Simultaneous Recovery of Display Panel Waste Glass and Wastewater Boron by Chemical Oxo-precipitation with Fluidized-Bed Heterogeneous Crystallization.

ABSTRACT: Silica-based carrier is a promising material for recovery of metal and nonmetal contaminants in chemical oxo-precipitation-fluidized bed crystallization (COP-FBC) system. Boron species are an essential element for plant growth and can cause health concerns in human beings at high concentrations in water environments. The composition of thin-film transistor liquid crystal display (TFT-LCD) contains a wide variety of metal oxides and can be tailored as promising functional mesoporous carriers for boron crystallization recovery in the presence of barium ions and hydrogen peroxide. In this study, waste-derived mesoporous aluminosilicate (MAS) nanomaterial in the presence of barium ions and hydrogen peroxide was used as a carrier for sustainable recovery of crystallized boron, a priority wastewaters pollutant. The MAS shows the hierarchically homogeneous distribution of nanostructured aluminosilicate particles with an average size of 12.8 ± 3.6 nm on the surface after the activation with Na2CO3 at 1000 °C. Moreover, the negatively charged surface and the mesoporous structure of MAS enhance the adsorption of Ba2+ onto MAS, and the Langmuir adsorption capacity of 105 mg/g is achieved, which is conducive to the enhancement of the recovery of boron species. Moreover, the recovery efficiency and crystallization ratio of boron by MAS can be up to 84.5 and 93.4%, respectively. The cross-sectional scanning electron microscopy images and the high-temperature X-ray diffraction results confirm the boron recovery mechanism that the negatively charged functional group as well as the mesoporosity of MAS triggers the rapid formation of needle-shaped precipitates of barium peroxoborate, and then converted to barium borate after calcination at 1050 °C. Results obtained in this study clearly demonstrate the possibility of fabricating environmentally benign mesoporous aluminosilicate adsorbents from TFT-LCD waste to sustainably recover and crystallize boron species from water and wastewater in COP-FBC.

SUBMITTER: Tsai CK

PROVIDER: S-EPMC6714614 | biostudies-literature | 2019 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Simultaneous Recovery of Display Panel Waste Glass and Wastewater Boron by Chemical Oxo-precipitation with Fluidized-Bed Heterogeneous Crystallization.

Tsai Cheng-Kuo CK Lee Nien-Tsu NT Huang Gaw-Hau GH Suzuki Yoshikazu Y Doong Ruey-An RA

ACS omega 20190816 9

Silica-based carrier is a promising material for recovery of metal and nonmetal contaminants in chemical oxo-precipitation-fluidized bed crystallization (COP-FBC) system. Boron species are an essential element for plant growth and can cause health concerns in human beings at high concentrations in water environments. The composition of thin-film transistor liquid crystal display (TFT-LCD) contains a wide variety of metal oxides and can be tailored as promising functional mesoporous carriers for ...[more]

PMID: 31497724

Similar Datasets

Project description:Each year about 7.6 million tons of waste glasses are landfilled without recycling, reclaiming or upcycling. Herein we have developed a solvent free upcycling method for recycled glass waste (RG) by remanufacturing it into porous recycled glass microspheres (PRGMs) with a view to explore removal of organic pollutants such as organic dyes. PRGMs were prepared via flame spheroidisation process and characterised using Scanning Electron Microscopy (SEM), X-ray diffraction (XRD), Brunauer–Emmett–Teller (BET) and Mercury Intrusion Porosimetry (MIP) analysis. PRGMs exhibited 69% porosity with overall pore volume and pore area of 0.84 cm3/g and 8.6 cm2/g, respectively (from MIP) and a surface area of 8 m2/g. Acid red 88 (AR88) and Methylene blue (MB) were explored as a model source of pollutants. Results showed that removal of AR88 and MB by PRGMs was influenced by pH of the dye solution, PRGMs doses, and dye concentrations. From the batch process experiments, adsorption and coagulation processes were observed for AR88 dye whilst MB dye removal was attributed only to adsorption process. The maximum monolayer adsorption capacity (qe) recorded for AR88, and MB were 78 mg/g and 20 mg/g, respectively. XPS and FTIR studies further confirmed that the adsorption process was due to electrostatic interaction and hydrogen bond formation. Furthermore, dye removal capacity of the PRGMs was also investigated for column adsorption process experiments. Based on the Thomas model, the calculated adsorption capacities at flow rates of 2.2 mL/min and 0.5 mL/min were 250 mg/g and 231 mg/g, respectively which were much higher than the batch scale Langmuir monolayer adsorption capacity (qe) values. It is suggested that a synergistic effect of adsorption/coagulation followed by filtration processes was responsible for the higher adsorption capacities observed from the column adsorption studies. This study also demonstrated that PRGMs produced from recycled glass waste could directly be applied to the next cyclic experiment with similar dye removal capability. Thus, highlighting the circular economy scope of using waste inorganic materials for alternate applications such as pre-screening materials in wastewater treatment applications.

Dataset Information

Simultaneous Recovery of Display Panel Waste Glass and Wastewater Boron by Chemical Oxo-precipitation with Fluidized-Bed Heterogeneous Crystallization.

Publications

Simultaneous Recovery of Display Panel Waste Glass and Wastewater Boron by Chemical Oxo-precipitation with Fluidized-Bed Heterogeneous Crystallization.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets