Preparation of Silica Aerogel/Resin Composites and Their Application in Dental Restorative Materials
Ontology highlight
ABSTRACT:
SUBMITTER: Cheng J
PROVIDER: S-EPMC9323775 | biostudies-literature |
REPOSITORIES: biostudies-literature
Similar Datasets
Project description:Resin-based composites are widely used as dental restorative materials due to their excellent properties. They must have high modulus, high hardness, and be chemically inert while minimizing moisture uptake. To fulfill these higher standard prerequisites and properties, continuous improvements in each of their components are required. This study develops novel composites with multiple biofunctions. Light-cured Bis-GMA/TEGDMA dental resin (RK)/layered double hydroxide intercalated with fluoride ions (LDH-F)/calcium bentonite (Bt) hybrid composites were prepared. The loading ratio of LDH-F to Bt was varied, ranging from 2.5/2.5 to 10/10 parts per hundred RK and structural, mechanical, and biological properties were studied. The incorporation of even small mass fractions (e.g., 2.5 wt % of LDH-F and 2.5 wt % of Bt) in RK dental resin significantly improved the mechanical properties of the pristine resin. The synthetized materials showed antibacterial and antibiofilm effects against three bacterial strains isolated from healthy volunteers' saliva (Streptococcus spp., Bacteroides fragilis, and Staphylococcus epidermidis) without affecting its ability to induce dental pulp stem cells differentiation into odontoblast-like cells. The capability to balance between the antibiofilm activity and dental pulp stem cells differentiation in addition with improved mechanical properties make these materials a promising strategy in preventive and restorative dentistry.
| S-EPMC7077377 | biostudies-literature
Project description:A methyl methacrylate (MMA) -based resin cement is one of the popular luting agents to bond a dental restorative material in dental treatments. Bond strength of the MMA-based resin cement with adhesive primer to each restorative material is important for clinical success in prosthodontic treatments without debonding or fracture failures of the restoration such as a dental crown and post. However, open data on the bonding properties of combined use of the MMA-based resin cement and appropriate primers is limited. This article provides data on the bond strength and fracture mode of the 4-META/MMA-TBB resin cement (MMA-based resin cement) to the restorative materials (silver alloy, gold alloy, feldspathic porcelain, and zirconia) with four types of primer. Each restorative material was applied with the adhesive primer and bonded with the MMA-based resin cement. The cement-bonded samples were subjected to a thermocycling in which the materials were immersed alternately in water baths at 5 °C and 55 °C for 10,000 cycles. The bond strength between the resin cement and each restorative material was measured by means of a conventional tensile bond strength test. The fracture modes of the examined samples were observed and determined. The measured tensile bond strengths were statistically analysed using one-way analysis of variance (ANOVA), followed by Tukey's multiple comparison test.
| S-EPMC7586068 | biostudies-literature
Project description:Silica aerogel microspheres based on alkali silica sol were synthesized using the emulsion method. The experimental results revealed that the silica aerogel microspheres (4-20 µm in diameter) were mesoporous solids with an average pore diameter ranging from 6 to 35 nm. The tapping densities and specific surface areas of the aerogel microspheres are in the range of 0.112-0.287 g/cm³ and 207.5-660.6 m²/g, respectively. The diameter of the silica aerogel microspheres could be tailored by varying the processing conditions including agitation rate, water/oil ratio, mass ratio of Span 80: Tween 80, and emulsifier concentration. The effects of these parameters on the morphology and textural properties of the synthesized silica aerogel microspheres were systematically investigated. Such silica aerogel microspheres can be used to prepare large-scale silica aerogels at an ambient pressure for applications in separation and high efficiency catalysis, which requires features of high porosity and easy fill and recovery.
| S-EPMC5506966 | biostudies-literature
Project description:Herein, the microwave-assisted wet precipitation method was used to obtain materials consisting of mesoporous silica (SBA-15) and calcium orthophosphates (CaP). Composites were prepared through immersion of mesoporous silica in different calcification coating solutions and then exposed to microwave radiation. The composites were characterized in terms of molecular structure, crystallinity, morphology, chemical composition, and mineralization potential by Fourier-transform infrared spectroscopy (FTIR), powder X-ray diffraction (XRD), and scanning electron microscopy equipped with energy-dispersive X-ray spectroscopy (SEM-EDX). The application of microwave irradiation resulted in the formation of different types of calcium orthophosphates such as calcium deficient hydroxyapatite (CDHA), octacalcium phosphate (OCP), and amorphous calcium phosphate (ACP) on the SBA-15 surface, depending on the type of coating solution. The composites for which the progressive formation of hydroxyapatite during incubation in simulated body fluid was observed were further used in the production of final pharmaceutical forms: membranes, granules, and pellets. All of the obtained pharmaceutical forms preserved mineralization properties.
| S-EPMC7796352 | biostudies-literature
Project description:A great number of different types of materials have been used in dentistry as intermediate restoratives. Among them, new resin-based bases have been released in the dental market. The present study focuses on the identification of the organic eluates released from such materials and the study of their surface microstructure in combination with their corresponding elemental composition. For this purpose, the following materials were used:ACTIVA™BioACTIVE-BASE/LINER™, Ketac™Bond Glass Ionomer, SDR™ and Vitrebond™Light Cure Glass Ionomer Liner/Base. Methanolic leachates derived from polymerized materials were analyzed by means of gas chromatography-mass spectrometry (GC-MS). Scanning electron microscopy(SEM) was used for the surface monitoring of suitably prepared specimens. The GC-MS analysis revealed the elution of twenty different substances from the three resin-based materials, while none was eluted from the glass ionomer base. The SEM analysis for Vitrebond™ presented small pits, the one for Ketac™Bond presented elongated cracks, while no voids were present for ACTIVA™BioACTIVE-BASE/LINER™ and SDR™. Moreover, the resin matrix of some dental materials may inhibit elements' accumulation on the surface layers. Particularly, the detected organic eluents may be related to potential toxic effects.
| S-EPMC7180687 | biostudies-literature
Project description:Step-growth thiol-Michael photopolymerizable resins, constituting an alternative chemistry to the current methacrylate-based chain-growth polymerizations, were developed and evaluated for use as dental restorative materials. The beneficial features inherent to anion-mediated thiol-Michael polymerizations were explored, such as rapid photocuring, low stress generation, ester content tunability, and improved mechanical performance in a moist environment. An ester-free tetrafunctional thiol and a ultraviolet-sensitive photobase generator were implemented to facilitate thiol-Michael photopolymerization. Thiol-Michael resins of varied ester content were fabricated under suitable light activation. Polymerization kinetics and shrinkage stress were determined with Fourier-transform infrared spectroscopy coupled with tensometery measurements. Thermomechanical properties of new materials were evaluated by dynamic mechanical analysis and in 3-point bending stress-strain experiments. Photopolymerization kinetics, polymerization shrinkage stress, glass transition temperature, flexural modulus, flexural toughness, and water sorption/solubility were compared between different thiol-Michael systems and the BisGMA/TEGDMA control. Furthermore, the mechanical performance of 2 thiol-Michael composites and a control composite were compared before and after extensive conditioning in water. All photobase-catalyzed thiol-Michael polymerization matrices achieved >90% conversion with a dramatic reduction in shrinkage stress as compared with the unfilled dimethacrylate control. One prototype of ester-free thiol-Michael formulations had significantly better water uptake properties than the BisGMA/TEGDMA control system. Although exhibiting relatively lower Young's modulus and glass transition temperatures, highly uniform thiol-Michael materials achieved much higher toughness than the BisGMA/TEGDMA control. Moreover, low-ester thiol-Michael composite systems show stable mechanical performance even after extensive water treatment. Although further resin/curing methodology optimization is required, the photopolymerized thiol-Michael prototype resins can now be recognized as promising candidates for implementation in composite dental restorative materials.
| S-EPMC5958372 | biostudies-literature
Project description:A multi-functional modifier, which could improve the mechanical and thermal performance simultaneously, is significant in composites production. Herein, inspired by the chemistry of mussel, an interfacial modifier named FPD was designed and synthesized through one simple step, which was attached by three functional groups (including catechol, N-H bond, and DOPO). Due to the innate properties of each functional group, FPD played multiple roles: adhere to the ramie fibers from catechol and cure with the epoxy resin from -NH-, an antiflaming property from DOPO, and the compatibilizer between ramie fibers and epoxy resin was also improved by changing the polarity of ramie fiber. All of the above functions can be proved by means of water contact angle (WCA), atomic force microscope (AFM), and scanning electron microscopy (SEM), etc. After solidification, the ramie fiber/epoxy composites demonstrated superior performances in terms of good mechanical properties and excellent flame retardant property. With the addition of 30 wt.% FPD, the tensile strength and modulus of the ramie/epoxy composite showed an improvement of 37.1% and 60.9%, and flexural strength and modulus of the composite were improved by 8.9% and 19.3% comparing with no addition composite. Moreover, the composite could achieve the goal for V-0 rating in the UL-94 test and LOI value was 34.6% when the addition of FPD reached 30 wt.%. This work provided us with an efficient method for fabricating nature fiber/epoxy composites with good properties.
