Multifunctional Cement Composites Strain and Damage Sensors Applied on Reinforced Concrete (RC) Structural Elements.

ABSTRACT: In this research, strain-sensing and damage-sensing functional properties of cement composites have been studied on a conventional reinforced concrete (RC) beam. Carbon nanofiber (CNFCC) and fiber (CFCC) cement composites were used as sensors on a 4 m long RC beam. Different casting conditions (in situ or attached), service location (under tension or compression) and electrical contacts (embedded or superficial) were compared. Both CNFCC and CFCC were suitable as strain sensors in reversible (elastic) sensing condition testing. CNFCC showed higher sensitivities (gage factor up to 191.8), while CFCC only reached gage factors values of 178.9 (tension) or 49.5 (compression). Furthermore, damage-sensing tests were run, increasing the applied load progressively up to the RC beam failure. In these conditions, CNFCC sensors were also strain sensitive, but no damage sensing mechanism was detected for the strain levels achieved during the tests. Hence, these cement composites could act as strain sensors, even for severe damaged structures near to their collapse.

SUBMITTER: Baeza FJ

PROVIDER: S-EPMC5512802 | biostudies-other | 2013 Mar

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Flexural Strengthening of Concrete Slab-Type Elements with Textile Reinforced Concrete.

Project description:This paper deals with flexural strengthening of reinforced concrete (RC) slabs with a carbon textile reinforced concrete (TRC) system. The surface coating treatment was applied to a carbon grid-type textile to increase the bond strength. Short fibers were incorporated into the matrix to mitigate the formation of shrinkage-induced cracks. The tensile properties of the TRC system were evaluated by a direct tensile test with a dumbbell-type grip method. The tensile test results indicated that the effect of the surface coating treatment of the textile on the bonding behavior of the textile within the TRC system was significant. Furthermore, the incorporation of short fibers in the matrix was effective to mitigate shrinkage-induced crack formation and to improve the tensile properties of the TRC system. Six full-scale slab specimens were strengthened with the TRC system and, subsequently, failure tested. The ultimate load-carrying capacity of the strengthened slabs was compared with that of an unstrengthened slab as well as the theoretical solutions. The failure test results indicated that the stiffness and the ultimate flexural capacity of the strengthened slab were at least 112% and 165% greater, respectively, than that of the unstrengthened slab. The test results further indicated that the strengthening effect was not linearly proportional to the amount of textile reinforcement.

| S-EPMC7287817 | biostudies-literature

Early Crack Detection of Reinforced Concrete Structure Using Embedded Sensors.

Project description:The damage in reinforced concrete (RC) structures can be induced either by the dynamic or static load. The inspection technologies available today have difficulty in detecting slowly progressive, locally limited damage, especially in hard-to-reach areas in the superstructure. The four-point bending test on the benchmark RC structure was used as a test of the quality and sensitivity of the embedded sensors. It allowed assessment of whether any cracking and propagation that occurs with the embedded sensors can be detected. Various methods are used for the analysis of the ultrasonic signals. By determining the feature from the ultrasonic signals, the changes in the whole structure are evaluated. The structural degradation of the RC benchmark structure was tested using various non-destructive testing methods to obtain a comprehensive decision about structural condition. It is shown that the ultrasonic sensors can detect a crack with a probability of detection of 100%, also before it is visible by the naked eye and other techniques, even if the damage is not in the direct path of the ultrasonic wave. The obtained results confirmed that early crack detection is possible using the developed methodology based on embedded and external sensors and advanced signal processing.

| S-EPMC6767232 | biostudies-literature

Tensile and Flexural Properties of Cement Composites Reinforced with Flax Nonwoven Fabrics.

Project description:The aim of this study is to develop a process to produce high-performance cement-based composites reinforced with flax nonwoven fabrics, analyzing the influence of the fabric structure-thickness and entanglement-on mechanical behavior under flexural and tensile loadings. For this purpose, composite with flax nonwoven fabrics with different thicknesses were first prepared and their cement infiltration was evaluated with backscattered electron (BSE) images. The nonwoven fabrics with the optimized thickness were then subjected to a water treatment to improve their stability to humid environments and the fiber-matrix adhesion. For a fixed thickness, the effect of the nonwoven entanglement on the mechanical behavior was evaluated under flexural and direct tension tests. The obtained results indicate that the flax nonwoven fabric reinforcement leads to cement composites with substantial enhancement of ductility.

| S-EPMC5459217 | biostudies-literature

Electrochemical Characterization and Inhibiting Mechanism on Calcium Leaching of Graphene Oxide Reinforced Cement Composites.

Project description:Calcium leaching is a degradation progress inside hardened cement composites, where Ca2+ ions in cement pore solution can migrate into the aggressive solution. In this work, calcium leaching of graphene oxide (GO) reinforced cement composites was effectively characterized by combined techniques of electrochemical impedance spectroscopy (EIS) and scanning electron microscope (SEM). Inhibiting mechanism of GO on calcium leaching of the composites was also examined. The obtained results show that the diameter of the semi-circle of the Nyquist curves of leached samples with GO addition decreased less than that of controlled samples. After leaching for 35 days, loss rate of model impedance RCCP of leached samples with 0, 0.05, 0.1, 0.15, and 0.2 wt.% GO addition was 94.85%, 84.07%, 79.66%, 75.34%, and 68.75%, respectively. Therefore, GO addition can significantly mitigate calcium leaching of cement composites, since it can absorb Ca2+ ions in cement pore solution, as well as improve the microstructure of the composites. In addition, coupling leaching depth and compressive strength loss were accurately predicted by using the impedance RCCP.

| S-EPMC6409634 | biostudies-literature

Mechanical Characterization of High-Performance Steel-Fiber Reinforced Cement Composites with Self-Healing Effect.

Project description:The crack self-healing behavior of high-performance steel-fiber reinforced cement composites (HPSFRCs) was investigated. High-strength deformed steel fibers were employed in a high strength mortar with very fine silica sand to decreasing the crack width by generating higher interfacial bond strength. The width of micro-cracks, strongly affected by the type of fiber and sand, clearly produced the effects on the self-healing behavior. The use of fine silica sand in HPSFRCs with high strength deformed steel fibers successfully led to rapid healing owing to very fine cracks with width less than 20 µm. The use of very fine silica sand instead of normal sand produced 17%-19% higher tensile strength and 51%-58% smaller width of micro-cracks.

| S-EPMC5453159 | biostudies-literature

Nano-Inclusions Applied in Cement-Matrix Composites: A Review.

Project description:Research on cement-based materials is trying to exploit the synergies that nanomaterials can provide. This paper describes the findings reported in the last decade on the improvement of these materials regarding, on the one hand, their mechanical performance and, on the other hand, the new properties they provide. These features are mainly based on the electrical and chemical characteristics of nanomaterials, thus allowing cement-based elements to acquire "smart" functions. In this paper, we provide a quantitative approach to the reinforcements achieved to date. The fundamental concepts of nanoscience are introduced and the need of both sophisticated devices to identify nanostructures and techniques to disperse nanomaterials in the cement paste are also highlighted. Promising results have been obtained, but, in order to turn these advances into commercial products, technical, social and standardisation barriers should be overcome. From the results collected, it can be deduced that nanomaterials are able to reduce the consumption of cement because of their reinforcing effect, as well as to convert cement-based products into electric/thermal sensors or crack repairing materials. The main obstacle to foster the implementation of such applications worldwide is the high cost of their synthesis and dispersion techniques, especially for carbon nanotubes and graphene oxide.

| S-EPMC5456970 | biostudies-other

Application of Rotation Rate Sensors in Modal and Vibration Analyses of Reinforced Concrete Beams.

Project description:The recent rapid development of rotation rate sensor technology opens new opportunities for their application in more and more fields. In this paper, the potential of rotational sensors for the modal analysis of full-scale civil engineering structural elements is experimentally examined. For this purpose, vibrations of two 6-m long beams made of ultra-high performance concrete (UHPC) were measured using microelectromechanical system (MEMS) rotation rate sensors. The beams were excited to vibrations using an impact hammer and a dynamic vibration exciter. The results of the experiment show that by using rotation rate sensors, one can directly obtain derivatives of mode shapes and deflection shapes. These derivatives of mode shapes, often called "rotational modes", bring more information regarding possible local stiffness variations than the traditional transversal and deflection mode shapes, so their extraction during structural health monitoring is particularly useful. Previously, the rotational modes could only be obtained indirectly (e.g., by central difference approximation). Here, with the application of rotation rate sensors, one can obtain rotational modes and deflection shapes with a higher precision. Furthermore, the average strain rate and dynamic strain were acquired using the rotation rate sensors. The laboratory experiments demonstrated that rotation rate sensors were matured enough to be used in the monitoring and modal analyses of full-scale civil engineering elements (e.g., reinforced concrete beams).

| S-EPMC7506681 | biostudies-literature

Nanoscaled Mechanical Properties of Cement Composites Reinforced with Carbon Nanofibers.

Project description:This paper reports the effects of carbon nanofibers (CNFs) on nanoscaled mechanical properties of cement composites. CNFs were added to cement composites at the filler loading of 0.2 wt % (by wt. of cement). Micrographs based on scanning electron microscopy (SEM) show that CNFs are capable of forming strong interfacial bonding with cement matrices. Experimental results using nanoindentation reveal that the addition of CNFs in cement composites increases the proportions of high-density calcium-silicate-hydrate gel (HD-CSH) compared to low-density CSH gel. It was also found that the inclusion of CNFs increases the compressive strength of cement composites.

| S-EPMC5554043 | biostudies-other

Comparative assessment of impact analysis methods applied to large commercial aircraft crash on reinforced concrete containment.

Project description:The precise evaluation of the potential damage caused by large commercial aircraft crash into civil structures, especially nuclear power plants (NPPs), has become essential design consideration. In this study, impact of Boeing 767 against rigid wall and outer containment building (reinforced concrete) of an NPP are simulated in ANSYS/LS-DYNA by using both force time history and missile target interaction methods with impact velocities ranging from 100 m/s to 150 m/s. The results show that impact loads, displacements, stresses for concrete and steel reinforcement, and damaged elements are higher in case of force time history method than missile target interaction method, making the former relatively conservative. It is observed that no perforation or scabbing takes place in case of 100 m/s impact speed, thus preventing any potential leakage. With full mass of Boeing 767 and impact velocity slightly above 100 m/s, the outer containment building can prevent local failure modes. At impact velocity higher than 120 m/s, scabbing and perforations are dominant. This concludes that in design and assessment of NPP structures against aircraft loadings, sufficient thickness or consideration of steel plates are essential to account for local failure modes and overall structural integrity. Furthermore, validation and application of detail 3D finite element and material models to full-scale impact analysis have been carried out to expand the existing database. In rigid wall impact analysis, the impact forces and impulses from FE analysis and Riera's method correspond well, which satisfies the recommendations of relevant standards and further ensure the accuracy of results in full-scale impact analysis. The methodology presented in this paper is extremely effective in simulating structural evaluation of full-scale aircraft impact on important facilities such as NPPs.

| S-EPMC7529203 | biostudies-literature

Mechanical Properties of Chopped Basalt Fiber-Reinforced Lightweight Aggregate Concrete and Chopped Polyacrylonitrile Fiber Reinforced Lightweight Aggregate Concrete.

Project description:In this study, an experimental investigation was conducted on the mechanical properties of lightweight aggregate concrete (LWAC) with different chopped fibers, including basalt fiber (BF) and polyacrylonitrile fiber (PANF). The LWAC performance was studied in regard to compressive strength, splitting tensile strength and shear strength at age of 28 days. In addition, the oven-dried density and water absorption were measured as well to confirm whether the specimens match the requirement of standard. In total, seven different mixture groups were designed and approximately 104 LWAC samples were tested. The test results showed that the oven-dried densities of the LWAC mixtures were in range of 1.819-1.844 t/m3 which satisfied the definition of LWAC by Chinese Standard. Additionally, water absorption decreased with the increasing of fiber content. The development tendency of the specific strength of LWAC was the same as that of the cube compressive strength. The addition of fibers had a significant effect on reducing water absorption. Adding BF and PANF into concrete had a relatively slight impact on the compressive strength but had an obvious effect on splitting tensile strength, flexural strength and shear strength enhancement, respectively. In that regard, a 1.5% fiber volume fraction of BF and PANF showed the maximum increase in strength. The use of BF and PANF could change the failure morphologies of splitting tensile and flexural destruction but almost had slight impact on the shear failure morphology. The strength enhancement parameter ? was proposed to quantify the improvement effect of fibers on cube compressive strength, splitting tensile strength, flexural strength and shear strength, respectively. And the calculation results showed good agreement with test value.

| S-EPMC7178649 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data