Crystallization and precipitation of phosphate from swine wastewater by magnesium metal corrosion.

ABSTRACT: This paper presents a unique approach for magnesium dosage in struvite precipitation by Mg metal corrosion. The experimental results showed that using an air bubbling column filled with Mg metal and graphite pellets for the magnesium dosage was the optimal operation mode, which could significantly accelerate the corrosion of the Mg metal pellets due to the presence of graphite granules. The reaction mechanism experiments revealed that the solution pH could be used as the indicator for struvite crystallization by the process. Increases in the Mg metal dosage, mass ratio of graphite and magnesium metal (G:M) and airflow rate could rapidly increase the solution pH. When all three conditions were at 10 g L(-1), 1:1 and 1 L min(-1), respectively, the phosphate recovery efficiency reached 97.5%. To achieve a high level of automation for the phosphate recovery process, a continuous-flow reactor immersed with the graphite-magnesium air bubbling column was designed to harvest the phosphate from actual swine wastewater. Under conditions of intermittently supplementing small amounts of Mg metal pellets, approximately 95% of the phosphate could be stably recovered as struvite of 95.8% (±0.5) purity. An economic analysis indicated that the process proposed was technically simple and economically feasible.

SUBMITTER: Huang H

PROVIDER: S-EPMC4642316 | biostudies-other | 2015

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:Silica-based carrier is a promising material for recovery of metal and nonmetal contaminants in chemical oxo-precipitation-fluidized bed crystallization (COP-FBC) system. Boron species are an essential element for plant growth and can cause health concerns in human beings at high concentrations in water environments. The composition of thin-film transistor liquid crystal display (TFT-LCD) contains a wide variety of metal oxides and can be tailored as promising functional mesoporous carriers for boron crystallization recovery in the presence of barium ions and hydrogen peroxide. In this study, waste-derived mesoporous aluminosilicate (MAS) nanomaterial in the presence of barium ions and hydrogen peroxide was used as a carrier for sustainable recovery of crystallized boron, a priority wastewaters pollutant. The MAS shows the hierarchically homogeneous distribution of nanostructured aluminosilicate particles with an average size of 12.8 ± 3.6 nm on the surface after the activation with Na2CO3 at 1000 °C. Moreover, the negatively charged surface and the mesoporous structure of MAS enhance the adsorption of Ba2+ onto MAS, and the Langmuir adsorption capacity of 105 mg/g is achieved, which is conducive to the enhancement of the recovery of boron species. Moreover, the recovery efficiency and crystallization ratio of boron by MAS can be up to 84.5 and 93.4%, respectively. The cross-sectional scanning electron microscopy images and the high-temperature X-ray diffraction results confirm the boron recovery mechanism that the negatively charged functional group as well as the mesoporosity of MAS triggers the rapid formation of needle-shaped precipitates of barium peroxoborate, and then converted to barium borate after calcination at 1050 °C. Results obtained in this study clearly demonstrate the possibility of fabricating environmentally benign mesoporous aluminosilicate adsorbents from TFT-LCD waste to sustainably recover and crystallize boron species from water and wastewater in COP-FBC.

Dataset Information

Crystallization and precipitation of phosphate from swine wastewater by magnesium metal corrosion.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets