanical properties of 3D printed acrylonitrile butadiene styrene (ABS) materials. Configuration named 55'° was based on the optimal winding angle in filament-wound pipes, which provides them exceptional mechanical performance and durability. Also in the case of 3D printed samples, it resulted in the best impact strength, comparing to other raster angles, despite relatively weaker tensile performance. Interestingly, all 3D printed samples showed surprisingly high values of impact strength considering their calculated brittleness, which provides new insights into understanding the mechanical performance of 3D printed structures. Simultaneously, it proves that, despite extensive research works related to FDM technology, there is still a lot of investigation required for a proper understanding of this process.

| S-EPMC7013835 | biostudies-literature

The chemical, mechanical, and physical properties of 3D printed materials composed of TiO2-ABS nanocomposites.

Project description:To expand the chemical capabilities of 3D printed structures generated from commercial thermoplastic printers, we have produced and printed polymer filaments that contain inorganic nanoparticles. TiO2 was dispersed into acrylonitrile butadiene styrene (ABS) and extruded into filaments with 1.75 mm diameters. We produced filaments with TiO2 compositions of 1%, 5%, and 10% (kg/kg) and printed structures using a commercial 3D printer. Our experiments suggest that ABS undergoes minor degradation in the presence of TiO2 during the different processing steps. The measured mechanical properties (strain and Young's modulus) for all of the composites are similar to those of structures printed from the pure polymer. TiO2 incorporation at 1% negatively affects the stress at breaking point and the flexural stress. Structures produced from the 5 and 10% nanocomposites display a higher breaking point stress than those printed from the pure polymer. TiO2 within the printed matrix was able to quench the intrinsic fluorescence of the polymer. TiO2 was also able to photocatalyze the degradation of a rhodamine 6G in solution. These experiments display chemical reactivity in nanocomposites that are printed using commercial 3D printers, and we expect that our methodology will help to inform others who seek to incorporate catalytic nanoparticles in 3D printed structures.

| S-EPMC4929622 | biostudies-literature

Microwave dielectric characterisation of 3D-printed BaTiO3/ABS polymer composites.

Project description:3D printing is used extensively in product prototyping and continues to emerge as a viable option for the direct manufacture of final parts. It is known that dielectric materials with relatively high real permittivity-which are required in important technology sectors such as electronics and communications-may be 3D printed using a variety of techniques. Among these, the fused deposition of polymer composites is particularly straightforward but the range of dielectric permittivities available through commercial feedstock materials is limited. Here we report on the fabrication of a series of composites composed of various loadings of BaTiO3 microparticles in the polymer acrylonitrile butadiene styrene (ABS), which may be used with a commercial desktop 3D printer to produce printed parts containing user-defined regions with high permittivity. The microwave dielectric properties of printed parts with BaTiO3 loadings up to 70 wt% were characterised using a 15 GHz split post dielectric resonator and had real relative permittivities in the range 2.6-8.7 and loss tangents in the range 0.005-0.027. Permittivities were reproducible over the entire process, and matched those of bulk unprinted materials, to within ~1%, suggesting that the technique may be employed as a viable manufacturing process for dielectric composites.

| S-EPMC4778131 | biostudies-other

Neutron Shielding Performance of 3D-Printed Boron Carbide PEEK Composites.

Project description:Polyethylene is used as a traditional shielding material in the nuclear industry, but still suffers from low softening point, poor mechanical properties, and difficult machining. In this study, novel boron carbide polyether-ether-ketone (PEEK) composites with different mass ratios were prepared and tested as fast neutron absorbers. Next, shielding test pieces with low porosity were rapidly manufactured through the fused deposition modeling (FDM)-3D printing optimization process. The respective heat resistances, mechanical properties, and neutron shielding characteristics of as-obtained PEEK and boron carbide PEEK composites with different thicknesses were then evaluated. At load of 0.45 MPa, the heat deformation temperature of boron carbide PEEK increased with the boron carbide content. The heat deformation temperature of 30% wt. boron carbide PEEK was recorded as 308.4 °C. After heat treatment, both tensile strength and flexural strength of PEEK and PEEK composites rose by 40%-50% and 65%-78%, respectively. Moreover, the as-prepared composites showed excellent fast neutron shielding performances. For shielding test pieces with thicknesses between 40 mm and 100 mm, the neutron shielding rates exhibited exponential variation as a function of boron carbide content. The addition of 5%-15% boron carbide significantly changed the curvature of the shielding rate curve, suggesting an optimal amount of boron carbide. Meanwhile, the integrated shielding/structure may effectively shield neutron radiation, thereby ensuring optimal shielding performances. In sum, further optimization of the proposed process could achieve lightweight materials with less consumables and small volume.

| S-EPMC7287577 | biostudies-literature

Toward 3D Printed Hydrogen Storage Materials Made with ABS-MOF Composites.

Project description:The push to advance efficient, renewable, and clean energy sources has brought with it an effort to generate materials that are capable of storing hydrogen. Metal-organic framework materials (MOFs) have been the focus of many such studies as they are categorized for their large internal surface areas. We have addressed one of the major shortcomings of MOFs (their processibility) by creating and 3D printing a composite of acrylonitrile butadiene styrene (ABS) and MOF-5, a prototypical MOF, which is often used to benchmark H2 uptake capacity of other MOFs. The ABS-MOF-5 composites can be printed at MOF-5 compositions of 10% and below. Other physical and mechanical properties of the polymer (glass transition temperature, stress and strain at the breaking point, and Young's modulus) either remain unchanged or show some degree of hardening due to the interaction between the polymer and the MOF. We do observe some MOF-5 degradation through the blending process, likely due to the ambient humidity through the purification and solvent casting steps. Even with this degradation, the MOF still retains some of its ability to uptake H2, seen in the ability of the composite to uptake more H2 than the pure polymer. The experiments and results described here represent a significant first step toward 3D printing MOF-5-based materials for H2 storage.

| S-EPMC5890337 | biostudies-literature

The Surface Characterisation of Fused Filament Fabricated (FFF) 3D Printed PEEK/Hydroxyapatite Composites.

Project description:Polyetheretherketone (PEEK) is a high-performance thermoplastic polymer which has found increasing application in orthopaedics and has shown a lot of promise for 'made-to-measure' implants via additive manufacturing approaches. However, PEEK is bioinert and needs to undergo surface modification to make it at least osteoconductive to ensure a more rapid, improved, and stable fixation that will last longer in vivo. One approach to solving this issue is to modify PEEK with bioactive agents such as hydroxyapatite (HA). The work reported in this study demonstrates the direct 3D printing of PEEK/HA composites of up to 30 weight percent (wt%) HA using a Fused Filament Fabrication (FFF) approach. The surface characteristics and in vitro properties of the composite materials were investigated. X-ray diffraction revealed the samples to be semi-crystalline in nature, with X-ray Photoelectron Spectroscopy and Time-of-Flight Secondary Ion Mass Spectrometry revealing HA materials were available in the uppermost surface of all the 3D printed samples. In vitro testing of the samples at 7 days demonstrated that the PEEK/HA composite surfaces supported the adherence and growth of viable U-2 OS osteoblast like cells. These results demonstrate that FFF can deliver bioactive HA on the surface of PEEK bio-composites in a one-step 3D printing process.

| S-EPMC8471434 | biostudies-literature

3D-printed lightweight dorsal skin fold chambers from PEEK reduce chamber-related animal distress.

Project description:The dorsal skinfold chamber is one of the most important in vivo models for repetitive longitudinal assessment of microcirculation and inflammation. This study aimed to refine this model by introducing a new lightweight chamber made from polyetheretherketone (PEEK). Body weight, burrowing activity, distress, faecal corticosterone metabolites and the tilting angle of the chambers were analysed in mice carrying either a standard titanium chamber or a PEEK chamber. Data was obtained before chamber preparation and over a postoperative period of three weeks. In the early postoperative phase, reduced body weight and increased faecal corticosterone metabolites were found in mice with titanium chambers. Chamber tilting and tilting-related complications were reduced in mice with PEEK chambers. The distress score was significantly increased in both groups after chamber preparation, but only returned to preoperative values in mice with PEEK chambers. In summary, we have shown that light chambers reduce animal distress and may extend the maximum dorsal skinfold chamber observation time. Chambers made of PEEK are particularly suitable for this purpose: They are autoclavable, sufficiently stable to withstand rodent bites, inexpensive, and widely available through 3D printing.

| S-EPMC9270450 | biostudies-literature

Quantitative Assessment of Point-of-Care 3D-Printed Patient-Specific Polyetheretherketone (PEEK) Cranial Implants.

Project description:Recent advancements in medical imaging, virtual surgical planning (VSP), and three-dimensional (3D) printing have potentially changed how today's craniomaxillofacial surgeons use patient information for customized treatments. Over the years, polyetheretherketone (PEEK) has emerged as the biomaterial of choice to reconstruct craniofacial defects. With advancements in additive manufacturing (AM) systems, prospects for the point-of-care (POC) 3D printing of PEEK patient-specific implants (PSIs) have emerged. Consequently, investigating the clinical reliability of POC-manufactured PEEK implants has become a necessary endeavor. Therefore, this paper aims to provide a quantitative assessment of POC-manufactured, 3D-printed PEEK PSIs for cranial reconstruction through characterization of the geometrical, morphological, and biomechanical aspects of the in-hospital 3D-printed PEEK cranial implants. The study results revealed that the printed customized cranial implants had high dimensional accuracy and repeatability, displaying clinically acceptable morphologic similarity concerning fit and contours continuity. From a biomechanical standpoint, it was noticed that the tested implants had variable peak load values with discrete fracture patterns and failed at a mean (SD) peak load of 798.38 ± 211.45 N. In conclusion, the results of this preclinical study are in line with cranial implant expectations; however, specific attributes have scope for further improvements.

| S-EPMC8395180 | biostudies-literature

A 3D Printed Toolbox for Opto-Mechanical Components.

Project description:In this article we present the development of a set of opto-mechanical components (a kinematic mount, a translation stage and an integrating sphere) that can be easily built using a 3D printer based on Fused Filament Fabrication (FFF) and parts that can be found in any hardware store. Here we provide a brief description of the 3D models used and some details on the fabrication process. Moreover, with the help of three simple experimental setups, we evaluate the performance of the opto-mechanical components developed by doing a quantitative comparison with its commercial counterparts. Our results indicate that the components fabricated are highly customizable, low-cost, require a short time to be fabricated and surprisingly, offer a performance that compares favorably with respect to low-end commercial alternatives.

| S-EPMC5242500 | biostudies-literature

Enhancing Supercapacitor Electrochemical Performance with 3D Printed Cellular PEEK/MWCNT Electrodes Coated with PEDOT: PSS.

Project description:In this study, we examine the electrochemical performance of supercapacitor (SC) electrodes made from 3D-printed nanocomposites. These composites consist of multiwalled carbon nanotubes (MWCNTs) and polyether ether ketone (PEEK), coated with poly(3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS). The electrochemical performance of a 3D-printed PEEK/MWCNT solid electrode with a surface area density of 1.2 mm-1 is compared to two distinct periodically porous PEEK/MWCNT electrodes with surface area densities of 7.3 and 7.1 mm-1. To enhance SC performance, the 3D-printed electrodes are coated with a conductive polymer, PEDOT:PSS. The architected cellular electrodes exhibit significantly improved capacitive properties, with the cellular electrode (7.1 mm-1) displaying a capacitance nearly four times greater than that of the solid 3D-printed electrode-based SCs. Moreover, the PEDOT:PSS-coated cellular electrode (7.1 mm-1) demonstrates a high specific capacitance of 12.55 mF·cm-3 at 50 mV·s-1, contrasting to SCs based on 3D-printed cellular electrodes (4.09 mF·cm-3 at 50 mV·s-1) without the coating. The conductive PEDOT:PSS coating proves effective in reducing surface resistance, resulting in a decreased voltage drop during the SCs' charging and discharging processes. Ultimately, the 3D-printed cellular nanocomposite electrode with the conductive polymer coating achieves an energy density of 1.98 μW h·cm-3 at a current of 70 μA. This study underscores how the combined effect of the surface area density of porous electrodes enabled by 3D printing, along with the conductivity imparted by the polymer coating, synergistically improves the energy storage performance.

| S-EPMC11307982 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data