Fabrication of inclined non-symmetrical periodic micro-structures using Direct Laser Interference Patterning.

ABSTRACT: The direct fabrication of microstructures, having a non-symmetrical morphology with controllable inclination, presents nowadays a challenging task. Natural examples of surfaces with inclined topographies have shown to provide anisotropic functionalities, which have attracted the interest of several researchers in the last years. This work presents a microfabrication technique for producing microstructures with a determined and controllable inclination angle using two-beam Direct Laser Interference Patterning. Polyimide foils are irradiated with a 4 ns UV (266 nm) laser source producing line-like structures with a period varying from 4.6 µm to 16.5 µm. The inclinations, retrieved by tilting the sample with respect to the optical axis of the setup, are changed from 0° to 75°, introducing a well controllable and defined inclination of the structure walls. The structuring parameters (laser fluence, number of laser pulses and interference period) as well as the inclination of the microstructures are correlated with the global tilting of the sample. As a result, a determined laser fluence and number of pulses are necessary to observe a remarkable non-symmetrical morphology of the structures. In addition, the presence of structural undercuts is reported, which opens the possibility for developing new direction-dependent properties on polymeric materials. As an example, preliminary results on light diffraction are presented, showing a similar behavior as blazed diffraction gratings.

SUBMITTER: Alamri S

PROVIDER: S-EPMC6443938 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:The nucleation of bubbles on solid surfaces is an important phenomenon in nature and technological processes like electrolysis. During proton-exchange membrane electrolysis, the nucleation and separation of the electrically nonconductive oxygen in the anodic cycle plays a crucial role to minimize the overpotential it causes in the system. This increases the efficiency of the process, making renewable energy sources and the "power-to-gas" strategy more viable. A promising approach is to optimize gas separation by surface functionalization in order to apply a more advantageous interface to industrial materials. In this work, the connection between the wettability and bubble nucleation of oxygen is investigated. For tailoring the wettability of Ti64 substrates, the direct laser interference patterning method is applied. A laser source with a wavelength of 1064 nm and a pulse duration of 12 ps is used to generate periodic pillar-like structures with different depths up to ∼5 μm. The resulting surface properties are characterized by water contact angle measurement, scanning electron microscopy, confocal microscopy, and X-ray photon spectroscopy. It was possible to generate structures with a water contact angle ranging from 20° up to nearly superhydrophobic conditions. The different wettabilities are validated based on X-ray photon spectroscopy and the different elemental composition of the samples. The results indicate that the surface character of the substrate adapts depending on the surrounding media and needs more time to reach a steady state for deeper structures. A custom setup is used to expose the functionalized surfaces to oxygen-oversaturated solutions. It is shown that a higher hydrophobicity of the structured surface yields a stronger interaction with the dissolved gas. This significantly enhances the oxygen nucleation up to nearly 350% by generating approximately 20 times more nucleation spots, but also smaller bubble sizes and a reduced detachment rate.

Dataset Information

Fabrication of inclined non-symmetrical periodic micro-structures using Direct Laser Interference Patterning.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets