Preparation and characterization of functionalized heparin-loaded poly-Ɛ-caprolactone fibrous mats to prevent infection with human papillomaviruses.

ABSTRACT: In this study, heparin-loaded poly-ɛ-caprolactone (PCL) fibrous mats were prepared and characterized based on their physical, cytotoxic, thermal, and biological properties. The main objective of the work described here was to test the hypothesis that incorporation of heparin into a PCL carrier could serve as bio-compatible material capable of inhibiting Human Papillomavirus (HPV) infection. The idea of firmly anchoring heparin to capture soluble virus, vs. a slow heparin release to inhibit a virus in solution was tested. Thus, one material was produced via conventional heparin matrix encapsulation and electrohydrodynamic fiber processing in one step. A second type of material was obtained via heparin crosslinking. This was achieved by running a carbodiimide/N-hydroxysuccinimide (EDC/NHS) coupling reaction on preformed PCL fibers. In vitro HPV16 L1 protein binding capacity studies were performed. Infectivity assays were done using HPV16 pseudoviruses (PsVs) carrying a GFP plasmid to directly test the ability of the fibrous mats to prevent internalization of HPV PsVs. The crosslinked heparin material presented a dissociation constant (Kd) value comparable to those found in the literature for different heparin-protein L1 peptide interactions. Both materials significantly reduced internalization of HPV PsVs, with a reduction of 94% of PsVs internalization when matrix encapsulated heparin-loaded material was present. Differences in performance between the two proposed structures are discussed.

SUBMITTER: Gonzalez D

PROVIDER: S-EPMC6028096 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Electrospun chitosan-graft-poly (ɛ-caprolactone)/poly (ɛ-caprolactone) nanofibrous scaffolds for retinal tissue engineering.

Project description:A promising therapy for retinal diseases is to employ biodegradable scaffolds to deliver retinal progenitor cells (RPCs) for repairing damaged or diseased retinal tissue. In the present study, cationic chitosan-graft-poly(ɛ-caprolactone)/polycaprolactone (CS-PCL/PCL) hybrid scaffolds were successfully prepared by electrospinning. Characterization of the obtained nanofibrous scaffolds indicated that zeta-potential, fiber diameter, and the content of amino groups on their surface were closely correlated with the amount of CS-PCL in CS-PCL/PCL scaffolds. To assess the cell-scaffold interaction, mice RPCs (mRPCs) were cultured on the electrospun scaffolds for 7 days. In-vitro proliferation assays revealed that mRPCs proliferated faster on the CS-PCL/PCL (20/80) scaffolds than the other electrospun scaffolds. Scanning electron microscopy and the real-time quantitative polymerase chain reaction results showed that mRPCs grown on CS-PCL/PCL (20/80) scaffolds were more likely to differentiate towards retinal neurons than those on PCL scaffolds. Taken together, these results suggest that CS-PCL/PCL(20/80) scaffolds have potential application in retinal tissue engineering.

| S-EPMC3075910 | biostudies-literature

Melt electrospinning of daunorubicin hydrochloride-loaded poly (?-caprolactone) fibrous membrane for tumor therapy.

Project description:Daunorubicin hydrochloride is a cell-cycle non-specific antitumor drug with a high therapeutic effect. The present study outlines the fabrication of daunorubicin hydrochloride-loaded poly (?-caprolactone) (PCL) fibrous membranes by melt electrospinning for potential application in localized tumor therapy. The diameters of the drug-loaded fibers prepared with varying concentrations of daunorubicin hydrochloride (1, 5, and 10 wt%) were 2.48 ± 1.25, 2.51 ± 0.78, and 2.49 ± 1.58 ?m, respectively. Fluorescence images indicated that the hydrophobic drug was dispersed in the hydrophilic PCL fibers in their aggregated state. The drug release profiles of the drug-loaded PCL melt electrospun fibrous membranes were approximately linear, with slow release rates and long-term release periods, and no observed burst release. The MTT assay was used to examine the cytotoxic effect of the released daunorubicin hydrochloride on HeLa and glioma cells (U87) in vitro. The inhibition ratios of HeLa and glioma cells following treatment with membranes prepared with 1, 5, and 10 wt% daunorubicin hydrochloride were 62.69%, 76.12%, and 85.07% and 62.50%, 77.27%, and 84.66%, respectively. Therefore, PCL melt electrospun fibrous membranes loaded with daunorubicin hydrochloride may be used in the local administration of oncotherapy.

| S-EPMC5935042 | biostudies-literature

Gelatinase-stimuli strategy enhances the tumor delivery and therapeutic efficacy of docetaxel-loaded poly(ethylene glycol)-poly(ɛ-caprolactone) nanoparticles.

Project description:Nanoscale drug carriers have been extensively developed to improve drug therapeutic efficiency. However, delivery of chemotherapeutic agents to tumor tissues and cells has not been favorably managed. In this study, we developed a novel "intelligent" nanoparticle, consisting of a gelatinase-cleavage peptide with poly(ethylene glycol) (PEG) and poly(ɛ-caprolactone) (PCL)-based structure for tumor-targeted docetaxel delivery (DOC-TNPs). The docetaxel-loaded PEG-PCL nanoparticles (DOC-NPs) that did not display gelatinase-stimuli behaviors were used as a control. We found clear evidence that the DOC-TNPs were transformed by gelatinases, allowing drug release and enhancing the cellular uptake of DOC (P < 0.01). In vivo biodistribution study demonstrated that targeted DOC-TNPs could accumulate and remain in the tumor regions, whereas non-targeted DOC-NPs rapidly eliminated from the tumor tissues. DOC-TNPs exhibited higher tumor growth suppression than commercialized Taxotere(®) (docetaxel; Jiangsu Hengrui Medicine Company, Jiangsu, China) and DOC-NPs on hepatic H22 tumor model via intravenous administration (P < 0.01). Both in vitro and in vivo experiments suggest that the gelatinase-mediated nanoscale delivery system is promising for improvement of antitumor efficacy in various overexpressed gelatinase cancers.

| S-EPMC3265997 | biostudies-literature

Development of Poly(ɛ-caprolactone) Scaffold Loaded with Simvastatin and Beta-Cyclodextrin Modified Hydroxyapatite Inclusion Complex for Bone Tissue Engineering.

Project description:In this study, we developed poly(ɛ-caprolactone) (PCL) 3D scaffolds using a solid free form fabrication (SFF) technique. β-cyclodextrin (βCD) was grafted to hydroxyapatite (HAp) and this βCD grafted HAp was coated onto the PCL scaffold surface, followed by drug loading through an inclusion complex interaction between the βCD and adamantane (AD) or between βCD and simvastatin (SIM). The scaffold structure was characterized by scanning electron microscopy (SEM). The release profile of simvastatin in the β-CD grafted HAp was also evaluated. Osteogenic differentiation of adipose-derived stromal cells (ADSCs) was examined using an alkaline phosphatase activity (ALP) assay. The results suggest that drug loaded PCL-HAp 3-D scaffolds enhances osteogenic differentiation of ADSCs.

| S-EPMC6432564 | biostudies-literature

Controlling Topography and Crystallinity of Melt Electrowritten Poly(ɛ-Caprolactone) Fibers.

Project description:Melt electrowriting (MEW) is an aspiring 3D printing technology with an unprecedented resolution among fiber-based printing technologies. It offers the ability to direct-write predefined designs utilizing a jet of molten polymer to fabricate constructs composed of fibers with diameters of only a few micrometers. These dimensions enable unique construct properties. Poly(ɛ-caprolactone) (PCL), a semicrystalline polymer mainly used for biomedical and life science applications, is the most prominent material for MEW and exhibits excellent printing properties. Despite the wealth of melt electrowritten constructs that have been fabricated by MEW, a detailed investigation, especially regarding fiber analysis on a macro- and microlevel is still lacking. Hence, this study systematically examines the influence of process parameters such as spinneret diameter, feeding pressure, and collector velocity on the diameter and particularly the topography of PCL fibers and sheds light on how these parameters affect the mechanical properties and crystallinity. A correlation between the mechanical properties, crystallite size, and roughness of the deposited fiber, depending on the collector velocity and applied feeding pressure, is revealed. These findings are used to print constructs composed of fibers with different microtopography without affecting the fiber diameter and thus the macroscopic assembly of the printed constructs.

| S-EPMC9828622 | biostudies-literature

Physical and Antibacterial Properties of Peppermint Essential Oil Loaded Poly (?-caprolactone) (PCL) Electrospun Fiber Mats for Wound Healing.

Project description:The aim of this study was to fabricate and characterize various concentrations of peppermint essential oil (PEP) loaded on poly(?-caprolactone) (PCL) electrospun fiber mats for healing applications, where PEP was intended to impart antibacterial activity to the fibers. SEM images illustrated that the morphology of all electrospun fiber mats was smooth, uniform, and bead-free. The average fiber diameter was reduced by the addition of PEP from 1.6 ± 0.1 to 1.0 ± 0.2 ?m. Functional groups of the fibers were determined by Raman spectroscopy. Gas chromatography-mass spectroscopy (GC-MS) analysis demonstrated the actual PEP content in the samples. In vitro degradation was determined by measuring weight loss and their morphology change, showing that the electrospun fibers slightly degraded by the addition of PEP. The wettability of PCL and PEP loaded electrospun fiber mats was measured by determining contact angle and it was shown that wettability increased with the incorporation of PEP. The antimicrobial activity results revealed that PEP loaded PCL electrospun fiber mats exhibited inhibition against Staphylococcus aureus (gram-positive) and Escherichia coli (gram-negative) bacteria. In addition, an in-vitro cell viability assay using normal human dermal fibroblast (NHDF) cells revealed improved cell viability on PCL, PCLPEP1.5, PCLPEP3, and PCLGEL6 electrospun fiber mats compared to the control (CNT) after 48 h cell culture. Our findings showed for the first time PEP loaded PCL electrospun fiber mats with antibiotic-free antibacterial activity as promising candidates for wound healing applications.

| S-EPMC6988806 | biostudies-literature

Poly(ɛ-caprolactone)/gelatin composite electrospun scaffolds with porous crater-like structures for tissue engineering.

Project description:Electrospinning has been widely used to fabricate scaffolds imitating the structure of natural extracellular matrix (ECM). However, conventional electrospinning produces tightly compacted nanofiber layers with only small superficial pores and a lack of bioactivity, which limit the usefulness of electrospinning in biomedical applications. Thus, a porous poly(ε-caprolactone) (PCL)/gelatin composite electrospun scaffold with crater-like structures was developed. Porous crater-like structures were created on the scaffold by a gas foaming/salt leaching process; this unique fiber structure had more large pore areas and higher porosity than the conventional electrospun fiber network. Various ratios of PCL/gelatin (concentration ratios: 100/0, 75/25, and 50/50) composite electrospun scaffolds with and without crater-like structures were characterized by their microstructures, surface chemistry, degradation, mechanical properties, and ability to facilitate cell growth and infiltration. The combination of PCL and gelatin endowed the scaffold with both structural stability of PCL and bioactivity of gelatin. All ratios of scaffolds with crater-like structures showed fairly similar surface chemistry, degradation rates, and mechanical properties to equivalent scaffolds without crater-like structures; however, craterized scaffolds displayed higher human mesenchymal stem cell (hMSC) proliferation and infiltration throughout the scaffolds after 7-day culture. Therefore, these results demonstrated that PCL/gelatin composite electrospun scaffolds with crater-like structures can provide a structurally and biochemically improved three-dimensional ECM-mimicking microenvironment.

| S-EPMC5206917 | biostudies-literature

Properties, X-ray data and 2D WAXD fitting procedures of melt-spun poly(ɛ-caprolactone).

Project description:Rheological and thermal properties of the poly(ɛ-caprolactone) (PCL) polymer are presented in Section 1.1. Section 1.2 summarizes results of melt-spun PCL filaments. Specifically, we show the necking point stabilization during high-speed online drawing in Section 1.2.1, filament morphology in Section 1.2.2, wide-angle X-ray diffraction (WAXD) fitting results in Section 1.2.3, WAXD patterns of aged fibers in Section 1.2.4, crystallinity analysis in Section 1.2.5 and small-angle X-ray scattering (SAXS) analysis results in Section 1.2.6. Details about the materials, experimental and analytical methods are given in Section 2. Of particular interest may be the simulation and fitting procedures of 2D WAXD patterns, which are summarized in Section 2.7.2. For more information see the publication by Selli et al. 'Mesophase in melt-spun poly(ɛ-caprolactone) filaments: structure-mechanical property relationship' [1].

| S-EPMC7479331 | biostudies-literature

In vivo vascularization of MSC-loaded porous hydroxyapatite constructs coated with VEGF-functionalized collagen/heparin multilayers.

Project description:Rapid and adequate vascularization is vital to the long-term success of porous orbital enucleation implants. In this study, porous hydroxyapatite (HA) scaffolds coated with vascular endothelial growth factor (VEGF)-functionalized collagen (COL)/heparin (HEP) multilayers (porosity 75%, pore size 316.8 ± 77.1 ?m, VEGF dose 3.39 ng/mm(3)) were fabricated to enhance vascularization by inducing the differentiation of mesenchymal stem cells (MSCs) to endothelial cells. The in vitro immunofluorescence staining, quantitative real-time polymerase chain reaction (qRT-PCR), and western blotting results demonstrated that the expression of the endothelial differentiation markers CD31, Flk-1, and von Willebrand factor (vWF) was significantly increased in the HA/(COL/HEP)5/VEGF/MSCs group compared with the HA/VEGF/MSCs group. Moreover, the HA/(COL/HEP)5 scaffolds showed a better entrapment of the MSCs and accelerated cell proliferation. The in vivo assays showed that the number of newly formed vessels within the constructs after 28 d was significantly higher in the HA/(COL/HEP)5/VEGF/MSCs group (51.9 ± 6.3/mm(2)) than in the HA (26.7 ± 2.3/mm(2)) and HA/VEGF/MSCs (38.2 ± 2.4/mm(2)) groups. The qRT-PCR and west rn blotting results demonstrated that the HA/(COL/HEP)5/VEGF/MSCs group also had the highest expression of CD31, Flk-1, and vWF at both the mRNA and protein levels.

| S-EPMC4726420 | biostudies-literature

Multicomponent Non-Woven Fibrous Mats with Balanced Processing and Functional Properties.

Project description:The mimicking of the architectonics of native tissue, biodegradable non-woven fibrous mats is one of the most promising forms of scaffolding for tissue engineering. The key properties needed for their successful application in vivo, such as biodegradability, biocompatibility, morphology, mechanical properties, etc., rely on their composition and appropriate 3D structure. A multicomponent system based on biodegradable synthetic (polycaprolactone, oligo-/polylactide) and natural (chitosan, gelatin) polymers, providing the desired processing characteristics and functionality to non-woven mats fabricated via the electrospinning technique, was developed. The solid-state reactive blending of these components provided a one-step synthesis of amphiphilic graft copolymer with an ability to form stable ultra-fine dispersions in chlorinated solvents, which could be successfully used as casting solvents for the electrospinning technique. The synthesized graft copolymer was analyzed with the aim of fractional analysis, dynamic laser scattering, FTIR-spectroscopy and DSC. Casting solution characteristics, namely viscosity, surface tension, and electroconductivity, as well as electrospinning parameters, were studied and optimized. The morphology, chemical structure of the surface layer, mechanical properties and cytocompatibility were analyzed to confirm the appropriate functionality of the formed fibrous materials as scaffolds for tissue engineering.

| S-EPMC7563478 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data