| S-EPMC10537050 | biostudies-literature
Project description:Silica aerogels are a class of materials that can be tailored in terms of their final properties and surface chemistry. They can be synthesized with specific features to be used as adsorbents, resulting in improved performance for wastewater pollutants' removal. The purpose of this research was to investigate the effect of amino functionalization and the addition of carbon nanostructures to silica aerogels made from methyltrimethoxysilane (MTMS) on their removal capacities for various contaminants in aqueous solutions. The MTMS-based aerogels successfully removed various organic compounds and drugs, achieving adsorption capacities of 170 mg⋅g-1 for toluene and 200 mg⋅g-1 for xylene. For initial concentrations up to 50 mg⋅L-1, removals greater than 71% were obtained for amoxicillin, and superior to 96% for naproxen. The addition of a co-precursor containing amine groups and/or carbon nanomaterials was proven to be a valuable tool in the development of new adsorbents by altering the aerogels' properties and enhancing their adsorption capacities. Therefore, this work demonstrates the potential of these materials as an alternative to industrial sorbents due to their high and fast removal efficiency, less than 60 min for the organic compounds, towards different types of pollutants.
| S-EPMC10059775 | biostudies-literature
Project description:This article contains data related to the research article titled "Compressive strength of glass ionomer and composite resin. In vitro study" (Blanco et al., 2017). The presented data gives information about the compressive strength of two restorative materials (Tetric N-Ceram® resin and Vitremer TM® resin) in class I cavities in birradicular premolars. The dental organs were subjected to a compressive vertical force at different deeps of cavities preparation until obtain fracture of the restorative material. Compression Resistance values of 380.5 are obtained; 387; 399.2; 419.9; 422.4; 428; 432.1 and 429 N for Tetric N-Ceram® and 349.4 resin; 350.2; 356.1; 369; 390.7; 416.2; 424 and 426.8 for the Vitremer TM® ionomer. There are significant statistical differences (p < 0.05) between restorative materials. The resin Tetric N-Ceram®, showed higher resistance to compression than Vitremer TM® resin in all depths.
| S-EPMC6660634 | biostudies-literature
Project description:A long-time drawback of dental composites is that they accumulate more biofilms and plaques than amalgam and glass ionomer restorative materials. It would be highly desirable to develop a new composite with reduced biofilm growth, while avoiding the non-esthetics of amalgam and low strength of glass ionomer. The objectives of this study were to: (1) develop a protein-repellent composite with reduced biofilms matching amalgam and glass ionomer for the first time; and (2) investigate their protein adsorption, biofilms, and mechanical properties. Five materials were tested: A new composite containing 3% of protein-repellent 2-methacryloyloxyethyl phosphorylcholine (MPC); the composite with 0% MPC as control; commercial composite control; dental amalgam; resin-modified glass ionomer (RMGI). A dental plaque microcosm biofilm model with human saliva as inoculum was used to investigate metabolic activity, colony-forming units (CFU), and lactic acid production. Composite with 3% MPC had flexural strength similar to those with 0% MPC and commercial composite control (p > 0.1), and much greater than RMGI (p < 0.05). Composite with 3% MPC had protein adsorption that was only 1/10 that of control composites (p < 0.05). Composite with 3% MPC had biofilm CFU and lactic acid much lower than control composites (p < 0.05). Biofilm growth, metabolic activity and lactic acid on the new composite with 3% MPC were reduced to the low level of amalgam and RMGI (p > 0.1). In conclusion, a new protein-repellent dental resin composite reduced oral biofilm growth and acid production to the low levels of non-esthetic amalgam and RMGI for the first time. The long-held conclusion that dental composites accumulate more biofilms than amalgam and glass ionomer is no longer true. The novel composite is promising to finally overcome the major biofilm-accumulation drawback of dental composites in order to reduce biofilm acids and secondary caries.
| S-EPMC5457238 | biostudies-other