One-Step Synthesis of Ag@TiO? Nanoparticles for Enhanced Photocatalytic Performance.

ABSTRACT: Polyamide network polymers (PNP) modified TiO? nanoparticles (NPs) were decorated with Ag NPs in hydrothermal gel method, forming one-step synthesized photocatalysts, Ag@TiO? NPs. The effect of PNP and the amount of Ag NPs added were investigated in this work. PNP acted as a nanocage to prevent TiO? aggregation and capture Ag accurately, which could effectively control product sizes and improve dispersibility in solvents. Simultaneously, TiO? NPs modified with Ag NPs exhibited remarkable photocatalytic effects. One-step synthesis simplified the experimental process and avoided the agglomeration of silver ions during the secondary reaction, achieving the purpose of uniform distribution at a specific location of TiO? NPs. The prepared Ag@TiO? NPs-0.5 could remove 79.49% of Methyl Orange (MO) after 3 h of ultraviolet light irradiation, which was 2.7 times higher than the reaction rate of pure TiO? NPs. It also exhibited good photoactivity under Visible light conditions. Moreover, the mineralization rate of MO over the Ag@TiO2 NPs-0.5 could be up to 72.32% under UV light and 47.08% under Visible light irradiation, which revealed that the prepared catalysts could effectively degrade most of the MO to CO? and H?O. The samples also demonstrated the excellent stability and easy recyclability with over 90% of the original catalytic level for MO degradation. The photocatalysts studied also exerted broad application prospects such as photovoltaic hydrogen production, electronic sensors and biomedicine.

SUBMITTER: Zhang Y

PROVIDER: S-EPMC6316728 | biostudies-literature | 2018 Dec

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:In this article, the TiO2/SiO2-np nanocomposite multilayer films were synthesized in a single step by reactive magnetron sputtering combined with a nanoparticle aerosol jet. The SiO2 nanoparticles (SiO2-np) were introduced into a growing TiO2 thin film with different time sequences during deposition for a fixed duration. The SiO2-np acting as impurities are introduced into the TiO2 to willingly disturb its growth and to cause growth defects in order to increase the specific surface area of the photocatalytic film. In reason of the non-photoactive properties of the SiO2 nanoparticles, their introduction allows us to study only the effects induced on the film morphology, microstructure, and photocatalytic properties by their incorporation. The fractographies and topographies reveal strong changes in the morphologies depending on the time sequence of the nanoparticle introduction in the thin films. The introduction of SiO2-np from the beginning of the TiO2 film growth leads to the formation of high and large growth defects resulting in a highly diffusive surface. In addition, XRD analysis shows that the crystallite size tends to decrease as the composite film layer gets closer to the surface. Their photocatalytic performance is obtained by following the degradation of orange G dye under UV-visible irradiation. The photocatalytic performance is not only related to the specific surface area of the catalyst film, and the coverage of the photoactive phase on the surface, but also to the crystal quality of the photoactive phase. Furthermore, the samples exhibit good photostability, maintaining the same activity after four degradation cycles. In the specific case of TiO2/SiO2-np, it is demonstrated that the introduction of the nanoparticles only at the beginning of the film growth is more efficient than a continuous introduction. This result suggests that this original process allows the use of a relevant strategy for the nanoparticle introduction according to the required functionality.

Dataset Information

One-Step Synthesis of Ag@TiO? Nanoparticles for Enhanced Photocatalytic Performance.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets