Low modulus biomimetic microgel particles with high loading of hemoglobin.

ABSTRACT: We synthesized extremely deformable red blood cell-like microgel particles and loaded them with bovine hemoglobin (Hb) to potentiate oxygen transport. With similar shape and size as red blood cells (RBCs), the particles were fabricated using the PRINT (particle replication in nonwetting templates) technique. Low cross-linking of the hydrogel resulted in very low mesh density for these particles, allowing passive diffusion of hemoglobin throughout the particles. Hb was secured in the particles through covalent conjugation of the lysine groups of Hb to carboxyl groups in the particles via EDC/NHS coupling. Confocal microscopy of particles bound to fluorescent dye-labeled Hb confirmed the uniform distribution of Hb throughout the particle interior, as opposed to the surface conjugation only. High loading ratios, up to 5 times the amount of Hb to polymer by weight, were obtained without a significant effect on particle stability and shape, though particle diameter decreased slightly with Hb conjugation. Analysis of the protein by circular dichroism (CD) spectroscopy showed that the secondary structure of Hb was unperturbed by conjugation to the particles. Methemoglobin in the particles could be maintained at a low level and the loaded Hb could still bind oxygen, as studied by UV-vis spectroscopy. Hb-loaded particles with moderate loading ratios demonstrated excellent deformability in microfluidic devices, easily deforming to pass through restricted pores half as wide as the diameter of the particles. The suspension of concentrated particles with a Hb concentration of 5.2 g/dL showed comparable viscosity to that of mouse blood, and the particles remained intact even after being sheared at a constant high rate (1000 1/s) for 10 min. Armed with the ability to control size, shape, deformability, and loading of Hb into RBC mimics, we will discuss the implications for artificial blood.

SUBMITTER: Chen K

PROVIDER: S-EPMC3438367 | biostudies-literature | 2012 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Low modulus biomimetic microgel particles with high loading of hemoglobin.

Chen Kai K Merkel Timothy J TJ Pandya Ashish A Napier Mary E ME Luft J Christopher JC Daniel Will W Sheiko Sergei S DeSimone Joseph M JM

Biomacromolecules 20120817 9

We synthesized extremely deformable red blood cell-like microgel particles and loaded them with bovine hemoglobin (Hb) to potentiate oxygen transport. With similar shape and size as red blood cells (RBCs), the particles were fabricated using the PRINT (particle replication in nonwetting templates) technique. Low cross-linking of the hydrogel resulted in very low mesh density for these particles, allowing passive diffusion of hemoglobin throughout the particles. Hb was secured in the particles th ...[more]

PMID: 22852860

Similar Datasets

Project description:Starch-based emulsion microgel particles with different starch (15 and 20 wt %) and oil contents (0-15 wt %) were synthesized, and their lubrication performance under physiological conditions was investigated. Emulsion microgels were subjected to skin mimicking or oral cavity mimicking conditions, i.e., smooth hydrophobic polydimethylsiloxane ball-on-disc tribological tests, in the absence or presence of salivary enzyme (?-amylase). In the absence of enzyme, emulsion microgel particles (30-60 vol % particle content) conserved the lubricating properties of emulsion droplets, providing considerably lower friction coefficients (? ? 0.1) in the mixed lubrication regime compared to plain microgel particles (0 wt % oil). Upon addition of enzyme, the lubrication performance of emulsion microgel particles became strongly dependent on the particles' oil content. Microgel particles encapsulating 5-10 wt % oil showed a double plateau mixed lubrication regime having a lowest friction coefficient ? ? 0.03 and highest ? ? 0.1, the latter higher than with plain microgel particles. An oil content of 15 wt % was necessary for the microgel particles to lubricate similarly to the emulsion droplets, where both systems showed a normal mixed lubrication regime with ? ? 0.03. The observed trends in tribology, theoretical considerations, and the combined results of rheology, light scattering, and confocal fluorescence microscopy suggested that the mechanism behind the low friction coefficients was a synergistic enzyme- and shear-triggered release of the emulsion droplets, improving lubrication. The present work thus demonstrates experimentally and theoretically a novel biolubricant additive with stimuli-responsive properties capable of providing efficient boundary lubrication between soft polymeric surfaces. At the same time, the additive should provide an effective delivery vehicle for oil soluble ingredients in aqueous media. These findings demonstrate that emulsion microgel particles can be developed into multifunctional biolubricant additives for future use in numerous soft matter applications where both lubrication and controlled release of bioactives are essential.

Dataset Information

Low modulus biomimetic microgel particles with high loading of hemoglobin.

Publications

Low modulus biomimetic microgel particles with high loading of hemoglobin.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets