Shear bond strength and adhesive remnant index of orthodontic brackets bonded to enamel using adhesive systems mixed with TiO2 nanoparticles.

ABSTRACT: INTRODUCTION:It is recently suggested that titanium dioxide (TiO2) nanoparticles can be added to bracket luting agents in order to reduce bacterial activity and protect the enamel. However, it is not known if this addition can affect the shear bond strength (SBS) below clinically acceptable levels. Therefore, this study examined this matter within a comprehensive setup. METHODS:This in vitro experimental study was conducted on 120 extracted human premolars randomly divided into four groups (n=30): in groups 1 and 2, Transbond XT light-cured composite with or without TiO2 was applied on bracket base; in groups 3 and 4, Resilience light-cured composite with or without TiO2 was used. Brackets were bonded to teeth. Specimens in each group (n=30) were divided into three subgroups of 10 each; then incubated at 37°C for one day, one month, or three months. The SBS and adhesive remnant index (ARI) were calculated and compared statistically within groups. RESULTS:The SBS was not significantly different at one day, one month or three months (p>0.05) but composites without TiO2 had a significantly higher mean SBS than composites containing TiO2 (p<0.001). The SBS of Transbond XT was significantly higher than that of Resilience (p<0.001). No significant differences were noted in ARI scores based on the type of composite or addition of TiO2 (p>0.05). CONCLUSIONS:Addition of TiO2 nanoparticles to Transbond XT decreased its SBS to the level of SBS of Resilience without TiO2; thus, TiO2 nanoparticles may be added to Transbond XT composite for use in the clinical setting.

SUBMITTER: Behnaz M

PROVIDER: S-EPMC6150699 | biostudies-other | 2018 Aug

REPOSITORIES: biostudies-other

ACCESS DATA

Publications

Shear bond strength and adhesive remnant index of orthodontic brackets bonded to enamel using adhesive systems mixed with TiO2 nanoparticles.

Behnaz Mohammad M Dalaie Kazem K Mirmohammadsadeghi Hoori H Salehi Hamed H Rakhshan Vahid V Aslani Farzin F

Dental press journal of orthodontics 20180801 4

<h4>Introduction</h4>It is recently suggested that titanium dioxide (TiO2) nanoparticles can be added to bracket luting agents in order to reduce bacterial activity and protect the enamel. However, it is not known if this addition can affect the shear bond strength (SBS) below clinically acceptable levels. Therefore, this study examined this matter within a comprehensive setup.<h4>Methods</h4>This in vitro experimental study was conducted on 120 extracted human premolars randomly divided into fo ...[more]

PMID: 30304159

Similar Datasets

Project description:Introduction: Remineralizing agents may be used for the treatment of white spot lesions (WSLs) prior to bracket bonding. However, some concerns exist regarding their possible interference with the etching and bonding process, negatively affecting the bond strength. This study aimed to assess the effect of two remineralizing agents with/without CO2 laser irradiation on the mechanical properties and shear bond strength (SBS) of demineralized enamel to the orthodontic bracket. Methods: This study evaluated 60 premolar teeth in 6 groups (n=10) as follows: (I) sound enamel, (II) demineralized enamel, (III) Nupro remineralizing agent (N), (IV) Nupro and CO2 laser (N/L), (V) Teethmate remineralizing agent (T), and (VI) Teethmate and CO2 laser (T/L). The remineralizing agents were applied to the enamel surfaces after their immersion in a demineralizing solution for 5 days. In groups IV and VI, the CO2 laser with a 10.6 ?m wavelength, 10 ms pulse duration, a 50 Hz repetition rate, 0.3 mm beam diameter and 0.7 W power was irradiated after applying the remineralizing agents. Brackets were bonded to the enamel surfaces and SBS was measured by a universal testing machine. For the assessment of enamel microhardness, 20 sections of molar teeth were divided into 4 groups (n=5; N, N/L, T, T/L) and their microhardness was measured before demineralization, after demineralization and after remineralization. X-ray diffraction (XRD) analysis, field-emission scanning electron microscopy (FESEM) and energy-dispersive spectrometry (EDS) were carried out to assess the formation of hydroxyapatite. The atomic percentages of the C, O, P, Ca, Na, Si, F and Ca/P ratio were determined by EDS analysis. Results: The SBS significantly decreased in group II (P<0.001). There was no significant difference among the groups I, III, IV, V and VI (P<0.05). This finding was similar to the microhardness results, which showed an increase in microhardness after remineralization (P<0.05), with no difference among the remineralizing agents. The Ca/P ratio was the highest in the Nupro group and the lowest in the demineralized group. Conclusion: Remineralizing agents can significantly improve the microhardness and structural properties of demineralized enamel to a level similar to that of sound enamel with no adverse effect on SBS to orthodontic brackets.

Dataset Information

Shear bond strength and adhesive remnant index of orthodontic brackets bonded to enamel using adhesive systems mixed with TiO2 nanoparticles.

Publications

Shear bond strength and adhesive remnant index of orthodontic brackets bonded to enamel using adhesive systems mixed with TiO2 nanoparticles.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets