The Effects of in Situ-Formed Silver Nanoparticles on the Electrical Properties of Epoxy Resin Filled with Silver Nanowires.

ABSTRACT: A novel method for preparing epoxy/silver nanocomposites was developed via the in situ formation of silver nanoparticles (AgNPs) within the epoxy resin matrix while using silver nanowires (AgNWs) as a conductive filler. The silver?imidazole complex was synthesized from silver acetate (AgAc) and 1-(2-cyanoethyl)-2-ethyl-4-methylimidazole (imidazole). AgNPs were generated in situ during the curing of the epoxy resin through the thermal decomposition of the AgAc?imidazole complex, which was capable of reducing Ag? to Ag by itself. The released imidazole acted as a catalyst to cure the epoxy. Additionally, after the curing process, the in situ-generated AgNPs were stabilized by the formed epoxy network. Therefore, by using the thermal decomposition method, uniformly dispersed AgNPs of approximately 100 nm were formed in situ in the epoxy matrix filled with AgNWs. It was observed that the nanocomposites containing in situ-formed AgNPs exhibited isotropic electrical properties in the epoxy resins in the presence of AgNWs.

SUBMITTER: Song GS

PROVIDER: S-EPMC6432508 | biostudies-literature | 2016 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

The Effects of in Situ-Formed Silver Nanoparticles on the Electrical Properties of Epoxy Resin Filled with Silver Nanowires.

Song Gwang-Seok GS Lee Dai Soo DS Kang Ilho I

Polymers 20160421 4

A novel method for preparing epoxy/silver nanocomposites was developed via the <i>in situ</i> formation of silver nanoparticles (AgNPs) within the epoxy resin matrix while using silver nanowires (AgNWs) as a conductive filler. The silver⁻imidazole complex was synthesized from silver acetate (AgAc) and 1-(2-cyanoethyl)-2-ethyl-4-methylimidazole (imidazole). AgNPs were generated <i>in situ</i> during the curing of the epoxy resin through the thermal decomposition of the AgAc⁻imidazole complex, whi ...[more]

PMID: 30979250

Similar Datasets

Project description:Graphene nanoplatelets (GNP) and carbon nanotubes (CNT) are used to enhance electrical and mechanical properties of epoxy-based nanocomposites. Despite the evidence of synergetic effects in the hybrid GNP-CNT-epoxy system, there is still a lack of studies that focus on the influence of different dispersion methods on the final properties of these ternary systems. In the present work, direct and indirect ultrasonication methods were used to prepare single- and hybrid-filled GNP-CNT-epoxy nanocomposites, varying the amplitude and time of sonication in order to investigate their effect on electrical and thermomechanical properties. Impedance spectroscopy was combined with rheology and electron microscopy to show that high-power direct sonication tends to degrade electrical conductivity in GNP-CNT-epoxy nanocomposites due to damage caused in the nanoparticles. CNT-filled samples were mostly benefitted by low-power direct sonication, achieving an electrical conductivity of 1.3 × 10-3 S·m-1 at 0.25 wt.% loading, while indirect sonication was not able to properly disperse the CNTs and led to a conductivity of 1.6 ± 1.3 × 10-5. Conversely, specimens filled with 2.5 wt. % of GNP and processed by indirect sonication displayed an electrical conductivity that is up to 4 orders of magnitude higher than when processed by direct sonication, achieving 5.6 × 10-7 S·m-1. The introduction of GNP flakes improved the dispersion state and conductivity in hybrid specimens processed by indirect sonication, but at the same time impaired these properties for high-power direct sonication. It is argued that this contradictory effect is caused by a selective localization of shorter CNTs onto GNPs due to strong π-π interactions when direct sonication is used. Dynamic mechanical analysis showed that the addition of nanofillers improved epoxy's storage modulus by up to 84%, but this property is mostly insensitive to the different processing parameters. Decrease in crosslinking degree and presence of residual solvent confirmed by Fourier-transform infrared spectroscopy, however, diminished the glass transition temperature of the nanocomposites by up to 40% when compared to the neat resin due to plasticization effects.

Project description:Objective:To compare the elastic modulus, flexural strength, and hardness of an experimental resin based composite (RBC) with and without containing silver nanoparticles (AgNPs) and bioactive glass (BAG) with a commercially available RBC. Methods:This study was conducted, during the period August 2016-May 2018, at the Department of Dental Materials, Peshawar Dental College, Peshawar (Pakistan) and Department of Chemistry, University of Montreal, Canada. Test specimens made in the commercial RBC acted as Group-1 (G1). An experimental RBC containing 70 wt % filler content was synthesized. It was first used as such to prepare test specimens to act as the experimental control group (G2). This RBC was then modified by adding various amounts of BAG (5%, 10% and 15%) and a fixed amount of 0.009% AgNPs to use the so modified RBCs for preparing the test specimens to belong to three groups (G3, G4 & G5). The AgNPs had been synthesized in situ by reduction of salt during photo-polymerization. Flexural strength (FS), elastic modulus (EM) and Vickers hardness were determined using universal testing machine and hardness tester respectively. Data were analyzed using one-way ANOVA and Tukey post-hoc test. Results:Except for G3 restorations showing significantly lower mean FS value, the FS for those in the other groups were not significantly different (p>0.05). Elastic modulus of the experimental RBC restorations was though higher than those of the others but the difference was statistically insignificant (p>0.05). Reduced Vickers hardness values were documented for the restorations in the G4 and G5 compared to those in the G3 but again the difference was insignificant (p>0.05). Flexural strength and hardness values of the test specimens in the experimental RBCs were significantly lower than those made in the commercial hybrid RBC (p<0.05). Conclusion:BAG and AgNPs addition to the experimental RBC in the mentioned concentration adversely affected the tested mechanical properties.

Dataset Information

The Effects of in Situ-Formed Silver Nanoparticles on the Electrical Properties of Epoxy Resin Filled with Silver Nanowires.

Publications

The Effects of in Situ-Formed Silver Nanoparticles on the Electrical Properties of Epoxy Resin Filled with Silver Nanowires.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets