The resistance of cortical bone tissue to failure under cyclic loading is reduced with alendronate.

ABSTRACT: Bisphosphonates are the most prescribed preventative treatment for osteoporosis. However, their long-term use has recently been associated with atypical fractures of cortical bone in patients who present with low-energy induced breaks of unclear pathophysiology. The effects of bisphosphonates on the mechanical properties of cortical bone have been exclusively studied under simple, monotonic, quasi-static loading. This study examined the cyclic fatigue properties of bisphosphonate-treated cortical bone at a level in which tissue damage initiates and is accumulated prior to frank fracture in low-energy situations. Physiologically relevant, dynamic, 4-point bending applied to beams (1.5 mm × 0.5 mm × 10 mm) machined from dog rib (n=12/group) demonstrated mechanical failure and micro-architectural features that were dependent on drug dose (3 groups: 0, 0.2, 1.0mg/kg/day; alendronate [ALN] for 3 years) with cortical bone tissue elastic modulus (initial cycles of loading) reduced by 21% (p<0.001) and fatigue life (number of cycles to failure) reduced in a stress-life approach by greater than 3-fold with ALN1.0 (p<0.05). While not affecting the number of osteons, ALN treatment reduced other features associated with bone remodeling, such as the size of osteons (-14%; ALN1.0: 10.5±1.8, VEH: 12.2±1.6, ×10(3) ?m2; p<0.01) and the density of osteocyte lacunae (-20%; ALN1.0: 11.4±3.3, VEH: 14.3±3.6, ×10(2) #/mm2; p<0.05). Furthermore, the osteocyte lacunar density was directly proportional to initial elastic modulus when the groups were pooled (R=0.54, p<0.01). These findings suggest that the structural components normally contributing to healthy cortical bone tissue are altered by high-dose ALN treatment and contribute to reduced mechanical properties under cyclic loading conditions.

SUBMITTER: Bajaj D

PROVIDER: S-EPMC4041841 | biostudies-literature | 2014 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

The resistance of cortical bone tissue to failure under cyclic loading is reduced with alendronate.

Bajaj Devendra D Geissler Joseph R JR Allen Matthew R MR Burr David B DB Fritton J C JC

Bone 20140401

Bisphosphonates are the most prescribed preventative treatment for osteoporosis. However, their long-term use has recently been associated with atypical fractures of cortical bone in patients who present with low-energy induced breaks of unclear pathophysiology. The effects of bisphosphonates on the mechanical properties of cortical bone have been exclusively studied under simple, monotonic, quasi-static loading. This study examined the cyclic fatigue properties of bisphosphonate-treated cortica ...[more]

PMID: 24704262

Similar Datasets

Project description:Classic studies in bone mechanobiology have established the importance of loading parameters on the anabolic response. Most of these early studies were done using loading methods not currently in favor, and using non-murine species. Our objective was to re-examine the effects of several loading parameters on the response of cortical bone using the contemporary murine axial tibial compression model. We subjected tibias of 5-month old, female C57Bl/6 mice to cyclic (4?Hz) mechanical loading and examined bone formation responses using dynamic and static histomorphometry. First, using a reference protocol of 1,200 cycles/day, 5 days/week for 2 weeks, we confirmed the significant influence of peak strain magnitude on periosteal mineralizing surface (Ps.MS/BS) and bone formation rate (Ps.BFR/BS) (p?<?0.05, ANOVA). There was a significant induction of periosteal lamellar bone at a lower threshold of approx. -1,000??? and a transition from lamellar-woven bone near -2,000???. In contrast, on the endocortical surface, bone formation indices did not exhibit a load magnitude-dependent response and no incidence of woven bone. Next, we found that reducing daily cycle number from 1,200 to 300 to 60 did not diminish the bone formation response (p?>?0.05). On the other hand, reducing the daily frequency of loading from 5 consecutive days/week to 3 alternate days/week significantly diminished the periosteal response, from a loading-induced increase in Ps.MS/BS of 38% (loaded vs. control) for 5 days/week to only 15% for 3 days/week (p?<?0.05). Finally, we determined that reducing the study duration from 2 to 1 weeks of loading did not affect bone formation outcomes. In conclusion, cyclic loading to -1,800??? peak strain, at 4?Hz and 60 cycles/day for 5 consecutive days (1 week) induces an increase in periosteal lamellar bone formation with minimal incidence of woven bone in 5-month-old C57Bl/6 female mice. Our results provide a basis for reduction of loading duration (daily cycles and study length) without loss of anabolic effect as measured by dynamic histomorphometry. © 2017 Orthopaedic Research Society. Published by Wiley Periodicals, Inc. J Orthop Res 36:682-691, 2018.

Project description:Bone is a unique living tissue, which responds to the mechanical stimuli regularly imposed on it. Adolescence facilitates a favorable condition for the skeleton that enables the exercise to positively influence bone architecture and overall strength. However, it is still dubious for how long the skeletal benefits gained in adolescence is preserved at adulthood. The current study aims to use a rat model to investigate the effects of in vivo low- (LI), medium- (MI), and high- (HI) intensity cyclic loadings applied during puberty on longitudinal bone development, morphometry, and biomechanics during adolescence as well as at adulthood. Forty-two young (4-week-old) male rats were randomized into control, sham, LI, MI, and HI groups. After a 5 day/week for 8 weeks cyclic loading regime applied on the right tibia, loaded rats underwent a subsequent 41-week, normal cage activity period. Right tibias were removed at 52 weeks of age, and a comprehensive assessment was performed using μCT, mechanical testing, and finite element analysis. HI and MI groups exhibited reduced body weight and food intake at the end of the loading period compared with shams, but these effects disappeared afterward. HI cyclic loading increased BMD, bone volume fraction, trabecular thickness, trabecular number, and decreased trabecular spacing after loading. All loading-induced benefits, except BMD, persisted until the end of the normal cage activity period. Moreover, HI loading induced enhanced bone area, periosteal perimeter, and moment of inertia, which remained up to the 52nd week. After the normal cage activity at adulthood, the HI group showed increased ultimate force and stress, stiffness, postyield displacement and energy, and toughness compared with the sham group. Overall, our findings suggest that even though both trabecular and cortical bone drifted through age-related changes during aging, HI cyclic loading performed during adolescence can render lifelong benefits in bone microstructure and biomechanics. © 2020 The Authors. JBMR Plus published by Wiley Periodicals, Inc. on behalf of American Society for Bone and Mineral Research.

Dataset Information

The resistance of cortical bone tissue to failure under cyclic loading is reduced with alendronate.

Publications

The resistance of cortical bone tissue to failure under cyclic loading is reduced with alendronate.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets