Cathode coating using LiInO₂-LiI composite for stable sulfide-based all-solid-state batteries.

ABSTRACT: All-solid-state batteries with inorganic solid electrolytes are ideal to overcome the safety issues related to the flammable organic electrolyte in lithium ion batteries. Sulfide materials are promising inorganic electrolytes due to their high ionic conductivity and good elasticity. Nevertheless, their application is limited by their high reactivity and instability at the cathode/electrolyte (Li[Ni_0.8Co_0.15Al_0.05]O₂/75Li₂S-22P₂S₅-3Li₂SO₄) interface. In this study, LiInO₂ and LiInO₂-LiI were introduced as new cathode coating materials to suppress such undesirable reactions. The LiInO₂-LiI composite coating layer reduced the undesirable interfacial reactions and prevented the diffusion of S and P ions from the sulfide electrolyte to the oxide cathode. Moreover, the electrochemical properties of all-solid-state cells were improved by the cathode coating. The LiInO₂-LiI-coated electrode presented better rate capability and lower impedance than the pristine and LiInO₂-coated electrodes. Hence, the LiInO₂-LiI composite coating was successful at improving the cathode stability while providing superior electrochemical properties.

SUBMITTER: Kwak HW

PROVIDER: S-EPMC6543035 | biostudies-literature | 2019 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

A stable cathode-solid electrolyte composite for high-voltage, long-cycle-life solid-state sodium-ion batteries.

Project description:Rechargeable solid-state sodium-ion batteries (SSSBs) hold great promise for safer and more energy-dense energy storage. However, the poor electrochemical stability between current sulfide-based solid electrolytes and high-voltage oxide cathodes has limited their long-term cycling performance and practicality. Here, we report the discovery of the ion conductor Na3-xY1-xZrxCl6 (NYZC) that is both electrochemically stable (up to 3.8 V vs. Na/Na+) and chemically compatible with oxide cathodes. Its high ionic conductivity of 6.6 × 10-5 S cm-1 at ambient temperature, several orders of magnitude higher than oxide coatings, is attributed to abundant Na vacancies and cooperative MCl6 rotation, resulting in an extremely low interfacial impedance. A SSSB comprising a NaCrO2 + NYZC composite cathode, Na3PS4 electrolyte, and Na-Sn anode exhibits an exceptional first-cycle Coulombic efficiency of 97.1% at room temperature and can cycle over 1000 cycles with 89.3% capacity retention at 40 °C. These findings highlight the immense potential of halides for SSSB applications.

| S-EPMC7902639 | biostudies-literature

Rational Optimization of Cathode Composites for Sulfide-Based All-Solid-State Batteries.

Project description:All-solid-state lithium-ion batteries with argyrodite solid electrolytes have been developed to attain high conductivities of 10-3 S cm-1 in studies aiming at fast ionic conductivity of electrolytes. However, no matter how high the ionic conductivity of the electrolyte, the design of the cathode composite is often the bottleneck for high performance. Thus, optimization of the composite cathode formulation is of utmost importance. Unfortunately, many reports limit their studies to only a few parameters of the whole electrode formulation. In addition, different measurement setups and testing conditions employed for all-solid-state batteries make a comparison of results from mutually independent studies quite difficult. Therefore, a detailed investigation on different key parameters for preparation of cathodes employed in all-solid-state batteries is presented here. Employing a rational approach for optimization of composite cathodes using solid sulfide electrolytes elucidated the influence of different parameters on the cycling performance. First, powder electrodes made without binders are investigated to optimize several parameters, including the active materials' particle morphology, the nature and amount of the conductive additive, the particle size of the solid electrolyte, as well as the active material-to-solid electrolyte ratio. Finally, cast electrodes are examined to determine the influence of a binder on cycling performance.

| S-EPMC9866434 | biostudies-literature

All-Solid-State Lithium-Ion Batteries with Oxide/Sulfide Composite Electrolytes.

Project description:Li6.3La3Zr1.65W0.35O12 (LLZO)-Li6PS5Cl (LPSC) composite electrolytes and all-solid-state cells containing LLZO-LPSC were fabricated by cold pressing at room temperature. The LPSC:LLZO ratio was varied, and the microstructure, ionic conductivity, and electrochemical performance of the corresponding composite electrolytes were investigated; the ionic conductivity of the composite electrolytes was three or four orders of magnitude higher than that of LLZO. The high conductivity of the composite electrolytes was attributed to the enhanced relative density and the rule of mixture for soft LPSC particles with high lithium-ion conductivity (~10-4 S·cm-1). The specific capacities of all-solid-state cells (ASSCs) consisting of a LiNi0.8Co0.1Mn0.1O2 (NCM811) cathode and the composite electrolytes of LLZO:LPSC = 7:3 and 6:4 were 163 and 167 mAh·g-1, respectively, at 0.1 C and room temperature. Moreover, the charge-discharge curves of the ASSCs with the composite electrolytes revealed that a good interfacial contact was successfully formed between the NCM811 cathode and the LLZO-LPSC composite electrolyte.

| S-EPMC8073507 | biostudies-literature

Elucidating Ion Transport Phenomena in Sulfide/Polymer Composite Electrolytes for Practical Solid-State Batteries.

Project description:Despite the enormous interest in inorganic/polymer composite solid-state electrolytes (CSEs) for solid-state batteries (SSBs), the underlying ion transport phenomena in CSEs have not yet been elucidated. Here, we address this issue by formulating a mechanistic understanding of bi-percolating ion channels formation and ion conduction across inorganic-polymer electrolyte interfaces in CSEs. A model CSE is composed of argyrodite-type Li6PS5Cl (LPSCl) and gel polymer electrolyte (GPE, including Li+-glyme complex as an ion-conducting medium). The percolation threshold of the LPSCl phase in the CSE strongly depends on the elasticity of the GPE phase. Additionally, manipulating the solvation/desolvation behavior of the Li+-glyme complex in the GPE facilitates ion conduction across the LPSCl-GPE interface. The resulting scalable CSE (area = 8 × 6 (cm × cm), thickness ~ 40 μm) can be assembled with a high-mass-loading LiNi0.7Co0.15Mn0.15O2 cathode (areal-mass-loading = 39 mg cm-2) and a graphite anode (negative (N)/positive (P) capacity ratio = 1.1) in order to fabricate an SSB full cell with bi-cell configuration. Under this constrained cell condition, the SSB full cell exhibits high volumetric energy density (480 Wh Lcell-1) and stable cyclability at 25 °C, far exceeding the values reported by previous CSE-based SSBs.

| S-EPMC10344856 | biostudies-literature

Li7La3Zr2O12-co-LiNbO3 Surface Modification Improves the Interface Stability between Cathode and Sulfide Solid-State Electrolyte in All-Solid-State Batteries.

Project description:With the rapid development of energy storage and electric vehicles, thiophosphate-based all-solid-state batteries (ASSBs) are considered the most promising power source. In order to commercialize ASSBs, the interfacial problem between high-voltage cathode active materials and thiophosphate-based solid-state electrolytes needs to be solved in a simple, effective way. Surface coatings are considered the most promising approach to solving the interfacial problem because surface coatings could prevent direct physical contact between cathode active materials and thiophosphate-based solid-state electrolytes. In this work, Li7La3Zr2O12 (LLZO) and LiNbO3 (LNO) coatings for LiCoO2 (LCO) were fabricated by in-situ interfacial growth of two high-Li+ conductive oxide electrolytes on the LCO surface and tested for thiophosphate-based ASSBs. The coatings were obtained from a two-step traditional sol-gel coatings process, the inner coatings were LNO, and the surface coatings were LLZO. Electrochemical evaluations confirmed that the two-layer coatings are beneficial for ASSBs. ASSBs containing LLZO-co-LNO coatings LiCoO2 (LLZO&LNO@LCO) significantly improved long-term cycling performance and discharge capacity compared with those assembled from uncoated LCO. LLZO&LNO@LCO||Li6PS5Cl (LPSC)||Li-In delivered discharge capacities of 138.8 mAh/g, 101.8 mAh/g, 60.2 mAh/g, and 40.2 mAh/g at 0.05 C, 0.1 C, 0.2 C, and 0.5 C under room temperature, respectively, and better capacity retentions of 98% after 300 cycles at 0.05 C. The results highlighted promising low-cost and scalable cathode material coatings for ASSBs.

| S-EPMC9967944 | biostudies-literature

Functionalized Sulfide Solid Electrolyte with Air-Stable and Chemical-Resistant Oxysulfide Nanolayer for All-Solid-State Batteries.

Project description:Sulfide solid electrolytes (SEs) with high Li-ion conductivities (σion) and soft mechanical properties have limited applications in wet casting processes for commercial all-solid-state batteries (ASSBs) because of their inherent atmospheric and chemical instabilities. In this study, we fabricated sulfide SEs with a novel core-shell structure via environmental mechanical alloying, while providing sufficient control of the partial pressure of oxygen. This powder possesses notable atmospheric stability and chemical resistance because it is covered with a stable oxysulfide nanolayer that prevents deterioration of the bulk region. The core-shell SEs showed a σion of more than 2.50 mS cm-1 after air exposure (for 30 min) and reaction with slurry chemicals (mixing and drying for 31 min), which was approximately 82.8% of the initial σion. The ASSB cell fabricated through wet casting provided an initial discharge capacity of 125.6 mAh g-1. The core-shell SEs thus exhibited improved powder stability and reliability in the presence of chemicals used in various wet casting processes for commercial ASSBs.

| S-EPMC7558032 | biostudies-literature

Oxygen Transport through Amorphous Cathode Coatings in Solid-State Batteries.

Project description:All solid-state batteries (SSBs) are considered the most promising path to enabling higher energy-density portable energy, while concurrently improving safety as compared to current liquid electrolyte solutions. However, the desire for high energy necessitates the choice of high-voltage cathodes, such as nickel-rich layered oxides, where degradation phenomena related to oxygen loss and structural densification at the cathode surface are known to significantly compromise the cycle and thermal stability. In this work, we show, for the first time, that even in an SSB, and when protected by an intact amorphous coating, the LiNi0.5Mn0.3Co0.2O2 (NMC532) surface transforms from a layered structure into a rocksalt-like structure after electrochemical cycling. The transformation of the surface structure of the Li3B11O18 (LBO)-coated NMC532 cathode in a thiophosphate-based solid-state cell is characterized by high-resolution complementary electron microscopy techniques and electron energy loss spectroscopy. Ab initio molecular dynamics corroborate facile transport of O2- in the LBO coating and in other typical coating materials. This work identifies that oxygen loss remains a formidable challenge and barrier to long-cycle life high-energy storage, even in SSBs with durable, amorphous cathode coatings, and directs attention to considering oxygen permeability as an important new design criteria for coating materials.

| S-EPMC10976630 | biostudies-literature

Influence of Iron Sulfide Nanoparticle Sizes in Solid-State Batteries*.

Project description:Given the inherent performance limitations of intercalation-based lithium-ion batteries, solid-state conversion batteries are promising systems for future energy storage. A high specific capacity and natural abundancy make iron disulfide (FeS2 ) a promising cathode-active material. In this work, FeS2 nanoparticles were prepared solvothermally. By adjusting the synthesis conditions, samples with average particle diameters between 10 nm and 35 nm were synthesized. The electrochemical performance was evaluated in solid-state cells with a Li-argyrodite solid electrolyte. While the reduction of FeS2 was found to be irreversible in the initial discharge, a stable cycling of the reduced species was observed subsequently. A positive effect of smaller particle dimensions on FeS2 utilization was identified, which can be attributed to a higher interfacial contact area and shortened diffusion pathways inside the FeS2 particles. These results highlight the general importance of morphological design to exploit the promising theoretical capacity of conversion electrodes in solid-state batteries.

| S-EPMC8456928 | biostudies-literature

Closed-loop cathode recycling in solid-state batteries enabled by supramolecular electrolytes.

Project description:Deconstructing solid-state batteries (SSBs) to physically separated cathode and solid-electrolyte particles remains intensive, as does the remanufacturing of cathodes and separators from the recovered materials. To address this challenge, we designed supramolecular organo-ionic (ORION) electrolytes that are viscoelastic solids at battery operating temperatures (-40° to 45°C) yet are viscoelastic liquids above 100°C, which enables both the fabrication of high-quality SSBs and the recycling of their cathodes at end of life. SSBs implementing ORION electrolytes alongside Li metal anodes and either LFP or NMC cathodes were operated for hundreds of cycles at 45°C with less than 20% capacity fade. Using a low-temperature solvent process, we isolated the cathode from the electrolyte and demonstrated that refurbished cells recover 90% of their initial capacity and sustain it for an additional 100 cycles with 84% capacity retention in their second life.

| S-EPMC10421023 | biostudies-literature

Argyrodite-Li6PS5Cl/Polymer-based Highly Conductive Composite Electrolyte for All-Solid-State Batteries.

Project description:Solid-state batteries (SSBs) that incorporate the argyrodite-Li6PS5Cl (LPSCl) electrolyte hold potential as substitutes for conventional lithium-ion batteries (LIBs). However, the mismatched interface between the LPSCl electrolyte and electrodes leads to increased interfacial resistance and the rapid growth of lithium (Li) dendrites. These factors significantly impede the feasibility of their widespread industrial application. In this study, we developed a composite electrolyte of the LPSCl/polymer to enhance the contact between the electrolyte and electrodes and suppress dendrite formation at the grain boundary of the LPSCl ceramic. The monomer, triethylene glycol dimethacrylate (TEGDMA), is utilized for in situ polymerization through thermal curing to create the argyrodite LPSCl/polymer composite electrolyte. Additionally, the ball-milling technique was employed to modify the morphology and particle size of the LPSCl ceramic. The ball-milled LPSCl/polymer composite electrolyte demonstrates slightly higher ionic conductivity (ca. 2.21 × 10-4 S/cm) compared to the as-received LPSCl/polymer composite electrolyte (ca. 1.65 × 10-4 S/cm) at 25 °C. Furthermore, both composite electrolytes exhibit excellent compatibility with Li-metal and display cycling stability for up to 1000 h (375 cycles), whereas the as-received LPSCl and ball-milled LPSCl electrolytes maintain stability for up to 600 h (225 cycles) at a current density of 0.4 mA/cm2. The SSB with the ball-milled LPSCl/polymer composite electrolyte delivers high specific discharge capacity (138 mA h/g), Coulombic efficiency (99.97%), and better capacity retention at 0.1C, utilizing the battery configuration of coated NMC811//electrolyte//Li-Indium (In) at 25 °C.

| S-EPMC10934263 | biostudies-literature