Temperature and Copper Concentration Effects on the Formation of Graphene-Encapsulated Copper Nanoparticles from Kraft Lignin.
Ontology highlight
ABSTRACT:
SUBMITTER: Leng W
PROVIDER: S-EPMC5554058 | biostudies-other | 2017 Jun
REPOSITORIES: biostudies-other
Similar Datasets
Project description:Effects of physical and chemical states of iron-based catalysts on the formation of carbon-encapsulated iron nanoparticles (CEINs) synthesized thermally from kraft lignin were investigated. Experimental results indicated that if solution-based iron nitrate (FeN) was used as an iron source for the catalyst, CEINs observed were α-Fe and γ-Fe-based cores encapsulated by few layers graphitic-carbon (mostly 1-5 layers) and the majority of these CEINs were embedded in amorphous carbon matrix. The formation of graphitic-carbon shells is believed based on the dissolution and precipitation mechanism of amorphous carbon acting as the carbon source. If solid-based iron nanoparticles (FePs) were used as the catalyst, CEINs observed were α-Fe, γ-Fe, and Fe₃C-based cores encapsulated with tangled graphitic-carbon nanoribbons and carbon tubules and the majority of these CEINs were found along the edge of amorphous carbon matrix. The growth of tangled graphitic-carbon nanoribbons and carbon tubules is based on a chemical vapor decomposition process, i.e., the carbonaceous gases from kraft lignin decomposition served as the carbon source.
| S-EPMC5793637 | biostudies-literature
Project description:Porous graphene was photothermally induced from kraft lignin via direct laser writing. This laser-induced graphene (LIG) possessed a hierarchical structure with a three-dimensional (3D) interconnected network ideal for its transfer from the kraft lignin/poly(ethylene oxide) (KL/PEO) film onto polydimethylsiloxane (PDMS). The resultant LIG/PDMS composite was shown to keep the intrinsic porous structure and electrically active sites of LIG. The supercapacitors (SCs) fabricated using the LIG/PDMS composite exhibited good electrochemical performance and excellent cyclic stability. More than 90% capacitance was retained after 10?000 cycles. Moreover, due to their high flexibility, the SCs were able to endure bending deformation without significantly sacrificing their capacitance. The proposed technology for the fabrication of flexible SCs based on lignin-derived LIG demonstrated great potential to use a low-cost, renewable material for the manufacture of portable and wearable electronics.
| S-EPMC7315590 | biostudies-literature
Project description:The complex chemical structure and the fact that many areas in pulping and lignin chemistry still remain unresolved are challenges associated with exploiting lignin. In this study, we address questions regarding the formation and chemical nature of the insoluble residual lignin, the presence of fatty acids in kraft lignin, and the origin of secoisolariciresinol structures. A mild thermal treatment of lignin at maximum kraft-cooking temperatures (∼170 °C) with tall oil fatty acids (TOFA) or in an inert solvent (decane) produced highly insoluble products. However, acetylation of these samples enabled detailed chemical characterization by nuclear magnetic resonance (NMR) spectroscopy. The results show that the secoisolariciresinol (β-β) structure in kraft lignin is formed by rearrangement of the β-aryl ether structure. Furthermore, fatty acids bind covalently to kraft lignin by reacting with the stilbene structures present. It is highly probable that these reactions also occur during kraft pulping, and this phenomenon has an impact on controlling the present kraft pulping process along with the development of new products from kraft lignin.
| S-EPMC8278485 | biostudies-literature
Project description:BackgroundLignin is a potential feedstock for microbial conversion into various chemicals. However, the microbial degradation rate of native or technical lignin is low, and chemical depolymerization is needed to obtain reasonable conversion rates. In the current study, nine bacterial strains belonging to the Pseudomonas and Rhodococcus genera were evaluated for their ability to grow on alkaline-treated softwood lignin as a sole carbon source.ResultsPseudomonas fluorescens DSM 50090 and Rhodococcus opacus DSM1069 showed the best growth of the tested species on plates with lignin. Further evaluation of P. fluorescens and R. opacus was made in liquid cultivations with depolymerized softwood Kraft lignin (DL) at a concentration of 1 g/L. Size-exclusion chromatography (SEC) showed that R. opacus consumed most of the available lower-molecular weight compounds (approximately 0.1-0.4 kDa) in the DL, but the weight distribution of larger fractions was almost unaffected. Importantly, the consumed compounds included guaiacol-one of the main monomers in the DL. SEC analysis of P. fluorescens culture broth, in contrast, did not show a large conversion of low-molecular weight compounds, and guaiacol remained unconsumed. However, a significant shift in molecular weight distribution towards lower average weights was seen after cultivation with P. fluorescens.ConclusionsRhodococcus opacus and P. fluorescens were identified as two potential microbial candidates for the conversion/consumption of base-catalyzed depolymerized lignin, acting on low- and high-molecular weight lignin fragments, respectively. These findings will be of relevance for designing bioconversion of softwood Kraft lignin.
| S-EPMC6420747 | biostudies-literature
Project description:BackgroundLignin is a potential feedstock for microbial conversion into various chemicals. However, the degradation rate of native or technical lignin is low, and depolymerization is needed to obtain reasonable conversion rates. In the current study, base-catalyzed depolymerization-using NaOH (5 wt%)-of softwood Kraft lignin was conducted in a continuous-flow reactor system at temperatures in the range 190-240 °C and residence times of 1 or 2 min. The ability of growth of nine bacterial strains belonging to the genera Pseudomonas and Rhodococcus was tested using the alkaline-treated lignin as a sole carbon source.ResultsPseudomonas fluorescens and Rhodococcus opacus showed the best growth of the tested species on plates with lignin. Further evaluation of P. fluorescens and R. opacus was made in liquid cultivations with depolymerized lignin (DL) at a concentration of 1 g/L. Size exclusion chromatography (SEC) showed that R. opacus consumed most of the available lower molecular weight compounds (approximately 0.1-0.4 kDa) in the DL, but the weight distribution of larger fractions was almost unaffected. Importantly, the consumed compounds included guaiacol-one of the main monomers in the DL. SEC analysis of P. fluorescens culture broth, in contrast, did not show a large conversion of low molecular weight compounds, and guaiacol remained unconsumed. However, a significant shift in molecular weight distribution towards lower average weights was seen.ConclusionsRhodococcus opacus and P. fluorescens were identified as two potential microbial candidates for the conversion/consumption of base-catalyzed depolymerized lignin, acting on low and high molecular weight lignin fragments, respectively. These findings will be of relevance for designing bioconversion of softwood Kraft lignin.
| S-EPMC6123935 | biostudies-literature
Project description:Graphene-covered silver nanoparticles were prepared directly on highly oriented pyrolytic graphite substrates and characterized by atomic force microscopy. UV–Vis reflectance spectroscopy was used to measure the shift in the local surface plasmon resonance (LSPR) upon exposure to acetone, ethanol, 2-propanol, toluene, and water vapor. The optical responses were found to be substance-specific, as also demonstrated by principal component analysis. Point defects were introduced in the structure of the graphene overlayer by O2 plasma. The LSPR was affected by the plasma treatment, but it was completely recovered using subsequent annealing. It was found that the presence of defects increased the response for toluene and water while decreasing it for acetone.
| S-EPMC9319566 | biostudies-literature
Project description:Lignin has recently attracted the attention of the scientific community, as a suitable raw material for biomedical applications. In this work, acetylated lignin was used to encapsulate five different porphyrins, aiming to preserve their photophysical properties, and for further use as antibacterial treatment. The obtained nanoparticles were physically characterized, through dynamic light scattering size measurement, polydispersity index and zeta potential values. Additionally, the photophysical properties of the nanoparticles, namely UV-vis absorption, fluorescence emission, singlet oxygen production and photobleaching, were compared with those of the free porphyrins. It was found that all the porphyrins were susceptible to encapsulation, with an observed decrease in their fluorescence quantum yield and singlet oxygen production. These nanoparticles were able to exert an effective photodynamic bactericide effect (blue-LED light, 450-460 nm, 15 J/cm2) on Staphylococcus aureus and Escherichia coli. Furthermore, it was achieved a photodynamic bactericidal activity on an encapsulated lipophillic porphyrin, where the free porphyrin failed to diminish the bacterial survival. In this work it was demonstrated that acetylated lignin encapsulation works as a universal, cheap and green material for the delivery of porphyrins, while preserving their photophysical properties.
| S-EPMC8147155 | biostudies-literature
Project description:The synthesis and characterisation of a lignin-based elastomer system using lignin-epoxy-resins is presented. Untreated kraft black liquor was used to synthesise glycidyl lignin or black liquor-based epoxy resin (BLER), following a published procedure. A flexible, elastomeric thermoset was produced by cross-linking BLER with succinic anhydride (SA). The produced material was characterised in respect to its chemical, thermal, mechanical and swelling characteristics. In addition, vertical burning tests were performed. The obtained lignin-based elastomeric thermoset had a tensile strength of 1.0 ± 0.20 MPa and elastic moduli of 1.6 ± 1.4 and 0.44 ± 0.35 MPa at 5% and 50% elongation, respectively. A maximum elongation of 151 ± 49% was found.
| S-EPMC11217878 | biostudies-literature
Project description:Lignin from different biomasses possess biological antioxidation and antimicrobial activities, which depend on the number of functional groups and the molecular weight of lignin. In this work, organosolv fractionation was carried out to prepare the lignin fraction with a suitable structure to tailor excellent biological activities. Gel permeation chromatography (GPC) analysis showed that decreased molecular weight lignin fractions were obtained by sequentially organosolv fractionation with anhydrous acetone, 50% acetone and 37.5% hexanes. Nuclear magnetic resonance (NMR) results indicated that the lignin fractions with lower molecular weight had fewer substructures and a higher phenolic hydroxyl content, which was positively correlated with their antioxidation ability. Both of the original lignin and fractionated lignins possessed the ability to inhibit the growth of Gram-negative bacteria (Escherichia coli and Salmonella) and Gram-positive bacteria (Streptococcus and Staphylococcus aureus) by destroying the cell wall of bacteria in vitro, in which the lignin fraction with the lowest molecular weight and highest phenolic hydroxyl content (L3) showed the best performance. Besides, the L3 lignin showed the ability to ameliorate Escherichia coli-induced diarrhea damages of mice to improve the formation of intestinal contents in vivo. These results imply that a lignin fraction with a tailored structure from bamboo lignin can be used as a novel antimicrobial agent in the biomedical field.
| S-EPMC8188334 | biostudies-literature
Project description:Kraft lignin (KL) is extensively produced in industry but is mainly burned as fuel. To broaden its use, KL was grafted with dodecyl glycidyl ether to alter its thermal properties. The reaction of KL with dodecyl glycidyl ether (DGE) was analyzed using nuclear magnetic resonance (NMR), Fourier infrared spectroscopy (FT-IR) and elemental analysis. Alternatively, KL was methylated to mask its phenolic hydroxy groups to investigate how phenolic hydroxy groups impact the grafting of the alkyl chain of DGE onto lignin (methylated Kraft lignin, MKL). The methylation facilitated the molecular weight enhancement and thermal stability reduction of Kraft lignin via grafting with DGE. The influence of grafting alkyl chains on the structural and thermal properties of KL and MKL was studied using thermogravimetric analysis and differential scanning calorimetry analysis. Our data suggest that, due to their high molecular weights and lower glass transition temperatures, the produced lignin derivatives may be promising feedstocks for composite production.
| S-EPMC6786095 | biostudies-literature