Anomalous Plastic Deformation and Sputtering of Ion Irradiated Silicon Nanowires.

ABSTRACT: Silicon nanowires of various diameters were irradiated with 100 keV and 300 keV Ar(+) ions on a rotatable and heatable stage. Irradiation at elevated temperatures above 300 °C retains the geometry of the nanostructure and sputtering can be gauged accurately. The diameter dependence of the sputtering shows a maximum if the ion range matches the nanowire diameter, which is in good agreement with Monte Carlo simulations based on binary collisions. Nanowires irradiated at room temperature, however, amorphize and deform plastically. So far, plastic deformation has not been observed in bulk silicon at such low ion energies. The magnitude and direction of the deformation is independent of the ion-beam direction and cannot be explained with mass-transport in a binary collision cascade but only by collective movement of atoms in the collision cascade with the given boundary conditions of a high surface to volume ratio.

SUBMITTER: Johannes A

PROVIDER: S-EPMC4463547 | biostudies-literature | 2015 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Anomalous Plastic Deformation and Sputtering of Ion Irradiated Silicon Nanowires.

Johannes Andreas A Noack Stefan S Wesch Werner W Glaser Markus M Lugstein Alois A Ronning Carsten C

Nano letters 20150518 6

Silicon nanowires of various diameters were irradiated with 100 keV and 300 keV Ar(+) ions on a rotatable and heatable stage. Irradiation at elevated temperatures above 300 °C retains the geometry of the nanostructure and sputtering can be gauged accurately. The diameter dependence of the sputtering shows a maximum if the ion range matches the nanowire diameter, which is in good agreement with Monte Carlo simulations based on binary collisions. Nanowires irradiated at room temperature, however, ...[more]

PMID: 25951108

Similar Datasets

Atomic Configuration of Point Defect Clusters in Ion-Irradiated Silicon Carbide.

Project description:Silicon Carbide (SiC) is a promising cladding material for accident-tolerant fuel in light water reactors due to its excellent resistance to chemical attacks at high temperatures, which can prevent severe accident-induced environmental disasters. Although it has been known for decades that radiation-induced swelling at low temperatures is driven by the formation of black spot defects with sizes smaller than 2 nm in irradiated SiC, the structure of these defect clusters and the mechanism of lattice expansion have not been clarified and remain as one of the most important scientific issues in nuclear materials research. Here we report the atomic configuration of defect clusters using Cs-corrected transmission electron microscopy and molecular dynamics to determine the mechanism of these defects to radiation swelling. This study also provides compelling evidence that irradiation-induced point defect clusters are vacancy-rich clusters and lattice expansion results from the homogenous distribution of unrecovered interstitials in the material.

| S-EPMC5676775 | biostudies-literature

Kinked silicon nanowires-enabled interweaving electrode configuration for lithium-ion batteries.

Project description:A tri-dimensional interweaving kinked silicon nanowires (k-SiNWs) assembly, with a Ni current collector co-integrated, is evaluated as electrode configuration for lithium ion batteries. The large-scale fabrication of k-SiNWs is based on a procedure for continuous metal assisted chemical etching of Si, supported by a chemical peeling step that enables the reuse of the Si substrate. The kinks are triggered by a simple, repetitive etch-quench sequence in a HF and H2O2-based etchant. We find that the inter-locking frameworks of k-SiNWs and multi-walled carbon nanotubes exhibit beneficial mechanical properties with a foam-like behavior amplified by the kinks and a suitable porosity for a minimal electrode deformation upon Li insertion. In addition, ionic liquid electrolyte systems associated with the integrated Ni current collector repress the detrimental effects related to the Si-Li alloying reaction, enabling high cycling stability with 80% capacity retention (1695 mAh/gSi) after 100 cycles. Areal capacities of 2.42 mAh/cm2 (1276 mAh/gelectrode) can be achieved at the maximum evaluated thickness (corresponding to 1.3 mgSi/cm2). This work emphasizes the versatility of the metal assisted chemical etching for the synthesis of advanced Si nanostructures for high performance lithium ion battery electrodes.

| S-EPMC6023865 | biostudies-literature

Effect of Ion Irradiation on Nanoindentation Fracture and Deformation in Silicon Carbide

Project description:Silicon carbide is desirable for many nuclear applications, making it necessary to understand how it deforms after irradiation. Ion implantation combined with nanoindentation is commonly used to measure radiation-induced changes to mechanical properties; hardness and modulus can be calculated from load–displacement curves, and fracture toughness can be estimated from surface crack lengths. Further insight into indentation deformation and fracture is required to understand the observed changes to mechanical properties caused by irradiation. This paper investigates indentation deformation using high-resolution electron backscatter diffraction (HR-EBSD) and Raman spectroscopy. Significant differences exist after irradiation: fracture is suppressed by swelling-induced compressive residual stresses, and the plastically deformed region extends further from the indentation. During focused ion beam cross-sectioning, indentation cracks grow, and residual stresses are modified. The results clarify the mechanisms responsible for the modification of apparent hardness and apparent indentation toughness values caused by the compressive residual stresses in ion-implanted specimens. Supplementary Information The online version contains supplementary material available at 10.1007/s11837-021-04636-8.

| S-EPMC8549939 | biostudies-literature

Nanoindentation dataset of silicon and hafnia doped silicon coatings produced by magnetron sputtering.

Project description:Mechanical properties of three different coatings comprising of pure silicon, 36 mol% HfO2-doped silicon and 60 mol% HfO2-doped silicon on SiC substrate material were obtained by nanoindentation. The coatings aim at oxidation protective layers in environmental barrier coating systems for SiC/SiC ceramic matrix composites (CMC). The examined coatings were produced by physical vapour deposition (magnetron sputtering) and have been tested under cycling conditions between room temperature and 1523?K until 100?h accumulated hot time. In order to measure the hardness and the reduced Young's modulus, a Berkovich tip has been used with a constant depth modulus of 100?nm and 160?nm. Two depth moduli have been chosen to investigate a possible volume impact on the mechanical properties. Six successfully produced indents have been averaged to examine the hardness and reduced Young's modulus. The testing has been done on polished cross sections thereby minimising the impact of the substrate material on the measured values. This article provides data related to "Hafnia-doped Silicon Bond Coats manufactured by PVD for SiC/SiC CMCs".

| S-EPMC7306585 | biostudies-literature

Modification of the optical and structural properties of ZnO nanowires by low-energy Ar+ ion sputtering.

Project description:The effects of low-energy (?2 kV) Ar+ irradiation on the optical and structural properties of zinc oxide (ZnO) nanowires (NWs) grown by a simple and cost-effective low-temperature technique were investigated. Both photoluminescence spectra from ZnO NW-coated films and cathodoluminescence analysis of individual ZnO NWs demonstrated obvious evidences of ultraviolet/visible luminescent enhancement with respect to irradiation fluence. Annihilation of the thinner ZnO NWs after the ion bombardment was appreciated by means of high-resolution scanning electron microscopy and transmission electron microscopy (TEM), which results in an increasing NW mean diameter for increasing irradiation fluences. Corresponding structural analysis by TEM pointed out not only significant changes in the morphology but also in the microstructure of these NWs, revealing certain radiation-sensitive behavior. The possible mechanisms accounting for the decrease of the deep-level emissions in the NWs with the increasing irradiation fluences are discussed according to their structural modifications.

| S-EPMC3648432 | biostudies-other

Machine learning plastic deformation of crystals.

Project description:Plastic deformation of micron-scale crystalline solids exhibits stress-strain curves with significant sample-to-sample variations. It is a pertinent question if this variability is purely random or to some extent predictable. Here we show, by employing machine learning techniques such as regression neural networks and support vector machines that deformation predictability evolves with strain and crystal size. Using data from discrete dislocations dynamics simulations, the machine learning models are trained to infer the mapping from features of the pre-existing dislocation configuration to the stress-strain curves. The predictability vs strain relation is non-monotonic and exhibits a system size effect: larger systems are more predictable. Stochastic deformation avalanches give rise to fundamental limits of deformation predictability for intermediate strains. However, the large-strain deformation dynamics of the samples can be predicted surprisingly well.

| S-EPMC6294252 | biostudies-literature

Plastic deformation of protein monolayers.

Project description:Globular proteins are peculiar solids that display both local stability of their conformation and the ability to undergo large cooperative changes of shape (conformational changes). If one forces a large deformation of the molecule, such that the structure is necessarily changed, it is not obvious whether the deformed globule can still remain a solid or whether it will melt. Is it possible to plastically deform a protein? Here we investigate this question with a micro-mechanical experiment on a small region (approximately 10 molecules) of a protein monolayer adsorbed on a rigid surface. For the two proteins studied, albumin and myoglobin, we observed that the molecules can be substantially deformed (approximately 1-2 nm deformation) by comparatively small stresses applied for sufficiently long times. The deformation is irreversible, and the protein remains in the solid state (i.e., displays a nonzero shear modulus). The dynamics of the deformation is approximately logarithmic in time, similar to creep in solids. These results show that globular proteins adsorbed on a surface can be plastically deformed.

| S-EPMC1302309 | biostudies-other

One-Dimensional Porous Silicon Nanowires with Large Surface Area for Fast Charge⁻Discharge Lithium-Ion Batteries.

Project description:In this study, one-dimensional porous silicon nanowire (1D⁻PSiNW) arrays were fabricated by one-step metal-assisted chemical etching (MACE) to etch phosphorus-doped silicon wafers. The as-prepared mesoporous 1D⁻PSiNW arrays here had especially high specific surface areas of 323.47 m²·g-1 and were applied as anodes to achieve fast charge⁻discharge performance for lithium ion batteries (LIBs). The 1D⁻PSiNWs anodes with feature size of ~7 nm exhibited reversible specific capacity of 2061.1 mAh·g-1 after 1000 cycles at a high current density of 1.5 A·g-1. Moreover, under the ultrafast charge⁻discharge current rate of 16.0 A·g-1, the 1D⁻PSiNWs anodes still maintained 586.7 mAh·g-1 capacity even after 5000 cycles. This nanoporous 1D⁻PSiNW with high surface area is a potential anode candidate for the ultrafast charge⁻discharge in LIBs with high specific capacity and superior cycling performance.

| S-EPMC5977299 | biostudies-literature

Plastic Deformation Modes of CuZr/Cu Multilayers.

Project description:We synthesized CuZr/Cu multilayers and performed nanoindentation testing to explore the dependence of plastic deformation modes on the thickness of CuZr layers. The Cu layers were 18 nm thick and the CuZr layers varied in thickness from 4 nm to 100 nm. We observed continuous plastic co-deformation in the 4 nm and 10 nm CuZr - 18 nm Cu multilayers and plastic-induced shear instability in thick CuZr layers (>20 nm). The plastic co-deformation is ascribed to the nucleation and interaction of shear transformation zones in CuZr layers at the adjacent interfaces, while the shear instability is associated with the nucleation and propagation of shear bands in CuZr layers. Shear bands are initialized in the CuZr layers due to the accumulated glide dislocations along CuZr-Cu interfaces, and propagate into adjacent Cu layers via slips on {111} plane non-parallel to the interface. Due to crystallographic constraint of the Cu layers, shear bands are approximately parallel to {111} plane in the Cu layer.

| S-EPMC4794738 | biostudies-literature

Photocatalytic Properties of Porous Silicon Nanowires.

Project description:Porous silicon nanowires are synthesized through metal assisted wet-chemical etch of highly-doped silicon wafer. The resulted porous silicon nanowires exhibit a large surface area of 337 m(2)·g(-1) and a wide spectrum absorption across the entire ultraviolet, visible and near infrared regime. We further demonstrate that platinum nanoparticles can be loaded onto the surface of the porous silicon nanowires with controlled density. These combined advancements make the porous silicon nanowires an interesting material for photocatalytic applications. We show that the porous silicon nanowires and platinum nanoparticle loaded porous silicon nanowires can be used as effective photocatalysts for photocatalytic degradation of organic dyes and toxic pollutants under visible irradiation, and thus are of significant interest for organic waste treatment and environmental remediation.

| S-EPMC3242411 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data