Preparation, Characteristics, and Application of Bifunctional TiO2 Sheets.

ABSTRACT: TiO2 is a high-reflectance material for preparing sheets during dry reagent chemical tests in detail. In this study, bifunctional TiO2 sheets with diffusive and reflective properties were prepared using TiO2 microspheres (particle size 2-3 µm) and cellulose acetate (CA). Factors such as the CA dosage, water content, mixing time, and the choice of surfactant were investigated. The structure and properties of the bifunctional TiO2 sheets were characterized by thermogravimetry and differential thermal analysis (TG-DAT), scanning electron microscopy (SEM), dynamic contact angle test and reflectance spectroscopy. By studying the above experimental results, it was concluded that the most optimal preparation conditions for preparing the bi-functional TiO2 sheets under natural drying conditions were as follows: the mass ratio of CA to TiO2 microspheres was 0.05:1; Triton-100 was used to improve the diffusion performance of the bifunctional sheets, after mixing for 5 h and coating. The light reflectivity of the bifunctional TiO2 sheets in the 420 to 800 nm range was higher than 90%. Serum diffused in the bifunctional TiO2 sheets reacted in the reagent sheets and formed uniform colorful spots. Considering the repeatability of spot proportion and light reflectivity, the sheet offered a uniform serum diffusion and good repeatability. So, the bifunctional TiO2 sheets are nominated as a promising material for dry chemical diagnostic reagents.

SUBMITTER: Guo X

PROVIDER: S-EPMC7178338 | biostudies-literature | 2020 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Preparation, Characteristics, and Application of Bifunctional TiO2 Sheets.

Guo Xiaoyan X Liu Jiaqi J Liu Lixia L Yang Suohe S He Guangxiang G Jin Haibo H

Materials (Basel, Switzerland) 20200401 7

TiO2 is a high-reflectance material for preparing sheets during dry reagent chemical tests in detail. In this study, bifunctional TiO2 sheets with diffusive and reflective properties were prepared using TiO2 microspheres (particle size 2-3 µm) and cellulose acetate (CA). Factors such as the CA dosage, water content, mixing time, and the choice of surfactant were investigated. The structure and properties of the bifunctional TiO2 sheets were characteriz ...[more]

PMID: 32244682

Similar Datasets

Project description:Introduction:Regenerative therapy using chondrocyte sheets is effective for osteoarthritis. The clinical application of chondrocyte sheet therapy is expected to be further advanced by the use of a feasible cryopreservation technique. Previously, we developed a chondrocyte sheet vitrification method; however, it was too complex to be used for routine clinical application. Here, we aimed to develop a prototype method for vitrifying chondrocyte sheets for clinical practice. Methods:We developed a "circulating vitrification bag" as a container to process cell sheets for vitrification in an efficient and sanitary fashion. Moreover, we invented the "vitrification storage box", which is useful for the vitrification of cell sheets, long-term preservation, and transportation. These devices were used to vitrify rabbit chondrocyte sheets, which were then assessed for their structural characteristics and the viability of the component cells after rewarming. Results:In all cell sheet samples (n = 7) vitrified by the circulating vitrification bag method, the integrity of the sheet structure was maintained, and the cell survival rate was similar to that of non-vitrified samples (91.0 ± 2.9% vs. 90.0 ± 3.0%). Proteoglycan and type II collagen, which are major components of cartilage, were densely and evenly distributed throughout the chondrocyte sheet subjected to vitrification similarly to that observed in the non-vitrified sheet. After long-term storage using the vitrification storage box, the cell sheets maintained normal structure and cell viability (survival rate: 81.2 ± 1.0% vs. 84.3 ± 1.8%) compared to the non-vitrified sheet. Conclusion:Our results indicate that the circulating vitrification bag method is an effective approach for realizing the clinical application of vitrified chondrocyte sheets. The vitrification storage box is also useful for the long-term preservation of vitrified cell sheets, further enhancing the feasibility of the clinical application of cryopreserved chondrocyte sheets.

Dataset Information

Preparation, Characteristics, and Application of Bifunctional TiO2 Sheets.

Publications

Preparation, Characteristics, and Application of Bifunctional TiO<sub>2</sub> Sheets.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets