Solute clustering and supersaturated solid solution of AlSi10Mg alloy fabricated by selective laser melting.
Ontology highlight
ABSTRACT:
SUBMITTER: Maeshima T
PROVIDER: S-EPMC6370582 | biostudies-literature | 2019 Feb
REPOSITORIES: biostudies-literature
Similar Datasets
Project description:AlSi10Mg alloy branches were fabricated by selective laser melting (SLM), and the branches were employed to evaluate their effect on the mechanical properties. When the porous branches were compressed along its building direction, the tree column structures-type AlSi10Mg alloy branches collapsed twice, which had typical elastic, shear, collapse, and densification stages. The compressive stress concentration at the interface between the support and the porous body caused the fracture of the tree column structures-type AlSi10Mg alloy branches. The fracture surface indicated that the prepared tree-type branches were distributed with different shapes of dimples, and the Si content inside the dimples was higher than that of the edge. The morphology of the Al-Si eutectic structure formed by SLM and the stress concentration at the Al/Al-Si-eutectic interface affected the fracture morphology and Si content distribution.
| S-EPMC7560194 | biostudies-literature
Project description:The aim of this review is to analyze and to summarize the state of the art of the processing of aluminum alloys, and in particular of the AlSi10Mg alloy, obtained by means of the Additive Manufacturing (AM) technique known as Selective Laser Melting (SLM). This process is gaining interest worldwide, thanks to the possibility of obtaining a freeform fabrication coupled with high mechanical properties related to a very fine microstructure. However, SLM is very complex, from a physical point of view, due to the interaction between a concentrated laser source and metallic powders, and to the extremely rapid melting and the subsequent fast solidification. The effects of the main process variables on the properties of the final parts are analyzed in this review: from the starting powder properties, such as shape and powder size distribution, to the main process parameters, such as laser power and speed, layer thickness, and scanning strategy. Furthermore, a detailed overview on the microstructure of the AlSi10Mg material, with the related tensile and fatigue properties of the final SLM parts, in some cases after different heat treatments, is presented.
| S-EPMC5344617 | biostudies-other
Project description:Multi-laser beam selective laser melting (SLM) technology based on a powder bed has been used to manufacture AlSi10Mg samples. The AlSi10Mg alloy was used as research material to systematically study the performance consistency of both the laser overlap areas and the isolated areas of the multi-laser beam SLM manufactured parts. The microstructures and mechanical properties of all isolated and overlap processing areas were compared under optimized process parameters. It was discovered that there is a raised platform at the junction of the overlap areas and the isolated areas of the multi-laser SLM samples. The roughness is significantly reduced after two scans. However, the surface roughness of the samples is highest after four scans. As the number of laser scans increases, the relative density of the overlap areas of the samples improves, and there is no significant change in hardness. The tensile properties of the tensile samples are poor when the overlap area width is 0, 0.1, or 0.2 mm. When the widths of the overlap areas are equal to or greater than 0.3 mm, there is no significant difference in the tensile strength between the overlap and the isolated areas.
| S-EPMC6316947 | biostudies-other
Project description:Ti-6Al-4V (TC4) titanium alloy parts were successfully fabricated by laser melting deposition (LMD) technology in this study. Proper normalizing temperatures were presented in detailed for bulk LMD specimens. Optical microscope, scanning electron microscopy, X-ray diffraction, and electronic universal testing machine were used to characterize the microstructures, phase compositions, the tensile properties and hardness of the TC4 alloy parts treated using different normalizing temperature. The experimental results showed that the as-fabricated LMD specimens' microstructures mainly consisted of ?-Ti phase with a small amount of ?-Ti phase. After normalizing treatment, in the area of ?-Ti phase, the recrystallized length and width of ?-Ti phase both increased. When normalizing in the (? + ?) phase field, the elongated primary ?-Ti phase in the as-deposited state was truncated due to the precipitation of ?-Ti phase and became a short rod-like primary ?-Ti phase. In as-fabricated microstructure, the ?-Ti phase was precipitated between different short rod-shaped ?-Ti phases distributed as basketweave. After normalizing treatment at 990 for two hours with subsequent air cooling, the TC4 titanium alloy had significant different microstructures from original sample produced by LMD. The normalizing treatment methods and temperature can be qualified as a prospective heat treatment of titanium alloy fabricating by laser melting deposition.
| S-EPMC7560422 | biostudies-literature
Project description:The dynamic metallurgical characteristics of the selective laser melting (SLM) process offer fabricated materials with non-equilibrium microstructures compared to their cast and wrought counterparts. To date, few studies on the precipitation kinetics of SLM processed heat-treatable alloys have been reported, despite the importance of obtaining such detailed knowledge for optimizing the mechanical properties. In this study, for the first time, the precipitation behavior of an SLM fabricated Al-Mn-Sc alloy was systematically investigated over the temperature range of 300-450 °C. The combination of in-situ synchrotron-based ultra-small angle X-ray scattering (USAXS), small angle X-ray scattering (SAXS) and X-ray diffraction (XRD) revealed the continuous evolution of Al6Mn and Al3Sc precipitates upon isothermal heating in both precipitate structure and morphology, which was confirmed by ex-situ transmission electron microscopy (TEM) studies. A pseudo-delay nucleation and growth phenomenon of the Al3Sc precipitates was observed for the SLM fabricated Al-Mn-Sc alloy. This phenomenon was attributed to the preformed Sc clusters in the as-fabricated condition due to the intrinsic heat treatment effect induced by the unique layer-by-layer building nature of SLM. The growth kinetics for the Al6Mn and Al3Sc precipitates were established based on the in-situ X-ray studies, with the respective activation energies determined to be (74 ± 4) kJ/mol and (63 ± 9) kJ/mol. The role of the precipitate evolution on the final mechanical properties was evaluated by tensile testing, and an observed discontinuous yielding phenomenon was effectively alleviated with increased aging temperatures.
| S-EPMC7574377 | biostudies-literature
Project description:Microstructures and age-hardening phenomena of directly aged (artificial aged) AlSi10Mg alloys fabricated by laser powder bed fusion (LPBF) were characterized using scanning transmission electron microscopy, atom probe tomography, and Vickers hardness testing. The microstructure derived from overlapping melt pools has a full cellular structure consisting of eutectic Si walls surrounding α-Al cells. In the initial stage of aging, solute clusters with density on the order of 1024/m3 were formed in α-Al cells. By prolonging the aging time further, fine Si particles of about 50 nm in diameter precipitated. Before Si precipitation, the hardness of the aged sample was clearly greater than that of the as-built state. With further aging time, the hardness increased further because of the Si precipitation. Cluster analysis revealed that the number density and the size of clusters increased from as-built state by aging, whereas the types of the solute clusters remained almost unchanged by aging. The results indicate that the nanoscale clusters within the α-Al cells, which increase via aging, produce age-hardening effect.
| S-EPMC10955321 | biostudies-literature
Project description:Results of a study on microstructural evolution of eutectic Sn-57 wt.% Bi processed with cooling rates of 10-2, 1 K s-1 and approximately 105 K s-1 are presented. In order to distinguish different mechanisms of microstructure formation, a comparison with microstructures of different hypoeutectic alloys with compositions down to below the maximum solubility of Bi in Sn-Bi is undertaken. It is found that at the cooling rates of 10-2 and 1 K s-1, coupled eutectic growth occurs, leading to lamellar structures with different length scales. At the rapid quenching rates of approximately 105 K s-1, structure formation in the eutectic alloy is qualitatively different. Partitionless solidification resulting in a supersaturated solid solution with the initial composition is observed in both eutectic and hypoeutectic alloys. It is shown that the observed microstructure of the rapidly solidified alloys forms by the decomposition of the supersaturated solid solution. This article is part of the theme issue 'Heterogeneous materials: metastable and non-ergodic internal structures'.
| S-EPMC6460057 | biostudies-literature
Project description:The laser power bed fusion approach has been successfully employed to manufacture Mo(Si,Al)2-based composites through the selective laser melting of a MoSi2-30 wt.% AlSi10Mg mixture for high-temperature structural applications. Composites were manufactured by leveraging the in situ reaction of the components during printing at 150-300 W laser power, 500-1000 mm·s-1 laser scanning speed, and 100-134 J·mm-3 volumetric energy density. Microcomputed tomography scans indicated a negligible induced porosity throughout the specimens. The fully dense Mo(Si1-x,Alx)2-based composites, with hardness exceeding 545 HV1 and low roughness for both the top (horizontal) and side (vertical) surfaces, demonstrated that laser-based additive manufacturing can be exploited to create unique structures containing hexagonal Mo(Si0.67Al0.33)2.
| S-EPMC7504486 | biostudies-literature
Project description:This study characterized properties of Ti-6Al-4V ELI (extra low interstitial, ASTM grade 23) specimens fabricated by a laser beam melting (LBM) and an electron beam melting (EBM) system for dental applications. Titanium alloy specimens were made into required size and shape for each standard test using fabrication methods. The LBM specimens were made by an LBM machine utilizing 20 µm of Ti-6Al-4V ELI powder. Ti-6Al-4V ELI specimens were also fabricated by an EBM using 40 µm of Ti-6Al-4V ELI powder (average diameter, 40 µm: Arcam ABÒ) in a vacuum. As a control, cast Ti-6Al-4V ELI specimens (Cast) were made using a centrifugal casting machine in an MgO-based mold. Also, a wrought form of Ti-6Al-4V ELI (Wrought) was used as a control. The mechanical properties, corrosion properties and grindability (wear properties) were evaluated and data was analyzed using ANOVA and a non-parametric method (α = 0.05). The strength of the LBM and wrought specimens were similar, whereas the EBM specimens were slightly lower than those two specimens. The hardness of both the LBM and EBM specimens was similar and slightly higher than that of the cast and wrought alloys. For the higher grindability speed at 1,250 m/min, the volume loss of Ti64 LBM and EBM showed no significant differences among all the fabrication methods. LBM and EBM exhibited favorable results in fabricating dental appliances with excellent properties as found for specimens made by other fabricating methods.
| S-EPMC5448875 | biostudies-other
Project description:Catalytic Rh-based alloy nanoparticles (NPs) with inhomogeneous solid-solution structures were prepared from homogeneous solid-solution alloy NPs. Compared with homogeneous alloy NPs, these inhomogeneous alloy NPs exhibited enhanced catalytic activity and superior catalytic durability. Homogeneous solid-solution alloy NPs consisting of Rh and other immiscible noble metals were synthesized by laser-induced nucleation method in metallic ion solutions. STEM elemental mapping and EDS composition analysis of the particles clearly demonstrated that all the constituents were uniformly dispersed within the NPs. Moreover, the compositions of the alloys were nearly identical to the initial feeding ratios of metallic ions in the mixed solutions, strongly indicating the formation of equimolar solid-solution alloy NPs over the entire composition range. Although the catalytic stability of these Rh-based homogeneous alloy NPs during CO oxidation was improved, their catalytic activity was comparable to that of pure metal catalysts, owing to the uniform local structure at the atomic level. However, the catalytic activity of the alloy NPs was enhanced by heat treatment, which introduced inhomogeneity in the atomic distribution within the NPs. The enhanced activity was due to dissimilar interfaces in the inhomogeneous solid-solution alloy NPs.
| S-EPMC9076014 | biostudies-literature