Construction of Ferric-Oxide-Doped Nickel–Iron Hydroxide Electrocatalysts by Magnetic-Field-Assisted Chemical Corrosion toward Boosted Oxygen Evolution Reaction
Ontology highlight
ABSTRACT:
SUBMITTER:
PROVIDER: S-EPMC11242944 | biostudies-literature | 2024 Jul
REPOSITORIES: biostudies-literature
Similar Datasets
Project description:The oxygen evolution reaction (OER) is the key reaction in water splitting systems, but compared with the hydrogen evolution reaction (HER), the OER exhibits slow reaction kinetics. In this work, boron doping into nickel-iron layered double hydroxide (NiFe LDH) was evaluated for the enhancement of OER electrocatalytic activity. To fabricate boron-doped NiFe LDH (B:NiFe LDH), gaseous boronization, a gas-solid reaction between boron gas and NiFe LDH, was conducted at a relatively low temperature. Subsequently, catalyst activation was performed through electrochemical oxidation for maximization of boron doping and improved OER performance. As a result, it was possible to obtain a remarkably reduced overpotential of 229 mV at 10 mA cm-2 compared to that of pristine NiFe LDH (315 mV) due to the effect of facile charge-transfer resistance by boron doping and improved active sites by electrochemical oxidation.
| S-EPMC8695062 | biostudies-literature
Project description:The efficient oxygen evolution reaction (OER) and oxygen reduction reaction (ORR) catalyst materials are crucial in the energy research domain due to their tunability. Structural modification in perovskites such as lanthanum cerates (LaCeO3) upon doping at A or B sites significantly affects the surface activity and enhances the catalysis efficacy. Herein, B-site nickel-doped lanthanum cerate (LaCe1-xNixO3±δ) nanopowders were applied as ORR indicators in high-temperature electrochemical impedance spectroscopy for solid-oxide fuel cell (SOFC) tests and in cyclic voltammetric OER investigations in alkaline medium. The integration into SOFC applications, via solid-state EIS in a co-pressed three-layered cell with LCNiO as cathode, is investigated in an oxygen-methane environment and reveals augmented conductivity with temperatures of 700-850°C. The higher electrokinetic parameters-including diffusion coefficients, Do heterogeneous rate constant, ko, and peak current density for OER in KOH-methanol at a LCNiO-9-modified glassy carbon electrode-serve as robust gauges of catalytic performance. CV indicators and EIS conductivities of LaCe1-xNixO3±δ nanomaterials indicate promising potencies for electrocatalytic energy applications.
| S-EPMC9731227 | biostudies-literature
Project description:Production of hydrogen through water splitting is one of the green and the most practical solutions to cope with the energy crisis and greenhouse effect. However, oxygen evolution reaction (OER) being a sluggish step, the use of precious metal-based catalysts is the main impediment toward the viability of water splitting. In this work, amorphous copper oxide and doped binary- and ternary-metal oxides (containing CoII, NiII, and CuII) have been prepared on the surface of fluorine-doped tin oxide by a facile electrodeposition route followed by thermal treatment. The fabricated electrodes have been employed as efficient binder-free OER electrocatalysts possessing a high electrochemical surface area due to their amorphous nature. The cobalt-nickel-doped copper oxide (ternary-metal oxide)-based electrode showed promising OER activity with a high current density of 100 mA cm-2 at 1.65 V versus RHE that escalates to 313 mA cm-2 at 1.76 V in alkaline media at pH 14. The high activity of the ternary-metal oxide-based electrode was further supported by a smaller semicircle in the Nyquist plot. Furthermore, all metal-oxide-based electrodes offered high stability when tested for continuous production of oxygen for 50 h. This work highlights the synthesis of efficient and cost-effective amorphous metal-based oxide catalysts to execute electrocatalytic OER employing an electrodeposition approach.
| S-EPMC8340103 | biostudies-literature
Project description:In this paper, low-pressure 95%Ar-5%H2, pure Ar, and 95%Ar-5%O2 plasmas were used for post-treatment of ruthenium (Ru) deposited on nickel foam (NF) (Ru/NF). Ru/NF was then tested as a catalyst for a hydrogen evolution reaction. Significant improvement in electrocatalytic activity with the lowest overpotential and Tafel slope was observed in an alkaline electrolyte (1 M KOH) with 95%Ar-5%O2 plasma processing on Ru/NF. Linear scanning electrical impedance spectroscopy (EIS) and cyclic voltammetry (CV) also indicate the lowest interfacial impedance and largest electrical double layer capacitance. Experimental results with 0.1 M phosphate buffered saline (PBS) and 0.5 M H2SO4 electrolytes were also demonstrated and compared.
| S-EPMC9000553 | biostudies-literature
Project description:Efficient electrocatalysts catalyzing oxygen evolution reaction (OER) in alkaline media is highly desirable for large-scale hydrogen production from water splitting. Here we report the direct electrodeposition of cerium-doped nickel hydroxide nanosheets on carbon fiber paper and its prominent performance in catalyzing the OER. The composite generates a current density of 100 mA cm-2 at an overpotential of 320 mV, rivaling the performance of most reported OER catalysts and commercially available RuO2. X-ray photoelectron spectroscopy analysis shows strong electronic interaction between Ni(OH)2 and CeO2, making a great contribution to the OER enhancement.
| S-EPMC9064652 | biostudies-literature
Project description:The strong ligand effect in B-doped Pd-based (PdB) catalysts renders them a promising anode for constructing formic acid fuel cells (FAFCs) exhibiting high power density and outstanding stability. However, the enhancement of the oxidation barrier is unavoidable in this alloy system owing to the electron transfer (ET) from B to Pd. In this study, a hydrogen doping strategy is employed to open charge freedom in PdB compounds and boost their formic acid oxidation reaction (FAOR) activity by suppressing the ET process. The resulting hydrogen-doped PdB (PdBH) exhibits an ultrahigh mass activity of up to 1.2A mg-1 Pd, which is 3.23 times that of the PdB catalyst and 9.55 times that of Pd black. Detailed experimental and theoretical studies show that the interstitial hydrogen leads to enhanced orbital hybridization and reduced electron density around Pd. This optimized ligand effect weakens the carbon monoxide adsorption and increases the direct pathway preference of PdBH, resulting in its outstanding catalytic activity for the FAOR. The development of this high-performance hydrogen-doped PdB catalyst is an important step toward the construction of advanced light element co-doped metal catalysts.
| S-EPMC11425968 | biostudies-literature
Project description:A novel and facile two-step strategy has been designed to prepare high performance bi-transition-metals (Fe- and Mo-) carbide supported on nitrogen-doped graphene (FeMo-NG) as electrocatalysts for oxygen reduction reactions (ORR). The as-synthesized FeMo carbide -NG catalysts exhibit excellent electrocatalytic activities for ORR in alkaline solution, with high onset potential (-0.09 V vs. saturated KCl Ag/AgCl), nearly four electron transfer number (nearly 4) and high kinetic-limiting current density (up to 3.5 mA cm(-2) at -0.8 V vs. Ag/AgCl). Furthermore, FeMo carbide -NG composites show good cycle stability and much better toxicity tolerance durability than the commercial Pt/C catalyst, paving their application in high-performance fuel cell and lithium-air batteries.
| S-EPMC4441168 | biostudies-literature
Project description:Nitrogen-containing superporous activated carbons were prepared by chemical polymerization of aniline and nitrogen functionalization by organic routes. The resulting N-doped carbon materials were carbonized at high temperatures (600⁻800 °C) in inert atmosphere. X-ray Photoelectron Spectroscopy (XPS) revealed that nitrogen amount ranges from 1 to 4 at.% and the nature of the nitrogen groups depends on the treatment temperature. All samples were assessed as electrocatalysts for the oxygen reduction reaction (ORR) in alkaline solution (0.1 M KOH) in order to understand the role of well-developed microporosity as well as the different nitrogen functionalities on the electrocatalytic performance in ORR. It was observed that nitrogen groups generated at high temperatures were highly selective towards the water formation. Among the investigated samples, polyaniline-derived activated carbon carbonized at 800 °C displayed the best performance (onset potential of 0.88 V versus RHE and an electron transfer number of 3.4), which was attributed to the highest concentration of N⁻C⁻O sites.
| S-EPMC6515461 | biostudies-literature
Project description:The exploration of earth-abundant electrocatalysts with high performance for the oxygen evolution reaction (OER) is eminently desirable and remains a significant challenge. The composite of the metal-organic framework (MOF) Ni10Co-BTC (BTC = 1,3,5-benzenetricarboxylate) and the highly conductive carbon material ketjenblack (KB) could be easily obtained from the MOF synthesis in the presence of KB in a one-step solvothermal reaction. The composite and the pristine MOF perform better than commercially available Ni/NiO nanoparticles under the same conditions for the OER. Activation of the nickel-cobalt clusters from the MOF can be seen under the applied anodic potential, which steadily boosts the OER performance. Ni10Co-BTC and Ni10Co-BTC/KB are used as sacrificial agents and undergo structural changes during electrochemical measurements, the stabilized materials show good OER performances.
| S-EPMC8875730 | biostudies-literature
Project description:Nickel-titanium (NiTi) alloys show broad applicability in biomedical fields. However, the unexpected aggregation of bacteria and the corrosion of body fluid on NiTi-based medical devices often lead to the leakage of nickel ions, resulting in inevitable allergic and cytotoxic activities. Therefore, the capture and detection of nickel ions are important to avoid serious adverse reactions caused by NiTi-based medical devices. Herein, we presented a nickel ion capture strategy by the combination of zwitterionic hydrogels as anti-bacteria layers and carbon disulfide (CS2) components as nickel-catchers (Ni-catchers). On the one hand, the hydration layer of zwitterionic hydrogel can efficiently inhibit bacteria adhesion and reduce nickel ions leakage from NiTi corrosion. On the other hand, Ni-catchers can capture leaked nickel ions from NiTi alloy actively by chelation reaction. Therefore, this strategy shows great capabilities in resisting bacteria adhesion and capturing nickel ions, providing the potential possibility for the detection of nickel ion leakage for implantable biomedical materials and devices.
| S-EPMC8264594 | biostudies-literature