3C-SiC Growth on Inverted Silicon Pyramids Patterned Substrate.

ABSTRACT: This work reports on the properties of cubic silicon carbide (3C-SiC) grown epitaxially on a patterned silicon substrate composed of squared inverted silicon pyramids (ISP). This compliant substrate prevents stacking faults, usually found at the SiC/Si interface, from reaching the surface. We investigated the effect of the size of the inverted pyramid on the epilayer quality. We noted that anti-phase boundaries (APBs) develop between adjacent faces of the pyramid and that the SiC/Si interfaces have the same polarity on both pyramid faces. The structure of the heterointerface was investigated. Moreover, due to the emergence of APB at the vertex of the pyramid, voids buried on the epilayer form. We demonstrated that careful control of the growth parameters allows modification of the height of the void and the density of APBs, improving SiC epitaxy quality.

SUBMITTER: Zimbone M

PROVIDER: S-EPMC6829442 | biostudies-literature | 2019 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

3C-SiC Growth on Inverted Silicon Pyramids Patterned Substrate.

Zimbone Massimo M Zielinski Marcin M Bongiorno Corrado C Calabretta Cristiano C Anzalone Ruggero R Scalese Silvia S Fisicaro Giuseppe G La Magna Antonino A Mancarella Fulvio F La Via Francesco F

Materials (Basel, Switzerland) 20191018 20

This work reports on the properties of cubic silicon carbide (3C-SiC) grown epitaxially on a patterned silicon substrate composed of squared inverted silicon pyramids (ISP). This compliant substrate prevents stacking faults, usually found at the SiC/Si interface, from reaching the surface. We investigated the effect of the size of the inverted pyramid on the epilayer quality. We noted that anti-phase boundaries (APBs) develop between adjacent faces of the pyramid and that the SiC/Si interfaces h ...[more]

PMID: 31635213

Similar Datasets

Mesporous 3C-SiC Hollow Fibers.

Project description:In the present work, for the first time, we reported the exploration of mesoporous 3C-SiC hollow fibers via single-spinneret electrospinning of polyureasilazane (PSN) and polyvinylpyrrolidone (PVP) solution followed by high-temperature pyrolysis treatment. The resultant products were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), high-resolution transmission electron microscopy (HRTEM) and N2 adsorption. The as-prepared hollow fibers with totally mesoporous walls were uniformly sized in diameter and high purity in morphology. They were composed of single-crystalline 3C-SiC nanoparticles with a surface area of 21.75 m2/g and average pore diameter of ~34 nm. The PSN concentration played a determined role on the formation of hollow fibers rather than the conventional solid counterparts, enabling their growth in a tunable manner. A possible mechanism was proposed for the formation of mesoporous SiC hollow fiber.

| S-EPMC5432512 | biostudies-literature

The paradox of inverted biomass pyramids in kelp forest fish communities.

Project description:Theory predicts that bottom-heavy biomass pyramids or 'stacks' should predominate in real-world communities if trophic-level increases with body size (mean predator-to-prey mass ratio (PPMR) more than 1). However, recent research suggests that inverted biomass pyramids (IBPs) characterize relatively pristine reef fish communities. Here, we estimated the slope of a kelp forest fish community biomass spectrum from underwater visual surveys. The observed biomass spectrum slope is strongly positive, reflecting an IBP. This is incongruous with theory because this steep positive slope would only be expected if trophic position decreased with increasing body size (consumer-to-resource mass ratio, less than 1). We then used ?(15)N signatures of fish muscle tissue to quantify the relationship between trophic position and body size and instead detected strong evidence for the opposite, with PPMR ? 1650 (50% credible interval 280-12 000). The natural history of kelp forest reef fishes suggests that this paradox could arise from energetic subsidies in the form of movement of mobile consumers across habitats, and from seasonally pulsed production inputs at small body sizes. There were four to five times more biomass at large body sizes (1-2 kg) than would be expected in a closed steady-state community providing a measure of the magnitude of subsidies.

| S-EPMC4936041 | biostudies-literature

Phenotype modulation of VSMCs on patterned substrate

Project description:Loss of contractility and acquisition of an epithelial phenotype of vascular smooth muscle cells (VSMCs) are key events in proliferative vascular pathologies such as atherosclerosis and post-angioplastic restenosis. There is no proper cell culture system allowing VSMC differentiation so that it is difficult to delineate the molecular mechanism responsible for proliferative vasculopathy. We investigated whether a micro-patterned substrate could restore the contractile phenotype of VSMCs in vitro. To induce and maintain the differentiated VSMC phenotype in vitro, we introduced a micro-patterned groove substrate to modulate the morphology and function of VSMCs.

2013-11-14 | E-MTAB-1888 | biostudies-arrayexpress

Kinetic surface roughening and wafer bow control in heteroepitaxial growth of 3C-SiC on Si(111) substrates.

Project description:A thin, chemically inert 3C-SiC layer between GaN and Si helps not only to avoid the "melt-back" effect, but also to inhibit the crack generation in the grown GaN layers. The quality of GaN layer is heavily dependent on the unique properties of the available 3C-SiC/Si templates. In this paper, the parameters influencing the roughness, crystalline quality, and wafer bow are investigated and engineered to obtain high quality, low roughness 3C-SiC/Si templates suitable for subsequent GaN growth and device processing. Kinetic surface roughening and SiC growth mechanisms, which depend on both deposition temperature and off-cut angle, are reported for heteroepitaxial growth of 3C-SiC on Si substrates. The narrower terrace width on 4° off-axis Si enhances the step-flow growth at 1200 °C, with the roughness of 3C-SiC remaining constant with increasing thickness, corresponding to a scaling exponent of zero. Crack-free 3C-SiC grown on 150-mm Si substrate with a wafer bow of less than 20 μm was achieved. Both concave and convex wafer bow can be obtained by in situ tuning of the deposited SiC layer thicknesses. The 3C-SiC grown on off-axis Si, compared to that grown on on-axis Si, has lower surface roughness, better crystallinity, and smaller bow magnitude.

| S-EPMC4614071 | biostudies-other

Impact of Nitrogen on the Selective Closure of Stacking Faults in 3C-SiC.

Project description:Despite the promising properties, the problem of cubic silicon carbide (3C-SiC) heteroepitaxy on silicon has not yet been resolved and its use in microelectronics is limited by the presence of extensive defects. In this paper, we used microphotoluminescence (μ-PL), molten KOH etching, and high-resolution scanning transmission electron microscopy (HRSTEM) to investigate the effect of nitrogen doping on the distribution of stacking faults (SFs) and assess how increasing dosages of nitrogen during chemical vapor deposition (CVD) growth inhibits the development of SFs. An innovative angle-resolved SEM observation approach of molten KOH-etched samples resulted in detailed statistics on the density of the different types of defects as a function of the growth thickness of 3C-SiC free-standing samples with varied levels of nitrogen doping. Moreover, we proceeded to shed light on defects revealed by a diamond-shaped pit. In the past, they were conventionally associated with dislocations (Ds) due to what happens in 4H-SiC, where the formation of pits is always linked with the presence of Ds. In this work, the supposed Ds were observed at high magnification (by HRSTEM), demonstrating that principally they are partial dislocations (PDs) that delimit an SF, whose development and propagation are suppressed by the presence of nitrogen. These results were compared with VESTA simulations, which allowed to simulate the 3C-SiC lattice to design two 3C-lattice domains delimited by different types of SFs. In addition, through previous experimental evidence, a preferential impact of nitrogen on the closure of 6H-like SFs was observed as compared to 4H-like SFs.

| S-EPMC9354508 | biostudies-literature

Piezoresistive effect in p-type 3C-SiC at high temperatures characterized using Joule heating.

Project description:Cubic silicon carbide is a promising material for Micro Electro Mechanical Systems (MEMS) applications in harsh environ-ments and bioapplications thanks to its large band gap, chemical inertness, excellent corrosion tolerance and capability of growth on a Si substrate. This paper reports the piezoresistive effect of p-type single crystalline 3C-SiC characterized at high temperatures, using an in situ measurement method. The experimental results show that the highly doped p-type 3C-SiC possesses a relatively stable gauge factor of approximately 25 to 28 at temperatures varying from 300 K to 573 K. The in situ method proposed in this study also demonstrated that, the combination of the piezoresistive and thermoresistive effects can increase the gauge factor of p-type 3C-SiC to approximately 20% at 573 K. The increase in gauge factor based on the combination of these phenomena could enhance the sensitivity of SiC based MEMS mechanical sensors.

| S-EPMC4923857 | biostudies-literature

Suppression of 3C-Inclusion Formation during Growth of 4H-SiC Si-Face Homoepitaxial Layers with a 1° Off-Angle.

Project description:We grew epitaxial layers on 4H-silicon carbide (SiC) Si-face substrates with a 1° off-angle. The suppression of 3C-inclusion formation during growth at a high C/Si ratio was investigated, because a growth technique with a high C/Si ratio is needed to decrease residual nitrogen incorporation. 3C inclusions were generated both at the interface between the substrate and epitaxial layer, and during epitaxial growth. 3C-SiC nucleation is proposed to trigger the formation of 3C inclusions. We suppressed 3C-inclusion formation by performing deep in situ etching and using a high C/Si ratio, which removed substrate surface damage and improved the 4H-SiC stability, respectively. The as-grown epitaxial layers had rough surfaces because of step bunching due to the deep in situ etching, but the rough surface became smooth after chemical mechanical polishing treatment. These techniques allow the growth of epitaxial layers with 1° off-angles for a wide range of doping concentrations.

| S-EPMC5456011 | biostudies-other

C0.3N0.7Ti-SiC Toughed Silicon Nitride Hybrids with Non-Oxide Additives Ti3SiC2.

Project description:In situ grown C0.3N0.7Ti and SiC, which derived from non-oxide additives Ti3SiC2, are proposed to densify silicon nitride (Si3N4) ceramics with enhanced mechanical performance via hot-press sintering. Remarkable increase of density from 79.20% to 95.48% could be achieved for Si3N4 ceramics with 5 vol.% Ti3SiC2 when sintered at 1600 °C. As expected, higher sintering temperature 1700 °C could further promote densification of Si3N4 ceramics filled with Ti3SiC2. The capillarity of decomposed Si from Ti3SiC2, and in situ reaction between nonstoichiometric TiCx and Si3N4 were believed to be responsible for densification of Si3N4 ceramics. An obvious enhancement of flexural strength and fracture toughness for Si3N4 with x vol.% Ti3SiC2 (x = 1~20) ceramics was observed. The maximum flexural strength of 795 MPa for Si3N4 composites with 5 vol.% Ti3SiC2 and maximum fracture toughness of 6.97 MPa·m1/2 for Si3N4 composites with 20 vol.% Ti3SiC2 are achieved via hot-press sintering at 1700 °C. Pull out of elongated Si3N4 grains, crack bridging, crack branching and crack deflection were demonstrated to dominate enhance fracture toughness of Si3N4 composites.

| S-EPMC7143876 | biostudies-literature

Maskless inverted pyramid texturization of silicon.

Project description:We discovered a technical solution of such outstanding importance that it can trigger new approaches in silicon wet etching processing and, in particular, photovoltaic cell manufacturing. The so called inverted pyramid arrays, outperforming conventional pyramid textures and black silicon because of their superior light-trapping and structure characteristics, can currently only be achieved using more complex techniques involving lithography, laser processing, etc. Importantly, our data demonstrate a feasibility of inverted pyramidal texturization of silicon by maskless Cu-nanoparticles assisted etching in Cu(NO3)2 / HF / H2O2 / H2O solutions and as such may have significant impacts on communities of fellow researchers and industrialists.

| S-EPMC4451685 | biostudies-other

Direct Growth of Patterned Vertical Graphene Using Thermal Stress Mismatch between Barrier Layer and Substrate.

Project description:Vertical graphene (VG) combines the excellent properties of conventional graphene with a unique vertical nanosheet structure, and has shown tremendous promise in the field of electronics and composites. However, its complex surface morphology brings great difficulties to micro-nano fabrication, especially regarding photolithography induced nanosheet collapse and remaining chemical residues. Here, we demonstrate an innovative method for directly growing patterned VG on a SiO2/Si substrate. A patterned Cr film was deposited on the substrate as a barrier layer. The VG was synthesized by PECVD on both the patterned Cr film and the exposed SiO2/Si substrate. During the cooling process, the patterned Cr film covered by VG naturally peeled off from the substrate due to the thermal stress mismatch, while the VG directly grown on the SiO2/Si substrate was remained. The temperature-dependent thermal stress distribution in each layer was analyzed using finite element simulations, and the separation mechanism of the Cr film from the substrate was explained. This method avoids the contamination and damage caused by the VG photolithography process. Our work is expected to provide a convenient and reliable solution for the manufacture of VG-based electronic devices.

| S-EPMC10097022 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data