Investigation of nanoyarn preparation by modified electrospinning setup.

ABSTRACT: Higher ordered structures of nanofibers, including nanofiber-based yarns and cables, have a variety of potential applications, including wearable health monitoring systems, artificial tendons, and medical sutures. In this study, twisted assemblies of polyacrylonitrile (PAN), polyvinylidene fluoride trifluoroethylene (PVDF-TrFE), and polycaprolactone (PCL) nanofibers were fabricated via a modified electrospinning setup, consisting of a rotating cone-shaped copper collector, two syringe pumps, and two high voltage power supplies. The fiber diameters and twist angles varied as a function of the rotary speed of the collector. Mechanical testing of the yarns revealed that PVDF-TrFe and PCL yarns have a higher strain-to-failure than PAN yarns, reaching 307% for PCL nanoyarns. For the first time, the porosity of nanofiber yarns was studied as a function of twist angle, showing that PAN nanoyarns are more porous than PCL yarns.

SUBMITTER: Levitt AS

PROVIDER: S-EPMC5455769 | biostudies-literature | 2017 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Investigation of nanoyarn preparation by modified electrospinning setup.

Levitt Ariana S AS Knittel Chelsea E CE Vallett Richard R Koerner Michael M Dion Genevieve G Schauer Caroline L CL

Journal of applied polymer science 20170116 19

Higher ordered structures of nanofibers, including nanofiber-based yarns and cables, have a variety of potential applications, including wearable health monitoring systems, artificial tendons, and medical sutures. In this study, twisted assemblies of polyacrylonitrile (PAN), polyvinylidene fluoride trifluoroethylene (PVDF-TrFE), and polycaprolactone (PCL) nanofibers were fabricated via a modified electrospinning setup, consisting of a rotating cone-shaped copper collector, two syringe pumps, and ...[more]

PMID: 28579635

Similar Datasets

Low-cost FDM 3D-printed modular electrospray/electrospinning setup for biomedical applications.

Project description:Here, we report on the inexpensive fabrication of an electrospray/electrospinning setup by fused deposition modelling (FDM) 3D printing and provide the files and parameters needed to print this versatile device. Both electrospray and electrospinning technologies are widely used for pharmaceutical, healthcare and bioengineering applications. The setup was designed to be modular, thus its parts can be exchanged easily. The design provides a safe setup, ensuring that the users are not exposed to the high voltage parts of the setup. PLA, PVA, and a thermoplastic elastomer filament were used for the 3D printing. The filament cost was $100 USD and the rig was printed in 6?days. An Ultimaker 3 FDM 3D printer was used with dual print heads, and the PVA was used as a water-soluble support structure. The end part of the setup had several gas channels, allowing a uniform gas flowing against the direction of the nanoparticles/nanofibers, enhancing the drying process by enhancing the evaporation rate. The setup was tested in both electrospray and electrospinning modes successfully. Both the .sldprt and .stl files are provided for free download.

| S-EPMC7333274 | biostudies-literature

Preparation of biopolymer fibers by electrospinning from room temperature ionic liquids.

Project description:Electrospinning is a versatile process used to prepare micro- and nano- sized fibers from various polymers dissolved in volatile solvents. In this report, cellulose and cellulose-heparin composite fibers are prepared from nonvolatile room temperature ionic liquid (RTIL) solvents by electrospinning. RTILs are extracted from the biopolymer fiber after the fiber formation using a cosolvent. Micron to nanometer sized, branched fibers were obtained from 10% (w/w) concentration of polysaccharide biopolymer in RTIL solution with an applied voltage of 15-20 kV. Cellulose-heparin composite fibers showed anticoagulant activity, demonstrating that the bioactivity of heparin remained unaffected even on exposure to a high voltage involved in electrospinning.

| S-EPMC4777308 | biostudies-literature

Preparation and Performance of Ultra-Fine Polypropylene Antibacterial Fibers via Melt Electrospinning.

Project description:Polypropylene (PP) fibers are employed commonly as the raw material of technical textiles (nonwovens), and the research focuses on fine-denier fibers and their functionalities. In this work, antibacterial PP masterbatches with different dosage (1-5 wt.%) of nano-ZnO particles as the antibacterial agent were prepared via a twin-screw extruder. The as-prepared PP masterbatches were electrospun on a home-made electrospinning device to afford ultra-fine PP fibers. The morphologies of as-spun ultrathin PP fibers with 16 μm of average diameter were observed by SEM. The structure and element distribution were characterized by means of energy-dispersive spectroscopy (EDS) and Fourier-transfer infrared spectroscopy (FTIR), respectively. There was some zinc obviously distributed on the surface when a dosage of ZnO more than 1 wt.% was used, which contributed to the antibacterial activity. The crystallinity of PP fibers was not affected strongly by the dosage of ZnO based on the differential scanning calorimetry (DSC) heating curves, while thermal decomposition improved with the increase in ZnO content, and the mechanical strength decreased predictably with the increase in inorganic ZnO content.

| S-EPMC7182946 | biostudies-literature

Influence of Polymer Relaxation Time on the Electrospinning Process: Numerical Investigation.

Project description:"Electrospinnability", or the ease with which a solution can be used to obtain bead-free uniform fibers, depends on a large number of parameters, including solution properties, process parameters and ambient conditions. In this study, the effect of the polymer relaxation time on electrospinning of dilute polymer solutions is investigated numerically. It is shown that elastic stresses (ES) increase exponentially with the Deborah number ( D e ). For each polymer concentration there exists a critical D e below which the ES are insufficient to overcome capillary stresses (CS) and lead to the formation of beaded fibers. However, above the critical D e , there is a higher probability of the ES overcoming the CS and leading to the formation of uniform fibers. This analysis suggests the possibility of improved electrospinnability even with dilute polymer solutions, provided the relaxation time is sufficiently large. It is also found that changes in the drag coefficient due to change in the polymer conformation and self-concentration of polymer molecules would become significant for the electrospinning of polymer solutions with a longer relaxation time and high conductivity.

| S-EPMC6418928 | biostudies-literature

An investigation of alkaline phosphatase enzymatic activity after electrospinning and electrospraying.

Project description:The high target specificity and multifunctionality of proteins has led to great interest in their clinical use. To this end, the development of delivery systems capable of preserving their bioactivity and improving bioavailability is pivotal to achieve high effectiveness and satisfactory therapeutic outcomes. Electrohydrodynamic (EHD) techniques, namely electrospinning and electrospraying, have been widely explored for protein encapsulation and delivery. In this work, monoaxial and coaxial electrospinning and electrospraying were used to encapsulate alkaline phosphatase (ALP) into poly(ethylene oxide) fibres and particles, respectively, and the effects of the processing techniques on the integrity and bioactivity of the enzyme were assessed. A full morphological and physicochemical characterisation of the blend and core-shell products was performed. ALP was successfully encapsulated within monolithic and core-shell electrospun fibres and electrosprayed particles, with drug loadings and encapsulation efficiencies of up to 21% and 99%, respectively. Monoaxial and coaxial electrospinning were equally effective in preserving ALP function, leading to no activity loss compared to fresh aqueous solutions of the enzyme. While the same result was observed for monoaxial electrospraying, coaxial electrospraying of ALP caused a 40% reduction in its bioactivity, which was attributed to the high voltage (22.5 kV) used during processing. This demonstrates that choosing between blend and coaxial EHD processing for protein encapsulation is not always straightforward, being highly dependent on the chosen therapeutic agent and the effects of the processing conditions on its bioactivity.

| S-EPMC8312041 | biostudies-literature

Preparation of Hydrophobic Film by Electrospinning for Rapid SERS Detection of Trace Triazophos.

Project description:For real application, it is an urgent demand to fabricate stable and flexible surface-enhanced Raman scattering (SERS) substrates with high enhancement factors in a large-scale and facile way. Herein, by using the electrospinning technique, a hydrophobic and flexible poly(styrene-co-butadiene) (SB) fibrous membrane is obtained, which is beneficial for modification of silver nanoparticles (Ag NPs) colloid in a small region and then formation of more "hot spots" by drying; the final SERS substrate is designated as Ag/SB. Hydrophobic Ag/SB can efficiently capture heterocyclic molecules into the vicinity of hot spots of Ag NPs. Such Ag/SB films are used to quantitatively detect trace triazophos residue on fruit peels or in the juice, and the limit of detection (LOD) of 2.5 × 10-8 M is achieved. Ag/SB films possess a capability to resist heat. As a case, 6-mercaptopurine (6MP) that just barely dissolves in 90 °C water is picked for conducting Ag/SB-film-based experiments.

| S-EPMC7436116 | biostudies-literature

Biodegradable and Reusable Cellulose-Based Nanofiber Membrane Preparation for Mask Filter by Electrospinning.

Project description:Environmentally friendly face masks with high filtration efficiency are in urgent need to fight against the COVID-19 pandemic, as well as other airborne viruses, bacteria and particulate matters. In this study, coaxial electrospinning was employed to fabricate a lithium chloride enhanced cellulose acetate/thermoplastic polyurethanes (CA/TPU-LiCl) face mask nanofiber filtration membrane, which was biodegradable and reusable. The analysis results show that the CA/TPU-LiCl membrane had an excellent filtration performance: when the filtration efficiency reached 99.8%, the pressure drop was only 52 Pa. The membrane also had an outstanding reusability. The filtration performance maintained at 98.2% after 10 test cycles, and an alcohol immersion disinfection treatment showed no effect on its filtration performance. In summary, the CA/TPU-LiCl nanofiber membrane made in this work is a promising biodegradable and reusable filtration material with a wide range of potential applications, including high-performance face mask.

| S-EPMC8777847 | biostudies-literature

High-Throughput Fabrication of Quality Nanofibers Using a Modified Free Surface Electrospinning.

Project description:Based on bubble electrospinning (BE), a modified free surface electrospinning (MFSE) using a cone-shaped air nozzle combined with a solution reservoir made of copper tubes was presented to increase the production of quality nanofibers. In the MFSE process, sodium dodecyl benzene sulfonates (SDBS) were added in the electrospun solution to generate bubbles on a liquid surface. The effects of applied voltage and generated bubbles on the morphology and production of nanofibers were investigated experimentally and theoretically. The theoretical analysis results of the electric field were in good agreement with the experimental data and showed that the quality and production of nanofibers were improved with the increase of applied voltage, and the generated bubbles would decrease the quality and production of nanofibers.

| S-EPMC5529302 | biostudies-other

Poly(3-hydroxybutyrate) production in an integrated electromicrobial setup: Investigation under stress-inducing conditions.

Project description:Poly(3-hydroxybutyrate) (PHB), a biodegradable polymer, can be produced by different microorganisms. The PHB belongs to the family of polyhydroxyalkanoate (PHA) that mostly accumulates as a granule in the cytoplasm of microorganisms to store carbon and energy. In this study, we established an integrated one-pot electromicrobial setup in which carbon dioxide is reduced to formate electrochemically, followed by sequential microbial conversion into PHB, using the two model strains, Methylobacterium extorquens AM1 and Cupriavidus necator H16. This setup allows to investigate the influence of different stress conditions, such as coexisting electrolysis, relatively high salinity, nutrient limitation, and starvation, on the production of PHB. The overall PHB production efficiency was analyzed in reasonably short reaction cycles typically as short as 8 h. As a result, the PHB formation was detected with C. necator H16 as a biocatalyst only when the electrolysis was operated in the same solution. The specificity of the source of PHB production is discussed, such as salinity, electricity, concurrent hydrogen production, and the possible involvement of reactive oxygen species (ROS).

| S-EPMC5919402 | biostudies-literature

Efficient low-cost preparation of <i>trans</i>-cyclooctenes using a simplified flow setup for photoisomerization.

Project description:AbstractBioorthogonal ligations have emerged as highly versatile chemical tools for biomedical research. The exceptionally fast reaction between 1,2,4,5-tetrazines and trans-cyclooctenes (TCOs), also known as tetrazine ligation, is frequently used in this regard. Growing numbers of applications for the tetrazine ligation led to an increased demand for TCO compounds, whose commercial availability is still very limited. Reported photochemical procedures for the preparation of TCOs using flow chemistry are straightforward and high yielding but require expensive equipment. Within this contribution, we present the construction and characterization of a low-cost flow photoreactor assembled from readily accessible components. Syntheses of all commonly used trans-cyclooctene derivatives were successfully carried out using the described system. We are convinced that the presented system for photoisomerization will promote access to bioorthogonally reactive TCO derivatives.Graphical abstract

| S-EPMC4785212 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data