Use of Cement Kiln Dust, Blast Furnace Slag and Marble Sludge in the Manufacture of Sustainable Artificial Aggregates by Means of Cold Bonding Pelletization.

ABSTRACT: In this work, three different samples of solid industrial wastes cement kiln dust (CKD), granulated blast furnace slag and marble sludge were employed in a cold bonding pelletization process for the sustainable production of artificial aggregates. The activating action of CKD components on the hydraulic behavior of the slag was explored by evaluating the neo-formed phases present in several hydrated pastes. Particularly, the influence of free CaO and sulfates amount in the two CKD samples on slag reactivity was evaluated. Cold bonded artificial aggregates were characterized by determining physical and mechanical properties of two selected size fractions of the granules for each studied mixture. Eighteen types of granules were employed in C28/35 concrete manufacture where coarser natural aggregate were substituted with the artificial ones. Finally, lightweight concretes were obtained, proving the suitability of the cold bonding pelletization process in artificial aggregate sustainable production.

SUBMITTER: Colangelo F

PROVIDER: S-EPMC5521239 | biostudies-other | 2013 Jul

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Geopolymer Based on Mechanically Activated Air-cooled Blast Furnace Slag.

Project description:An efficient solution to increase the sustainability of building materials is to replace Portland cement with alkali-activated materials (AAM). Precursors for those systems are often based on water-cooled ground granulated blast furnace slags (GGBFS). Quenching of blast furnace slag can be done also by air but in that case, the final product is crystalline and with a very low reactivity. The present study aimed to evaluate the cementitious properties of a mechanically activated (MCA) air-cooled blast furnace slag (ACBFS) used as a precursor in sodium silicate alkali-activated systems. The unreactive ACBFS was processed in a planetary ball mill and its cementing performances were compared with an alkali-activated water-cooled GGBFS. Mixes based on mechanically activated ACBFS reached the 7-days compressive strength of 35 MPa and the 28-days compressive strength 45 MPa. The GGBFS-based samples showed generally higher compressive strength values.

| S-EPMC7085006 | biostudies-literature

Durability of Fibre-Reinforced Calcium Aluminate Cement (CAC)-Ground Granulated Blast Furnace Slag (GGBFS) Blended Mortar after Sulfuric Acid Attack.

Project description:Concrete wastewater infrastructures are important to modern society but are susceptible to sulfuric acid attack when exposed to an aggressive environment. Fibre-reinforced mortar has been adopted as a promising coating and lining material for degraded reinforced concrete structures due to its unique crack control and excellent anti-corrosion ability. This paper aims to evaluate the performance of polyethylene (PE) fibre-reinforced calcium aluminate cement (CAC)-ground granulated blast furnace slag (GGBFS) blended strain-hardening mortar after sulfuric acid immersion, which represented the aggressive sewer environment. Specimens were exposed to 3% sulfuric acid solution for up to 112 days. Visual, physical and mechanical performance such as water absorption ability, sorptivity, compressive and direct tensile strength were evaluated before and after sulfuric acid attack. In addition, micro-structure changes to the samples after sulfuric acid attack were also assessed by X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM) to further understand the deterioration mechanism. The results show that overall fibre-reinforced calcium aluminate cement (CAC)-based samples performed significantly better than fibre-reinforced ordinary Portland cement (OPC)-based samples as well as mortar samples in sulfuric acid solution in regard to visual observations, penetration depth, direct tensile strength and compressive reduction. Gypsum generation in the cementitious matrix of both CAC and OPC-based systems was the main reason behind the deterioration mechanism after acid attack exposure. Moreover, laboratory sulfuric acid testing has been proven for successfully screening the cementitious material against an acidic environment. This method can be considered to design the service life of concrete wastewater pipes.

| S-EPMC7503559 | biostudies-literature

Long-Term Stabilization/Solidification of Arsenic-Contaminated Sludge by a Blast Furnace Slag-Based Cementitious Material: Functions of CaO and NaCl.

Project description:Arsenic is a kind of element widely distributed in the environment that may pose a threat to the ecological environment and human health, while effective remediation and sustainable utilization of arsenic-containing sludge is a challenge. Based on stabilization/solidification blast furnace slag-based cementitious materials (BCMs), this study innovatively proposes to improve the arsenic (As) solidification efficiency and long-term stability by using the activation mode of CaO and NaCl. The effects of different factors on the properties of the BCM were measured by unconfined compressive strength (UCS) tests, X-ray diffraction, Fourier transform infrared spectroscopy, and scanning electron microscopy. The long-term stability and safety of the BCM were verified by leaching toxicity and improved three stage continuous extraction method (BCR) tests. Experimental results show that the addition of CaO provides conditions for the formation of ettringite (AFt), thus promoting the crystal growth of AFt. The addition of NaCl can promote the formation of Cl-AFt and play a good long-term stabilizing role. When the content of the alkali activator is 10% and the modulus is 1.0, the contents of CaO and NaCl are 10 and 1%, respectively. The BCM has the best efficiency in terms of UCS and As solidification. The UCS at 28 days was 5.4 MPa, and the leaching concentration of As was 0.309 mg/L, and the As solidification efficiency was up to 99.9%. In the improved BCR test, the proportions of residual and oxidizable states of arsenic increased by 19.6 and 13.5%, respectively, and the stability of heavy metals improved. These findings show that the BCM has good long-term stability and safety. Overall, this study shows that CaO and NaCl significantly increase the output of AFt and achieve the purpose of efficient and stable solidification of As by the BCM.

| S-EPMC9475631 | biostudies-literature

Properties of Foamed Mortar Prepared with Granulated Blast-Furnace Slag.

Project description:Foamed mortar with a density of 1300 kg/m³ was prepared. In the initial laboratory trials, water-to-cement (w/c) ratios ranging from 0.54 to 0.64 were tested to determine the optimal value for foamed mortar corresponding to the highest compressive strength without compromising its fresh state properties. With the obtained optimal w/c ratio of 0.56, two types of foamed mortar were prepared, namely cement-foamed mortar (CFM) and slag-foamed mortar (SFM, 50% cement was replaced by slag weight). Four different curing conditions were adopted for both types of foamed mortar to assess their compressive strength, ultrasonic pulse velocity (UPV) and thermal insulation performance. The test results indicated that utilizing 50% of slag as cement replacement in the production of foamed mortar improved the compressive strength, UPV and thermal insulation properties. Additionally, the initial water curing of seven days gained higher compressive strength and increased UPV values as compared to the air cured and natural weather curing samples. However, this positive effect was more pronounced in the case of compressive strength than in the UPV and thermal conductivity of foamed mortar.

| S-EPMC5455276 | biostudies-other

Recovery of scandium and neodymium from blast furnace slag using acid baking-water leaching.

Project description:The current study puts the emphasis on developing a pyro-hydrometallurgical process, called acid baking-water leaching, to recover scandium and neodymium from blast furnace slag produced by the ironmaking industry. In this process, the feed is mixed with concentrated sulfuric acid, digested at 200-400 °C, and leached in water at ambient conditions. This process offers several advantages including less acidic waste generation and rapid kinetics. With fundamental investigations into the digestion mechanism, acid to slag mass ratio and baking temperature are determined to have the most significant positive and negative impacts, respectively. At low acid to slag ratio, the silicate bearing phases in the feed do not digest, resulting in low extraction. At 200 °C baking temperature, a hydrated aluminum sulfate ((Al(H2O)6)2(SO4)3(H2O)4.4) phase with weak hydrogen bonds is formed that leaches in water rapidly (<10 min); while at 400 °C, Al2(SO4)3 with strong ionic bonds is formed that leaches at slower kinetics (>4 h). Fundamental investigations into the water leaching process indicate that the diffusion of water through the firm solid product (ash layer) is the rate determining step. We expect the results of this study would help enable valorization of industrial byproducts, in particular ironmaking slag.

| S-EPMC9056533 | biostudies-literature

Reactivation of a Retarded Suspension of Ground Granulated Blast-Furnace Slag.

Project description:An effective retarded suspension of ground granulated blast-furnace slag (GGBFS) needs a strong activator to reactivate the hydration. In this research study, sodium hydroxide (NaOH) as an alkali activator in two different concentrations (30 and 50 wt.%) was used to overcome the retardation and give the hardened GGBFS the reasonable strength. The study was carried out with a mixture of GGBFS, a solution of 1.0 wt.% d-gluconic acid (C₆H12O₇) as a retarder in the mixing water and a methyl cellulose as a stabilizer. The reactivation was executed after seven different periods (up to 28 days) after the system was retarded. The following investigations were performed: slump test, measurement of ultrasonic (US) velocity, compressive strength and gross density, thermogravimetry (TG) and scanning electron microscopy (SEM). The analyses of the hardened samples were carried out seven, 28 and 90 days after the reactivation. The result of the study is an effective reactivation of a retarded suspension. In this case, the activator with 50 wt.% NaOH shows a very high performance. The setting time of the reactivated binders is much longer compared to the reference, but, in the longer term, the compressive strength and the progress of the hydration exceed the performance of the reference.

| S-EPMC5456691 | biostudies-other

Properties of Concrete Using Treated Low-Class Recycled Coarse Aggregate and Blast Furnace Slag Sand.

Project description:Since high quality natural aggregates are becoming scarce, it is important that industrial recycled products and by-products are used as aggregates for concrete. In Japan, the use of recycled aggregate (RG) is encouraged. Since, strength and durability of recycled aggregate concrete is lower than that of normal aggregate concrete, the use of recycled aggregate has not been significant. In order to improve physical properties of concrete using recycled coarse aggregate, blast furnace slag sand has been proposed. Recently, blast furnace slag sand is expected to improve durability, freezing, and thawing damage of concrete in Japan. Properties of fresh and hardened concrete bleeding, compressive strength, and resistance to freezing and thawing which are caused by the rapid freezing and thawing test using liquid nitrogen is a high loader than the JIS A 1148 A method that were investigated. As a result, concrete using treated low-class recycled coarse aggregate and 50% or 30% replacement of crushed sand with blast furnace slag sand showed the best results, in terms of bleeding, resistance to freezing and thawing.

| S-EPMC7078881 | biostudies-literature

Effect of the Formation of Amorphous Networks on the Structure and Hydration Characteristics of Granulated Blast Furnace Slag.

Project description:The slag obtained in the process of pig iron smelting has been widely used, but the variational hydration activity always is a significant factor affecting its quality. In this experiment, the laboratory simulated slag was prepared by adjusting the chemical composition and cooling method. The experiment primary characterized the structure and hydration process with different types of slag by using MAS NMR, XRD, compressive strength, ICP, SEM, and hydration heat, then obtained the influence of the composition of the network former S/A (the mass ratio of SiO2 and Al2O3 in chemical composition) and amorphous phase content on its structure and hydration activity. The result shows that lowering the S/A value can reduce the degree of vitreous polymerization in the slag; reducing the S/A value of the slag can make the slag hydration time advance, and consequently, the cumulative exotherm increases, the liquid phase Ca/Si and Al/Si ionic ratio increases, and the hydration product changes from C-S-H gel to C-A-S-H gel, which ultimately leads to an increase in compressive strength. In the high S/A value slag, the formation of the trace crystal phase of gehlenite is beneficial to reduce the degree of polymerization of the amorphous.

| S-EPMC7143658 | biostudies-literature

Using Experimental Statistical Models for Predicting Strength and Deformability of Self-Compacting Concrete with Ground Blast-Furnace Slag.

Project description:Ground blast-furnace slag is one of the waste products available in Ukraine and other countries. It is obtained at metallurgical enterprises in huge quantities and can be efficiently used for concrete production. The article is devoted to obtaining experimental-statistical models of the influence of technological factors that determine the composition of self-compacting concrete (SCC) based on ground blast-furnace slag and polycarboxylate superplasticizer on compressive strength, tensile strength, prismatic strength, elastic modulus and crack resistance. Analysis of the investigated factors' influence on the specified SCC properties is carried out and positive influence of blast-furnace slag and superplasticizer simultaneous action on durability and deformation characteristics is studied. A design method of SCC composition design using the obtained mathematical models is developed. It allows for the consideration of a set of necessary parameters simultaneously. A numerical example is given.

| S-EPMC9228754 | biostudies-literature

Biomethanation of blast furnace gas using anaerobic granular sludge <i>via</i> addition of hydrogen.

Project description:The high concentrations of CO (toxic) and CO2 (greenhouse gases) in blast furnace gas (a by-product of steelworks) reflect its low calorific value. In this study, anaerobic granular sludge was used to convert carbon from blast furnace gas to methane via exogenous hydrogen addition. The inhibition of methane production by CO partial pressure (P CO) was found to start from 0.4 atm. The intermediate metabolites from CO to methane including acetate, propionate, and H2 accumulated at higher CO concentrations in the presence of 2-bromoethanesulfonic acid. After the introduction of H2 and blast furnace gas, although the hydrogen partial pressure (P H2 ) up to 1.54 atm resulted in the maximum CH4 yield, the whole system was not stable due to the accumulation of a large amount of volatile fatty acids. The optimum P H2 on CH4 production from the simulated blast furnace gas, 5.32 mmol g-1 VSS, was determined at 0.88 atm in this study.

| S-EPMC9083107 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data