Large Improvement in the Mechanical Properties of Polyurethane Nanocomposites Based on a Highly Concentrated Graphite Nanoplate/Polyol Masterbatch.

ABSTRACT: In this study, a highly concentrated graphite nanoplate (GNP)/polyol masterbatch was prepared by the exfoliation of natural graphite in an aqueous system using cetyltrimethylammonium bromide and the replacement of aqueous solution with a polyol, viz. poly(tetramethylene ether glycol), and it was subsequently used to prepare polyurethane (PU) nanocomposites by simple dilution. The polyol in the masterbatch efficiently prevented the aggregation of GNPs during the preparation of PU nanocomposite. In addition, the dispersed GNPs in the masterbatch exhibited rheological behavior of lyotropic liquid crystalline materials. In this study, the manufacture and application methods of the GNP/polyol masterbatch were discussed, enabling the facile manufacture of the PU/GNP nanocomposites with excellent mechanical properties. In addition, the manner in which the GNP alignment affected the microphase separation of PU in the nanocomposites was investigated, which determined the improvement in the mechanical properties of the nanocomposites. High-performance PU/GNP nanocomposites are thought to be manufactured from the GNP/polyol masterbatch by the simple dilution to 0.1 wt% GNP in the nanocomposite.

SUBMITTER: Lee SH

PROVIDER: S-EPMC6474002 | biostudies-literature | 2019 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Large Improvement in the Mechanical Properties of Polyurethane Nanocomposites Based on a Highly Concentrated Graphite Nanoplate/Polyol Masterbatch.

Lee Sang-Hyub SH Oh Cho-Rong CR Lee Dai-Soo DS

Nanomaterials (Basel, Switzerland) 20190307 3

In this study, a highly concentrated graphite nanoplate (GNP)/polyol masterbatch was prepared by the exfoliation of natural graphite in an aqueous system using cetyltrimethylammonium bromide and the replacement of aqueous solution with a polyol, viz. poly(tetramethylene ether glycol), and it was subsequently used to prepare polyurethane (PU) nanocomposites by simple dilution. The polyol in the masterbatch efficiently prevented the aggregation of GNPs during the preparation of PU nanocomposite. I ...[more]

PMID: 30866440

Similar Datasets

Project description:Dual-ion batteries (DIBs) generally operate beyond 4.7 V vs Li+/Li0 and rely on the intercalation of both cations and anions in graphite electrodes. Major challenges facing the development of DIBs are linked to electrolyte decomposition at the cathode-electrolyte interface (CEI), graphite exfoliation, and corrosion of Al current collectors. In this work, X-ray photoelectron spectroscopy (XPS) is employed to gain a broad understanding of the nature and dynamics of the CEI built on anion-intercalated graphite cycled both in highly concentrated electrolytes (HCEs) of common lithium salts (LiPF6, LiFSI, and LiTFSI) in carbonate solvents and in a typical ionic liquid. Though Al metal current collectors were adequately stable in all HCEs, the Coulombic efficiency was substantially higher for HCEs based on LiFSI and LiTFSI salts. Specific capacities ranging from 80 to 100 mAh g-1 were achieved with a Coulombic efficiency above 90% over extended cycling, but cells with LiPF6-based electrolytes were characterized by <70% Coulombic efficiency and specific capacities of merely ca. 60 mAh g-1. The poor performance in LiPF6-containing electrolytes is indicative of the continual buildup of decomposition products at the interface due to oxidation, forming a thick interfacial layer rich in LixPFy, POxFy, LixPOyFz, and organic carbonates as evidenced by XPS. In contrast, insights from XPS analyses suggested that anion intercalation and deintercalation processes in the range from 3 to 5.1 V give rise to scant or extremely thin surface layers on graphite electrodes cycled in LiFSI- and LiTFSI-containing HCEs, even allowing for probing anions intercalated in the near-surface bulk. In addition, ex situ Raman, SEM and TEM characterizations revealed the presence of a thick coating on graphite particles cycled in LiPF6-based electrolytes regardless of salt concentration, while hardly any surface film was observed in the case of concentrated LiFSI and LiTFSI electrolytes.

Dataset Information

Large Improvement in the Mechanical Properties of Polyurethane Nanocomposites Based on a Highly Concentrated Graphite Nanoplate/Polyol Masterbatch.

Publications

Large Improvement in the Mechanical Properties of Polyurethane Nanocomposites Based on a Highly Concentrated Graphite Nanoplate/Polyol Masterbatch.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets