Thermal Stability and Fire Properties of Salen and Metallosalens as Fire Retardants in Thermoplastic Polyurethane (TPU).

ABSTRACT: This study deals with the synthesis and evaluation of salen based derivatives as fire retardants in thermoplastic polyurethane. Salens, hydroxysalens and their first row transition metal complexes (salen-M) were synthesized (Copper, Manganese, Nickel and Zinc). They were then incorporated in thermoplastic polyurethane (TPU) with a loading as low as 10:1 weight ratio. The thermal stability as well as the fire properties of the formulations were evaluated. Thermogravimetric analysis (TGA) showed that different coordination metals on the salen could induce different decomposition pathways when mixed with TPU. The Pyrolysis Combustion Flow Calorimetry (PCFC) results showed that some M-salen have the ability to significantly decrease the peak heat release rate (-61% compared to neat TPU) and total heat released (-63% compared to neat TPU) when formulated at 10:1 wt % ratio in TPU. Mass Loss Cone Calorimetry (MLC) results have shown that some additives (salen-Cu and salen-Mn) exhibit very promising performance and they are good candidates as flame-retardants for TPU.

SUBMITTER: Ramgobin A

PROVIDER: S-EPMC5554046 | biostudies-other | 2017 Jun

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Evaluation of the Thermal Stability and Surface Characteristics of Thermoplastic Polyurethane V-Belt.

Project description:This article proposes thermography as a non-contact diagnostic tool for assessing drive reliability. The application of this technique during the operation of the belt transmission with a heat-welded thermoplastic polyurethane V-belt was presented. The V-belt temperature changes depending on the braking torque load at different values of the rotational speed of the active pulley, which were adopted as diagnostic characteristics. In this paper, the surface morphology of the polyurethane (PU) belts was assessed on the basis of microscopic and hardness tests. A surface roughness tester was used to evaluate the surface wear. The surface morphology and topography of the materials was determined by scanning electron microscopy (SEM) and optical microscopy. It was found that the most favorable operating conditions occurred when the temperature values of active and passive connectors were similar and the temperature difference between them was small. The mechanical and structure results indicate that the wear of the PU belt was slight, which provided stability and operational reliability for V-belt transmission. The microscopic images lacked clear traces of cracks and scratches on the surface, which was confirmed by the SEM observations.

| S-EPMC7178032 | biostudies-literature

Mechanical Properties of Nonwoven Reinforced Thermoplastic Polyurethane Composites.

Project description:Reinforcement of flexible fibre reinforced plastic (FRP) composites with standard textile fibres is a potential low cost solution to less critical loading applications. The mechanical behaviour of FRPs based on mechanically bonded nonwoven preforms composed of either low or high modulus fibres in a thermoplastic polyurethane (TPU) matrix were compared following compression moulding. Nonwoven preform fibre compositions were selected from lyocell, polyethylene terephthalate (PET), polyamide (PA) as well as para-aramid fibres (polyphenylene terephthalamide; PPTA). Reinforcement with standard fibres manifold improved the tensile modulus and strength of the reinforced composites and the relationship between fibre, fabric and composite's mechanical properties was studied. The linear density of fibres and the punch density, a key process variable used to consolidate the nonwoven preform, were varied to study the influence on resulting FRP mechanical properties. In summary, increasing the strength and degree of consolidation of nonwoven preforms did not translate to an increase in the strength of resulting fibre reinforced TPU-composites. The TPU composite strength was mainly dependent upon constituent fibre stress-strain behaviour and fibre segment orientation distribution.

| S-EPMC5553526 | biostudies-literature

Influence of Characteristics of Thermoplastic Polyurethane on Graphene-Thermoplastic Polyurethane Composite Film.

Project description:Graphene-thermoplastic polyurethane (G-TPU) composite films were fabricated by traditional blending method and tape casting process with commercial graphene sheets as functional fillers and TPU masterbatches of four different melting points as matrix, respectively. The effects of matrix on the distribution of graphene, the electrical conductivity, and infrared (IR) light thermal properties of the G-TPU composite films were investigated. The experimental results reveal that the characteristics of TPU has little influence on the electrical conductivity of the G-TPU composite films, although the four TPU solutions have different viscosities. However, under the same graphene mass content, the thermal conductivity of four G-TPU composite films with different melting points is significantly different. The four kinds of G-TPU composite films have obvious infrared (IR) thermal effect. There is little difference in the temperatures between the composite films prepared by TPU with melting a point of 100 °C, 120 °C, and 140 °C, respectively; however, when the content of graphene is less than 5 wt%, the temperature of the composite film prepared by TPU with a melting point of 163 °C is obviously lower than that of the other three composite films. The possible reason for this phenomenon is related to the structure of TPU.

| S-EPMC7911175 | biostudies-literature

Multi-scale thermal stability of a hard thermoplastic protein-based material.

Project description:Although thermoplastic materials are mostly derived from petro-chemicals, it would be highly desirable, from a sustainability perspective, to produce them instead from renewable biopolymers. Unfortunately, biopolymers exhibiting thermoplastic behaviour and which preserve their mechanical properties post processing are essentially non-existent. The robust sucker ring teeth (SRT) from squid and cuttlefish are one notable exception of thermoplastic biopolymers. Here we describe thermoplastic processing of squid SRT via hot extrusion of fibres, demonstrating the potential suitability of these materials for large-scale thermal forming. Using high-resolution in situ X-ray diffraction and vibrational spectroscopy, we elucidate the molecular and nanoscale features responsible for this behaviour and show that SRT consist of semi-crystalline polymers, whereby heat-resistant, nanocrystalline β-sheets embedded within an amorphous matrix are organized into a hexagonally packed nanofibrillar lattice. This study provides key insights for the molecular design of biomimetic protein- and peptide-based thermoplastic structural biopolymers with potential biomedical and 3D printing applications.

| S-EPMC4595719 | biostudies-literature

Properties of Graphene/Shape Memory Thermoplastic Polyurethane Composites Actuating by Various Methods.

Project description:Shape memory behavior of crystalline shape memory polyurethane (SPU) reinforced with graphene, which utilizes melting temperature as a shape recovery temperature, was examined with various external actuating stimuli such as direct heating, resistive heating, and infrared (IR) heating. Compatibility of graphene with crystalline SPU was adjusted by altering the structure of the hard segment of the SPU, by changing the structure of the graphene, and by changing the preparation method of the graphene/SPU composite. The SPU made of aromatic 4,4'-diphenylmethane diisocyanate (MSPU) exhibited better compatibility with graphene, having an aromatic structure, compared to that made of the aliphatic hexamethylene diisocyanate. The finely dispersed graphene effectively reinforced MSPU, improved shape recovery of MSPU, and served effectively as a filler, triggering shape recovery by resistive or IR heating. Compatibility was enhanced when the graphene was modified with methanol. This improved shape recovery by direct heating, but worsened the conductivity of the composite, and consequently the efficiency of resistive heating for shape recovery also declined. Graphene modified with methanol was more effective than pristine graphene in terms of shape recovery by IR heating.

| S-EPMC5453273 | biostudies-other

Influence of the Characteristics of Expandable Graphite on the Morphology, Thermal Properties, Fire Behaviour and Compression Performance of a Rigid Polyurethane Foam.

Project description:Three types of expandable graphite (EG) differing in particle size and expansion volume, are compared as flame retardant additives to rigid polyurethane foams (RPUFs). In this paper we discuss microstructure, thermal stability, fire behavior, and compression performance. We find that ell size distributions were less homogeneous and cell size was reduced. Furthermore, thermal conductivity increased along with EG loading. Thermogravimetric analysis (TGA) showed that EG only increased residue yield differently. The results indicate that a higher expansion of EG increased the limiting oxygen index (LOI) value, whereas a bigger particle size EG improved the rating of the vertical burning test (UL94). Results from the cone calorimeter test showed that a bigger particle size EG effectively reduced peak of heat release rate (pHRR). Furthermore, a higher expansion, led to a decrease in smoke production (TSP). The combination of both characteristics gives extraordinary results. The physical⁻mechanical characterization of the EG/RPUF foams revealed that their compression performance decreased slightly, mostly due to the effect of a bigger size EG.

| S-EPMC6401788 | biostudies-literature

Experimental Study of Fire Hazards of Thermal-Insulation Material in Diesel Locomotive: Aluminum-Polyurethane.

Project description:This work investigated experimentally and theoretically the fire hazards of thermal-insulation materials used in diesel locomotives under different radiation heat fluxes. Based on the experimental results, the critical heat flux for ignition was determined to be 6.15 kW/m² and 16.39 kW/m² for pure polyurethane and aluminum-polyurethane respectively. A theoretical model was established for both to predict the fire behaviors under different circumstances. The fire behavior of the materials was evaluated based on the flashover and the total heat release rate (HRR). The fire hazards levels were classified based on different experimental results. It was found that the fire resistance performance of aluminum-polyurethane is much better than that of pure-polyurethane under various external heat fluxes. The concentration of toxic pyrolysis volatiles generated from aluminum-polyurethane materials is much higher than that of pure polyurethane materials, especially when the heat flux is below 50 kW/m². The hazard index HI during peak width time was proposed based on the comprehensive impact of time and concentrations. The predicted HI in this model coincides with the existed N-gas and FED models which are generally used to evaluate the fire gas hazard in previous researches. The integrated model named HNF was proposed as well to estimate the fire hazards of materials by interpolation and weighted average calculation.

| S-EPMC5456725 | biostudies-other

Self-Healing and Mechanical Properties of Thermoplastic Polyurethane/Eugenol-Based Phenoxy Resin Blends via Exchange Reactions.

Project description:The possibility of exchange reactions and thermal self-healing in blends of thermoplastic polyurethane (TPU) and phenoxy resin was investigated herein. The analyses were based on characterization obtained via differential scanning calorimetry (DSC), Fourier transform infrared spectroscopy (FTIR), dynamic mechanical analysis (DMA), and tensile test. A new phenoxy resin was synthesized from eugenol, and blends with different types of TPU were prepared to investigate the exchange reaction, thermal self-healing, and mechanical properties. The influence of phenoxy resin content on the mechanical behavior and healing efficiency was studied. Improvement of storage modulus owing to the increase of phenoxy resin content was observed. Results suggest that the exchange reaction between phenoxy- and ester-type TPU occurred during thermal treatment. However, little exchange occurred between phenoxy resin and ether-type TPU. Specifically, only ester-type TPU exhibited a significant exchange reaction in the phenoxy resin blend. Furthermore, in the presence of a catalyst (e.g., zinc acetate), the exchange reaction readily occurred, and the healing efficiency improved by the addition of the catalyst and increase in the phenoxy content.

| S-EPMC7284341 | biostudies-literature

Influence of the Halloysite Nanotube (HNT) Addition on Selected Mechanical and Biological Properties of Thermoplastic Polyurethane.

Project description:Halloysite nanotube (HNT) additions to the thermoplastic polyurethane (TPU) system were thoroughly evaluated in this study. The resultant composites have been designed for future personalized intervertebral disc implant applications, which requires additional technology to obtain the appropriate geometry unique to each patient. These requirements can be fulfilled using 3D printing. In this work, a technology was developed to produce filaments for fused deposition modeling (FDM). Nanocomposites were prepared using variable HNT content (1, 2, and 3 wt.%). The nanostructure of the resultant composites was confirmed using scanning transmission electron microscopy (STEM). Mechanical tests were used to measure the tensile modulus, stress, and elongation the composites and TPU matrix. Nanocomposites with 2% HNT content were able to withstand 26% increased stress and 50% increased elongation compared to pure TPU before fracturing in addition to a 13% reduction in the friction coefficient. A MTT cytotoxicity assay confirmed the cytotoxicity of all tested materials against human epidermal keratinocyte cells (HaCaT).

| S-EPMC8269716 | biostudies-literature

Silicone-Containing Biodegradable Smart Elastomeric Thermoplastic Hyperbranched Polyurethane.

Project description:Silicone-containing biobased hyperbranched polyurethane thermoplastic elastomers at different compositions were reported for the first time. The structures of the polymers were evaluated from Fourier transform infrared spectroscopy, NMR, X-ray diffraction, and energy-dispersive X-ray spectroscopy analyses. The synthesized elastomers possess high molecular weight (1.11-1.38 × 105 g·mol-1) and low glass transition temperature (from -40.0 to -27.3 °C). These polymers exhibited multistimuli responsive excellent repeatable intrinsic self-healing (100% efficiency), shape recovery (100%), and efficient self-cleaning (contact angle 102°-107°) abilities along with exceptional elongation at break (2834-3145%), high toughness (123.3-167.8 MJ·m-3), good impact resistance (18.3-20.3 kJ·m-1), and adequate tensile strength (5.9-6.9 MPa). Furthermore, high thermal stability (253-263 °C) as well as excellent UV and chemical resistance was also found for the polymers. Most interestingly, controlled bacterial biodegradation under exposure of Pseudomonas aeruginosa bacterial strains demonstrated them as sustainable materials. Therefore, such biobased novel thermoplastic polyurethane elastomers with self-healing, self-cleaning, and shape memory effects possess great potential for their advanced multifaceted applications.

| S-EPMC6045386 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data