Continuous Mesoporous Aluminum Oxide Film with Perpendicularly Oriented Mesopore Channels.

ABSTRACT: Mesoporous aluminum oxide (MAO) films with perpendicularly oriented cylindrical mesopores (pore diameter: ca. 10 nm) were successfully deposited on a glass substrate by a surfactant-templating approach using aluminum nitrate as an aluminum source. The perpendicular orientation of mesopores was confirmed by grazing-incidence small-angle X-ray scattering and neutron reflection experiments. The thickness of the MAO film was around 100 nm, with a surface roughness of less than 6 nm. Since the inner surface of MAO pores was positively charged, negatively charged glucose oxidase molecules could be densely loaded into the cylindrical mesopores without significant loss of enzymatic activity. The present MAO film is potentially useful as an inorganic host material for an enzyme toward the development of a biocatalytic system.

SUBMITTER: Shibuya Y

PROVIDER: S-EPMC6822217 | biostudies-literature | 2019 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Continuous Mesoporous Aluminum Oxide Film with Perpendicularly Oriented Mesopore Channels.

Shibuya Yuuta Y Katayama Kazuya K Akutsu-Suyama Kazuhiro K Yamaguchi Akira A

ACS omega 20191018 18

Mesoporous aluminum oxide (MAO) films with perpendicularly oriented cylindrical mesopores (pore diameter: ca. 10 nm) were successfully deposited on a glass substrate by a surfactant-templating approach using aluminum nitrate as an aluminum source. The perpendicular orientation of mesopores was confirmed by grazing-incidence small-angle X-ray scattering and neutron reflection experiments. The thickness of the MAO film was around 100 nm, with a surface roughness of less than 6 nm. Since the inner ...[more]

PMID: 31681898

Similar Datasets

Low Surface Roughness Graphene Oxide Film Reduced with Aluminum Film Deposited by Magnetron Sputtering.

Project description:Graphene film has wide applications in optoelectronic and photovoltaic devices. A novel and facile method was reported for the reduction of graphene oxide (GO) film by electron transfer and nascent hydrogen produced between aluminum (Al) film deposited by magnetron sputtering and hydrochloric acid (HCl) solution for only 5 min, significantly shorter than by other chemical reduction methods. The thickness of Al film was controlled utilizing a metal detection sensor. The effect of the thickness of Al film and the concentration of HCl solution during the reduction was explored. The optimal thickness of Al film was obtained by UV-Vis spectroscopy and electrical conductivity measurement of reduced GO film. Atomic force microscope images could show the continuous film clearly, which resulted from the overlap of GO flakes, the film had a relatively flat surface morphology, and the surface roughness reduced from 7.68 to 3.13 nm after the Al reduction. The film sheet resistance can be obviously reduced, and it reached 9.38 kΩ/sq with a high transmittance of 80% (at 550 nm). The mechanism of the GO film reduction by electron transfer and nascent hydrogen during the procedure was also proposed and analyzed.

| S-EPMC8227777 | biostudies-literature

High catalytic activity of oriented 2.0.0 copper(I) oxide grown on graphene film.

Project description:Metal oxide nanoparticles supported on graphene exhibit high catalytic activity for oxidation, reduction and coupling reactions. Here we show that pyrolysis at 900 °C under inert atmosphere of copper(II) nitrate embedded in chitosan films affords 1.1.1 facet-oriented copper nanoplatelets supported on few-layered graphene. Oriented (1.1.1) copper nanoplatelets on graphene undergo spontaneous oxidation to render oriented (2.0.0) copper(I) oxide nanoplatelets on few-layered graphene. These films containing oriented copper(I) oxide exhibit as catalyst turnover numbers that can be three orders of magnitude higher for the Ullmann-type coupling, dehydrogenative coupling of dimethylphenylsilane with n-butanol and C-N cross-coupling than those of analogous unoriented graphene-supported copper(I) oxide nanoplatelets.

| S-EPMC4634216 | biostudies-literature

Magnetic Field Magnitudes Needed for Skyrmion Generation in a General Perpendicularly Magnetized Film.

Project description:Due to its topological protection, the magnetic skyrmion has been intensively studied for both fundamental aspects and spintronics applications. However, despite recent advancements in skyrmion research, the deterministic creation of isolated skyrmions in a generic perpendicularly magnetized film is still one of the most essential and challenging techniques. Here, we present a method to create magnetic skyrmions in typical perpendicular magnetic anisotropy (PMA) films by applying a magnetic field pulse and a method to determine the magnitude of the required external magnetic fields. Furthermore, to demonstrate the usefulness of this result for future skyrmion research, we also experimentally study the PMA dependence on the minimum size of skyrmions. Although field-driven skyrmion generation is unsuitable for device application, this result can provide an easier approach for obtaining isolated skyrmions, making skyrmion-based research more accessible.

| S-EPMC9650724 | biostudies-literature

Perpendicularly oriented sub-10-nm block copolymer lamellae by atmospheric thermal annealing for one minute.

Project description:The directed self-assembly (DSA) of block co-polymers (BCPs) can realize next-generation lithography for semiconductors and a variety of soft materials. It is imperative to simultaneously achieve many requirements such as a high resolution, orientation control of micro-domains, etch selectivity, rapid and mild annealing, a low cost, and compatibility with manufacturing for developing suitable BCPs. Here, we describe a new design for modified polysiloxane-based BCPs targeted for sub-10-nm-wide lines, which are able to form perpendicularly oriented lamellar structures in thin films. The hydroxyl groups in the side chains introduced in the polysiloxane block provide a good balance with the polystyrene surface free energy, thereby leading to the perpendicular orientation. Moreover, this orientation can be completed in only one minute at 130?°C in an air atmosphere. Oxygen plasma etching for the thin films results in the achievement of a line width of 8.5?nm.

| S-EPMC4726028 | biostudies-literature

Human Aquaporin 4 Gating Dynamics under Perpendicularly-Oriented Electric-Field Impulses: A Molecular Dynamics Study.

Project description:Human aquaporin 4 has been studied using molecular dynamics (MD) simulations in the absence and presence of pulses of external static electric fields. The pulses were 10 ns in duration and 0.012-0.065 V/Å in intensity acting along both directions perpendicular to the pores. Water permeability and the dipolar response of all residues of interest (including the selectivity filter) within the pores have been studied. Results showed decreased levels of water osmotic permeability within aquaporin channels during orthogonally-oriented field impulses, although care must be taken with regard to statistical certainty. This can be explained observing enhanced "dipolar flipping" of certain key residues, especially serine 211, histidine 201, arginine 216, histidine 95 and cysteine 178. These residues are placed at the extracellular end of the pore (serine 211, histidine 201, and arginine 216) and at the cytoplasm end (histidine 95 and cysteine 178), with the key role in gating mechanism, hence influencing water permeability.

| S-EPMC4964506 | biostudies-literature

Boron Nitride-Titania Mesoporous Film Heterostructures.

Project description:The fabrication of optically active heterostructures in the shape of mesostructured thin films is a highly challenging task. It requires an integrated process to allow in one-step incorporating the two-dimensional materials within the mesoporous ordered host without disrupting the pore organization. Hexagonal boron nitride (BN) nanosheets have been successfully introduced into titania mesoporous films using a template-assisted sol-gel synthesis and evaporation-induced self-assembly. Two types of BN sheets have been used, with and without defects, to investigate the role of defects in heterostructure properties. It has been found that the defects increase the ultraviolet radiation A (UVA) absorbance and enhance the photocatalytic response of the film. The BN sheets are optically transparent and do not exhibit any photocatalytic property but contribute to anatase crystallization via heterogeneous nucleation.

| S-EPMC8280735 | biostudies-literature

An iridescent film of porous anodic aluminum oxide with alternatingly electrodeposited Cu and SiO<sub>2</sub> nanoparticles.

Project description:The structurally colored surface of anodic aluminum oxide (AAO) is highly useful for decoration and anti-counterfeiting applications, which are of significance for both scientific and industrial communities. This study presents the first demonstration of the fabrication of an iridescent film of porous AAO on an industrial aluminum alloy substrate, with alternatingly electrodeposited Cu and SiO2 nanoparticles (NPs). A rainbow effect was effectively obtained for the optimized sample with appropriate alternating electrodeposition times. The structure and optical properties of a series of the electrodeposited AAO-based thin film were investigated. The Cu and SiO2 NPs were found to be uniformly deposited into the porous structure of the AAO film, and the alternating electrodeposition repeating twice led to the formation of the optimal AAO-based thin film that exhibited a rainbow effect and superior anti-corrosion performance.

| S-EPMC6444397 | biostudies-literature

The effect of interface anisotropy on demagnetization progress in perpendicularly oriented hard/soft exchange-coupled multilayers.

Project description:The demagnetization progress of various hard/soft multilayers with perpendicular crystalline anisotropy has been studied by a micromagnetic model, incorporating the effect of the interface anisotropy, which is evident on the nucleation field when the soft layer thickness is small. Both microscopic and macroscopic hysteresis loops as well as angular distributions for the magnetizations in the thickness direction have been calculated, taking into account of realistic values of the interface anisotropy. The formula for the nucleation field has been derived analytically, where the nucleation field increases linearly with the interface anisotropy for a wide thickness region. While the nucleation field could change by more than 90% due to the influence of the interface anisotropy, the interface anisotropy has no effect on the pinning field or the coercivity, but it has some slight influence on the angular distributions. On the other hand, positive interface anisotropy enhances the remanence and the energy products, whereas negative interface anisotropy deteriorates both of them. Comparison with the experimental data justifies our calculation, indicating that negative interface anisotropy should be avoided in the experiment.

| S-EPMC5487335 | biostudies-literature

Single-crystalline aluminum film for ultraviolet plasmonic nanolasers.

Project description:Significant advances have been made in the development of plasmonic devices in the past decade. Plasmonic nanolasers, which display interesting properties, have come to play an important role in biomedicine, chemical sensors, information technology, and optical integrated circuits. However, nanoscale plasmonic devices, particularly those operating in the ultraviolet regime, are extremely sensitive to the metal and interface quality. Thus, these factors have a significant bearing on the development of ultraviolet plasmonic devices. Here, by addressing these material-related issues, we demonstrate a low-threshold, high-characteristic-temperature metal-oxide-semiconductor ZnO nanolaser that operates at room temperature. The template for the ZnO nanowires consists of a flat single-crystalline Al film grown by molecular beam epitaxy and an ultrasmooth Al2O3 spacer layer synthesized by atomic layer deposition. By effectively reducing the surface plasmon scattering and metal intrinsic absorption losses, the high-quality metal film and the sharp interfaces formed between the layers boost the device performance. This work should pave the way for the use of ultraviolet plasmonic nanolasers and related devices in a wider range of applications.

| S-EPMC4728607 | biostudies-literature

Electrical, Structural, Optical, and Adhesive Characteristics of Aluminum-Doped Tin Oxide Thin Films for Transparent Flexible Thin-Film Transistor Applications.

Project description:The properties of Al-doped SnOx films deposited via reactive co-sputtering were examined in terms of their potential applications for the fabrication of transparent and flexible electronic devices. Al 2.2-atom %-doped SnOx thin-film transistors (TFTs) exhibit improved semiconductor characteristics compared to non-doped films, with a lower sub-threshold swing of ~0.68 Vdec-1, increased on/off current ratio of ~8 × 10?, threshold voltage (Vth) near 0 V, and markedly reduced (by 81%) Vth instability in air, attributable to the decrease in oxygen vacancy defects induced by the strong oxidizing potential of Al. Al-doped SnOx films maintain amorphous crystallinity, an optical transmittance of ~97%, and an adhesive strength (to a plastic substrate) of over 0.7 kgf/mm; such films are thus promising semiconductor candidates for fabrication of transparent flexible TFTs.

| S-EPMC6337128 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data