Influence of Epoxidized Canola Oil (eCO) and Cellulose Nanocrystals (CNCs) on the Mechanical and Thermal Properties of Polyhydroxybutyrate (PHB)-Poly(lactic acid) (PLA) Blends.

ABSTRACT: Two major obstacles to utilizing polyhydroxybutyrate (PHB)-a biodegradable and biocompatible polymer-in commercial applications are its low tensile yield strength (<10 MPa) and elongation at break (~5%). In this work, we investigated the modification of the mechanical properties of PHB through the use of a variety of bio-derived additives. Poly(lactic acid) (PLA) and sugarcane-sourced cellulose nanocrystals (CNCs) were proposed as mechanical reinforcing elements, and epoxidized canola oil (eCO) was utilized as a green plasticizer. Zinc acetate was added to PHB and PLA blends in order to improve blending. Composites were mixed in a micro-extruder, and the resulting filaments were molded into 2-mm sheets utilizing a hot-press prior to characterization. The inclusion of the various additives was found to influence the crystallization process of PHB without affecting thermal stability. In general, the addition of PLA and, to a lesser degree, CNCs, resulted in an increase in the Young's modulus of the material, while the addition of eCO improved the strain at break. Overall, samples containing eCO and PLA (at concentrations of 10 wt %, and 25 wt %, respectively) demonstrated the best mechanical properties in terms of Young's modulus, tensile strength and strain at break.

SUBMITTER: Lopera-Valle A

PROVIDER: S-EPMC6631437 | biostudies-literature | 2019 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Influence of Epoxidized Canola Oil (eCO) and Cellulose Nanocrystals (CNCs) on the Mechanical and Thermal Properties of Polyhydroxybutyrate (PHB)-Poly(lactic acid) (PLA) Blends.

Lopera-Valle Adrián A Caputo Joseph V JV Leão Rosineide R Sauvageau Dominic D Luz Sandra Maria SM Elias Anastasia A

Polymers 20190529 6

Two major obstacles to utilizing polyhydroxybutyrate (PHB)-a biodegradable and biocompatible polymer-in commercial applications are its low tensile yield strength (<10 MPa) and elongation at break (~5%). In this work, we investigated the modification of the mechanical properties of PHB through the use of a variety of bio-derived additives. Poly(lactic acid) (PLA) and sugarcane-sourced cellulose nanocrystals (CNCs) were proposed as mechanical reinforcing elements, and epoxidized canola oil (eCO) ...[more]

PMID: 31146438

Similar Datasets

Project description:In modern life petroleum-based plastic has become indispensable due to its frequent use as an easily available and a low cost packaging and moulding material. However, its rapidly growing use is causing aquatic and terrestrial pollution. Under these circumstances, research and development for biodegradable plastic (bioplastics) is inevitable. Polyhydroxybutyrate (PHB), a type of microbial polyester that accumulates as a carbon/energy storage material in various microorganisms can be a good alternative. In this study, 23 cyanobacterial strains (15 heterocystous and 8 non-heterocystous) were screened for PHB production. The highest PHB (6.44% w/w of dry cells) was detected in Nostoc muscorum NCCU- 442 and the lowest in Spirulina platensis NCCU-S5 (0.51% w/w of dry cells), whereas no PHB was found in Cylindrospermum sp., Oscillatoria sp. and Plectonema sp. Presence of PHB granules in Nostoc muscorum NCCU- 442 was confirmed microscopically with Sudan black B and Nile red A staining. Pretreatment of biomass with methanol: acetone: water: dimethylformamide [40: 40: 18: 2 (MAD-I)] with 2 h magnetic bar stirring followed by 30 h continuous chloroform soxhlet extraction acted as optimal extraction conditions. Optimized physicochemical conditions viz. 7.5 pH, 30°C temperature, 10:14 h light:dark periods with 0.4% glucose (as additional carbon source), 1.0 gl-1 sodium chloride and phosphorus deficiency yielded 26.37% PHB on 7th day instead of 21st day. Using FTIR, 1H NMR and GC-MS, extracted polymer was identified as PHB. Thermal properties (melting temperature, decomposition temperatures etc.) of the extracted polymer were determined by TGA and DSC. Further, the polymer showed good tensile strength and young's modulus with a low extension to break ratio comparable to petrochemical plastic. Biodegradability potential tested as weight loss percentage showed efficient degradation (24.58%) of PHB within 60 days by mixed microbial culture in comparison to petrochemical plastic.

Project description:BackgroundPlastic plays a crucial role in everyday life of human living, nevertheless it represents an undeniable source of land and water pollution. Polyhydroxybutyrate (PHB) is a bio-based and biodegradable polyester, which can be naturally produced by microorganisms capable of converting and accumulating carbon as intracellular granules. Hence, PHB-producing strains stand out as an alternative source to fossil-derived counterparts. However, the extraction strategy affects the recovery efficiency and the quality of PHB. In this study, PHB was produced by a genetically modified Escherichia coli strain and successively extracted using dimethyl carbonate (DMC) and ethanol as alternative solvent and polishing agent to chloroform and hexane. Eventually, a Life Cycle Assessment (LCA) study was performed for evaluating the environmental and health impact of using DMC.ResultsExtraction yield and purity of PHB obtained via DMC, were quantified, and compared with those obtained via chloroform-based extraction. PHB yield values from DMC-based extraction were similar to or higher than those achieved by using chloroform (≥ 67%). To optimize the performance of extraction via DMC, different experimental conditions were tested, varying the biomass state (dry or wet) and the mixing time, in presence or in absence of a paper filter. Among 60, 90, 120 min, the mid-value allowed to achieve high extraction yield, both for dry and wet biomass. Physical and molecular dependence on the biomass state and solvent/antisolvent choice was established. The comparative LCA analysis promoted the application of DMC/ethanol rather than chloroform/hexane, as the best choice in terms of health prevention. However, an elevated impact score was achieved by DMC in the environmental-like categories in contrast with a minor contribution by its counterpart.ConclusionThe multifaceted exploration of DMC-based PHB extraction herein reported extends the knowledge of the variables affecting PHB purification process. This work offers novel and valuable insights into PHB extraction process, including environmental aspects not discussed so far. The findings of our research question the DMC as a green solvent, though also the choice of the antisolvent can influence the impact on the examined categories.

Dataset Information

Influence of Epoxidized Canola Oil (eCO) and Cellulose Nanocrystals (CNCs) on the Mechanical and Thermal Properties of Polyhydroxybutyrate (PHB)-Poly(lactic acid) (PLA) Blends.

Publications

Influence of Epoxidized Canola Oil (eCO) and Cellulose Nanocrystals (CNCs) on the Mechanical and Thermal Properties of Polyhydroxybutyrate (PHB)-Poly(lactic acid) (PLA) Blends.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets