Effect of HCOOK/Ethanol on Fe/HUSY, Ni/HUSY, and Ni-Fe/HUSY Catalysts on Lignin Depolymerization to Benzyl Alcohols and Bioaromatics.

ABSTRACT: We have investigated the production of benzyl alcohols and bioaromatics via the reductive lignin depolymerization process over Fe/H-style ultrastable Y (HUSY), Ni/HUSY, and Ni-Fe/HUSY catalysts using HCOOK/ETOH in air. Synergy effect between HCOOK and the catalysts improved the depolymerization process, resulting in a higher bio-oil recovery. HCOOK does not act solely as an in situ hydrogen source; it also interacts with lignin to enable its initial depolymerization via a base-catalyzed mechanism to low-molecular-weight fragments, and in tandem with the catalyst, the hydrogenolysis rate of the depolymerized lignin monomers was enhanced. Fe/HUSY displayed an excellent activity for the catalytic reductive step in contrast to Ni/HUSY and Ni-Fe/HUSY by facilitating methoxy group removal via hydrogenolysis, thereby contributing to the yield and stabilization of the low-molecular-weight aromatics [diethyl ether (DEE)-soluble products]. Fe/HUSY gave the highest DEE product yield of >99 wt % and a total benzyl alcohol yield of 16 wt % with a total selectivity of 47 wt % (60 wt % for aromatic alcohols). Fe/HUSY was reused for the lignin depolymerization reaction without much loss of its initial activity, giving 13 wt % yield of benzyl alcohols with a selectivity of 58 wt % (77 wt % for aromatic alcohols).

SUBMITTER: Wanmolee W

PROVIDER: S-EPMC6796940 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Role of Fe Species of Ni-Based Catalysts for Efficient Low-Temperature Ethanol Steam Reforming.

Project description:The suppression of methane and coke formation over Ni-based catalysts for low temperature ethanol steam reforming remains challenging. This paper describes the structural evolution of Fe-modified Ni/MgAl2O4 catalysts and the influence of iron species on methane and coke suppression for low temperature ethanol steam reforming. Ni-Fe alloy catalysts are gradually oxidized by water to generate Ni-rich alloy and γ-Fe2O3 species at steam-to-carbon ratio of 4. The electron transfer from iron to nickel within Ni-Fe alloy weakens the CO adsorption and effectively alleviates the CO/CO2 methanation. The oxidation capacity of γ-Fe2O3 species promotes the transformation of ethoxy to acetate groups to avoid methane formation and the elimination of carbon deposits for anticoking. Ni10Fe10/MgAl2O4 shows a superior performance with a highest H2 yield of 4.6 mol/mol ethanol at 400 °C for 15 h. This research could potentially provide instructions for the design of Ni-based catalysts for low-temperature ethanol steam reforming.

| S-EPMC8479767 | biostudies-literature

Primary Benzylamines by Efficient N-Alkylation of Benzyl Alcohols Using Commercial Ni Catalysts and Easy-to-Handle Ammonia Sources.

Project description:Primary benzylamines are highly important building blocks in the pharmaceutical and polymer industry. An attractive catalytic approach to access these compounds is the direct coupling of benzyl alcohols with ammonia via the borrowing hydrogen methodology. However, this approach is usually hampered by a series of side-reactions, one of the most prominent being the overalkylation of the formed primary amine. Herein, we describe a robust catalytic methodology, which utilizes commercially available heterogeneous Ni catalysts and easy-to-handle ammonia sources, such as aqueous ammonia or ammonium salts, for the formation of primary benzylamines with good selectivity and scope. Notably, our method enables the conversion of potentially lignin-derived vanillyl alcohol to vanillylamine, which can be used to produce emerging biobased polymers or as pharma building blocks. Important sugar derived platform alcohols as well as long chain aliphatic primary alcohols can be successfully aminated. Moreover, we provide an alternative, sustainable route to p-xylylenediamine and m-xylylenediamine, important components of heat resistant polyamides such as Kevlar.

| S-EPMC6614922 | biostudies-literature

Synergy in Lignin Upgrading by a Combination of Cu-Based Mixed Oxide and Ni-Phosphide Catalysts in Supercritical Ethanol.

Project description:The depolymerization of lignin to bioaromatics usually requires a hydrodeoxygenation (HDO) step to lower the oxygen content. A mixed Cu-Mg-Al oxide (CuMgAlO x ) is an effective catalyst for the depolymerization of lignin in supercritical ethanol. We explored the use of Ni-based cocatalysts, i.e. Ni/SiO2, Ni2P/SiO2, and Ni/ASA (ASA = amorphous silica alumina), with the aim of combining lignin depolymerization and HDO in a single reaction step. While the silica-supported catalysts were themselves hardly active in lignin upgrading, Ni/ASA displayed comparable lignin monomer yield as CuMgAlO x . A drawback of using an acidic support is extensive dehydration of the ethanol solvent. Instead, combining CuMgAlO x with Ni/SiO2 and especially Ni2P/SiO2 proved to be effective in increasing the lignin monomer yield, while at the same time reducing the oxygen content of the products. With Ni2P/SiO2, the lignin monomer yield was 53 wt %, leading to nearly complete deoxygenation of the aromatic products.

| S-EPMC5384481 | biostudies-literature

Synergy between Fe and Ni in the optimal performance of (Ni,Fe)OOH catalysts for the oxygen evolution reaction.

Project description:The oxygen evolution reaction (OER) is critical to solar production of fuels, but the reaction mechanism underlying the performance for a best OER catalyst, Fe-doped NiOOH [(Ni,Fe)OOH], remains highly controversial. We used grand canonical quantum mechanics to predict the OER mechanisms including kinetics and thus overpotentials as a function of Fe content in (Ni,Fe)OOH catalysts. We find that density functional theory (DFT) without exact exchange predicts that addition of Fe does not reduce the overpotential much. However, DFT with exact exchange predicts dramatic improvement in performance for (Ni,Fe)OOH, leading to an overpotential of 0.42 V and a Tafel slope of 23 mV/decade (dec), in good agreement with experiments, 0.3-0.4 V and 30 mV/dec. We reveal that the high spin [Formula: see text] Fe(IV) leads to efficient formation of an active O radical intermediate, while the closed shell [Formula: see text] Ni(IV) catalyzes the subsequent O-O coupling, and thus it is the synergy between Fe and Ni that delivers the optimal performance for OER.

| S-EPMC6003342 | biostudies-literature

Electrochemical Aminoxyl-Mediated Oxidation of Primary Alcohols in Lignin to Carboxylic Acids: Polymer Modification and Depolymerization.

Project description:An electrochemical process has been developed for chemoselective oxidation of primary alcohols in lignin to the corresponding carboxylic acids. The electrochemical oxidation reactions proceed under mildly basic conditions and employ 2,2,6,6-tetramethyl-1-piperidine N-oxyl (TEMPO) and 4-acetamido-TEMPO (ACT) as catalytic mediators. Lignin model compounds and related alcohols are used to conduct structure-reactivity studies that provide insights into the origin of the reaction selectivity. The method is applied to the oxidation of lignin extracted from poplar wood chips via a mild acidolysis method, and the reaction affords a novel polyelectrolyte material. Gel permeation chromatography data for the oxidized lignin shows that this material has a molecular weight and molecular weight distribution very similar to that of the extracted lignin, but notable differences are also evident. Base titration reveals a significant increase in the acid content, and the oxidized lignin has much higher water solubility relative to the extracted lignin. Treatment of the oxidized lignin under acidic conditions results in depolymerization of the material into characterized aromatic monomers in nearly 30 wt% yield.

| S-EPMC7641471 | biostudies-literature

Methane Decomposition Over ZrO2-Supported Fe and Fe-Ni Catalysts-Effects of Doping La2O3 and WO3.

Project description:A leading method for hydrogen production that is free of carbon oxides is catalytic methane decomposition. In this research, Fe and Fe-Ni supported catalysts prepared by the wet impregnation method were used in methane decomposition. The effects of doping the parent support (ZrO2) with La2O3 and WO3 were studied. It was discovered that the support doped with La2O3 gave the best performance in terms of CH4 conversion, H2 yield, and stability at the test condition, 800°C and 4,000-ml h-1 g-1 cat. space velocity. The addition of Ni significantly improved the performance of all the monometallic catalysts. The catalysts were characterized by X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET), temperature-programmed reduction/oxidation (TPR/TPO), thermogravimetric analyzer (TGA), and microscopy (SEM and Raman) techniques. Phases of the different forms of Fe were identified by XRD. BET showed a drastic decline in the specific surface area of the catalysts with respect to the supports. TPR profiles revealed a progressive change in the valency of Fe in its combined form to the zero valence-free metal. The La2O3-promoted support gave the best performance and maintained good stability during the time on stream.

| S-EPMC7201101 | biostudies-literature

Redox Catalysis Facilitates Lignin Depolymerization.

Project description:Lignin is a recalcitrant and underexploited natural feedstock for aromatic commodity chemicals, and its degradation generally requires the use of high temperatures and harsh reaction conditions. Herein we present an ambient temperature one-pot process for the controlled oxidation and depolymerization of this potent resource. Harnessing the potential of electrocatalytic oxidation in conjugation with our photocatalytic cleavage methodology, we have developed an operationally simple procedure for selective fragmentation of ?-O-4 bonds with excellent mass recovery, which provides a unique opportunity to expand the existing lignin usage from energy source to commodity chemicals and synthetic building block source.

| S-EPMC5492418 | biostudies-literature

Enhancing the CO2 Electroreduction of Fe/Ni-Pentlandite Catalysts by S/Se Exchange.

Project description:The electrochemical reduction of CO2 is an attractive strategy towards the mitigation of environmental pollution and production of bulk chemicals as well as fuels by renewables. The bimetallic sulfide Fe4.5 Ni4.5 S8 (pentlandite) was recently reported as a cheap and robust catalyst for electrochemical water splitting, as well as for CO2 reduction with a solvent-dependent product selectivity. Inspired by numerous reports on monometallic sulfoselenides and selenides revealing higher catalytic activity for the CO2 reduction reaction (CO2 RR) than their sulfide counterparts, the authors investigated the influence of stepwise S/Se exchange in seleno-pentlandites Fe4.5 Ni4.5 S8-Y SeY (Y=1-5) and their ability to act as CO2 reducing catalysts. It is demonstrated that the incorporation of higher equivalents of selenium favors the CO2 RR with Fe4.5 Ni4.5 S4 Se4 revealing the highest activity for CO formation. Under galvanostatic conditions in acetonitrile, Fe4.5 Ni4.5 S4 Se4 generates CO with a Faradaic Efficiency close to 100?% at applied current densities of -50?mA?cm-2 and -100?mA?cm-2 . This work offers insight into the tunability of the pentlandite based electrocatalysts for the CO2 reduction reaction.

| S-EPMC7496145 | biostudies-literature

Monometallic Cerium Layered Double Hydroxide Supported Pd-Ni Nanoparticles as High Performance Catalysts for Lignin Hydrogenolysis.

Project description:Monometallic cerium layered double hydroxides (Ce-LDH) supports were successfully synthesized by a homogeneous alkalization route driven by hexamethylenetetramine (HMT). The formation of the Ce-LDH was confirmed and its structural and compositional properties studied by XRD, SEM, XPS, iodometric analyses and TGA. HT-XRD, N2-sorption and XRF analyses revealed that by increasing the calcination temperature from 200 to 800 °C, the Ce-LDH material transforms to ceria (CeO2) in four distinct phases, i.e., the loss of intramolecular water, dehydroxylation, removal of nitrate groups and removal of sulfate groups. When loaded with 2.5 wt% palladium (Pd) and 2.5 wt% nickel (Ni) and calcined at 500 °C, the PdNi-Ce-LDH-derived catalysts strongly outperform the PdNi-CeO2 benchmark catalyst in terms of conversion as well as selectivity for the hydrogenolysis of benzyl phenyl ether (BPE), a model compound for the ?-O-4 ether linkage in lignin. The PdNi-Ce-LDH catalysts showed full selectivity towards phenol and toluene while the PdNi-CeO2 catalysts showed additional oxidation of toluene to benzoic acid. The highest BPE conversion was observed with the PdNi-Ce-LDH catalyst calcined at 600 °C, which could be related to an optimum in morphological and compositional characteristics of the support.

| S-EPMC7040693 | biostudies-literature

Precious-metal free photoelectrochemical water splitting with immobilised molecular Ni and Fe redox catalysts.

Project description:Splitting water into hydrogen and oxygen with molecular catalysts and light has been a long-established challenge. Approaches in homogeneous systems have been met with little success and the integration of molecular catalysts in photoelectrochemical cells is challenging due to inaccessibility and incompatibility of functional hybrid molecule/material electrodes with long-term stability in aqueous solution. Here, we present the first example of light-driven water splitting achieved with precious-metal-free molecular catalysts driving both oxygen and hydrogen evolution reactions. Mesoporous TiO2 was employed as a low-cost scaffold with long-term stability for anchoring a phosphonic acid-modified nickel(ii) bis-diphosphine catalyst (NiP) for electrocatalytic proton reduction. A turnover number of 600 mol H2 per mol NiP was achieved after 8 h controlled-potential electrolysis at a modest overpotential of 250 mV. X-ray photoelectron, UV-vis and IR spectroscopies confirmed that the molecular structure of the Ni catalyst remains intact after prolonged hydrogen production, thereby reasserting the suitability of molecular catalysts in the development of effective, hydrogen-evolving materials. The relatively mild operating conditions of a pH 3 aqueous solution allowed this molecule-catalysed cathode to be combined with a molecular Fe(ii) catalyst-modified WO3 photoanode in a photoelectrochemical cell. Water splitting into H2 and O2 was achieved under solar light illumination with an applied bias of >0.6 V, which is below the thermodynamic potential (1.23 V) for water splitting and therefore allowed the storage of solar energy in the fuel H2.

| S-EPMC6013811 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data