Copolymers of vinyl-containing benzoxazine with vinyl monomers as precursors for high performance thermosets.

ABSTRACT: A benzoxazine containing a vinyl group (P-4va) was prepared by the reaction of phenol, 4-vinylaniline, and paraformaldehyde. A differential scanning calorimetry (DSC) study revealed that ring-opening polymerization of the benzoxazine and chain polymerization of the vinyl group occurred in the same temperature range. When 2,2'-azobisisobutyronitrile was added as a radical initiator to P-4va, however, only the vinyl groups were polymerized at lower temperature, giving oligo(P-4va) that contains pendent benzoxazine units. Radical copolymerization of P-4va with various vinyl monomers such as styrene, methyl methacrylate (MMA), and n-butyl acrylate (BuA) was examined. The chemical structure of the copolymers was confirmed by FT-IR and 1H-NMR to be one of polyolefins bearing benzoxazine units as the pendant groups. The weight-average molecular weights of the copolymers determined by size exclusion chromatography were to be in the range of 1900-51,500 depending on the comonomers. DSC of the copolymers showed that the maxima of the exothermic peaks corresponding to the ring-opening polymerization of the pendent benzoxazine units were observed in the temperature range of 229-250 °C. Thermal cure up to 240 °C of the copolymer films afforded homogenous transparent films with improved thermal properties. Tough cured film was obtained by the copolymerization with MMA, while a tough and flexible film was obtained by the copolymerization with BuA.

SUBMITTER: Takeichi T

PROVIDER: S-EPMC6272515 | biostudies-literature | 2015 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Copolymers of vinyl-containing benzoxazine with vinyl monomers as precursors for high performance thermosets.

Takeichi Tsutomu T Thongpradith Soulideth S Kawauchi Takehiro T

Molecules (Basel, Switzerland) 20150410 4

A benzoxazine containing a vinyl group (P-4va) was prepared by the reaction of phenol, 4-vinylaniline, and paraformaldehyde. A differential scanning calorimetry (DSC) study revealed that ring-opening polymerization of the benzoxazine and chain polymerization of the vinyl group occurred in the same temperature range. When 2,2'-azobisisobutyronitrile was added as a radical initiator to P-4va, however, only the vinyl groups were polymerized at lower temperature, giving oligo(P-4va) that contains pe ...[more]

PMID: 25867832

Similar Datasets

Project description:Water-insoluble cationic poly(vinyl alcohol) (PVA) films were fabricated using a mixed aqueous solution of PVA and poly([2-(methacryloyloxy)ethyl]trimethylammonium chloride (METAC)-co-methacrylic acid (MAAc)-co-5-methacrylamido-1,2-benzoxaborole (MAAmBO)) copolymer (3D). The surface of the PVA film is typically negatively charged, and simple fabrication methods for water-insoluble PVA films with cationic surface charges are required to expand their application fields. METAC, which has a permanent positive charge owing to the presence of a quaternary ammonium cation, was selected as the cationic unit. The MAAc and MAAmBO units were used as two types of cross-linking structures for the thermal cross-linking of the hydroxy and carboxy groups of the MAAc unit (covalent bonding) as well as the diol and benzoxaborole groups of the MAAmBO unit (dynamic covalent bonding). The films were thermally cross-linked at 135 °C for 4 h without the addition of materials. After immersion in surplus water at 80 °C for 3 h, the cross-linked PVA/3D films retained almost 100% of their weights. The ζ-potential of the water-insoluble PVA/3D film was 9.4 ± 0.8 mV. The PVA/3D film was strongly dyed using anionic acid red 1 (AR1) because of its positively charged surface. Interestingly, it could also be slightly dyed using cationic methylene blue (MB) and became transparent (original state) after immersion in water for 2 days. These results suggested that positive and negative charges coexisted in the PVA/3D film, and the surface properties were positively inclined. Moreover, the degree of hemolysis of the PVA/3D films was similar to that of the negative control, which showed high blood compatibility. To our knowledge, this is the first report on the fabrication of water-insoluble cationic PVA films using two types of cross-linking structures containing carboxy and benzoxaborole groups. The cross-linked PVA films were analyzed using Fourier transform infrared (FT-IR) spectroscopy, differential scanning calorimetry (DSC), and contact angle (CA) and ζ-potential measurement, as well as by determining the mechanical properties, adsorption of charged molecules, and biocompatibility. These readily fabricated water-insoluble PVA films with positive charges can show potential applications in sensors, adsorption systems, and antimicrobial materials.

Dataset Information

Copolymers of vinyl-containing benzoxazine with vinyl monomers as precursors for high performance thermosets.

Publications

Copolymers of vinyl-containing benzoxazine with vinyl monomers as precursors for high performance thermosets.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets