Using hyperbranched oligomer functionalized glass fillers to reduce shrinkage stress.


ABSTRACT: Fillers are widely utilized to enhance the mechanical properties of polymer resins. However, polymerization stress has the potential to increase due to the higher elastic modulus achieved upon filler addition. Here, we demonstrate a hyperbranched oligomer functionalized glass filler UV curable resin composite which is able to reduce the shrinkage stress without sacrificing mechanical properties.A 16-functional alkene-terminated hyperbranched oligomer is synthesized by thiol-acrylate and thiol-yne reactions and the product structure is analyzed by (1)H NMR, mass spectroscopy, and gel permeation chromatography. Surface functionalization of the glass filler is measured by thermogravimetric analysis. Reaction kinetics, mechanical properties and shrinkage stress are studied via Fourier transform infrared spectroscopy, dynamic mechanical analysis and a tensometer, respectively.Silica nanoparticles are functionalized with a flexible 16-functional alkene-terminated hyperbranched oligomer which is synthesized by multistage thiol-ene/yne reactions. 93% of the particle surface was covered by this oligomer and an interfacial layer ranging from 0.7 nm to 4.5 nm thickness is generated. A composite system with these functionalized silica nanoparticles incorporated into the thiol-yne-methacrylate resin demonstrates 30% reduction of shrinkage stress (from 0.9 MPa to 0.6 MPa) without sacrificing the modulus (3100 ± 300 MPa) or glass transition temperature (62 ± 3°C). Moreover, the shrinkage stress of the composite system builds up at much later stages of the polymerization as compared to the control system.Due to the capability of reducing shrinkage stress without sacrificing mechanical properties, this composite system will be a great candidate for dental composite applications.

SUBMITTER: Ye S 

PROVIDER: S-EPMC3410741 | biostudies-literature | 2012 Sep

REPOSITORIES: biostudies-literature

altmetric image

Publications

Using hyperbranched oligomer functionalized glass fillers to reduce shrinkage stress.

Ye Sheng S   Azarnoush Setareh S   Smith Ian R IR   Cramer Neil B NB   Stansbury Jeffrey W JW   Bowman Christopher N CN  

Dental materials : official publication of the Academy of Dental Materials 20120618 9


<h4>Objective</h4>Fillers are widely utilized to enhance the mechanical properties of polymer resins. However, polymerization stress has the potential to increase due to the higher elastic modulus achieved upon filler addition. Here, we demonstrate a hyperbranched oligomer functionalized glass filler UV curable resin composite which is able to reduce the shrinkage stress without sacrificing mechanical properties.<h4>Methods</h4>A 16-functional alkene-terminated hyperbranched oligomer is synthesi  ...[more]

Similar Datasets

| S-EPMC4325052 | biostudies-literature
| S-EPMC4949378 | biostudies-literature
| S-EPMC5456651 | biostudies-other
| S-EPMC5665588 | biostudies-literature
| S-EPMC3792419 | biostudies-literature
| S-EPMC4613196 | biostudies-literature
| S-EPMC4725866 | biostudies-literature
| S-EPMC4926210 | biostudies-literature
| S-EPMC7807744 | biostudies-literature
| S-EPMC6853616 | biostudies-literature