Optoelectronic performance of indium tin oxide thin films structured by sub-picosecond direct laser interference patterning.

ABSTRACT: A route to increase the efficiency of thin film solar cells is improving the light-trapping capacity by texturing the top Transparent Conductive Oxide (TCO) so that the sunlight reaching the solar absorber scatters into multiple directions. In this study, Indium Tin Oxide (ITO) thin films are treated by infrared sub-picosecond Direct Laser Interference Patterning (DLIP) to modify the surface topography. Surface analysis by scanning electron microscopy and confocal microscopy reveals the presence of periodic microchannels with a spatial period of 5 µm and an average height between 15 and 450 nm decorated with Laser-Induced Periodic Surface Structures (LIPSS) in the direction parallel to the microchannels. A relative increase in the average total and diffuse optical transmittances up to 10.7% and 1900%, respectively, was obtained in the 400-1000 nm spectral range as an outcome of the interaction of white light with the generated micro- and nanostructures. The estimation of Haacke's figure of merit suggests that the surface modification of ITO with fluence levels near the ablation threshold might enhance the performance of solar cells that employ ITO as a front electrode.

SUBMITTER: Heffner H

PROVIDER: S-EPMC10275878 | biostudies-literature | 2023 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Optoelectronic performance of indium tin oxide thin films structured by sub-picosecond direct laser interference patterning.

Heffner Herman H Soldera Marcos M Lasagni Andrés Fabián AF

Scientific reports 20230616 1

A route to increase the efficiency of thin film solar cells is improving the light-trapping capacity by texturing the top Transparent Conductive Oxide (TCO) so that the sunlight reaching the solar absorber scatters into multiple directions. In this study, Indium Tin Oxide (ITO) thin films are treated by infrared sub-picosecond Direct Laser Interference Patterning (DLIP) to modify the surface topography. Surface analysis by scanning electron microscopy and confocal microscopy reveals the presence ...[more]

PMID: 37328683

Similar Datasets

Project description:Fabrication and organosilane-functionalization and characterization of nanostructured ITO electrodes are reported. Nanostructured ITO electrodes were obtained by electron beam evaporation, and a subsequent annealing treatment was selectively performed to modify their crystalline state. An increase in geometrical surface area in comparison with thin-film electrodes area was observed by atomic force microscopy, implying higher electroactive surface area for nanostructured ITO electrodes and thus higher detection levels. To investigate the increase in detectability, chemical organosilane-functionalization of nanostructured ITO electrodes was performed. The formation of 3-glycidoxypropyltrimethoxysilane (GOPTS) layers was detected by X-ray photoelectron spectroscopy. As an indirect method to confirm the presence of organosilane molecules on the ITO substrates, cyclic voltammetry and electrochemical impedance spectroscopy (EIS) were also carried out. Cyclic voltammograms of functionalized ITO electrodes presented lower reduction-oxidation peak currents compared with non-functionalized ITO electrodes. These results demonstrate the presence of the epoxysilane coating on the ITO surface. EIS showed that organosilane-functionalized electrodes present higher polarization resistance, acting as an electronic barrier for the electron transfer between the conductive solution and the ITO electrode. The results of these electrochemical measurements, together with the significant difference in the X-ray spectra between bare ITO and organosilane-functionalized ITO substrates, may point to a new exploitable oxide-based nanostructured material for biosensing applications. As a first step towards sensing, rapid functionalization of such substrates and their application to electrochemical analysis is tested in this work. Interestingly, oxide-based materials are highly integrable with the silicon chip technology, which would permit the easy adaptation of such sensors into lab-on-a-chip configurations, providing benefits such as reduced size and weight to facilitate on-chip integration, and leading to low-cost mass production of microanalysis systems.

Dataset Information

Optoelectronic performance of indium tin oxide thin films structured by sub-picosecond direct laser interference patterning.

Publications

Optoelectronic performance of indium tin oxide thin films structured by sub-picosecond direct laser interference patterning.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets