Hardening and Strain Localisation in Helium-Ion-Implanted Tungsten.

ABSTRACT: Tungsten is the main candidate material for plasma-facing armour components in future fusion reactors. In-service, fusion neutron irradiation creates lattice defects through collision cascades. Helium, injected from plasma, aggravates damage by increasing defect retention. Both can be mimicked using helium-ion-implantation. In a recent study on 3000 appm helium-implanted tungsten (W-3000He), we hypothesized helium-induced irradiation hardening, followed by softening during deformation. The hypothesis was founded on observations of large increase in hardness, substantial pile-up and slip-step formation around nano-indents and Laue diffraction measurements of localised deformation underlying indents. Here we test this hypothesis by implementing it in a crystal plasticity finite element (CPFE) formulation, simulating nano-indentation in W-3000He at 300 K. The model considers thermally-activated dislocation glide through helium-defect obstacles, whose barrier strength is derived as a function of defect concentration and morphology. Only one fitting parameter is used for the simulated helium-implanted tungsten; defect removal rate. The simulation captures the localised large pile-up remarkably well and predicts confined fields of lattice distortions and geometrically necessary dislocation underlying indents which agree quantitatively with previous Laue measurements. Strain localisation is further confirmed through high resolution electron backscatter diffraction and transmission electron microscopy measurements on cross-section lift-outs from centre of nano-indents in W-3000He.

SUBMITTER: Das S

PROVIDER: S-EPMC6892934 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Engineering self-organising helium bubble lattices in tungsten.

Project description:The self-organisation of void and gas bubbles in solids into superlattices is an intriguing nanoscale phenomenon. Despite the discovery of these lattices 45 years ago, the atomistics behind the ordering mechanisms responsible for the formation of these nanostructures are yet to be fully elucidated. Here we report on the direct observation via transmission electron microscopy of the formation of bubble lattices under He ion bombardment. By careful control of the irradiation conditions, it has been possible to engineer the bubble size and spacing of the superlattice leading to important conclusions about the significance of vacancy supply in determining the physical characteristics of the system. Furthermore, no bubble lattice alignment was observed in the <111> directions pointing to a key driving mechanism for the formation of these ordered nanostructures being the two-dimensional diffusion of self-interstitial atoms.

| S-EPMC5552738 | biostudies-literature

In-Situ Helium Implantation and TEM Investigation of Radiation Tolerance to Helium Bubble Damage in Equiaxed Nanocrystalline Tungsten and Ultrafine Tungsten-TiC Alloy.

Project description:The use of ultrafine and nanocrystalline materials is a proposed pathway to mitigate irradiation damage in nuclear fusion components. Here, we examine the radiation tolerance of helium bubble formation in 85 nm (average grain size) nanocrystalline-equiaxed-grained tungsten and an ultrafine tungsten-TiC alloy under extreme low energy helium implantation at 1223 K via in-situ transmission electron microscope (TEM). Helium bubble damage evolution in terms of number density, size, and total volume contribution to grain matrices has been determined as a function of He+ implantation fluence. The outputs were compared to previously published results on severe plastically deformed (SPD) tungsten implanted under the same conditions. Large helium bubbles were formed on the grain boundaries and helium bubble damage evolution profiles are shown to differ among the different materials with less overall damage in the nanocrystalline tungsten. Compared to previous works, the results in this work indicate that the nanocrystalline tungsten should possess a fuzz formation threshold more than one order of magnitude higher than coarse-grained tungsten.

| S-EPMC7040824 | biostudies-literature

Extraordinary strain hardening by gradient structure.

Project description:Gradient structures have evolved over millions of years through natural selection and optimization in many biological systems such as bones and plant stems, where the structures change gradually from the surface to interior. The advantage of gradient structures is their maximization of physical and mechanical performance while minimizing material cost. Here we report that the gradient structure in engineering materials such as metals renders a unique extra strain hardening, which leads to high ductility. The grain-size gradient under uniaxial tension induces a macroscopic strain gradient and converts the applied uniaxial stress to multiaxial stresses due to the evolution of incompatible deformation along the gradient depth. Thereby the accumulation and interaction of dislocations are promoted, resulting in an extra strain hardening and an obvious strain hardening rate up-turn. Such extraordinary strain hardening, which is inherent to gradient structures and does not exist in homogeneous materials, provides a hitherto unknown strategy to develop strong and ductile materials by architecting heterogeneous nanostructures.

| S-EPMC4034219 | biostudies-literature

Rapid and damage-free outgassing of implanted helium from amorphous silicon oxycarbide.

Project description:Damage caused by implanted helium (He) is a major concern for material performance in future nuclear reactors. We use a combination of experiments and modeling to demonstrate that amorphous silicon oxycarbide (SiOC) is immune to He-induced damage. By contrast with other solids, where implanted He becomes immobilized in nanometer-scale precipitates, He in SiOC remains in solution and outgasses from the material via atomic-scale diffusion without damaging its free surfaces. Furthermore, the behavior of He in SiOC is not sensitive to the exact concentration of carbon and hydrogen in this material, indicating that the composition of SiOC may be tuned to optimize other properties without compromising resistance to implanted He.

| S-EPMC5864747 | biostudies-literature

The effects of helium, strontium, and silver triple ions implanted into SiC.

Project description:The effects of helium (He), silver (Ag) and strontium (Sr) ions triple implanted into polycrystalline silicon carbide (SiC) were investigated. Ag ions of 360 keV were first implanted into polycrystalline SiC to a fluence of 2 × 1016 cm-2 at 600 °C, followed by implantation of Sr ions of 280 keV to a fluence of 2 × 1016 cm-2 also at 600 °C (Ag + Sr-SiC). Some of Ag + Sr-SiC samples were then implanted with 17 keV He ions to a fluence of 1 × 10 17 cm-2 at 350 °C (Ag + Sr + He-SiC). Some of the dual (Ag + Sr-SiC) and triple (Ag + Sr + He-SiC) implanted samples were annealed at 1000 °C for 5 h. Both dual and triple implantation resulted in the accumulation of defects without amorphization of SiC structure. Moreover, triple implantation also resulted in formation of elongated He nano-bubbles and cavities in the damaged SiC accompanied by the appearance of blisters and craters on the surface. Healing of some structural defects was observed after annealing at 1000 °C in both dual and triple implanted samples. Implantation of Sr caused pre-implanted Ag to form precipitates indicating some limited migration while implantation of He caused some migration of both Ag and Sr. The migration of Ag was accompanied by formation of bigger precipitates trapped in He-cavities. Annealing the triple implanted caused the migration of both Ag and Sr governed by trapping of both implanted species by cavities due to some exo-diffusion of He. No migration was observed in the dual implanted samples annealed at 1000 °C. Hence, He bubbles assisted migration of implants and He cavities trap the implanted species.

| S-EPMC10585298 | biostudies-literature

Strain Hardening in Graphene Foams under Shear.

Project description:Strain hardening is an important issue for the design and application of materials. The strain hardening of graphene foams has been widely observed but poorly understood. Here, by adopting the coarse-grained molecular dynamics method, we systematically investigated the microscopic mechanism and influencing factors of strain hardening and related mechanical properties of graphene foams under shear loading. We found that the strain hardening is induced by cumulative nonlocalized bond-breakings and rearrangements of microstructures. Furthermore, it can be effectively tuned by the number of graphene layers and cross-link densities, i.e., the strain hardening would emerge at a smaller shear strain for the graphene foams with thicker sheets and/or more cross-links. In addition, the shear stiffness G of graphene foams increases linearly with the cross-link density and exponentially with the number of graphene layers n by G ∼ n 1.95. These findings not only improve our understanding of the promising bulk materials but also pave the way for optimizing structural design in wide applications based on their mechanical properties.

| S-EPMC8427771 | biostudies-literature

Mechanical Behavior of Printed Strain Hardening Cementitious Composites.

Project description:Extrusion based additive manufacturing of cementitious materials has demonstrated strong potential to become widely used in the construction industry. However, the use of this technique in practice is conditioned by a feasible solution to implement reinforcement in such automated process. One of the most successful ductile materials in civil engineering, strain hardening cementitious composites (SHCC) have a high potential to be employed for three-dimensional printing. The match between the tailored brittle matrix and ductility of the fibres enables these composites to develop multiple cracks when loaded under tension. Using previously developed mixtures, this study investigates the physical and mechanical performance of printed SHCC. The anisotropic behavior of the materials is explored by means of mechanical tests in several directions and micro computed tomography tests. The results demonstrated a composite showing strain hardening behavior in two directions explained by the fibre orientation found in the printed elements. Moreover, the printing technique used also has guaranteed an enhanced bond in between the printed layers.

| S-EPMC7287622 | biostudies-literature

Microscopic Origin of Strain Hardening in Methane Hydrate.

Project description:It has been reported for a long time that methane hydrate presents strain hardening, whereas the strength of normal ice weakens with increasing strain after an ultimate strength. However, the microscopic origin of these differences is not known. Here, we investigated the mechanical characteristics of methane hydrate and normal ice by compressive deformation test using molecular dynamics simulations. It is shown that methane hydrate exhibits strain hardening only if the hydrate is confined to a certain finite cross-sectional area that is normal to the compression direction. For normal ice, it does not present strain hardening under the same conditions. We show that hydrate guest methane molecules exhibit no long-distance diffusion when confined to a finite-size area. They appear to serve as non-deformable units that prevent hydrate structure failure, and thus are responsible for the strain-hardening phenomenon.

| S-EPMC4806379 | biostudies-literature

Effects of transition metal carbide dispersoids on helium bubble formation in dispersion-strengthened tungsten.

Project description:The formation of helium bubbles and subsequent property degradation poses a significant challenge to tungsten as a plasma-facing material in future long-pulse plasma-burning fusion reactors. In this study, we investigated helium bubble formation in dispersion-strengthened tungsten doped with transition metal carbides, including TaC, ZrC, and TiC. Of the three dispersoids, TaC exhibited the highest resistance to helium bubble formation, possibly due to the low vacancy mobility in the Group VB metal carbide and oxide phases. Under identical irradiation conditions, large helium bubbles formed at grain boundaries in tungsten, while no bubbles were observed at the interfaces between the carbide dispersoid and tungsten matrix. Moreover, our results showed the interfaces could suppress helium bubble formation in the nearby tungsten matrix, suggesting that the interfaces are more effective in trapping helium as tiny clusters. Our research provided new insights into optimizing the microstructure of dispersion-strengthened tungsten alloys to enhance their performance.

| S-EPMC10432386 | biostudies-literature

Imaging of carbon nanomembranes with helium ion microscopy.

Project description:Carbon nanomembranes (CNMs) prepared from aromatic self-assembled monolayers constitute a recently developed class of 2D materials. They are made by a combination of self-assembly, radiation-induced cross-linking and the detachment of the cross-linked SAM from its substrate. CNMs can be deposited on arbitrary substrates, including holey and perforated ones, as well as on metallic (transmission electron microscopy) grids. Therewith, freestanding membranes with a thickness of 1 nm and macroscopic lateral dimensions can be prepared. Although free-standing CNMs cannot be imaged by light microscopy, charged particle techniques can visualize them. However, CNMs are electrically insulating, which makes them sensitive to charging. We demonstrate that the helium ion microscope (HIM) is a good candidate for imaging freestanding CNMs due to its efficient charge compensation tool. Scanning with a beam of helium ions while recording the emitted secondary electrons generates the HIM images. The advantages of HIM are high resolution, high surface sensitivity and large depth of field. The effects of sample charging, imaging of multilayer CNMs as well as imaging artefacts are discussed.

| S-EPMC4578422 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data